固体超强酸SO_4~(2-)/ZrO_2-SiO_2的制备及其催化性能的研究

分别以氧氯化锆、硅溶胶和氨水为锆源、硅源和沉淀剂,采用共沉淀法制备Zr(OH)4-Si(OH)4,110℃干燥后经硫酸浸渍、干燥和焙烧制得SO42-/ZrO2-SiO2固体超强酸。XRD和比表面积测定结果表明,SiO2的引入对SO42-/ZrO2催化剂的结构产生了重要影响,从而使其比表面积明显增大。以所制备的SO42-/ZrO2-SiO2固体超强酸为催化剂,代替浓硫酸用于丁酸和丁醇的酯化反应,考察了硫酸浸渍液浓度、焙烧温度等制备条件对其催化性能的影响。结果表明,采用硫酸浸渍液浓度为1.0 mol/L,焙烧温度为550℃所制备的SO42-/ZrO2-SiO2催化剂,在丁醇和丁酸的物质的量比为1.2及不添加任何带水剂的条件下,丁酸丁酯的收率高达90%以上,优于SO42-/TiO2-WO3和TiSi W12O40/TiO2催化剂。     

SO_4~(2-)/ZrO_2固体超强酸催化剂上的酯化反应机理

与液体酸和酸性树脂催化剂相比,固体超强酸催化剂具有许多优点,如无腐蚀性、不污染环境、易与产物分离和重使用性等。通过沉淀、老化、过滤、洗涤、干燥、浸渍、焙烧等过程,从ZrOCl2·8H2O和(NH4)2SO4制备了SO42-/ZrO2固体超强酸催化剂;使用Hammett指示剂法和吡啶吸附的FT-IR光谱法测定了其酸强度和酸中心类型;以甲醇、乙酸和乙酸乙酯吸附在SO42-/ZrO2固体超强酸催化剂上的FT-IR光谱,推测酯化反应机理。结果表明,当焙烧温度高于500℃,SO42-/ZrO2可以形成超强酸,其表面上同时存在Lewis酸和Bronsted酸中心;在SO42-/ZrO2固体超强酸催化剂上,酯化反应既可以在Lewis酸中心进行,也可以在Bronsted酸中心上进行。     

SO42-/ZrO2-Al2O3固体超强酸催化合成苯甲酸乙酯

采用沉淀-浸渍法制备了SO42-/ZrO2-Al2O3,固体超强酸,研究了SO42-/ZrO2Al2O3固体超强酸催化苯甲酸与乙醇的酯化反应,结果表明最适宜的反应条件为锆铝摩尔比为l2,醇酸摩尔比为5,焙烧温度500～600℃,焙烧、反应各4 h,催化剂的用量为总量的6.64%.此外,还测定了含氯的固体酸的性能,比较了优化后的固体酸与浓硫酸催化性能.     

SO42-/ZrO2-Al2O3固体超强酸催化合成苯甲酸乙酯

采用沉淀-浸渍法制备了SO4^2-/ZrO2-Al2O3,固体超强酸,研究了SO4^2-/ZrO2-Al2O3固体超强酸催化苯甲酸与乙醇的酯化反应,结果表明最适宜的反应条件为：锆铝摩尔比为1：2,醇酸摩尔比为5,焙烧温度500～600℃,焙烧、反应各4 h,催化剂的用量为总量的6.64%。此外,还测定了含氯的固体酸的性能,比较了优化后的固体酸与浓硫酸催化性能。     

乙酯SO_4~(2-)/ZrO_2-Al_2O_3固体超强酸催化合成苯甲酸

采用沉淀-浸渍法制备了SO42-/ZrO2-Al2O3固体超强酸,研究了SO42-/ZrO2-Al2O3固体超强酸催化苯甲酸与乙醇的酯化反应,结果表明最适宜的反应条件为:锆铝摩尔比为1:2,醇酸摩尔比为5,焙烧温度500～600℃,焙烧、反应各4h,催化剂的用量为总量的6.64%。此外,还测定了含氯的固体酸的性能,比较了优化后的固体酸与浓硫酸催化性能。     

固体超强酸SO2-4/TiO2的制备及其在季戊四醇酯化反应中的催化性能

采用溶胶一凝胶法制备SO2-/TiO2固体超强酸,以异辛酸与季戊四醇的酯化反应为探针反应,考察浸渍液种类及浓度、焙烧温度对固体超强酸催化性能的影响.用流动指示剂法测定催化剂的酸强度,并采用原位吡啶吸附的IR谱图对催化剂进行表征.结果表明,在H2SO4浸渍液浓度为1.0 mol·L-1、500℃下焙烧3 h制备的SO2-4/TiO2催化剂活性最好,酯化率可达到85.0%.     

