聚苯酯填充聚四氟乙烯复合材料摩擦学行为研究

采用聚苯酯（Ekonol）、Ekonol／PAB纤维增强聚四氟乙烯（PTFE）制备利用转移膜润滑的摩擦副材料，并研究了两组材料在于摩擦条件下与9Cr18轴承钢对摩时的摩擦学性能；运用扫描电镜分析了两组材料磨损表面形貌和磨损机理。结果表明：随着Ekonol含量的增大，Ekonol填充PTFE复合材料的摩擦因数逐渐增大，当Ekonol质量分数超过25％时摩擦因数略有下降，磨损方式由以犁削磨损为主转变为以疲劳磨损为主；而Ekonol／PAB纤维填充门FE复合材料的摩擦因数，随Ekonol含量的增大而增大，磨损方式由以粘着磨损为主转变为以疲劳磨损为主。Ekonol／PAB纤维填充PTFE复合材料的摩擦学性能优于Ekonol填充PTFE复合材料。     

Ekonol/石墨/MoS2填料对PTFE力学和摩擦磨损性能的影响

研究了Ekonol含量对Ekonol／石墨／MoS2／P，PTFE复合材料的力学性能、摩擦磨损性能的影响，以及滑动速度、载荷对材料摩擦磨损性能的影响；用扫描电子显微镜观察了复合材料磨损后的表面形貌，并探讨了其磨损机制。结果表明：加入填料降低了材料的拉伸强度和弯曲强度，但提高了弯曲模量和硬度；同时填料能提高材料的磨损性能，但使摩擦因数升高了；当Ekonol含量较低时，磨损机制为粘着磨损，随着填料含量的增加，Ekonol分散到基体中，起到了承载作用，阻止了PTFE基体的带状破坏，磨损机制为疲劳磨损和轻微的粘着磨损；摩擦因数随载荷的增大而减小，随滑动速度的增大而增大，在相同的滑动时间内，磨痕宽度随载荷和滑动速度的增大而增大。     

Ekonol填充PTFE三层复合材料摩擦学性能研究

在端面摩擦磨损试验机上对Ekonol填充PTFE三层复合材料试样进行了常温干摩擦实验,探讨了Ekonol含量对材料摩擦磨损性能及磨损机制的影响.结果表明,随着Ekonol含量的增加,材料的摩擦因数逐渐增大,但总体上比较小(<0.14),表现出了较好的摩擦性能,同时材料的耐磨损性能随Ekonol含量的增加而增大,说明Ekonol的加入有利于改善材料的摩擦学性能.     

纳米粒子和聚四氟乙烯填充UHMWPE复合材料的摩擦磨损性能研究

以纳米氧化锌(ZnO)和纳米蒙脱土(MMT)及聚四氟乙烯(PTFE)作为复合填料,通过热压成型工艺制备了纳米ZnO-MMT及PTFE填充超高分子量聚乙烯(UHMWPE)复合材料,采用销-盘式摩擦磨损试验机考察了纳米粒子对复合材料摩擦磨损性能的影响,用扫描电子显微镜观察了复合材料磨损表面形貌。结果表明当PTFE和MMT的填充量均保持为质量分数6%,填充纳米ZnO质量分数为4%~6%时的复合材料可获得较好的摩擦磨损性能,与不含纳米ZnO的复合材料相比,其摩擦因数最低下降了11.1%,而磨损率下降了83.3%。当复合填料中纳米ZnO含量较低时,复合材料的磨损机制主要表现为不同程度的粘着磨损,但当复合填料中纳米ZnO含量较高时,复合材料的磨损机制主要表现不同程度的粘着磨损和磨粒磨损,同时其复合材料的摩擦磨损性能出现了恶化现象。     

软碳填充PTFE复合材料摩擦磨损性能研究

以不同含量的软碳为填料制备了PTFE基复合材料,测量了其机械性能,在M-2000型摩擦磨损试验机上研究其摩擦磨损行为,并探讨了其磨损机制.结果表明:软碳能提高PTFE复合材料的硬度,软碳/PTFE复合材料的耐磨性能优于纯PTFE,当软碳质量分数为7%时其耐磨性能最好.复合材料的摩擦因数随着软碳含量的增加而增加.摩擦表面的SEM观察发现:纯PTFE的摩擦表面分布着较明显的犁削和黏着磨损的痕迹,复合材料的摩擦表面均出现犁削,随着软碳含量的增加,犁削现象减轻,这表明以软碳作为填料可有效地抑制PTFE的磨损.     

