氧化铝赤泥盐酸浸出稀土元素研究

在用盐酸浸出氧化铝赤泥提取氧化钪的过程中,稀土元素镧,铈,钕也一同浸出,进入到浸出液中。研究了拜耳法赤泥盐酸浸出稀土元素镧,铈,钕的过程。研究了浸出温度、酸度、液固比和浸出时间对稀土元素浸出率的影响。研究结果表明,影响稀土浸出率的因素依次是浸出温度,盐酸浓度,配料液固比,和浸出时间。当接近沸点109℃浸出时,镧、铈、钕浸出率提高最快。盐酸酸度在4～5 mol.L-1时,浸出率升高较快,5～7 mol.L-1时,缓慢提高,当超过7 mol.L-1时,镧、铈、钕的浸出率基本不变化。当液固比为4.0时,镧、铈、钕元素的浸出率较低,仅为60%～75%之间,当液固比提高到5.0时,稀土元素的浸出率升高较快。随着浸出时间的延长,氧化稀土的浸出率从60～180 min时,缓慢提高,在180 min时达到最大值,超过180 min后,变化不大。在温度为沸点(109℃),液固比6.0,时间180 min。盐酸浓度7 mol.L-1的条件下浸出,赤泥中La,Ce,Nd的浸出率能达到95%以上。     

α—氯代环烷酸对稀土萃取的研究

本文首次报道了α-氯代环烷酸磺化煤油有机相对稀土La（Ⅱ）、Nd（Ⅱ）、Sm（Ⅱ）、Y（Ⅱ）在盐酸溶液中的萃取性能,结果表明:与相应的环烷酸相比,α-氯代环烷酸萃取稀土的半萃pH约下降0.85个pH单位,对环烷酸的改性有一定意义。     

电感耦合等离子体原子发射光谱法测定铝硅活塞合金中镧铈镨钕钇

采用硝酸和氢氟酸溶解样品,高氯酸冒烟赶氟避免生成氟化稀土沉淀,选择La 333.749nm、Ce 456.236nm、Pr 417.939nm、Nd 406.109nm及Y 371.030nm作为分析线,扣除背景点消除基体干扰,运用干扰系数法克服谱线间干扰,通过基体匹配法配制标准溶液系列消除基体效应的影响,使用电感耦合等离子体原子发射光谱法(ICP-AES)测定铝硅活塞合金中镧、铈、镨、钕和钇。结果表明:镧、铈的测定范围在0.01%~2.00%,镨、钕、钇的测定范围在0.005%~2.00%,校准曲线线性相关系数不小于0.9998。方法中各元素检出限为0.0003%~0.0018%。实验方法用于测定稀土铝合金合成试样中镧、铈、镨、钕和钇,结果的相对标准偏差(RSD,n=6)在0.50%~2.4%之间,加标回收率在94%~105%之间。实验方法用于含有稀土的铝合金标准样品中镧、铈、镨、钕和钇的测定,结果与电感耦合等离子体质谱法(ICP-MS)测定值相吻合,测定的稀土总量RE与认定值也相吻合。     

富集稀土磷酸溶液中稀土的萃取研究

研究了P204从富集稀土磷酸溶液中稀土元素钇、镧、钕的萃取行为,并考察了初始水相中P_2O_5浓度、萃取相比、萃取剂浓度、萃取时间对稀土萃取效果的影响。结果表明,低磷酸浓度、较大相比、较高萃取剂浓度和较长萃取时间有利于萃取稀土,并得到了萃取优化条件:初始水相中P_2O_5浓度10%、萃取相比V_0/V_1=3/1、萃取时间15min、P204浓度30%,在室温下萃取钇、镧、钕3种稀土,单级萃取率均可达到90%以上。     

PMBP和DPSO协萃剂负载泡塑萃取Sc~（3＋）、Y~（3＋）、La~（3＋

本文论述了ＰＭＢＰ和ＤＰＳＯ协萃剂负载于聚醚型聚氨酯泡沫塑料上，萃取微量稀土元素钪、钇、镧、镨和钕的最佳实验条件（萃取剂浓度、温度、酸度）。研究了它们的萃取性能（萃取百分率、分配比、萃取容量），说明它是实用的萃取方法。     

萃取流量参数对稀土槽分布的影响

以国内某稀土厂生产萃取线A的La/CePr/Nd萃取过程为研究对象,通过采集和分析萃取槽各级有机相和水相中稀土元素的含量,明确不同皂化有机相流量、料液流量、酸流量等条件对各级稀土元素含量分布和稀土总量的影响。适当提高皂化有机相流量、料液流量和酸流量,可使水相出口处La的含量较高,从而保证出口产品纯度,但会使55级有机相出口处有机相中Ce组分含量较高,Pr、Nd组分含量较低,增加下一系列分离Pr、Nd的压力。     

