壬基酚磺酸铜水乳剂防治病毒病试验研究

对壬基酚磺酸铜水乳剂防治黄瓜花叶病毒病（CMV）进行试验研究，结果表明，30％壬基酚磺酸铜水乳剂500－900倍液防治黄瓜和番茄上的该病毒防效高于65％和51％，防效与病毒A可湿性粉剂500倍液防效相当，是目前防治该病毒的好品种。     

20%大蒜素·丁香酚水乳剂的制备及生物活性

采用转相法制备20%大蒜素·丁香酚水乳剂,采用生长速率法测定其室内生物活性。20%大蒜素·丁香酚水乳剂的稳定配方为大蒜素5%、丁香酚15%、乳化剂WJ-630 4%、WJ-990 1%、聚乙二醇400 3%、乙二醇3%,去离子水补齐至100%。20%大蒜素·丁香酚水乳剂各项指标均符合水乳剂产品要求,对灰葡萄孢菌有较高的室内生物活性。     

40%噁草酮·丙草胺水乳剂的制备及生物活性

[目的]制备具有良好生物活性的40%噁草酮·丙草胺水乳剂。[方法]利用转相法制备40%噁草酮·丙草胺水乳剂,分别对配方中各个组分进行筛选,对制剂的室内生物活性及安全性进行研究。[结果]较优配方组成为噁草酮10.0%、丙草胺30.0%、T-80 3.0%、AEO-9 3.0%、AEO-3 2.0%、乙二醇3.0%、SAG 1522 0.5%、三乙醇胺0.15%,去离子水补足至100.0%。[结论]该制剂各项指标符合水乳剂相关标准。室内药效结果表明,该产品对稗草和鳢肠的防效达到90%以上,对水稻安全。     

几种药剂防治红龟蜡蚧药效试验

试验结果表明,药后7d,30%机油·石硫微乳剂500倍液对红龟蜡蚧的防效达到了96.21%;20%松脂酸钠可溶性粉剂100倍液和1.45%阿维·吡可湿性粉剂1000倍液的防效分别为85.43%和73.04%。     

0.3%壳聚糖水剂对番茄产量和病害发生的影响

试验发现0.3%壳聚糖水剂对番茄品质和产量的提高有明显的促进作用,其中500倍液可使单果重增加11.1%,产量提高21.7%。同时它可以明显提高番茄对病害的抵抗能力,抑制病害发生,且3次施药效果更佳,500倍液第3次施药后对番茄晚疫病防效达到74.0%,300倍液对绵疫病可达78.2%。300～500倍液壳聚糖对2种病害的防效与50%多菌灵600倍液防效相近。     

40%叶菌唑·戊唑醇水乳剂的研制

对溶剂、乳化剂等进行筛选,确定40%叶菌唑·戊唑醇水乳剂优化配方,并对其性能进行了测试。该水乳剂产品质量稳定,热贮14 d后,分解率5%,各项指标符合水乳剂的要求。田间药效试验结果表明,40%叶菌唑·戊唑醇水乳剂对小麦赤霉病防效优异。     

25%敌虫灵水乳剂根灌防治萝卜根蛆的药效试验

２５％敌虫灵（甲基异柳磷）水乳剂对萝卜根蛆具有较好的防治效果。根灌试验表明,２５％敌虫灵水乳剂５００倍液防效可达１００％,７５０倍液的防效为９５．２％,而１０００倍液的防效与４０％甲基异柳磷乳油１５００倍液的防效大致相同,但可降低成本３１．５％。试验结果表明田间应用的最佳稀释浓度为７５０￣１０００倍液。     

3种植物源杀虫剂对韭菜迟眼蕈蚊的毒力测定和田间药效评价

为筛选对韭菜迟眼蕈蚊防治效果好的环境友好型杀虫剂,开展了蛇床子素、苦参碱以及印楝素3种常见植物源杀虫剂对韭菜迟眼蕈蚊的室内毒力测定和田间药效试验。结果表明,采用胃毒触杀联合毒力法,药后72 h苦参碱、印楝素、蛇床子素的LC50值分别为36.94,99.95,197.07 mg/L。田间试验中,药后21 d,0.3%苦参碱水剂3 000,2 000倍液校正防效分别为72.85%、79.54%;0.5%印楝素乳油3 000,2 000倍液校正防效分别为69.10%、76.29%;0.4%蛇床子素乳油3 750,2 500倍液校正防效分别为65.14%、70.04%。     

25%丙环唑水乳剂防治香蕉叶斑病田间药效试验

2008年的田间试验表明,将25%丙环唑水乳剂稀释600倍、1000倍、2000倍进行喷雾,以25%丙环唑乳油1000倍为对照,通过调查病情指数计算防治效果。结果在稀释600～2000倍条件下,25%丙环唑水乳剂对香蕉叶斑病的防效为54.83%～77.16%,其中稀释1000倍的防效为61.94%～70.41%,与同等稀释倍数的25%丙环唑乳油的防效基本相当。     

4种杀菌剂对向日葵黑茎病的田间防治效果

选用4种杀菌剂对向日葵黑茎病进行田间防效试验,结果表明,10%苯醚甲环唑WG1000倍液、50%多菌灵WP500倍液、70%甲基硫菌灵WP800倍液的防效较高,分别为77%、73.4%、72.6%;经方差分析显著优于防效次之的50%嘧菌酯SC2000倍液(防效65.5%)和其他2种药剂。建议生产上使用10%苯醚甲环唑WG1000倍液、50%多菌灵WP500倍液、70%甲基硫菌灵WP800倍液。     

