| 低碳铝脱氧20钢钢水洁净度控制研究 |
| |
| 引用本文： | 屠兴圹,徐建飞,周淼,苏振伟,林俊,万文华.低碳铝脱氧20钢钢水洁净度控制研究[J].特殊钢,2022,43(3):35-38. |
| |
| 作者姓名： | 屠兴圹 徐建飞 周淼 苏振伟 林俊 万文华 |
| |
| 作者单位： | 中天钢铁集团有限公司技术中心，常州213011 |
| |
| 摘 要： | 为了研究120 t BOF-LF-RH-160 mm×160 mm坯CC工艺生产的铝脱氧20钢（/%:0.13～0.23C,0.17～0.37Si,0.35～0.65Mn,≤0.035P,≤0.035S,0.020～0.050Al）中非金属夹杂物的控制技术,对LF精炼过程中脱氧剂加入时机进行调整,并对精炼过程中非金属夹杂物类型与夹杂物数量进行分析。结果表明,转炉出钢后采用铝块脱氧,LF精炼进站非金属夹杂物主要为Al2O3,精炼结束前部分夹杂物由Al2O3转变为Al2O3·CaO,RH结束后非金属夹杂物密度3～4个/mm2,铸坯氧含量（7.48～8.18）×10-6;而转炉出钢后采用硅锰进行脱氧,精炼结束前采用铝线,精炼过程中夹杂物主要为MnO·SiO2,CaO含量小于5%,精炼结束非金属夹杂物控制为Al2O3,RH真空处理后,非金属夹杂物密度小于1.5个/mm2,铸坯氧含量（4.94～5.53）×10-6。因此,针对采用“BOF-LFRH-CC”工艺流程生产的含铝钢,提出精炼结束前将非金属夹杂物控制为Al2O3,同时运用RH真空高效去除夹杂物,以提高钢水的洁净度。
|
| 关 键 词： | 20钢 铝脱氧 非金属夹杂物 Al2O3 夹杂物去除 洁净度 |
| 收稿时间： | 2018-08-15 |
Study on Cleanliness Controlling of Liquid of Low Carbon Al-killed 0.20 C Steel |
| |
| TU Xingkuang,XU Jianfei,ZHOU Miao,SU Zhenwei,LIN Jun,WAN Wenhua.Study on Cleanliness Controlling of Liquid of Low Carbon Al-killed 0.20 C Steel[J].Special Steel,2022,43(3):35-38. |
| |
| Authors: | TU Xingkuang XU Jianfei ZHOU Miao SU Zhenwei LIN Jun WAN Wenhua |
| |
| Affiliation: | Technology Center, Zenith Steel Group Co Ltd, Changzhou, 213011 |
| |
| Abstract: | In order to study the control technology of nonmetallic inclusions in aluminum deoxidized 0. 20 C steel (/% ：0. 13 ~0.23C,0. 17 ?0.37Si,0.35 ~0.65Mn, ≤ 0.035P, ≤ 0.035S,0.020 - 0.050Al) produced by the process of “120 t BOF-LF-RH-160 mm x 160 mm billet CC”，the adding time of deoxidizer in LF refining process is adjusted, and the type and quantity of nonmetallic inclusions in the refining process are analyzed. The results show that the non-metallic inclusions in steel before LF refining are mainly Al2O3 with deoxidizing by aluminum block after BOF tapping, and some inclusions change from Al2O3 to Al2O3 , CaO before LF refining, and the density of non-metallic inclusions is 3 ~4 /mm2 after RH, and billet oxygen content is (7. 48 ~ 8. 18) x 10-6, But with liquid deoxidizing by silicon-manganese after BOF tapping, feeding aluminum wire before refining end, the inclusion in refining process is mainly MnO ? SiO2, and the CaO content is less than 5% , billet oxygen content is (4. 94 ?5. 53) x 10-6 , and the non-metallic inclusion is controlled to Al2O3 at the end of refining, and after RH vacuum treatment, the density of non-metallic inclusion is less than 1.5/mm2. Therefore, for the aluminum-containing steel produced by the " BOF-LF-RH-CC" process, it is proposed to control the nonmetallic inclusions to Al2O3 before the end of refining, and at the same time, RH vacuum is used to remove the inclusions efficiently, so as to improve the cleanliness of molten steel. |
| |
| Keywords: | |
|
| 点击此处可从《特殊钢》浏览原始摘要信息 |
|