化学镀银织物电磁屏蔽效能及透湿透气性能研究

为研究化学镀银对织物性能的影响,采用葡萄糖作还原剂对涤纶织物进行镀银,借助扫描电镜、网络分析仪、织物透湿仪、织物透气量仪等,对镀银织物的表面镀层形貌、织物的电磁屏蔽效能,以及织物的透湿、透气性能进行测试分析。结果表明:随着增重率的变大,织物的屏蔽效能增加,当增重率达到37%时,电磁屏蔽效能增加不明显,故应根据需要合理选择面料的镀层厚度;研究还发现镀层厚度对织物的透湿、透气性有影响。     

化学镀银涤纶织物的制备及其性能

利用化学镀方法制备镀银电磁屏蔽涤纶织物.分别采用场发射电镜( FE-SEM)、电子能谱(EDS)和X射线衍射(XRD)表征镀层的表面形貌、成分和结晶情况;考察了织物的厚度、增重率、耐摩擦色牢度、表面电阻、抗静电性、拉伸断裂强力、断裂伸长率、刚柔性、悬垂性以及透气性.结果表明:镀层为高纯度立方面心结构的单质银;化学镀银后...     

涤纶针织物银-镍-铜三层化学镀研究

采用化学镀技术,实现了涤纶针织物表面镀银-镍-铜,借助SEM、EDX和TG对镀层表面形貌、成分以及热性能进行了测试分析,并测试了化学镀织物的电磁波屏蔽效能和拉伸性能.结果表明,涤纶针织物化学镀银-镍-铜后热分解温度有所下降:镀银-镍-铜织物的电磁波屏蔽效能明显好于镀银-镍双层织物和镀镍织物;镀层的致密性和金属成分对电磁波屏蔽效能影响显著;化学镀涤纶针织物的应力-应变曲线同时具有金属和涤纶长丝的拉伸特性.主要受金属镀层厚度的影响.     

等离子体处理改善织物化学镀银质量的研究

使用扫描电镜对比了未处理和处理后进行化学镀银的织物的表面形态,发现经过等离子体处理过的涤纶织物化学镀层光洁度好,镀层均匀,耐磨性有所提高,且平均电磁波屏蔽效能优于未经等离子体处理的织物.     

化学镀银涤纶织物的制备及其导电性能

以葡萄糖为还原剂对涤纶织物进行化学镀银整理。采用EDS(能谱仪)和SEM(扫描电镜)分别表征镀层的化学元素成分和表面形貌,对镀银后织物的增厚增重率、耐摩擦性和表面方阻进行测试分析,并探讨了硝酸银和葡萄糖质量浓度、pH值、分散剂对涤纶织物增重率和表面方阻的影响。结果表明,采用2.4 g/L NaOH,pH值12.2,10g/LAgNO3,8g/L葡萄糖,乙醇60mL/L工艺的镀银织物方阻最小,为0.02Ω/cm2。     

涤纶织物化学镀镍的研究

采用化学镀镍技术对涤纶织物进行了酸性、碱性镀镍以及着色处理。借助SEM、X射线能谱仪对化学镀镍织物表面结构进行了表征和分析。测试了涤纶织物化学镀镍前后服用性能的变化，并对导电性和电磁波屏蔽性能进行了测试。结果表明，镀层均匀程度对电磁波屏蔽性能影响较大。随着镀镍层厚度的增加，电磁波屏蔽效能增速先增大后减小。酸性镀镍织物的电磁波屏蔽性能优于碱性镀镍织物。镀层织物经着铜色处理后，电磁波屏蔽性能有明显提高。当质量增加70％时，化学镀涤纶织物电磁屏蔽性能较好，同时服用性能变化不明显。     

涤纶织物镍-铜双层化学镀研究

采用化学镀技术进行涤纶织物表面镍-铜双层镀，并借助SEM、EDX和TG对镀层表面形貌、成分以及热性能进行了分析，还对化学镀织物的电磁波屏蔽、吸音和拉伸性能进行了测试。结果表明，涤纶织物化学镀镍—铜后热分解温度有所下降；当增重率小于一定值时，电磁波屏蔽性能主要受镀层均匀性影响；当增重率大于一定值后，电磁波屏蔽效能主要受镀层致密性和金属成分影响。化学镀织物的吸声性能与原织物基本相同，但在高频波段，吸声系数略大于原织物。化学镀织物的拉伸曲线同时具有金属和纤维的拉伸特性，主要受金属镀层厚度的影响。     