SO42-/TiO2固体超强酸的制备及表征

以TiO2为载体，采用沉淀浸渍法制备负载型SO4^2-／TiO2固体超强酸催化刑．运用酸强度测试、比表面积、全硫测定、IR、XRD等方法对所制备的催化剂进行表征．测试结果表明，所制备的催化剂具有固体酸催化刑的特征．并探讨焙烧温度及浸渍液浓度对固体超强酸结构及酸性的影响．     

固体超强酸SO_4~(2-)/TiO_2的制备及其在季戊四醇酯化反应中的催化性能

采用溶胶-凝胶法制备SO42-/TiO2固体超强酸,以异辛酸与季戊四醇的酯化反应为探针反应,考察浸渍液种类及浓度、焙烧温度对固体超强酸催化性能的影响。用流动指示剂法测定催化剂的酸强度,并采用原位吡啶吸附的IR谱图对催化剂进行表征。结果表明,在H2SO4浸渍液浓度为1.0 mol.L-1、500℃下焙烧3 h制备的SO42-/TiO2催化剂活性最好,酯化率可达到85.0%。     

焙烧温度对S2O8^2-／ZrO2介孔超强酸的结构与性能的影响

以硝酸锆为锆源,以阴离子表面活性剂十二烷基硫酸钠（SDS）为模板剂,S2O8^2-浸渍无定形Zr（OH）4,制得介孔S2O8^2-／ZrO2固体超强酸,通过N2吸附－脱附、XRD分析、Hammett非水滴定、TEM等方法,考察了不同焙烧温度对S2O8^2-／ZrO2介孔超强酸晶体结构、酸强度等性能的影响。结果表明,当焙烧温度600℃,S2O8^2-／ZrO2样品比表面积为140m2／g,平均孔径在3～4nm之间,酸强度H0≤-12．7,为介孔相固体超强酸。     

复合固体超强酸催化剂SO_4~（2-）/ZrO_2-Al_2O_3-WO_3的制备及表征

采用沉淀浸渍法制备复合固体超强酸催化剂SO24-/ZrO2-Al2O3-WO3,运用Hammett指示剂法、FT-IR、XRD、SEM、TGA和BET等对相应的催化剂进行表征,并研究了陈化温度、焙烧温度、浸渍液浓度等制备条件以及Al2O3、WO3等不同金属氧化物的引入对SO24-/ZrO2的影响。结果表明,低温陈化的试样具有较强的酸性和催化活性,添加Al2O3可增大催化剂的比表面积和酸度值,引入WO3有利于酸性的增强。复合固体催化剂SO42-/ZrO2-Al2O3-WO3的最佳制备方案是,陈化温度为-10℃、m（Al2O3）/m（ZrO2）为3.5、m（WO3）/m（ZrO2）为1、浸渍液（NH4）2SO4浓度为1.0 mol.L-1、焙烧温度为500℃。该催化剂用于乙酸正丁酯的合成,其酯化率达到98.5%。     

Bi2Sr2Co2Oy热电材料的制备

为了研究Bi2Sr2Co2Oy热电陶瓷的不同制备方法,实验采用固相反应法和溶胶-凝胶法制备Bi2Sr2Co2Oy陶瓷．用XRD,SEM等表征技术研究了样品的物相及显微组织形貌．结果表明：样品为单相,组织均匀,为层片状结构,且具有明显的c轴择优取向．     

BaF2-CaF2-CaCl2三元系熔盐电解体系的物理化学性质

研究了BaF2-CaF2-CaCl2三元系电解质体系的物理化学性质,为熔盐电解法制备Al-Ca合金奠定基础.采用阿基米德法,测定了BaF2-CaF2-CaCl2体系的密度;采用差热-热重分析法,测定了BaF2-CaF2-CaCl2体系初晶温度;采用连续变化电导池常数（CVCC）法,测定了BaF2-CaF2-CaCl2体系的电导率;采用循环伏安法研究了该体系的电化学行为.     