切片石蜡乳液的制备

石蜡一直存在难乳化、乳液稳定性差等问题。研究了以切片石蜡为原料,采用种子乳液聚合法,选择复配型乳化剂;讨论了乳化剂用量,乳化时间,乳化温度以及搅拌速度等因素对石蜡乳液稳定性和分散性的影响。结果表明:在乳化剂用量为乳液总量的10%,乳化时间为70 m in,乳化温度控制在(85±5)℃,搅拌速度为1500 r/m in的反应条件下,可制备出稳定的切片石蜡乳液。     

SA/SBR/PVAc三元地毯胶的研制

介绍了苯丙(SA)乳液、丁苯(SBR)胶乳、聚醋酸乙烯(PVAc)乳液三元地毯胶的制备方法、性能及应用情况。试验表明,该胶具有综合性能好、生产成本低等优点。     

Properties of PHMS‐g‐p [butylacrylate (BA)‐N‐hydroxyl‐methyl acrylamide (NMA)] graft copolymer emulsions

Emulsion graft copolymerization of poly(hydrogenmethylsiloxane) (PHMS) and butyl acrylate (BA) in the presence of functional comonomer N‐hydroxyl‐methyl acrylamide (NMA) was conducted by batch emulsion copolymerization to modify the properties of polysiloxane. Morphology of graft copolymer particles was characterized by transmission electron microscopy. The effect of polymerization method, PHMS content, initiator concentration, and NMA content on stability of emulsion, morphology, size of particle, and rheological properties were investigated. It has been found that stability of emulsion is better by semicontinuous emulsion polymerization than that of batch emulsion polymerization and it increased with increasing PHMS‐NMA concentration. Increasing PHMS concentration and NMA concentration, the particle size and the viscosities increase. The property of resistance to electrolytes of graft copolymer emulsions and swelling property of film were also discussed. Results showed PHMS‐g‐P [butylacrylate (BA)‐N‐hydroxyl‐methyl acrylamide (NMA)] graft copolymer emulsion has good resistance to electrolytes and the water absorption of its film increases with increasing BA‐NMA content grafted onto PHMS. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 2209–2217, 1999     

半连续乳液聚合法制备纳米苯丙乳液

探讨了苯乙烯和丙烯酸丁酯分别作为硬单体和软单体,用半连续乳液聚合工艺制备纳米苯丙乳液的条件;研究了乳化剂类型、配比、用量和乳液固体含量对乳液聚合及乳液涂膜性能的影响,特别是在不同条件下对制得的乳液粒径、黏度、凝聚率、贮存稳定性、钙离子稳定性、涂膜外观、吸水率、光泽度等的影响。结果表明,当乳化剂为SLS/OP复合乳化体系、其物质的量的比为2∶1、乳化剂用量为4%、乳液固体含量为40%时,可以得到纳米尺度的苯丙乳液,聚合反应稳定性和乳液性能良好。     

有机硅改性丙烯酸酯乳液研究进展

从改性方法,改性乳液的形态、结构与性能的关系两方面总结了有机硅改性丙烯酸酯乳液的研究工作。     

硅丙乳液的性能对比研究

通过平行对比试验,研究市场上的硅丙乳液在性能上的差异,并且与外墙纯丙和苯丙乳液中具有代表性的品牌进行对比,得出硅丙与纯丙和苯丙乳液在性能上的差异。     

天然松香改性苯丙乳液的制备及其性能研究

以苯乙烯(St)、甲基丙烯酸甲酯(MMA)、丙烯酸-2-乙基己酯(2-EHA)、丙烯酸-2-羟基乙酯(HEA)和丙烯酸(AA)为反应单体,利用天然松香乳液作为改性剂,通过乳液聚合的方式制备了松香-苯丙复合乳液。研究了乳化剂用量、引发剂用量、松香乳液用量和单体配比对乳液性能的影响。并通过TGA、DLS、TEM对所制备的复合乳液进行了表征。结果表明:当乳化剂用量为单体质量的5%、引发剂用量为单体质量的0.8%、松香乳液用量为单体质量的30%、m(硬单体)∶m(软单体)=2.5∶1时,制得的乳液呈白色泛蓝光,粒径为131 nm。成膜后,漆膜光滑透明,硬度(1H)、耐水性(接触角97.05°)和附着力(1级)等性能良好。     

一种丙烯酸改性乳化环氧树脂的制备与研究

提供了一种制备改性环氧树脂乳液的新方法,以丙烯酸酯类为聚合性单体,加入环氧树脂,利用乳液聚合方法制成了环氧树脂含量达50％的丙烯酸酯改性环氧树脂乳液。通过测试交联度,证明环氧树脂确实参与了聚合反应。同时,还对乳化剂、功能性单体以及环氧树脂含量对乳液稳定性、产品收率、吸水性以及各项力学性能的影响问题进行了研究,得出：丙烯酸对环氧树脂的聚合交联起到了决定性的作用,丙烯酰胺的引入大大提高了乳液的稳定性和力学性能,环氧树脂含量越多产品性能越接近纯环氧树脂,聚合应采用阴、非离子复合乳化剂。     

固体切片石蜡乳液制备新工艺

以固体切片石蜡为原料,采用种子乳液聚合法,利用HLB值理论,以复配型乳化剂制得O/D型加水转化为O/W型石蜡乳液,可降低固体石蜡用量,增加乳化水用量,减少生产成本。考察了乳化剂用量、乳化时间、乳化温度以及搅拌速度等因素对石蜡乳液稳定性和分散性的影响。正交实验结果表明:在乳化剂用量为乳液总量的8.6%,乳化时间90 min,乳化温度控制在80±5℃,搅拌速度1500 r/min的反应条件下,可制备出稳定的固体切片石蜡乳液。     

新型反应性乳化剂

详细介绍了近 10年来发展的新一代反应性乳化剂的结构、特性、选用原则以及在乳液聚合中的应用 ,由此制得的高性能乳液及其下游产品有良好的应用前景