基于空心微珠的功能织物开发

为了制备具有电磁波屏蔽、热防护功能的红外防伪面料，使用化学镀镍、镀铜和镀银等空心微珠分别对涤棉织物进行涂层整理，试验结果表明，当金属化空心微珠在涂层剂中形成三维导电网络结构时，电磁波屏蔽性能最好，其中葡萄糖镀银微珠屏蔽效果好于酒石酸钾钠镀银微珠，而且随着添加量的增加，电阻率逐渐降低，屏蔽效能增大。当添加量相同时，涂层织物热防护性能为：未镀空心微珠涂层织物〉葡萄糖镀银微珠涂层织物〉镀铜微珠涂层织物〉镀镍微珠涂层织物。     

封端阳离子水性聚氨酯在有机硅柔软剂中的应用

以葡萄糖为还原剂在涤纶织物上进行化学镀银。采用EDS、SEM分别表征镀层的化学元素成分和表面形貌,对镀银后织物的增厚增重率、断裂强力、断裂伸长率、耐摩擦性和表面方阻进行测试分析,并探讨了硝酸银和葡萄糖质量浓度、pH值、分散剂对涤纶织物增重率和表面方阻的影响。结果表明,采用2.4 g/L NaOH,pH值12.2,10 g/L AgNO3,8 g/L葡萄糖,70 mg/L聚乙二醇,乙醇60 ml/L工艺镀银织物的方阻最小,为0.02 Ω/cm2。     

染整前处理工艺对银纤维屏蔽织物的影响及原因

<正>电磁辐射已成为继空气污染、水污染、噪声污染之后的第4大污染源。人们越来越关注电磁辐射对人类的危害,伴随产生了涂层类、金属纤维类和镀银纤维类的电磁屏蔽材料。在各种电磁屏蔽材料中,镀银纤维具有镀层均匀性好、致密度高、电磁屏蔽效能好等优点,镀银纤维屏蔽织物具有质地轻薄、柔软透气、耐蚀抗菌、防电磁波效果好等优点。因此,镀银纤维屏蔽织物越来越受到人们的青睐。     

Hydroentangling knitted fabrics for improving abrasion resistance

Abstract

Hydroentangling is used as the mechanical finish to improve abrasion resistance of knitted fabrics. The hydroentangling process successfully reduced the amount of loose surface fibers and led to improved abrasion resistance. However, other properties such as fabric thickness and softness were also affected by the treatment.     

涤纶织物纳米TiO2颗粒化学复合镀银

采用化学镀技术,实现了不同分散剂分散纳米TiO2颗粒涤纶织物表面化学复合镀银,借助SEM、XRD和TG对镀层表面形貌、结构和织物热性能进行研究,测试织物的电磁波屏蔽、导电、耐磨、透气和光催化性能.结果表明:用PVP&T80作分散剂时,纳米TiO2的引入对镀层结构没有影响,但晶粒尺寸增大;随着纳米TiO2质量浓度的增加,...     

Electrical,electromagnetic shielding,and some physical properties of hybrid yarn-based knitted fabrics

Recently, increasing number of studies are performed on protective fabrics containing metal wires for electromagnetic shielding purposes. In the present paper, the hybrid fabrics in plain and rib structures were knitted by using single and double ply hybrid yarns obtained by acrylic (PAC) yarns plied with stainless steel wires having two different diameters. The physical properties including conductivity, air permeability, pilling, and abrasion resistance as well as electromagnetic shielding effectiveness (EMSE) were measured. The variations in EMSE as well as reflection, absorption, and transmission and in other physical properties of knitted hybrid fabrics were investigated considering wire content and weave structure. It was seen that an increase in the wire content significantly increased the conductivity. Rib fabrics exhibited better EMSE values as compared with plain fabrics. Fabrics using two-folded yarns exhibited better EMSE values. Fabrics using thinner wire exhibited higher EMSE values. The highest EMSE value was obtained for rib-knitted fabric with 35 micrometer (μm) stainless steel wire.     

