| 有机磷氮系-蒙脱土/LDPE纳米复合材料的制备及阻燃性能 |
| |
| 引用本文： | 黄国波,高建荣,贾建洪,盛卫坚,王旭. 有机磷氮系-蒙脱土/LDPE纳米复合材料的制备及阻燃性能[J]. 复合材料学报, 2010, 27(6): 45-52 |
| |
| 作者姓名： | 黄国波 高建荣 贾建洪 盛卫坚 王旭 |
| |
| 作者单位： | 浙江工业大学绿色化学合成技术国家重点实验室培育基地,杭州,310014;台州学院医药化工学院,临海,317000;浙江工业大学绿色化学合成技术国家重点实验室培育基地,杭州,310014 |
| |
| 基金项目： | 浙江省重中之重学科开放基金(20090519) |
| |
| 摘 要： | 以三氯氧磷和新戊二醇等为原料, 合成了一种新型磷氮型季铵盐(PAHAC), 通过红外光谱(FTIR)、 核磁共振氢谱(1H-NMR)和高分辨质谱(HRMS)表征化合物结构。利用PAHAC与钠基蒙脱土(Na-MMT)离子交换反应制备有机磷氮系蒙脱土阻燃剂(PAHACMMT)。FTIR和X射线衍射(XRD)研究表明: PAHAC通过离子交换对蒙脱土进行了有机化改性, 经20%质量分数的PAHAC改性后的MMT(20%PAHAC-MMT)层间距增至1.87nm, 20%PAHACMMT的热分解温度在310℃以上。透射电镜(TEM)分析结果表明, 20%PAHACMMT经LDPE熔融插层, 形成了插层剥离型纳米复合材料。锥形量热测试结果表明有机磷氮系蒙脱土/LDPE纳米复合材料具有良好的阻燃性能, 其中20%PAHACMMT(7%)/LDPE的热释放速率峰值(PHRR)比LDPE降低了21%, 热释放总量(THR)下降了9.5%。炭层的扫描电镜(SEM)分析结果表明, 20%PAHACMMT/LDPE燃烧后能形成致密的炭层, 起到良好的阻燃作用。
|
| 关 键 词： | 磷氮型 蒙脱土 阻燃剂 纳米复合材料 |
| 收稿时间： | 2009-11-19 |
| 修稿时间： | 2010-02-10 |
Preparation and flammability properties of phosphorus-nitrogen-montmorillonite/LDPE nanocomposites |
| |
| HUANG Guobo,GAO Jianrong,JIA Jianhong,SHENG Weijian,WANG Xu. Preparation and flammability properties of phosphorus-nitrogen-montmorillonite/LDPE nanocomposites[J]. Acta Materiae Compositae Sinica, 2010, 27(6): 45-52 |
| |
| Authors: | HUANG Guobo GAO Jianrong JIA Jianhong SHENG Weijian WANG Xu |
| |
| Affiliation: | (1. State Key Laboratory Breeding Base of Green Chemistry Synthesis Technology, Zhejiang University of Technology, Hangzhou 310014, China|2. School of Pharmaceutical and Chemical Engineering, Taizhou University, Linhai 317000, China) |
| |
| Abstract: | A novel phosphorus-nitrogen quaternary ammonium salts (PAHAC) was synthesized with phoshorus oxychloride and neopentyl glycol as main raw materials. PAHAC was characterized by FTIR, 1H-NMR and HRMS. Montmorillonite (MMT) modified with PAHAC (PAHACMMT) was prepared by ion-exchanging of Na+-montmorillonite (Na-MMT) and PAHAC. FTIR and XRD indicate that PAHAC is intercalated with Na-MMT and the layer spacing and the decomposition temperature of MMT modified with 20wt% PAHAC (20%PAHACMMT) is 1.87nm and 310℃, respectively. The results of TEM show that the intercalated-exploitated nanocomposite of 20%PAHACMMT/LDPE is formed by melting intercalation blending LDPE with 20%PAHACMMT. The flame retardancy of phosphorus-nitrogenmontmorillonite/LDPE nanocomposites was investigated by cone calorimeter test. The results show that the flame retardancy properties of phosphorus-nitrogen-montmorillonite/LDPE nanocomposites are good. In comparison with LDPE, the peak heat release rates (PHRR) and the total heat release (THR) of 20%PAHACMMT(7%)/LDPE reduce by 21% and 9.5%, respectively. The results of SEM show that the compact and dense char is formed for 20%PAHACMMT/LDPE nanocomposite after combustion, which can inhibit burning effectively. |
| |
| Keywords: | phosphorus-nitrogen montmorillonite flame retardant nanocomposite |