采用聚对苯二甲酸乙二醇酯(PET)与聚对苯二甲酸乙二醇酯聚对苯二甲酸丁二醇酯聚丁二醇共聚酯(CGP)以不同比例共混制得一系列的改性聚酯,研究了共混改性聚酯切片的热性能和流变性能。结果表明,随着CGP加入量的增加,PET/CGP共混体系的玻璃化转变温度Tg,冷结晶峰温度Tc和熔点Tm均有所下降,热稳定性比普通PET低;PET/CGP熔体呈现“切力变稀”现象,其表观黏度明显下降。     

PET/PBT合金性能研究进展

综述了熔融共混制备的聚对苯二甲酸乙二醇酯(PET)/聚对苯二甲酸丁二醇酯(PBT)合金的制备方法、结晶性能、熔融行为、相容性、加工稳定性及合金增强、增韧、阻燃改性的研究进展,并对PET/PBT合金的研究方向进行了展望。     

共聚改性聚酯的等温结晶动力学研究

<正> 一 引 言 高聚物的结晶性能,对于其加工过程及制品性能是十分重要的。因此,高聚物的结晶动力学和热力学至今仍是很重要的的课题。聚对苯二甲酸乙二酯(PET)的结晶动力学研究,已有许多文献作了详细报导。近来,对PET纤维进行了各种目的的改性,其中以改进染色性为目的的共聚改性,是在PET大分子链中引入各种改性剂以破坏其分子链的规整性,或者引入与染料分子有亲和     

聚酯纤维

20073053来自放线菌分离物酯酶生物催化改性的聚对苯二甲酸乙二酯纤维Alish M.…;Biocatalysis and Biotrans formation,2004,22(5/6),p.347(英)研究由放线菌生成的胞外酶改性聚对苯二甲酸乙二酯(PET)纤维,在含有PET纤维和软木酯的介质中分离培养,一种由脂肪族和芳香族各半组成     

PET/iPP复合材料非等温结晶动力学研究

采用示差扫描量热仪(DSC)研究了不同含量PET(聚对苯二甲酸乙二醇酯)纤维的PET/iPP(全同立构聚丙烯)复合材料的非等温结晶特性,考察了降温速率及PET纤维含量对PET/iPP复合材料非等温结晶性能的影响.结果表明,PET纤维可提高iPP的结晶温度.减少结晶时间,增大结晶速率.     

PET改性研究进展及应用现状

综述了聚对苯二甲酸乙二醇酯(PET)改性的最新研究进展,并针对 PET 冲击强度低以及结晶性能差的缺点,分析了其作为工程塑料改性的必要性。PET 的主要改性方法有共混改性、纳米复合材料改性以及添加成核剂、成核促进剂改性等。文中还简单介绍了 PET 的改性机理。最后,对 PET 的生产和应用进行了总结。     

化纤应用及处理

TQ347.720061262高频空气等离子处理导致聚对苯二甲酸乙二酯纤维的表面改性Riccardi Clauolia…;Applied Surface Science,2003,211(1~4),p.386(英)通过高频空气等离子处理对聚对苯二甲酸乙二酯(PET)纤维的化学和物理作表面改性与等离子体的放射参数和本身化学组成的特性有相应     

静电纺丝PET/PVA复合纳米纤维膜的制备及性能

使用聚乙烯醇(PVA)对聚对苯二甲酸乙二醇酯(PET)进行改性,静电纺丝法制备了PET/PVA纳米纤维复合膜,并采用戊二醛蒸气对其交联处理,通过扫描电子显微镜(SEM)观察了纤维形貌,通过热分析(DSC)、水接触角测试及拉伸测试,考察了制品的性能。结果表明,成功制备了力学性能良好、亲水性优异的纳米纤维复合膜。     

PET/MMT纳米复合材料的研究进展

综述了聚对苯二甲酸乙二酯(PET）/蒙脱土(MMT)纳米复合材料的2种制备方法、性能及其表征方法。MMT对PET的改性可以提高PET的阻隔性和结晶速率．并使PET拉伸模量和热变形温度大幅度提高,是目前PET改性的新方向。     