电磁波屏蔽织物服用性能影响因素的灰色优势分析

为探讨电磁波屏蔽织物服用性能,选取5种不同结构特征的金属纤维混纺织物,对其悬垂、耐磨、折痕回复、拉伸、透湿以及防电磁辐射性能进行测试.运用灰色系统控制理论方法,通过编程运算,得出灰色关联序,对金属纤维混纺电磁波屏蔽织物服用性能影响因素进行灰色关联的优势分析.结果表明:金属纤维含量对屏蔽织物服用性能的影响最为显著,其次为织物紧度、织物面密度、组织系数、织物厚度、纱线线密度.该研究结果可为电磁波屏蔽织物的进一步开发提供参考.     

竹炭改性涤纶/棉混纺针织物的性能研究

探讨了竹炭改性涤纶/棉混纺针织物的性能,对5种不同混纺比的竹炭改性涤纶棉混纺针织物的主要服用性能进行了测试分析。结果表明,随着竹炭改性涤纶纤维含量的增加,混纺针织物的透气性、悬垂性、刚柔性和保暖性越来越好,而耐磨性变化不明显,但顶破强力减小。     

水洗过程对织物性能和外观的影响

研究了水处理对织物外观和部分织物性能的影响。织物选用由两种不同线密度的纱线(分别为29.5tex和19.7tex)制备的20块平纹棉针织物,水处理(0、5、15和25次水洗)之后,测试对织物舒适度和美学性能有重要影响的一些织物性能(即织物厚度、透气性、抗起毛起球和耐磨牢度)的变化。结果表明,5次水洗过程对所测织物的厚度、透气性和磨损性的影响最大。     

透心硅油在亚麻纺织品柔软整理中的应用

针对亚麻织物存在弹性和柔软性差、手感粗糙、易起皱等缺点．特选取了有机硅柔软剂SD-G50透心硅油对其进行柔软整理。通过对处理前后织物的弯曲长度、折皱回复角和撕裂强力对比分析发现，用该柔软剂处理后的织物在柔软性和抗折皱性方而都有明显的改善，是比较理想的可应用于亚麻织物的柔软整理剂，同时确定了最佳工艺条件。     

嵌段改性硅油的合成及应用研究

以八甲基环四硅氧烷(以下简称D4)、四甲基二氢二硅氧烷为原料,在浓硫酸催化下,制得端基含氢硅油中间体.通过环氧氨化法将烯丙基环氧聚醚、端氨基聚醚引入分子链中制得高固含量多元嵌段共聚物,并利用红外光谱对产物结构进行了测试表征.将目标产物经冰醋酸和水稀释后可得到稳定的整理剂乳液,将其整理到粘胶纤维织物上,测试了柔软度、白度、摩擦系数,用X射线衍射、扫描电镜等方法对处理前后纤维织物进行了测试.结果表明:当整理剂用量为30 g/L时,纤维表面如同镀了一层光亮的薄膜,保留了粘胶纤维特有的沟槽形态,对粘胶纤维的吸湿、透气性影响较小,粘胶纤维织物的柔软度、白度、耐摩擦效果较好.     

PTT/绢丝混纺织物的风格及服用性能

为了将PTT纤维的形状记忆性与蚕丝优异的服用性能相互融合,以绢纺工艺将PTT纤维与绢丝混纺,制成混纺比为50:50的PTT/绢丝混纺纱,并以其为经纬纱设计织造了5种PTT/绢丝混纺面料,此外还以相同规格织造了3种纯绢纺纱对比试样。测定了这8种织物的手感、悬垂性及保形性(折皱回复性、拉伸回弹性)、透通性(透气、透湿性)和抗起毛起球性能,对比分析了PTT/绢丝混纺织物和纯绢丝织物的风格和服用性能。研究结果表明：PTT纤维对绢纺织物的风格与服用性能有良好的改善作用,与纯绢丝织物相比,PTT/绢丝混纺织物的折皱回复性、拉伸回弹性提高,柔软性和悬垂性好,滑糯性、透通性和抗起毛起球性能略差。