纳米Cu粉填充碳纤维/PTFE复合材料的摩擦磨损性能

考察纳米Cu粉含量、粒径对碳纤维/PTFE复合材料摩擦磨损性能的影响,采用扫描电子显微镜分析磨损面和对偶面转移膜形貌,并探讨其磨损机制。结果表明:纳米Cu粉能提高碳纤维/PTFE复合材料的耐磨性,在高载荷下,纳米Cu粉的增强效果更加明显;纳米Cu粉的粒径越小,复合材料的耐磨性越好;添加质量分数0.3%纳米Cu粉的碳纤维/PTFE复合材料耐磨性最优,1.4 m/s,200 N下实验条件下,其磨损率比未添加时降低了45%;SEM分析显示纳米Cu粉能在对偶面上形成平整致密的转移膜,具有显微增强作用。     

硬碳填充PTFE复合材料摩擦磨损性能研究

以硬碳为填料制备了PTFE基复合材料,并研究了该复合材料在干摩擦条件下与不锈钢对摩时的摩擦磨损行为,并探讨其磨损机制.实验结果表明:硬碳能提高FIFE硬度,硬碳/PTFE复合材料的耐磨性能明显优于纯PTFE.其摩擦因数随着硬碳含量的增加而减小.复合材料的摩擦表面SEM观察发现:纯PTFE摩擦表面分布着较明显的犁削和粘着磨损的痕迹,硬碳/PTFE的磨痕较浅,表明硬碳作为填料可有效地抑制FTFE的磨损.     

纳米Fe_3O_4磁性材料填充聚四氟乙烯的摩擦磨损性能

利用机械共混、冷压成型和烧结工艺制备不同含量的磁性纳米Fe3O4填充聚四氟乙烯(PTFE)复合密封材料,采用MM-200型摩擦磨损试验机考察其在干摩擦下与45#钢对磨时的摩擦磨损性能,借助扫描电子显微镜(SEM)对磨损表面形貌进行观察并分析磨损机制。结果表明:随磁性纳米Fe3O4含量的增加,复合材料的硬度显著提高,摩擦因数呈现先增大后减小再增大的变化趋势,耐磨性能得到明显改善;当Fe3O4质量分数为15%时,复合密封材料的摩擦因数较小,体积磨损率与纯PTFE相比降低两个数量级;随着Fe3O4含量的增加,磨损机制由纯PTFE的黏着磨损转变为黏着磨损与磨粒磨损共同作用。     

纳米Fe3O4填充聚四氟乙烯摩擦磨损性能的研究.doc

利用机械共混、冷压成型和烧结工艺制备不同含量的磁性纳米Fe3O4填充聚四氟乙烯(PTFE)复合密封材料,采用MM 200型摩擦磨损试验机考察其在干摩擦下与45#钢对磨时的摩擦磨损性能,借助扫描电子显微镜（SEM）对磨损表面形貌进行观察并分析磨损机制。结果表明：随磁性纳米Fe3O4含量的增加,复合材料的硬度显著提高,摩擦因数呈现先增大后减小再增大的变化趋势,耐磨性能得到明显改善;当Fe3O4质量分数为15%时,复合密封材料的摩擦因数较小,体积磨损率与纯PTFE相比降低两个数量级;随着Fe3O4含量的增加,磨损机制由纯PTFE的黏着磨损转变为黏着磨损与磨粒磨损共同作用。     

