| Ti和/或Nb对高温合金25Cr37Ni0.6Nb组织和力学性能的影响 |
| |
| 引用本文： | 陈道凤,郑宏光,马天军,单爱党. Ti和/或Nb对高温合金25Cr37Ni0.6Nb组织和力学性能的影响[J]. 特殊钢, 2014, 35(2): 47-50 |
| |
| 作者姓名： | 陈道凤 郑宏光 马天军 单爱党 |
| |
| 作者单位： | 1. 上海交通大学材料科学与工程学院，上海200240；2. 宝山钢铁股份有限公司研究院，上海201900； |
| |
| 摘 要： | 研究了150 kg真空感应炉冶炼并轧成30 mm板的0.05C-25Cr-37Ni-0.6Nb(0.6Nb),0.05C-25Cr-37Ni-0.6Nb-0.6Ti(0.6Nb-0.6Ti)和0.05C-25Cr-37Ni-1.8Nb(1.8Nb)3组合金1160~1220℃ 1 h空冷固溶处理的组织和性能。结果表明,与0.6Nb合金相比加Ti的(0.6Nb-0.6Ti)合金的晶粒明显粗化,析出相主要为微米级Ti(CN),室温强度降低,760℃蠕变性能降低;增加Nb含量的1.8Nb合金的晶粒细化,析出相主要为纳米级Nb(CN),室温强度和蠕变性能没有明显变化。
|
| 关 键 词： | 25Cr37Ni0.6Nb高温合金 Ti Nb 固溶处理 析出相 晶粒粗化 |
| 收稿时间： | 2013-09-17 |
Effect of Ti and/or Nb on Structure and Mechanical Properties of High Temperature Alloy 25Cr37Ni0.6Nb |
| |
| Chen Daofeng,Zheng Hongguang,Ma Tianjun,Shan Aidang. Effect of Ti and/or Nb on Structure and Mechanical Properties of High Temperature Alloy 25Cr37Ni0.6Nb[J]. Special Steel, 2014, 35(2): 47-50 |
| |
| Authors: | Chen Daofeng Zheng Hongguang Ma Tianjun Shan Aidang |
| |
| Affiliation: | 1. School of Material Science and Engineering, Shanghai Jiaotong University, Shanghai 200240 ；2. Research Institute, Baoshan Iron and Steel Co Ltd, Shanghai 201900 ; |
| |
| Abstract: | The structure and properties of three alloys 0.05C-25Cr-37Ni-0.6Nb(0.6Nb), 0.05C-25Cr-37Ni-0.6Nb-0.6Ti(0.6Nb-0.6Ti) and 0.05C-25Cr-37Ni-l.8Nb( 1.8Nb) melted by 150 kg vacuum induction furnace, rolled to 30 mm plate and solid-solution-treated at 1160-1220 ℃ for 1 h, air cooling have been studied. Results show that as compared with 0.6Nb alloy, the grains in 0.6Nb-0.6Ti alloy added Ti obviously coarsen, the main precipitates are micrometer-scale Ti( CN), the ambient strength and creep behavior at 760 ℃ of 0.6Nb-0.6Ti alloy decrease ； the 1.8Nb alloy got a raise in Nb content the grains fine, the main precipitates are nanometer-scale Nb(CN) , the ambient strength and creep behavior are not obviously changes. |
| |
| Keywords: | High Temperature Alloy 25Cr37Ni0.6Nb Ti Nb Solid-Solution Treatment Precipitates Grain Coarsening |