| 复合材料连续损伤力学模型在螺栓接头渐进失效预测中的应用 |
| |
| 引用本文： | 何柏灵,葛东云.复合材料连续损伤力学模型在螺栓接头渐进失效预测中的应用[J].复合材料学报,2020,37(8):2065-2075. |
| |
| 作者姓名： | 何柏灵 葛东云 |
| |
| 作者单位： | 1.广西科技大学 机械与交通工程学院，柳州 545006 |
| |
| 基金项目： | 广西高校中青年教师基础能力提升项目(2019 KY0365)；广西科技基地和人才专项(桂科AD19110150)；机械结构强度与振动国家重点实验室开放课题(SV2019-KF-12) |
| |
| 摘 要： | 提出考虑层合板面内(纤维和基体失效)和层间失效的复合材料连续损伤力学模型，对螺栓接头的渐进失效行为进行预测。基于Tsai-Wu强度准则，发展可以判定复合材料面内和层间失效的强度准则。采用幂指数衰减材料退化模型模拟复合材料的损伤扩展过程。建立连续损伤力学模型用以研究0°铺层比例和螺栓直径对复合材料螺栓接头挤压性能的影响，预测结果与实验结果吻合。结果表明:0°铺层比例过高，接头发生剪切破坏，降低连接结构承载能力；增大螺栓直径，层合板损伤受到抑制，可提高复合材料螺栓接头的挤压强度。
|
| 关 键 词： | 复合材料 螺栓接头 连续损伤力学模型 渐进失效 强度准则 |
| 收稿时间： | 2019-09-05 |
Application of continuum damage mechanics model for composites in progressive failure prediction of bolted joints |
| |
| Affiliation: | 1.School of Mechanical and Transportation Engineering, Guangxi University of Science and Technology, Liuzhou 545006, China2.State Key Laboratory for Strength and Vibration of Mechanical Structures, Xi’an Jiaotong University, Xi’an 710049, China3.School of Aerospace Engineering, Tsinghua University, Beijing 100084, China |
| |
| Abstract: | A continuum damage mechanics model for composites, considering the intralaminar (fibre and matrix failure) and interlaminar failure, was proposed to predict the progressive damage behavior of bolted joints. Based on Tsai-Wu strength criterion, a new failure-judgement formula was developed to distinguish the intralaminar and interlaminar failure. An exponent material degradation model was introduced to simulate the damage evolution of the composite. A continuum damage mechanics model was established to analyze the effect of 0° ply ratio and bolt diameter on the bearing characteristic of the composite bolted joints. The predicted results exhibit good agreement with the experimental results. These results show that high 0° ply ratio induces the shear-out failure of the composite bolted joints, decreasing the structural bearing capability. Increasing the bolt diameter can restrain the damage of the composite laminate and improve the bearing strength of the composite bolted joints. |
| |