H-526单组分水性木器漆用苯丙乳液的研制

以丙烯酸丁酯、苯乙烯为主反应单体,阴非离子乳化剂H-870A、CO-1220混合使用,在共聚反应体系中同时加入了0.6%具有多种活性官能团的交联单体有机硅氧烷和0.8%～1%双丙酮丙烯酰胺,控制反应温度在80～83℃,利用核壳乳液聚合法,研制成H-526水性木器漆用苯丙乳液。该乳液固含量为45%、MFT值为40℃,综合性能优异,适用于调制水性木器漆。     

水性木器涂料用自交联型丙烯酸酯乳液的制备与性能研究

采用半连续乳液聚合法合成了一种自交联型具有核壳结构的丙烯酸酯乳液,确定了交联单体MAA、DAAM和有机硅单体用量分别为单体总量3%、3%和1%(均为质量分数)时,乳液的综合性能更好,其固含量为50%,黏度为315m Pa·s,粒径为93 nm。该乳液可用于配制水性木器漆底漆和面漆,VOC含量低,快干,涂膜具有较好的丰满度、打磨性和透明度等性能,施工方便,喷涂一底一面即可获得很好的施工性能,缩短施工时间。     

有机硅改性醋丙乳液的制备与表征

采用半连续种子乳液聚合技术,以丙烯酸丁酯、醋酸乙烯酯和有机硅单体合成了有机硅改性醋丙乳液,并研究了有机硅含量、复合乳化剂配比、种子单体含量等对乳液聚合稳定性及乳液性能的影响。制备出的乳液稳定性良好,随着种子乳液单体含量的增加,乳胶粒粒径变小。     

水性聚氨酯-有机硅共聚物的制备与性能

以聚醚二元醇(GE2000)为软段,环氧树脂(E-20)为部分硬段,制备出有机硅交联改性的聚氨酯乳液,探讨了有机硅含量对乳液性能的影响。结果表明,随着有机硅含量增大,乳液黏度、分子量增大,胶膜耐水(溶剂)性、机械性能、疏水性增强。FTIR分析证实有机硅键合到聚氨酯结构中。SEM分析表明,有机硅改性聚氨酯胶膜结构致密。DSC与DMA分析表明,有机硅改性聚氨酯软硬段之间存在一定程度的微相分离,有机硅含量的增加提高了其耐热性能。     

高含量有机硅改性水性聚氨酯乳液的制备及性能研究

合成了高有机硅含量的水性聚氨酯稳定乳液。测量了有机硅含量对水接触角的影响,并对乳液的稳定性、黏度及涂膜的FT-IR、DSC、机械性能等进行了表征。     

有机硅改性丙烯酸酯乳液及其外墙涂料的研究

采用溶胀法制备有机硅改性丙烯酸酯复合乳液并配制外墙涂料，研究了有机硅含量、颜料体积浓度以及硅酸乙酯水解物含量对涂料性能的影响。结果表明，有机硅可大大改善丙烯酸酯乳液型外墙涂料的性能。     

木器涂料

0003284特别适用于木器的水稀释性快干清漆:PL170121[波兰专利]/波兰(NiesPodziewanski,L心ch)一1996.10.31一3页一297878(1993.2.26);护C C09D5102 题述清漆含有50一98份苯乙烯一丙烯酸醋-马来酸醋三元共聚物水分散体(固体分约50%)和卜10份甲基有机硅树脂水乳液(以固体计)。例如,木器漆用的一种透明涂料含有FG~8(50%苯乙烯一丙烯酸醋一马来酸醋三元共聚物水分散体)55.0份、40%的甲基有机硅树脂水乳液25.0份、多聚磷酸铰(阻燃剂)10刀份、木器用的黑色染料3.0份胶体二氧化硅2.0份和水5.0份。0003285室内用水稀释性透明木器漆及其制备:EP…     

有机硅/丙烯酸酯共聚物乳液性能的研究

采用反应型乳化剂烷基乙烯基磺酸钠 ( DNS-86)合成了有机硅改性丙烯酸酯共聚乳液 ,考察了乳液的表面张力、稳定性及流变性能。结果表明硅丙乳液的表面张力随有机硅单体用量的增加而减小 ;乳液的冻融稳定性和储存稳定性良好 ,符合涂料的使用要求 ;乳液为非牛顿流体 ,乳液的表观黏度随着有机硅含量的增加而降低。     

硅丙乳液及其硅丙外墙涂料的研制

研制了有机硅含量达20％以上的硅丙乳液及其硅丙外墙涂料。介绍了硅丙乳液及其硅丙外墙涂料的配方、制备工艺和性能指标。讨论了有机硅含量对涂料性能的影响。     

溶剂乳化剂对水性硝基木器漆乳液稳定性的影响

本文讨论了混合溶剂的组成对水乳化硝基木器漆性能的影响,研究了混合溶剂中添加DBE对提高水性硝基木器漆乳液稳定性的作用。简述了乳化剂对乳液稳定性的作用,实验数据表明,制备水包油(O/W)型水乳化硝基木器漆乳液时的最适宜HLB值范围为13.1～13.2。     

Study of the styrene–acrylic emulsion modified by hydroxyl-phosphate ester and its stoving varnish

A styrene–acrylic copolymer emulsion containing hydroxyl-phosphate as flash-rust functional monomer and hydroxypropyl acrylate as cross-linking monomer was synthesized. The effects of the hydroxyl phosphate dosage, the hydroxypropyl acrylate dosage as well as the ratio of soft to hard monomer on the emulsion and coating film were investigated. The results showed that the emulsion of 4% hydroxyl phosphate function monomer and 3% hydroxypropyl acrylate with soft and hard monomer ratio of 1:1.6 and modified emulsion and amino resin ratio of 6:1 resulted in a coating film with the best performance.     

