Cure kinetics of epoxy/MWCNTs nanocomposites: Nonisothermal calorimetric and rheokinetic techniques

Nonisothermal calorimetric and isothermal rheokinetic analyses were used to study cure kinetics of epoxy/anhydride systems containing very low concentration of pristine and amine‐functionalized multiwalled carbon nanotubes (MWCNTs). Isoconversional methods were applied in calorimetric modeling of cure kinetics. E _α vs. α dependency and autocatalytic nature of curing were identified for both types of nanocomposites by isoconversional models. Fall in E _α value from 90 to 82.5 kJ mol^?1 thanks to amine functionalization (with E _α of blank epoxy/anhydride of 80.3 kJ mol^?1) was indicative of high potential of nanocomposites to cure at low concentration of functionalized MWCNTs (0.1 g with respect to 100 g of resin). Times of gelation and vitrification of epoxy were measured using storage and loss modulus data provided by isothermal rheokinetic analysis, showing a drop upon attachment of amine groups to MWCNTs. In complete agreement with nonisothermal calorimetric studies, variation of storage and loss modulus of nanocomposites confirmed hindered/accelerated cure devoted to pristine/amine‐functionalized MWCNTs. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134 , 45221.     

Cure behavior and thermal stability analysis of multiwalled carbon nanotube/epoxy resin nanocomposites

As‐received multiwalled carbon nanotubes (MWCNTs) were first treated by a 3 : 1 (v/v) mixture of concentrated H₂SO₄/HNO₃ and further functionalized by ethylenediamine/dicyclohexylcarbodiimide/tetrahydrofuran solution. MWCNT/epoxy nanocomposites were prepared. Their cure behaviors were investigated by dynamic differential scanning calorimetry. Quantitative analysis of the activation energy as a function of the degree of curing was carried out by the Flynn‐Wall‐Ozawa method. The fitted multiple regression equations for values of the activation energy of different systems were obtained. MWCNTs have the retardation effect on the cure reaction of epoxy resin, while the functional groups on the surface of amine‐modified MWCNTs could accelerate the cure reactions. Thermal stability was studied by thermogravimetric analysis. The filling of amine‐modified MWCNTs is beneficial to lower the cure activation energy and improve thermal stability of the nanocomposite. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

The effects of triethylenetetramine grafting of multi‐walled carbon nanotubes on its dispersion,filler‐matrix interfacial interaction and the thermal properties of epoxy nanocomposites

This study describes the influence of triethylenetetramine (TETA) grafting of multi‐walled carbon nanotubes (MWCNTs) on the dispersion state, interfacial interaction, and thermal properties of epoxy nanocomposites. MWCNTs were first treated by a 3:1 (v/v) mixture of concentrated H₂SO₄/HNO₃, and then TETA grafting was performed. Chemically grafted MWCNT/bisphenol‐A glycidol ether epoxy resin/2‐ethyl‐4‐methylimidazole nanocomposites were prepared. TETA grafting could establish the connection of MWCNTs to the epoxy matrix and transform the smooth and nonreactive MWCNT surface into a hybrid material that possesses the characteristics of both MWCNTs and TETA, which facilitates homogeneous dispersion of MWCNTs and improves nanotube‐epoxy interfacial interaction. Therefore, the impact property, glass transition temperature, thermal stability, and thermal conductivity of epoxy nanocomposites are enhanced. POLYM. ENG. SCI., 2009. © 2009 Society of Plastics Engineers     

Microwave‐assisted synthesis and characterization of polyimide/functionalized MWCNT nanocomposites containing quinolyl moiety

