中文摘要: 本文利用一步溶剂热法制备CulnS2可见光光催化剂,运用XRD、SEM、BET等对材料进行表征分析。探究了前驱液Cu/ln摩尔比、温度、时间和捕获剂种类对CulnS2在可见光下光催化还原溶液中U(VI)的性能。研究结果表明：当Cu:ln=1:1,样品制备温度为200℃,制备时间为12h的条件下,所制备的CulnS2材料光催化还原U(VI)活性最佳,光催化还原过程的主要活性物质是O2-和e-。
中文关键词: CulnS2材料，可见光，光催化还原，U(Ⅵ)，因素
Abstract:Vsible light photocatalyst CulnS2 material was prepared by one-step solvothermal method. the composite photocatalyst was Characterized and analyzed the material with XRD, SEM, BET. TheSeffectsSofSCu/ln molar ratio, temperature, time and trapping agent types of precursor liquid were explored on the performance of CulnS2 photocatalytic reduction of U(VI) in solution under visible light. The results showed that Cu:ln=1:1, the sample preparation temperature is 200℃, and the preparation time is 12h, the prepared CulnS2 material has the best photocatalytic reduction activity for U(VI), and the main photocatalytic reduction process is The active substances are O2- and e-.
文章编号：YSJSGC20200668 中图分类号：X703.5 文献标志码：
基金项目:]：国家自然科学基金41761090;江西省自然科学基金20171ACB20021；东华理工大学研究生创新专项资金项目DHYC-202022
| 作者 | 单位 | |
| 何登武 | 东华理工大学 核资源与环境国家重点实验室 | HDW199537@163.com |
| 李冠超 | 广东省核工业地质局辐射环境监测中心 | |
| 李小燕* | 东华理工大学 核资源与环境国家重点实验室 | 372040739@qq.com |
| 王杨 | 东华理工大学 核资源与环境国家重点实验室 | |
| 王昱莹 | 东华理工大学 核资源与环境国家重点实验室 | |
| 付晓辉 | 东华理工大学 核资源与环境国家重点实验室 |
引用文本：
何登武,李冠超,李小燕,王杨,王昱莹,付晓辉.CulnS2光催化材料制备及光催化还原溶液中U(VI)的性能[J].有色金属工程,2021,(7):.
何登武,李冠超,李小燕,王杨,王昱莹,付晓辉.CulnS2光催化材料制备及光催化还原溶液中U(VI)的性能[J].有色金属工程,2021,(7):.
关注微信公众号