新型萃取剂NA萃取中重混合稀土的研究

研究了一种新型酸性磷类萃取剂NA萃取中重混合稀土的性能,探讨了萃取过程中有机相的皂化度、有机相组成、混合稀土料液中杂质含量、料液初始p H对新型萃取剂萃取饱和容量的影响以及反萃过程中反萃酸度对反萃性能的影响,同时还探讨了新型萃取剂的损耗率。试验结果表明,控制混合稀土料液浓度与铝浓度比≥222,与铁浓度比≥2543、有机相的皂化度0.64~0.68 mol·L~(-1)、有机相中磺化煤油∶新型萃取剂=1∶1(新型萃取剂浓度为1.45 mol·L~(-1))及混合稀土料液初始p H=1.2的工艺条件下,萃取过程分相效果好,新型萃取剂的饱和容量大于0.20 mol·L~(-1),比传统萃取剂P507的最佳萃取饱和容量高15%~20%左右,新型萃取剂的损耗率为0.42%~0.45%;反萃过程,采用盐酸作为反萃剂,只要控制盐酸浓度为3.0 mol·L~(-1)时,负载有机相的单级反萃率即可达到98%以上;研究结果表明,该新型萃取剂,具有萃取饱和容量大、溶解损失少、循环使用性能好、反萃酸度低的特点,可以大大降低槽体有机积存量、稀土积存量和酸耗量,减少投资成本,改善工作环境,具有广泛的应用前景。     

P292与Alamine336协同萃取稀土元素

进行了P292与Alamine336所构成混合萃取剂用于萃取稀土试验。结果表明,两种萃取剂混合萃取稀土元素具有正协同作用,当两者按照体积比2︰3进行混合,在相比4︰1,萃取时间3 min的条件下达到了较高的萃取率。对萃取稀土后的负载有机相用1.5 mol/L的盐酸能够将稀土完全反萃,反萃后的有机相与等体积的中性水混合3次后,有机相得到了充分的再生。该试验具有较好的重复性和循环性。     

从废石油裂解催化剂中回收稀土试验研究

研究了从粒度小于20μm、污染较重、不适宜复活的废催化剂中回收稀土。试验结果表明:控制浸出温度60℃、盐酸浓度3.33mol/L、浸出时间3h,废催化剂中91.3%~94.5%的镧、铈被浸出;用50%P507+50%磺化煤油,在温度25℃、萃取相比V_o∶Va=2∶1、萃取时间30min条件下从稀土浸出液中萃取镧铈,镧铈萃取率为94.5%;对负载有机相,采用1.8mol/L盐酸反萃取,控制相比V_o∶V_a=1∶3,稀土镧铈的反萃取率为98.1%;对反萃取液用草酸进行沉淀,沉淀物灼烧,获得工业级氧化镧铈产品。     

三烷基氧化膦萃取稀土元素的研究

研究了国产三烷基氧化膦(混合)对稀土元素La～Gd及Y硝酸盐的萃取.试验了30%三烷基氧化膦(TRPO)-煤油-硝酸体系中水相酸度0.5mol/L～7mol/L范围内轻稀土元素的分配比和相邻两稀土元素的分离因子,测定了TRPO稀土萃合物的组成,探讨了γ射线辐照对稀土元素萃取性能的影响.     

电感耦合等离子体原子发射光谱法测定赤泥浸出液中稀土元素

对赤泥浸出液中稀土元素含量进行测定可以指导研发人员初步判断赤泥中的稀土总量。采用5 mol/L盐酸浸取赤泥中稀土元素镧、铈、镨、钕、钪、钇,并采用电感耦合等离子体原子发射光谱法(ICP-AES)进行了测定。以功率、辅助气流量、分析泵速和积分时间为考察因素,各元素分析谱线的发射强度为考察指标,设计了L₉(3⁴)的正交试验,确定了电感耦合等离子体原子发射光谱仪的最佳工作条件为功率950 W、辅助气流量为0.50 L/min、分析泵速为100 r/min、积分时间为10 s。使用标准加入法绘制校准曲线,消除了基体及杂质元素对待测稀土元素测定的影响。各待测元素校准曲线的线性相关系数均不小于0.999 9,方法中稀土元素镧、铈、镨、钕、钪、钇的检出限在0.002 4～0.013 mg/L之间。按照实验方法测定赤泥浸出液实际样品中稀土元素镧、铈、镨、钕、钪、钇,结果的相对标准偏差(RSD,n=6)为0.21%～1.2%,回收率为96%～114%。采用实验方法和电感耦合等离子体质谱法(ICP-MS)分别对赤泥浸出液中的稀土元素镧、铈、镨、钕、钪、钇进行测定,两种方法的测定结果基本一致。     