Polyimide‐MWCNT nanocomposites were prepared by the reaction of a heterocyclic diamine monomer of bis(4‐amino‐3,5‐dimethylphenyl)‐2‐chloro‐3‐quinolylmethane (BACQM), pyromellitic dianhydride (PMDA) with unmodified MWCNT (MWCNT), acid‐functionalized MWCNT (acid‐MWCNT) or amine‐functionalized MWCNT (amine‐MWCNT) using microwave irradiation as well as by the conventional method. The structure of the monomer was confirmed by FTIR, ¹H‐NMR, and ¹³C‐NMR spectral techniques. The glass transition temperature (T_g) of the MWCNTs/polyimide nanocomposite was found to be higher than that of the unfilled polyimide system. The T_g's of both systems were higher when prepared with the microwave method than the conventional synthesis. The T_g's of the nanocomposites using acid and amine functionalized MWCNTs are greater than 300°C, in both methods. This is attributed to the presence of hydrogen bond and strong covalent bond in both the acid‐MWCNT/polyimide and amine‐MWCNT/polyimide systems. The morphological studies of the nanocomposites synthesized using microwave irradiation show that a distinct MWCNT nanofibrillar network is formed in the matrix when MWCNT or acid‐MWCNT is used. A homogeneous morphology, without distinct nanotube domains is seen when the amine‐MWCNT is covalently linked to the polymer. POLYM. COMPOS., 37:2417–2424, 2016. © 2015 Society of Plastics Engineers     

Enhanced Thermal Conductivity of Epoxy Composites with MWCNTs/AlN Hybrid Filler

To further improve the thermal conductivity of epoxy resin, the multi-walled carbon nanotube/aluminum nitride (MWCNTs/AlN) hybrid filler was employed to prepare thermal conductivity MWCNTs/AlN/epoxy composite by casting process, and the silane coupling reagent of γ-glycidoxy propyl trimethoxy silane(KH-560) was also used to functionalize the surface of MWCNTs and/or AlN. Results revealed that, the thermal conductivity of epoxy resin was improved remarkably with the addition of MWCNTs/AlN hybrid filler, a higher thermal conductivity of 1.04 W/mK could be achieved with 29 wt% MWCNTs/AlN hybrid filler (4 wt% MWCNTs +25 wt% AlN), about 5 times higher than that of native epoxy resin. And the epoxy composite with 29 wt% MWCNTs/AlN hybrid filler possessed better thermal conductivity and mechanical properties than those of single 5 wt% MWCNTs or 40 wt% AlN. The thermal decomposition temperature of MWCNTs/AlN/epoxy composite was increased with the addition of MWCNTs/AlN hybrid filler. For given filler loading, surface treatment of MWCNTs and/or AlN by KH-560 exhibited a positive effect on the thermal conductivity of epoxy composite.     

Investigation of cure kinetics in epoxy/multiwalled carbon nanotube nanocomposites

With the increased interest in thermoset resin nanocomposites, it is important to understand the effects of the material on nanoscale characteristics. In this study, a curing reaction of an epoxy resin, which contained 0.25, 0.50, or 1.00 wt % of multiwalled carbon nanotubes (MWCNTs), at different heating rates was monitored by differential scanning calorimetry; cure kinetics were also evaluated to establish a relationship between crosslinking (network formation) and mechanical properties. MWCNT concentrations above 0.25 wt % favored crosslinking formation and decreased the activation energy (E_a) in the curing reaction. Examination of the kinetic mechanism suggests that the MWCNT locally restricted the spatial volume and favored the formation of nodular morphology in the resin, especially for high MWCNT concentrations. The MWCNT exhibited some entanglement in the matrix, which hindered a more pronounced effect on the mechanical properties. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 39857.     

Preparation and thermal properties of bio‐based gallic acid epoxy/carbon nanotubes composites by cationic ring‐opening reaction

In order to prepare the bio‐based polymeric materials, a gallic acid epoxy resin (GA‐ER) is synthesized by using biodegradable gallic acid, and the nanocomposites of GA‐ER/glycidyl methacrylate (GMA)/multiwalled carbon nanotubes (MWCNTs) were prepared by dual hybrid cationic ring‐opening reaction. Differential scanning calorimetry (DSC) results show that the curing reaction temperature of the nanocomposites is between 150 and 225°C. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results suggest that MWCNTs are homodispersing in the GA‐ER/GMA matrix when the MWCNTs content is not more than 1.0 wt%. The glass transition temperature of the nanocomposite with 0.5 wt% MWCNTs is 9.3°C higher than that of pure resin system. The initial thermal degradation temperature and degradation activation energies E_a of the nanocomposite with 1.0 wt% MWCNTs is 10°C and 68.6 kJ/mol higher than that the pure resin system, respectively. POLYM. COMPOS., 37:3093–3102, 2016. © 2015 Society of Plastics Engineers     

