Cold-brittleness threshold and strength of low-carbon steel with chromium

Conclusions The effect of chromium in increasing the strength of heat treated steel under severe loading conditions conforms with the variation of the cold-brittleness threshold and plasticity of the material. With a high reserve plasticity (carbon concentration up to 0.1%) the addition of chromium within the limits investigated greatly increases the strength. With a carbon concentration of 0.3% the addition of up to 1% Cr also increases the strength and lowers the cold-brittleness threshold; further alloying raises the cold-brittleness threshold and induces negligible strengthening.All-Union Correspondence Mechanical Institute. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 9, pp. 70–72, September, 1969.     

拉伸加工中蓝脆与氢脆的产生及预防

通过油盖及端盖两种拉伸件的加工实例,分别分析了其在生产中出现拉裂缺陷的原因,由此介绍了拉伸加工中蓝脆与氢脆的产生并分别提出了各自的解决及预防措施。     

Research Progress on Brittleness of Iridium

由于铱的高熔点、优异的高温强度和抗腐蚀性能,是能够在极端恶劣条件下使用的唯一金属。虽然铱具有面心立方晶体结构,但它的断裂模式却为脆性断裂（穿晶脆性断裂和沿晶脆性断裂的混合断裂模式）。自从20世纪60年代人们发现了铱的异常脆性断裂行为以来,就展开了大量的研究工作。然而至今,关于铱的致脆机制仍未被澄清。本文综述了铱可能的致脆机制：杂质致脆、本征脆性和特殊缺陷结构致脆,讨论了铱变形与失效机制的研究现状,并对未来研究的重点与手段进行了展望     

Pickling and Plating Brittleness of Steel

The permalloy composition of 80% Ni, 20% Fe can be deposited from a Watts type bath using a mixture of Ni and Fe sulphates. Improvements in the bath have been made by adding thiourea to obtain better control of the composition by making the bath operation less sensitive to concentration and temperature effects. Stress has been shown to be important in determining the magnetic properties and methods of controlling this parameter are outlined.     

改善凝石混凝土脆性的试验研究

针对混凝土高脆性的不足,重点研究了不同配合比、掺合料和外加剂对凝石混凝土脆性的影响.通过改进掺合料、优化配合比和添加外加剂,在抗压强度不降低的情况下,改善了凝石混凝土的内部微观结构,降低混凝土的弹性模量,在一定程度上改善了材料的脆性.     

E级钢的回火脆性研究

E级钢( ZG25 MnCrNiMo)是货车车钩用材料.由于该钢具有高温回火脆性,在实际生产中冲击性能经常不合格,本文主要针对E级钢的回火脆性进行简要分析,提出解决方案.     

改善凝石混凝土脆性的试验研究

针对混凝土高脆性的不足，重点研究了不同配合比、掺合料和外加剂对凝石混凝土脆性的影响。通过改进掺合料、优化配合比和添加外加剂，在抗压强度不降低的情况下，改善了凝石混凝土的内部微观结构，降低混凝土的弹性模量，在一定程度上改善了材料的脆性。     

钛腐蚀氢脆及其防止措施

概述了钛制化工设备发生腐蚀氢脆原因、条件，并对若干事例进行解析，提出了防止腐蚀氢脆的对策。     

高锰钢低温脆性与微观断口形貌

对水韧状态及硬化状态的ZGMn13钢进行了系列冲击试验,结果表明:高锰钢冲击韧性随试验温度下降而降低,有明显的低温脆性。高锰钢微观断口有:韧窝断口、塑性沿晶断口、解理断口及混合断口。     

渗硼层脆性判据K的物理本质

从实验和理论上对显微硬度压痕结合声发射测量渗硼层脆性的合理性及其脆性判据Ｋ的物理意义进行了讨论。Ｋ值可以反映渗硼层显微压痕裂纹长度随负荷增加的变化率，因而可以表征渗硼层的脆性。根据断裂力学可以导出入与Ｇ＿（ＩＣ）之间存在如下关系：Ｋ＝β（Ｇ＿Ｉ－Ｇ＿（ＩＣ））。Ｋ值间接反映了渗硼层的断裂韧性，可以作为定量评价渗硼层本质脆性的力学参量。     

气体渗碳淬火件的氢脆问题