纳米碳黑与纳米石墨填充PTFE复合材料摩擦磨损性能比较研究

用M-2000摩擦磨损试验机对纳米碳黑和石墨填充PTFE复合材料进行了摩擦磨损性能研究,用扫描电子显微镜(SEM)对磨损表面进行观察.结果表明:2种碳纳米能够提高PTFE复合材料的耐磨性,其中纳米碳黑填充效果最佳.纳米碳黑和纳米石墨2种碳纳米的最佳添加量分别为7%和5%(质量分数).纳米石墨可以减小PTFE复合材料的摩擦因数,而纳米碳黑使得PTFE复合材料的摩擦因数增大,且含量越高,复合材料摩擦因数增幅越大.结晶型纳米石墨与PTFE基体的相容性较差,而无定形纳米碳黑与PTFE基体的相容性较好.     

纳米Al2O3弥散强化复合涂层的制备及耐磨性研究

将纳米Al2O3与Ni基自熔性合金F102的复合粉末用氧乙炔焰热喷焊工艺制各复合涂层，研究了纳米Al2O3的加入呈对组织和耐磨性的影响。结果表明，当纳米A12O3质量分数为0．25％时，涂层的耐磨性最好，与25％WC复合涂层的耐磨性相当。     

纳米表面工程与摩擦学

利用表面工程技术解决摩擦磨损问题具有高效、实用等特点。随着科学技术的迅速发展，纳米材料和纳米技术在表面工程中得到了广泛应用，由此出现了“纳米表面工程”。利用纳米表面工程技术制备的涂层和镀层有着非常优异的摩擦学性能。本文叙述了作者近年来的有关工作，包括热喷涂纳米陶瓷涂层、热喷涂纳米自润滑涂层、纳米陶瓷／聚合物复合涂层、纳米复合电镀层以及纳米电泳沉积层的摩擦磨损特性和机制。     

Tribological Behavior of Particles and Fiber-Reinforced Hybrid Nanocomposites

This article discusses the mechanical performance of alumina nanoparticles and randomly distributed short glass/carbon fiber-reinforced hybrid composites through microhardness and wear test. The open mold casting method was adapted to prepare the test coupons. The wear and friction behavior of composites sliding against hardened ground EN 32 steel in a pin-on-disc configuration is evaluated on a wear and friction tester. The microhardness properties of the neat epoxy, alumina nanoparticles, and alumina nanoparticle–embedded glass/carbon fiber–reinforced hybrid composites were determined. The morphology of the worn composites was analyzed with a scanning electron microscope. It was found that the particles as fillers contributed significantly to improve the mechanical properties and wear resistance of the polymer composites. This is because the fillers contributed to enhance the bonding strength between the fiber and the epoxy resin. Moreover, the wear and friction resistance of the glass/carbon fiber composites was increased by increasing the filler weight in the composite materials.     

基体表面粗糙度对纳米复合镀层组织及性能的影响

采用电刷镀技术在不同表面粗糙度的W18Cr4V高速钢基体上制备了纳米PTFE和纳米WC颗粒增强的镍基复合镀层,采用扫描电镜对纳米复合镀层的表面和截面形貌进行了观察,研究了基体表面粗糙度对纳米复合镀层耐磨性、耐蚀性和结合强度的影响.结果表明:随着基体表面粗糙度的减小,纳米复合镀层的表面更加平整致密,组织更加细小均匀,镀层厚度减小,镀层中的裂纹数量减少,镀层的耐磨性、耐蚀性和结合强度均得到明显提高.     