Thermal conductivity and dynamic mechanical property of glycidyl methacrylate‐grafted multiwalled carbon nanotube/epoxy composites

The well dispersed multiwalled carbon nanotube (MWCNT)/epoxy composites were prepared by functionalization of the MWCNT surfaces with glycidyl methacrylate (GMA). The morphology and thermal properties of the epoxy nanocomposites were investigated and compared with the surface characteristics of MWCNTs. GMA‐grafted MWCNTs improved the dispersion and interfacial adhesion in epoxy resin, and enhanced the network structure. The storage modulus of 3 phr GMA‐MWCNTs/epoxy composites at 50°C increased from 0.32 GPa to 2.87 GPa (enhanced by 799%) and the increased tanδ from 50.5°C to 61.7°C (increased by 11.2°C) comparing with neat epoxy resin, respectively. Furthermore, the thermal conductivity of 3 phr GMA‐MWCNTs/epoxy composite is increased by 183%, from 0.2042 W/mK (neat epoxy) to 0.5781 W/mK. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Effects of amino‐functionalized carbon nanotubes on the properties of amine‐terminated butadiene–acrylonitrile rubber‐toughened epoxy resins

Amino‐functionalized multiwalled carbon nanotubes (MWCNT‐NH₂s) as nanofillers were incorporated into diglycidyl ether of bisphenol A (DGEBA) toughened with amine‐terminated butadiene–acrylonitrile (ATBN). The curing kinetics, glass‐transition temperature (T_g), thermal stability, mechanical properties, and morphology of DGEBA/ATBN/MWCNT‐NH₂ nanocomposites were investigated by differential scanning calorimetry (DSC), thermogravimetric analysis, a universal test machine, and scanning electron microscopy. DSC dynamic kinetic studies showed that the addition of MWCNT‐NH₂s accelerated the curing reaction of the ATBN‐toughened epoxy resin. DSC results revealed that the T_g of the rubber‐toughened epoxy nanocomposites decreased nearly 10°C with 2 wt % MWCNT‐NH₂s. The thermogravimetric results show that the addition of MWCNT‐NH₂s enhanced the thermal stability of the ATBN‐toughened epoxy resin. The tensile strength, flexural strength, and flexural modulus of the DGEBA/ATBN/MWCNT‐NH₂ nanocomposites increased increasing MWCNT‐NH₂ contents, whereas the addition of the MWCNT‐NH₂s slightly decreased the elongation at break of the rubber‐toughened epoxy. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40472.     

A study on rheological behavior of MWCNTs/epoxy composites

Rheological behaviors of multiwalled carbon nanotubes (MWCNTs)/epoxy composites with various MWCNT contents were investigated by using a time sweep and frequency sweep experiment with oscillatory rheometry. The functional groups on the acid-treated MWCNTs were investigated by fourier transfer-infrared spectroscopy (FT-IR). The composites containing acid-treated MWCNTs exhibited faster gel time than pure epoxy resins. The storage (G′) and loss (G″) moduli of the composites showed solid-like behavior owing to interaction between the MWCNTs and the epoxy resins. The 1.0 wt% MWCNT composites had the highest crosslinking activation energy (E_c) due to good dispersion and strong interfacial bonding. These results imply that three-dimensional crosslinking might take place among the hydroxyl group in epoxy resins and the carbonyl or hydroxyl group in acid-treated MWCNTs.     