具有早期耐水汽性水性木器涂料的研制

开发了一种早期耐水汽性良好的单组分水性木器涂料,讨论了乳液的选择、成膜助剂的复配以及消光剂、手感助剂的选择搭配对涂料性能的影响。实验发现:以丙烯酸乳液、亲水型和憎水型搭配的成膜助剂组合、微粉化有机改性聚合物消光剂与有机硅类型的手感助剂制备的水性木器涂料涂膜具有较好的早期耐水汽性。该涂料产品适用于家庭涂装市场中消费者对浴室门等一些特殊部位的涂装应用场合,并已取得良好效果。     

New high performance two-component wood coatings comprised of a hydroxy functional acrylic emulsion and a water-dispersible polysiocyanate

Statistical methods were used to develop hydroxy functional acrylic emulsions for use with a water-dispersible polyisocyanate crosslinker. The resulting two-component waterborne coating systems were optimized for kitchen cabinet and office furniture applications. Key performance criteria included appearance and aesthetics, pot life, print and mar resistance, and chemical resistance involving both Kitchen Cabinet Manufacturers’ Association (KCMA) and office furniture requirements. Statistical analysis revealed several strong correlations between acrylic emulsion hydroxy level, particle size, composition T_g, polymerization process and wood coating performance. For example, smaller acrylic emulsion particle size was found to yield many performance benefits with few detriments. Coating formulation variables were also found to be significant. Ultimate coating hardness increased with water-dispersible polyisocyanate level, yet early hardness readings correlated negatively with water-dispersible polyisocyanate level. Plasticization and crosslinking effects were thought to be responsible. A higher ethylene glycol monbutyl ether (EB) coalescent level was found to correlate negatively with coating hardness, suggesting a reaction between the EB hydroxyl group and the water-dispersible polyisocyanate, resulting in plasticization of the coating. Coatings and Colorants Div., 100 Bayer Rd., Pittsburgh, PA 15205-9741 Performance Materials Div., 9921 Brecksville Rd., Brecksville, OH 44141-3259.     

水性羟基丙烯酸树脂合成及木器漆研制

以丙烯酸酯类单体为原料,采用预乳化半连续乳液聚合方式合成了水性羟基丙烯酸树脂,考查了羟基组分等因素对树脂的影响;将制备的水性羟基丙烯酸树脂同多种拜耳水性固化剂配制成双组分水性聚氨酯清漆,分析了不同的水性固化剂对漆膜性能的影响。     

软木专用水性双组分聚氨酯木器清漆的开发

以核壳型丙烯酸羟基乳液及亲水改性的异氰酸酯固化剂,开发了一种专用于软木涂装的水性双组分聚氨酯木器清漆,该涂料VOC低,涂膜干燥后具有优良的附着力、耐水性、耐醇性及抗粘连性等性能,达到软木制品饰面要求。     

具有可视胶化性能的水性双组分木器漆的研制

开发了一种木器用双组分水性聚氨酯涂料,该体系在到达活化期的同时可产生液态漆可视胶化的现象,且漆膜性能在活化期内各时间段均能保持稳定。重点讨论了乳液、配套固化剂对体系性能的影响。实验发现只有特定的乳液和固化剂搭配才能保证达到活化期内出现液态漆可视胶化以及漆膜性能在活化期内保持稳定的目标,并且该产品漆膜性能与溶剂型双组分聚氨酯木器涂料的相当。该涂料产品适合零售市场对水性木器漆的需求。     

水性聚氨酯的制备

要制得性能优良的木器用水性聚氨酯乳液,要从制备水性聚氨酯用的原料聚酯二元醇入手,文章设计分子量为1000的聚酯二元醇,它使用邻苯二甲酸酐和己二酸以摩尔比40∶60混合后再与乙二醇反应,制得的水性聚氨酯乳液,其化学稳定性、涂膜硬度,相对于单独用脂肪族聚酯二元醇制备的水性聚氨酯的性能要优。     

羟基磷酸酯共聚苯丙乳液的合成及其防腐性能

低温条件下,用甲基丙烯酸缩水甘油酯(GMA)和浓磷酸制备一种羟基磷酸酯功能单体,将其与丙烯酸酯类单体共聚制备一种功能性苯丙防锈乳液,对该改性苯丙乳液及其涂膜进行了性能测试,并采用IR、SEM、Tafel和粒径分析进行了表征。结果表明,所制备的乳液反应体系稳定,乳液粒径约为100 nm,粒径分布均匀并具有窄分布的特点;当羟基磷酸酯用量为单体总质量的4%时,其漆膜的耐水性及耐盐雾性能达到最佳,无闪蚀现象,腐蚀电流较小,为1.376×10-8A,说明涂层的耐腐蚀能力较强。     

木器涂料用苯丙微乳液的合成

以苯乙烯、甲基丙烯酸甲酯和丙烯酸丁酯为主要单体,过硫酸盐为引发剂,通过种子乳液聚合法合成了新型木器涂料用苯丙微乳液,研究了乳化剂的用量、阴离子非离子乳化剂配比、聚合工艺、功能性单体的种类和用量、软／硬单体组成对乳液和涂膜性能的影响。     

环境友好型高性能多用途涂料的研制

研究了一种不含壬基酚、超低VOC环境友好型高性能多用途涂料体系。该体系底漆由核壳结构、环氧改性的丙烯酸酯乳液配制,可用于水泥砂浆、木材、金属等多种基材表面;面漆则以硅丙乳液复配氟碳乳液,配合陶瓷微珠等功能性材料,具有良好的耐候、耐沾污性及硬度。