纳米TiN改性金属陶瓷刀具的磨损性能研究

研究了纳米TiN改性TiC金属陶瓷刀具（纳米改性金属陶瓷刀具，下同）与普通Ti（C，N）基金属陶瓷刀具及硬质合金刀具在切割正火态45钢时的磨损曲线及磨损机理。结果表明：纲米TiN改性TiC基金属陶瓷刀具的效果明显；与硬质合金刀具相比，纳米改性金属陶瓷刀具优良的综合性能使其具有更同的耐磨性。刀具的失效形式主要是磨损及崩刃。     

纳米硬质合金刀具切削Al/SiCp复合材料实验

SiC颗粒具有较高的硬度,使Al/SiCp复合材料在切削时刀具磨损剧烈。纳米硬质合金具有较高的硬度、韧性及良好的抗磨损能力。制备了纳米硬质合金刀具WC-7Co,对Al/SiCp复合材料进行了切削实验,研究了纳米硬质合金刀具磨损机理和Al/SiCp复合材料的切屑去除机理,以及刀尖处后刀面磨损值。研究认为,纳米硬质合金刀具磨损的机理为SiC颗粒的微切削作用引起的磨料磨损,及SiC颗粒对刀尖刃口的高频、断续冲击引起的微崩刃及微破损,Al/SiCp复合材料的切削实质是断续切削;Al/SiCp复合材料去除机理为切屑的崩碎去除;纳米硬质合金后刀面磨损值较普通硬质合金小30%~50%。     

On the abrasive wear behaviour of mineral filled polypropylene

The effects of mineral fillers on the wear resistance of polypropylene (PP) have been investigated. A general purpose homopolymer grade was used as the matrix. The mineral fillers investigated were talc, CaCO₃, BaSO₄ and fly ash, representing a range of morphology, size and hardness. The wear behaviour was assessed by pin-on-paper abrasion tests. The wear surfaces were examined using scanning electron microscopy (SEM). The addition of mineral fillers to the polypropylene matrix decreases the wear resistance under severe abrasive conditions. Under mild abrasive conditions the shape and size of the reinforcing filler influence the wear performance. The tensile strength behaviour of each composite, together with the physical properties of the fillers and a microscopic investigation into the modes of material deformation and removal are used to interpret this observed wear behaviour.     

纳米氧化镧和蛇纹石改性PTFE复合材料淡水环境摩擦学性能预测*

以聚四氟乙烯(PTFE)为基体,改性纳米氧化镧(nano-La_2O_3)、改性纳米蛇纹石(nano-serpentine)为添加剂,采用均匀设计法,制备nano-La_2O_3/nano-serpentine/PTFE复合材料。自制水环境模拟装置,设计并进行淡水环境复合材料摩擦学实验。使用Origin软件对实验数据进行曲线拟合,使用SPSS软件进行多元回归分析,得到摩擦学性能回归方程,通过MATLAB解出回归方程摩擦因数和磨损率理论最优解。以复合材料最优理论配比制作试件,进行摩擦学性能对比实验和磨损表面形貌分析。结果表明:复合材料摩擦学性能实验值与回归分析理论结果基本吻合,摩擦因数误差控制在5%以内,磨损率误差控制在10%以内,证明研究所用方法对复合材料摩擦学性能预测具有可行性。     

功率超声在电沉积Ni/纳米Al2O3复合镀层中应用

研究功率超声在纳米电沉积技术中的作用机理。结果表明 ,在电沉积Ni/纳米Al2 O3 复合镀层过程中 ,引入功率超声可有效解决纳米Al2 O3 粒子在镀液中的分散问题 ,使纳米Al2 O3 粒子均匀分布在复合镀层中 ,促进纳米Al2 O3 粒子与镀层基质金属的共沉积 ,并细化基质金属Ni的晶粒     

纳米Al2O3对聚四氟乙烯工程材料性能的影响

用压制和烧结的方法，制备了纳米Al2O3和聚四氟乙烯（PTFE）的复合材料。研究了纳米Al2O3粒子对PTFE的摩擦、磨损、硬度、耐冲击强度等性能的影响。结果表明：纳米Al2O3粒子不仅显著地提高了PTFE耐磨性，而且降低了PTFE的摩擦系数，同时使PTFE的硬度增大。对作用机理进行分析和探讨，提出了“纳米粒子在摩擦磨损表面产生富积及重新嵌入“的观点，为材料的改性研究提供参考。