Cure Kinetics and Thermal Properties of Octa(aminophenyl)-POSS/Bromobisphenol A Epoxy Resin Nanocomposites

The tetrabromobisphenol A epoxy resin (TBBPAER) was synthesized and Octa(aminophenyl) polyhedral oligomeric silsesquioxane (OAP-POSS) was used as a curing reagent of TBBPAER. The cure kinetics, the glass transition temperature, and the flame resistance of OAP-POSS/TBBPAER nanocomposites were investigated. The results show that the curing reaction could be described by the autocatalytic ?esták-Berggren (S-B) model. The average activation energy E _a is 129.59 KJ/mol, the maximal mechanical loss temperature (T _p) is 166°C, when the molar ratio (N _s) of amino group to epoxy group is 0.5. The oxygen index for fire resistance is 46 ～ 49 for different amounts of OAP-POSS.     

Cure behavior of epoxy/MWCNT nanocomposites: The effect of nanotube surface modification

The effect of carboxyl and fluorine modified multi-wall carbon nanotubes (MWCNTs) on the curing behavior of diglycidyl ether of bisphenol A (DGEBA) epoxy resin was studied using differential scanning calorimetry (DSC), rheology and infrared spectroscopy (IR). Activation energy (E_a) and rate constants (k) obtained from isothermal DSC were the same for the neat resin and fluorinated MWCNT system (47.7 and 47.5 kJ/mol, respectively) whereas samples containing carboxylated MWCNTs exhibited a higher activation energy (61.7 kJ/mol) and lower rate constant. Comparison of the activation energies, rate constants, gelation behavior and vitrification times for all of the samples suggests that the cure mechanisms of the neat resin and fluorinated sample are similar but different from the carboxylated sample. This can be explained by the difference in how the fluorinated nanotubes react with the epoxy resin compared to the carboxylated nanotubes. Although the two systems have different reaction mechanisms, both systems have similar degrees of conversion as calculated from the infrared spectroscopic data, glass transition temperature (T_g), and predictions based on DSC data. This difference in reaction mechanism may be attributed to differences in nanotube dispersion; the fluorinated MWCNT system is more uniformly dispersed in the matrix whereas the more heterogeneously dispersed carboxylated MWCNTs can hinder mobility of the reactive species and disrupt the reaction stoichiometry on the local scale.     

Influence of MWCTs and nanometal oxide/MWCTs hybrids on the thermal conduction of their acrylic-based nanocomposites

In this study, acrylic-based nanocomposites containing different contents of multi-walled carbon nanotubes (MWCNTs) and metal oxide nanoparticles (i.e., TiO₂, CuO and Fe₂O₃) were fabricated by solvent mixing method. The thermal conductivity of these samples was evaluated. The results indicated that the thermal conductivity of all fabricated samples was significantly improved even at small loading of MWCNTs. It was found that the thermal conductivity was enhanced by increase in MWCNTs content up to 5 wt%. Similarly, the metal oxide nanoparticles caused up to 75 % increment in thermal conductivity at 1.5 wt% of their loading in acrylic film. Contrary to expectations, the thermal conductivity of acrylic film was more increased by nanometal oxides (i.e., TiO₂, CuO and Fe₂O₃) than MWCNTs. The effect of hybridizing of nanometal oxide particles (1.5 wt%) and MWCNTs (1.5 wt%) on thermal conduction was investigated as well. It was found that hybridizing improved thermal conductivities by about 85, 94 and 97 % for Fe₂O₃, TiO₂ and CuO, respectively. Finally, the effects of TiO₂ pigment and CaCO₃ extender on the thermal conductivity of acrylic polymer and nano-TiO₂ acrylic composites were studied. It was found that TiO₂ could increase considerably thermal conduction of its acrylic films and acrylic nanocomposites.     

Styrene butadiene rubber/epoxidized natural rubber/carbon filler nanocomposites: microstructural development and cure characterization

