| 基于表面改性的国产T800碳纤维/高韧性环氧树脂复合材料胶接性能 |
| |
| 引用本文： | 翟全胜,苗春卉,崔海超,张晨乾,叶宏军. 基于表面改性的国产T800碳纤维/高韧性环氧树脂复合材料胶接性能[J]. 复合材料学报, 2021, 38(7): 2162-2171. DOI: 10.13801/j.cnki.fhclxb.20201016.002 |
| |
| 作者姓名： | 翟全胜 苗春卉 崔海超 张晨乾 叶宏军 |
| |
| 作者单位： | 航空工业制造技术研究院复材中心,北京101300 |
| |
| 摘 要： | 本文通过打磨、喷砂、等离子处理方法对国产T800碳纤维/高韧性环氧树脂复合材料的待胶接面进行改性,分别制备了J-116B胶膜和J-375胶膜的浮辊剥离性能及拉伸剪切性能试验件.测试了不同处理条件下J-116B胶膜和J-375胶膜的剥离和剪切性能.采用SEM对老化前后、未经刻蚀和刻蚀后的剥离试样形貌进行观察.采用接触角测...
|
| 关 键 词： | 二次胶接 界面 改性 打磨 喷砂 等离子体处理 |
| 收稿时间： | 2020-08-03 |
Bonding performance of domestic T800 carbon fiber/high toughness epoxy composite based on surface modification |
| |
| Affiliation: | AVIC Composite Corporation, Beijing 101300, China |
| |
| Abstract: | In this paper, the bonding surface of domestic T800 carbon fiber/high toughness epoxy composites was modified by grinding, sandblasting and plasma treatment. The test pieces of J-116B and J-375 adhesive films on floating roller peeling and tensile shear properties were prepared, respectively. The peel and shear properties of the J-116B and J-375 adhesive films were tested under different treatment conditions. The morphology of the samples before and after aging, without etching and after etching were observed by SEM. The contact angle tester was used to test the influence of different surface treatment methods on the wettability of the domestic T800 carbon fiber/high toughness epoxy composites bonding surface, and XPS was used to study the surface physicophysication performance of domestic T800 carbon fiber/high toughness epoxy composites before and after plasma treatment. The results show that J-375 film has better hygrothermal aging property although its room temperature peeling property is not as good as that of J-116B film. The failure mode of plasma treated domestic T800 carbon fiber/high toughness epoxy composites changed from adhesion failure to cohesive failure, so that the tensile shear and peel properties of the two films are significantly improved. This is because plasma treatment can recombine the molecular chain on the surface of the composite and form new active groups on the bonding surface. |
| |
| Keywords: | |