3项无卤阻燃工程塑料成果通过鉴定

<正>近日,北京华腾工程新材料有限责任公司的高性能无卤阻燃聚对苯二甲酸丁二醇酯(PBT)改性工程塑料、高性能无卤阻燃聚对苯二甲酸乙二醇酯(PET)改性工     

共混改性聚酯纤维的吸湿性能研究

利用设计开发的高亲水母粒与常规聚酯进行共混,对共混物的熔融与结晶行为进行了表征。合成的亲水性母粒与常规聚酯共混过程中具有良好的相容性,对不同添加量的改性聚酯的吸湿性进行了测试,建立了共混物表面接触角与吸水率对母粒添加量的关系曲线。选择添加6%的母粒进行试生产,对制备的短纤维进行力学性能、吸湿性能的表征。研究表明:改性聚酯短纤维具有良好的吸湿性能,通过纤维碱减量试验,结合扫描电镜表征手段对改性机制进行了进一步研究。经碱减量处理的改性纤维吸湿性呈下降的趋势,且随着碱浓度增加纤维表面的凹槽增加,分析推测亲水母粒分布在纤维的表面,从而改善了聚酯的吸湿性。     

成核母粒及螺杆组合对玻纤增强PET复合材料性能的影响

采用熔融插层法制备了一种高效成核母粒,研究了该成核母粒对玻璃纤维（GF）增强聚对苯二甲酸乙二醇酯(PET)复合材料性能的影响。结果表明,加入6 %(质量分数,下同)的成核母粒时,GF增强PET复合材料的起始结晶温度比纯PET高24.8 ℃,结晶温度范围比纯PET扩大了66.3 ℃,冷结晶峰基本消失,可在70 ℃的模温下进行注塑;同时探讨了螺杆组合对GF增强PET复合材料性能的影响,结果表明,螺杆前段的剪切太强会降低复合材料的冲击强度,通过优化螺杆组合,制备出综合性能优异的GF增强PET复合材料,其热变形温度为228 ℃,拉伸强度159 MPa,弯曲强度235 MPa,冲击强度101 J/m。     

Effect of high content of carbon black on non-isothermal crystallization behavior of poly(ethylene terephthalate)

With the aid of co-rotating twin screw extruder, poly(ethylene terephthalate) (PET)/carbon black (CB) masterbatches were fabricated through melt-compounding using a separate feeding and metering technique and their homogeneous dispersion morphologies were confirmed by scanning electron microscopy and transmission electron microscopy. Moreover, the ultimate content of CB in the masterbatches was verified via thermogravimetric analysis method. The non-isothermal crystallization process of pristine PET and PET/CB masterbatch were investigated by differential scanning calorimetry and the different methods such as Jeziorny modified Avrami equation, Ozawa equation, and the method developed by Mo were employed to analyze their non-isothermal crystallization kinetics. The results show that CB particles uniformly dispersed in PET matrix act as heterogeneous nucleating agents, while crystallization activation energy (ΔE) of PET/CB masterbatch is much greater than that of virgin PET according to Kissinger formula, Takhor model, and Augis-Bennett model. Whereas, the results obtained from the above mentioned three methods simultaneously demonstrate the addition of CB greatly increases crystallization temperature and crystallinity and accelerates crystallization rate. The results reveal that crystal growth has little effect on the crystallization rate and crystal nucleation dominates the crystallization process of PET/CB masterbatch containing very high CB loading (20 wt%).     