Microstructural development of elastomeric nanocomposites based on (50/50 wt%) styrene butadiene rubber (SBR) and epoxidized natural rubber (50 mol% epoxidation, ENR50) as the rubber matrix including two types of carbon fillers, carbon black (CB) and functionalized multiwall carbon nanotube (NH₂-MWCNT), which were prepared through melt mixing, was studied. The results from FTIR analysis show that there is interaction between functional groups on MWCNT surface and the rubber chains. The AFM analysis also indicates good dispersion of filler particles in the rubber phases. FESEM images from cryo-fractured surface of samples have revealed that nanotubes were rarely pulled out of matrix and their diameter increased, resulting from good interaction between MWCNTs and rubber chains. The DMA results confirm good interfacial interaction between them. Furthermore, the reduced difference between the two T_gs of phases (ΔT_g) shows that the incorporation of 3 phr MWCNT into the blend leads to increment in rubber phase compatibility but at higher MWCNT content (5 phr) due to lower Mooney viscosity of SBR phase, MWCNTs tend to remain in this phase. The bound rubber was adopted to characterize the polymer–filler interaction, showing that bound rubber content has an increasing trend with increasing in fillers content. The cure rheometric studies reveal that MWCNTs accelerate the cure process due to the presence of amine groups on the nanotube surface. In addition, the mechanical properties of samples show an increasing trend by increasing nano-filler content.

     

Synthesis of New PI/MWCNT Containing Sulfone Groups via In Situ Polymerization: Study on Thermal,Electrical, and Optical Properties

New series of polyimide (PI) nanocomposites reinforced with three different amounts of multiwalled carbon nanotubes (MWCNT; 0.5, 1, and 3 wt%) were prepared by casting, evaporation and thermal imidization. Homogeneous dispersion of MWCNT in PI matrix was investigated by transmission electron microscopy. The effects of MWCNT on the thermal properties of the PI were investigated by thermogravimetric analysis. The results showed that the thermal stability of the nanocomposites enhanced with the increasing MWCNTs content. The resultant PI/MWCNT nanocomposites were electrically conductive with significant conductivity enhancement at 3 wt% MWCNT, which is favorable for many practical uses.     

Effect of Phenol/Formaldehyde Stoichiometry on the Modification of Epoxy Resin Using Epoxidized Novolacs

ABSTRACT

Unmodified epoxy resins based on bisphenol A exhibit brittleness and low elongation after cure. This article reports the results of a study for improving the properties of epoxy resin by blending with suitable thermosets. Hybrid polymer networks of diglycidyl ether of bisphenol A (DGEBA) resin with epoxidized phenolic novolac resins (EPN) containing phenol and formaldehyde in different stoichiometric ratios were prepared by physical blending. The modified epoxy resins were found to exhibit improved mechanical and thermal properties compared to the neat resin. DGEBA resins containing 2.5 to 20 wt% of epoxidized novolac resins (EPN) prepared in various stoichiometric ratios (1:0.6, 1:0.7, 1:08, and 1:0.9) between phenol and formaldehyde were cured using a room temperature amine hardener. The cured samples were tested for mechanical properties such as tensile strength, modulus, elongation, and energy absorption at break. All the EPNs are seen to improve tensile strength, elongation, and energy absorption at break of the resin. The blend of DGEBA with 10 wt% of EPN-3 (1:0.8) exhibits maximum improvement in strength, elongation, and energy absorption. EPN loading above 10 wt% is found to lower these properties in a manner similar to the behavior of any filler material. The property profiles of epoxy–EPN blends imply a toughening action by epoxidized novolac resins and the extent of modification is found to depend on the molar ratio between phenol and formaldehyde in the novolac.     

Preparation and properties of multiwalled carbon nanotube/epoxy‐amine composites

Different amounts of multiwalled carbon tubes (MWCNTs) were incorporated into an epoxy resin based on diglycidyl ether of bisphenol A and both epoxy precursor and composite were cured with 4,4′‐diamino diphenyl sulfone. Transmission and scanning electron microscopy demonstrated that the carbon nanotubes are dispersed well in the epoxy matrix. Differential scanning calorimetry measurements confirmed the decrease in overall cure by the addition of MWCNTs. A decrease in volume shrinkage of the epoxy matrix caused by the addition of MWCNTs was observed by pressure–volume–temperature measurements. Thermomechanical and dynamic mechanical analysis were performed for the MWCNT/epoxy composites, showing that the T_g was slightly affected, whereas the dimensional stability and stiffness are improved by the addition of MWCNTs. Electrical conductivity measurements of the composite samples showed that an insulator to conductor transition takes place between 0.019 and 0.037 wt % MWCNTs. The addition of MWCNTs induces an increase in both impact strength (18%) and fracture toughness (38%) of the epoxy matrix with very low filler content. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Mechanical and thermal properties of epoxy-POSS reinforced-(biphenyl diol formaldehyde/epoxy hybrid resin) composites

