| 锐钛矿型TiO2 / MnFe2O4 核壳结构复合纳米颗粒的制备及其光催化特性 |
| |
| 引用本文： | 付乌有,杨海滨,刘冰冰,邹广田.锐钛矿型TiO2 / MnFe2O4 核壳结构复合纳米颗粒的制备及其光催化特性[J].复合材料学报,2007,24(3):136-140. |
| |
| 作者姓名： | 付乌有 杨海滨 刘冰冰 邹广田 |
| |
| 作者单位： | 吉林大学超硬材料国家重点实验室, 长春 130012 |
| |
| 基金项目： | 国家重点基础研究发展计划(973计划) |
| |
| 摘 要： | 采用柠檬酸盐前驱体技术, 合成了粒径约为20～70 nm 的尖晶石结构MnFe2O4 纳米颗粒, 用聚乙烯亚胺( PEI) 对MnFe2O4 纳米颗粒进行表面处理后, 以异丙醇钛为前驱物, 采用sol2gel 法在纳米MnFe2O4 表面包覆锐钛矿型TiO2 纳米层形成核壳结构。利用透射电子显微镜( TEM) 、X射线衍射仪(XRD) 和振动样品磁强计等测试手段对样品的结构、形貌、粒径以及磁学性能等进行了表征。采用罗丹明B 的光催化降解反应对所制催化剂的活性进行了评价。结果表明, 核壳结构TiO2 / MnFe2O4 复合纳米颗粒的光催化活性随着壳层厚度的增加而增强,当达到一定厚度以后, 其催化活性不随壳层厚度的增加而改变。复合颗粒中TiO2 含量达到30 wt % , 反应时间4 h时, TiO2 / MnFe2O4 磁性光催化剂对罗丹明B 的光降解率达到100 % , 与纯TiO2 纳米粉体的催化活性相当, 且光催化活性稳定, 是一种便于回收、可重复使用的高效光催化剂。
|
| 关 键 词： | MnFe2O4 / TiO2 核壳结构 复合纳米颗粒 磁性光催化剂 |
| 文章编号： | 1000-3851（2007）03-0136-05 |
| 收稿时间： | 2006-10-16 |
| 修稿时间： | 2006-10-162007-01-26 |
Preparation and photocatalytic property of anatase TiO2 / MnFe2O4core-shell structure nanoparticles |
| |
| FU Wuyou,YANG Haibin,LIU Bingbing,ZOU Guangtian.Preparation and photocatalytic property of anatase TiO2 / MnFe2O4core-shell structure nanoparticles[J].Acta Materiae Compositae Sinica,2007,24(3):136-140. |
| |
| Authors: | FU Wuyou YANG Haibin LIU Bingbing ZOU Guangtian |
| |
| Affiliation: | National Laboratory of Superhard Materials, Jilin University, Changchun 130012, China |
| |
| Abstract: | The anatase TiO2 / MnFe2O4 composite nanoparticles with a core-shell structure have been obtained. Thecore MnFe2O4 nanoparticles were synthesized by the co-precipitation method , and the shell TiO2 nanocrystals werederived using the sol-gel technology followed by a heat-t reatment at 450 ℃. The TiO2 / MnFe2O4 samples were characterized by X-ray diff raction (XRD) and t ransmission elect ron microscopy ( TEM) . The TiO2 / MnFe2O4 compositeparticles can be used as a magnetic photocatalyst , which can be fluidized and recovered by an applied magnetic fieldenhancing both the separation and mixing efficiency for recyclable fluids. When the mass f raction of TiO2 is 30 % andthere is enough UV illumination (4 h in our experiment s) , the photodegradation ratio of Rhodamine B by the composite of TiO2 / MnFe2O4 is 100 % , similar to that of the pure TiO2 . |
| |
| Keywords: | MnFe2O4/TiO2 |