| SP700/TC4钛合金蜂窝夹层结构钎焊工艺分析 |
| |
| 引用本文： | 苏頔瑶,静永娟,岳喜山,陈 林.SP700/TC4钛合金蜂窝夹层结构钎焊工艺分析[J].焊接学报,2018,39(4):119-123. |
| |
| 作者姓名： | 苏頔瑶 静永娟 岳喜山 陈 林 |
| |
| 作者单位： | 北京航空制造工程研究所航空焊接与连接技术航空科技重点实验室;中国人民解放军驻成飞公司军事代表室 |
| |
| 摘 要： | 采用非晶态Ti-Zr-Cu-Ni箔带钎料对SP700/TC4钛合金蜂窝结构进行钎焊工艺研究，分析了钎焊温度和保温时间对钎焊接头组织和力学性能的影响. 结果表明，当钎焊温度在875～890 ℃之间变化时，随温度升高，钎焊接头中元素扩散更为充分，接头拉脱强度持续增长；在890 ℃下保温2～4 h不同时长进行钎焊，接头的拉脱强度先逐渐增加，在保温时间为3.5 h时达到最大值，随后逐渐降低. 获得SP700/TC4钛合金蜂窝结构的较优钎焊工艺为890 ℃/3.5 h，该工艺下钎焊接头的室温拉脱强度、三点弯曲强度、平面压缩强度、L及W方向抗剪强度分别达到14.64，224.05，11.21，4.43及3.76 MPa，破坏部位均为TC4蜂窝芯.
|
| 关 键 词： | SP700钛合金 蜂窝夹层结构 钎焊 |
| 收稿时间： | 2016/11/9 0:00:00 |
Analysis on SP700/TC4 titanium alloy honeycomb sandwich brazing |
| |
| SU Diyao,JING Yongjuan,YUE Xishan,CHEN Lin.Analysis on SP700/TC4 titanium alloy honeycomb sandwich brazing[J].Transactions of The China Welding Institution,2018,39(4):119-123. |
| |
| Authors: | SU Diyao JING Yongjuan YUE Xishan CHEN Lin |
| |
| Abstract: | SP700/TC4 titanium alloy honeycomb sandwich construction is brazed by amorphous foil solder Ti-Zr-Cu-Ni. The effect of brazing temperature and holding time on microstructure of brazing interface and mechanical property has been researched. The results show that when the brazing temperature varies in the range from 875 ℃ to 890 ℃，with the increasing of the temperature, diffusion of the elements as well as the tensile strength of the weld could be better. When brazed at 890 ℃ with the holding time ranging from 2 h to 4 h, the tensile strength of the weld increases at first, and reaches the optimum with 3.5 h holding time, then decreases gradually. The optimized brazing technology is 890 ℃/3.5 h, with which the average tensile strength, three point bending strength, compression strength and L/W shear strength are 14.64, 224.05, 11.21, 4.43 and 3.76 MPa respectively, and the weak part is TC4 honeycomb core. |
| |
| Keywords: | SP700 titanium alloy honeycomb sandwich construction brazing |