To enhance the properties of epoxy composites, the biphenyl diol formaldehyde resin (BPFR) and glycidyloxypropyl polyhedral oligomeric silsesquioxane (G-POSS) were synthesized and used for modification of fiber-glass reinforced composites of epoxy resin (ER). The BPFR was employed to cure epoxy resin with different G-POSS contents and the laminates of fiber-glass reinforced hybrid composites prepared from BPFR, ER and G-POSS. The dynamic mechanical properties, thermal properties, mechanical and electrical properties of the hybrid composites were characterized by dynamic mechanical analyzer, thermogravimetric analyzer and electroproperty detector. The results showed that the T _g of the composites is increased with the addition of G-POSS. When the content of G-POSS is 5 wt%, the tensile and impact strength of the hybrid composites are 249.87 MPa and 63.83 kJ/m², respectively, which are all 30 % higher than those of non-added composites. At G-POSS content of 7 wt%, T _g of the material is 9.6 °C higher than pure BPFR/ER composite, and the initial decomposition temperature, T _id, is enhanced by about 29 °C. Dielectric constant, ε, and dielectric loss, tanδ, of the hybrid composites are between 0.53–0.7 and between 0.004–0.012, respectively.     

Improved impact strength of epoxy by the addition of functionalized multiwalled carbon nanotubes and reactive diluent

Multiwalled carbon nanotubes (MWCNTs), both oxidized and amine functionalized (triethylenetetramine—TETA), have been used to improve the mechanical properties of nanocomposites based on epoxy resin. The TGA and XPS analysis allowed the evaluation of the degree of chemical modification on MWCNTs. Nanocomposites were manufactured by a three‐roll milling process with 0.1, 0.5, and 1.0 wt % of MWCNT–COOH and MWCNT–COTETA. A series of nanocomposites with 5.0 wt % of reactive diluent was also prepared. Tensile and impact tests were conducted to evaluate the effects of the nanofillers and diluent on the mechanical properties of the nanocomposites. The results showed higher gains (258% increase) in the impact strength for nanocomposites manufactured with aminated MWCNTs. Optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to investigate the overall filler distribution, the dispersion of individual nanotubes, and the interface adhesion on the nanocomposites. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42587.     

Low percolation threshold and high electrical conductivity in melt‐blended polycarbonate/multiwall carbon nanotube nanocomposites in the presence of poly(ε‐caprolactone)

This study focuses on the electrical properties of polycarbonate (PC)/poly(ε‐caprolactone) (PCL)‐multiwall carbon nanotube (MWCNT) nanocomposites. MWCNTs were incorporated into thermoplastic PC matrix by simple melt blending using biodegradable PCL based concentrates with MWCNT loadings (3.5 wt%). Because of the lower interfacial energy between MWCNT and PCL, the nanotubes remain in their excellent dispersion state into matrix polymer. Thus, electrical percolation in PC/PCL‐MWCNT nanocomposites was obtained at lower MWCNT loading rather than direct incorporation of MWCNT into PC matrix. AC and DC electrical conductivity of miscible PC/PCL‐MWCNT nanocomposites were studied in a broad frequency range, 10¹?10⁶ Hz and resulted in low percolation threshold (p_c) of 0.14 wt%, and the critical exponent (t) of 2.09 from the scaling law equation. The plot of logσ_DC versus p^?1/3 showed linear variation and indicated the existence of tunneling conduction among MWCNTs. At low MWCNT loading, the influence of large polymeric gaps between conducting clusters is the reason for the frequency dependent electrical conductivity. Transmission electron microscopy and field emission scanning electron microscopy showed that MWCNTs were homogeneously dispersed and developed a continuous interconnected network path throughout the matrix phase and miscibility behavior of the polymer blend. POLYM. ENG. SCI., 54:646–659, 2014. © 2013 Society of Plastics Engineers