Preparing Process of Cerium Acetate and Rare Earth Acetate

Preparing process was presented and the influences of concentration of acetic acid, reaction temperature, the ratio of cerium carbonate and acetic acid, heat preservation time to the yield of cerium acetate were discussed.The crystalline cerium acetate and rare earth acetate such as ( La, Ce, Pr, Nd) (Ac) 3, ( Ce, Pr, Nd) (Ac) 3, ( Pr, Nd, Er,Y) (Ac) 3 and yttrium acetate were prepared under this condition.The shape, structure and composition of the crystals were determined by the methods of SEM, TG-DTA, X-ray diffraction and chemical analysis.The optimum prepared conditions of cerium acetate were described.This prepared process has characteristics such as simple process route, low cost, high yield, good quality, no pollution to environment, etc.     

Extraction and back-extraction behaviors of 14 rare earth elements from sulfuric acid medium by TODGA

The unique physical and chemical properties of rare earth elements lay the foundation for their extensive application. N,N,N',N' Tetra-octyl-3-oxopentanediamide(TODGA) is excellent in its ability of extracting rare earth elements and it is favored for green initiative. In this paper, the extraction and back-extraction of14 rare earth elements by TODGA were studied. Experiments show that in conditions of 6 mol/L sulfuric acid, the extraction temperature of 25 ℃,the phase ratio of 1:1 and 0.04 mol/LTODGA(aviation kerosene as the diluent), the extraction rates of 14 rare earth elements including lanthanum, cerium, praseodymium,neodymium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, and yttrium were 99.00%-99.73%. Mixed with hydrochloric acid and nitric acid(HCl 3.5 mol/L, HNO_30.5 mol/L), the recoveries of the 14 rare earth elements are 91.52%-99.91% when the extraction temperature is 25 ℃ and the ratio is 1:1. The following application is based on the optimum conditions above with practical samples(from the roasting production line of China North Rare Earth High-tech Company Limited) for extraction and back-extraction experiments. Experiments show that TODGA has excellent enrichment effect on 14 rare earth elements, the extraction rates are 91.36%-99.80%, the back-extraction rates are 87.29%-99.64% and the total recoveries are 81.19%-99.44%.     

稀土金属对纯镍铸铁焊条抗热裂性影响的研究

采用HRL-1型热裂纹试验机测试焊缝临界变形速度的方法，研究了常用稀土金属镧、铈、镨、钇及钕在纯镍铸铁焊条冷焊时。对焊缝临界变形速度VBL、焊缝微观组织以及热裂敏感性的影响规律。试验结果表明：焊缝中加入适量的稀土镧、铈、钇和镨。有脱硫、脱磷、去除晶界杂质的作用，每种稀土金属，偏离该最佳值都会使焊缝抗热裂性降低。纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。稀土镧、铈、钇和镨能在一定范围内显著提高焊缝临界变形速度VBL，改善纯镍铸铁焊缝抗热裂性能。     

中钇富镧稀土物料处理流程的选择

将一摩尔物质穿过液—液界面所需的能量对各种金属来说大体上是一个常数。选择设计的流程做到了萃取过程在相间传递的物质摩尔数尽可能减少。对中钇（含Ｙ２Ｏ３２０～４０％）富镧（含Ｌａ２Ｏ３２０～４０％）稀土物料，采用环烷酸进行镧钇和其它稀土的切割分离，再用Ｐ＿（５０７）分离镧钇，其它稀土用Ｐ＿（５０７）分组，后续的单一稀土分离流程可以方便地衔接。不仅流程简捷，技术先进，经济上也最为节省。     

Effects of Rare Earth Elements on Vigor Enhancement of Aged Spinach Seeds

Inthe 1 970s ,asakindofmicroelementfertilizerinagriculture ,rareearthelements (REEs)wereusedtoachieveanotablecropyieldinChina[1～ 3] .Alargenumberofexperimentsindicatedthatthegerminationrateandvigorofseedswereincreasedbythetreatmentwithrareearthelements ,andthegrowthofseedlingswasalsopromoted .Hongetal.provedthatsoakingseedswithLa3+ ,andCe3+ couldacceleratetheger minationofriceseeds ,greatlypromoteseedvigor ,in creasetherespirationofgerminatedseeds ,obviouslyactivatesomehydrolyticenzymessuch…