| 铜原位改性HMS材料的表征及抗菌性能 |
| |
| 引用本文： | 陈君华,王飞,程年寿,丁志杰,伏再辉,银董红.铜原位改性HMS材料的表征及抗菌性能[J].无机材料学报,2009,24(4):695-701. |
| |
| 作者姓名： | 陈君华 王飞 程年寿 丁志杰 伏再辉 银董红 |
| |
| 作者单位： | 1. 安徽科技学院 化学系， 凤阳 233100； 2. 南京林业大学 化工学院， 南京 210037； 3. 湖南师范大学 化学化工学院， 长沙 410081 |
| |
| 基金项目： | 安徽省高等学校自然科学基金，安徽科技学院重点学科基金 |
| |
| 摘 要： | 采用溶胶凝胶法，原位合成了铜改性的六方介孔硅 (Cu-HMS)无机抗菌材料. XRD、TG-DTA、ESR、UV-Vis、FT-IR、ESEM、EDS及N2吸附脱附等对材料结构与性能进行了表征；以大肠杆菌、金黄色葡萄球菌、枯草杆菌及芽孢杆菌作供试菌种，考察了材料的抗菌性能. 结果表明，材料粒子呈规则的叶片状，比表面积为553m2/g，平均孔径约3.6nm，铜以离子形式存在于材料的骨架结构中，材料具有良好的介孔结构和热稳定性，有优良的紫外-可见光吸收性能；在抗菌实验中，材料的抗菌效能较好，抗菌性能稳定持久. 材料用量20mg/L，12h即表现出明显的抑菌作用；用量为200mg/L时，24h后可彻底杀灭大肠杆菌、金黄色葡萄球菌及枯草杆菌.
|
| 关 键 词： | HMS 改性 表征 抗菌性能 |
| 收稿时间： | 2008-9-18 |
| 修稿时间： | 2008-11-9 |
Characterization and Antibacterial Ability of Copper-Modified Hexagonal Mesoporous Silica in situ |
| |
| CHEN Jun-Hua,WANG Fei,CHENG Nian-Shou,DING Zhi-Jie,FU Zhai-Hui,YIN Dong-Hong.Characterization and Antibacterial Ability of Copper-Modified Hexagonal Mesoporous Silica in situ[J].Journal of Inorganic Materials,2009,24(4):695-701. |
| |
| Authors: | CHEN Jun-Hua WANG Fei CHENG Nian-Shou DING Zhi-Jie FU Zhai-Hui YIN Dong-Hong |
| |
| Affiliation: | 1. Chemistry Department of Anhui Science and Technology University, Fengyang 233100, China; 2. College of Chemical Engineering, Nanjing Forestry University, Nanjing 210037, China; 3. College of Chemistry and Chemical Engineering, Hunan Normal University, Changsha 410081, China |
| |
| Abstract: | Copper modified hexagonal mesoporous silica (Cu-HMS) was in situ prepared with sol-gel method. The structure and the performance of Cu-HMS were characterized by XRD, TG-DTA, ESR, UV-Vis, FT-IR, ESEM, EDS and N2 adsorption desorption isotherms. Based on bacteriostasis experiments of E. coil, S. aureus, B. subtilis and G. bacillus, the antibacterial ability of the sample was also investigated. The results show that the particles of Cu-HMS look like regular thallus, the specific surface area is 533m2/g, the average pore size is 3.6nm, and the copper ions are presented in framework of the sample, especially. The sample has favorable mesoporous structure, thermal stability and ultraviolet-visible-light absorption ability. Furthermore, The bacteriostasis experimental results show that Cu-HMS has favourable and steady antibacterial ability. When the dosage of Cu-HMS is 20mg/L, the bacteriostasis ability may be visibly detected in 12h, while the dosage is up to 200mg/L, E. coil, S. aureus and B. subtilis may be killed after 24h. |
| |
| Keywords: | hexagonal mesoporous silica modification characterization antibacterial ability |