PET负离子纤维的制备及其性能研究

将经质量分数为3％的钛酸酯偶联剂表面修饰过的电气石粉体加入到聚酯(PET)中共混造粒后母粒法纺丝,制备PET负离子纤维。研究了电气石粉体含量对切片热力学性质、纤维结晶性能和力学性能以及负离子性能的影响。结果表明:随着电气石粉体含量的增加,纺丝温度适当降低,纤维结晶度降低,力学性能略有下降,质量分数为2％和4％粉体的纤维的负离子释放分别达到460个／cm3和480个／cm3。     

珍珠负离子复合功能涤纶的制备及其性能

将珍珠改性涤纶母粒与负离子母粒均匀混合后,通过熔融纺丝的方法制备出复合功能纤维,对其进行了灰分测试,并依据GB/T 5009—2003分析了纤维中氨基酸成分,结果显示:珍珠负离子改性涤纶中所含氨基酸种类多达18种,其中对纤维性能影响最为重要的酪氨酸质量分数为0.0012%。在室温条件下,使用空气负离子测试仪测试了复合功能纤维的负离子释放量及远红外线发射率,结果显示:该纤维负离子释放量最大值可达到6000个/cm3,远红外线发射率F(8¹4μm)>0.88。使用扫描电子显微镜观察了珍珠改性涤纶的微观结构,可见超细珍珠粒子较均匀地分布在纤维表面,并与纤维有着紧密的结合。     

载银纳米氧化锌改性PET纤维研究

用T-氨丙基三乙氧基硅烷处理过的载银纳米氧化锌抗菌剂与PET共混制得PET抗菌母粒,通过复合纺丝制得抗菌剂质量分数为1%的皮芯型抗菌PET纤维。结果表明:抗菌剂在抗菌PET纤维中均匀分散,抗菌PET纤维对大肠杆菌、金黄色葡萄球菌的杀菌率均达99%以上;抗菌PET纤维较PET纤维强度和结晶度有所下降,玻璃化转变温度有所提高,熔点和结晶温度变化不大。     

聚酯/碳纳米管共混纤维的抗静电性能

通过采用碳纳米管(CNTs)与聚酯(PET)切片混合制成抗静电母粒,再将抗静电母粒与PET切片共混纺丝制得PET/CNTs共混纤维。用纤维比电阻仪、摩擦式织物静电测试仪测量不同CNTs含量的共混纤维及其织物的抗静电性能。研究结果表明:添加少量的CNTs能明显改善聚酯纤维和织物的抗静电性能,共混纤维的抗静电性能随着CNTs添加量的增加而提高。     

防蚊型聚酯纤维纺丝研究

以普通聚酯(PET)切片为基本原料,添加防蚊母粒进行共混纺丝,研究防蚊母粒在PET切片中的分散性、热稳定性以及纺丝工艺对防蚊PET纤维的影响。结果表明:随着防蚊母粒含量的增加,防蚊PET纤维的强度逐渐降低,断裂伸长率逐渐增加;防蚊母粒具有较高的热稳定性,与PET的相容性很好。使用该防蚊母粒可以制备出性能较好的PET全拉伸丝,很好地满足了下游防蚊蚊帐布的要求。     

小本体聚丙烯共混改性汽车专用料的研制

以小本体聚丙烯（PP）为基料，通过与共聚丙烯9CPP）、聚烯烃弹性体（POE）、硅灰石以及其它且剂共混改性，制得保险杠、门板汽车专用料。检测分析表明，PP／CPP／POE／硅灰石共混体系配方设计合理、工艺路线、参数正确。当PP：CPP：POE：硅灰石质量比为45－48：26－29：19－22：4－6时，共混料完全可以满足汽车保险杠性能要求，当PP：CPP：POE：硅灰石质量比为45－50：27－29：3－6：17－20时，共混料完全可以满足汽车门板性能要求，研究中发现，POE改性PP的综合性能好于EPDM等传统增韧剂；硅灰石也有一定的增韧功能，部分起到了玻璃短纤维的作用。     

分子筛改性PET纤维的制备及其染色性能

采用分子筛、分散剂、偶联剂与PET切片共混纺丝制备分子筛改性PET纤维,讨论了分子筛的处理和加入方法等对改性PET纤维染色性能的影响。结果表明:母粒法纺丝比直接法纺丝好;对于分子筛与分散剂的混合,熔融法好于溶液法。当纤维中分子筛质量分数为3％时,改性PET纤维上染率提高2．45倍,加入适量的偶联剂后,其断裂强度较PET纤维提高约4％,上染率达到79．09％,分子筛在PET基体中分散均匀。