核壳型TiO2/COFe2O4与TiO2/SiO2/COFe2O4光催化剂的制备与性能研究

文章以CoFe2O4纳米颗粒为核,研究了制备核壳型TiO2/CoFe2O4和TiO2/SiO2/CoFe2O4光催化剂的适宜工艺;用XRD和TEM分析了产物的结构组成与形貌;以TNT为目标降解物考察了催化荆的活性.实验结果表明:以非晶CoFe2O4为核时易生成杂相,催化剂及所制备的复合颗粒的活性排序为:TiO2/SiO2/CoFe2O4＞TiO2＞TiO2/CoFe2O4＞SiO2/CoFe2O4.     

Thermal behavior and lithium ion conductivity of L2O-Al2O3-TiO2-SiO2-P2O5 glass-ceramics

A lithium ion conductive solid electrolyte, L2O-Al2O3-TiO2-SiO2-P2O5 glass with NASICON-type structure have been synthesized and transformed into glass-ceramic through thermal-treatment at various temperatures from 700 to 1 000 ℃ for 12 h. The differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and complex impedance techniques were employed to characterize the samples. The experimental results indicated that the capability of glass forming in this system is superior to that of L2O-Al2O3-TiO2-P2O5. The glass has an amorphous structure and resultant glass-ceramic mainly consisting of LiTi2(PO4)3 phases. Impurity phases AlPO4, TiO2, TiP2O7 and unidentified phase were observed. With the enhanced heat-treatment temperature, grain grew gradually and lithium ion conductivity of glass-ceramics increased accordingly, the related impedance semicircles were depressed gradually and even disappeared, which could be analytically explained by the coordinate action of the ’Constant phase element’ (CPE) model and the ’Concept of Mismatch and Relaxation’ model (CMR). When the sample is devitrified at 1 000 ℃, the maximum room temperature lithium ion conductivity comes up to 4.1×10-4 S/cm, which is suitable for the application as an electrolyte of all-solid-state lithium batteries.     

Fe~(2+)催化H_2O_2/Na_2S_2O_8氧化降解水中黄腐酸

利用Fe~(2+)催化H_2O_2或Na_2S_2O_8降解水中的黄腐酸,研究了诸因素(处理剂加量、pH和温度)对黄腐酸降解的影响。黄腐酸溶液颜色和TOC的去除,紫外区光吸收强度的降低都表明H_2O_2/Fe~(2+)体系对黄腐酸具有良好的降解效果;在pH=3.0、H_2O_2为400mg·L~(-1)、H_2O_2与Fe~(2+)物质的量的比为10∶1的条件下,处理100mg·L~(-1)黄腐酸溶液120 min,TOC去除率达到88.4%。Na_2S_2O_8/Fe~(2+)降解结果表明:在pH=3.0、Na_2S_2O_8为2 000mg·L~(-1),Fe~(2+)为5mmol·L~(-1),温度为50℃条件下处理100 mg·L~(-1)黄腐酸水样240min,TOC去除率为55.9%。分析降解效果和试剂成本可知,H_2O_2/Fe~(2+)法降解水中黄腐酸优于Na_2S_2O_8/Fe~(2+)法。     

Crystallization Mechanism of Na2O-CaO-Al2O3-SiO2-F Glass Containing Cr2O3

The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.     

GeO2-PbF2-ZnF2玻璃的Raman光谱和结构

用Ｒａｍａｎ光谱研究了ＧｅＯ２－ＰｂＦ２－ＺｎＦ２系统玻璃结构。结果表明,这种氟氧混合体系玻璃主要以［ＧｅＯ４－ｘＦｘ］四面体、［ＺｎＦ４］和［ＺｎＯ４］单元共同构成三维网络。网络中非桥氧或［ＧｅＯ４－ｘＦｘ］四面体的数量随Ｆ－／Ｏ２－比例增加而增加,而Ｆ－／Ｏ２－比例一定时,Ｚｎ２＋则能提高［ＧｅＯ４－ｘＦｘ］四面体的聚合度。     

IR Spectra Analysis of SiO_2-TiO_2-GeO_2 Gel Glass of CO_2 Laser Transmitting Hollow Waveguide

1　ＩｎｔｒｏｄｕｃｔｉｏｎＴｈｅｔｈｅｏｒｙｏｆｈｏｌｌｏｗｗａｖｅｇｕｉｄｅｆｏｒｔｒａｎｓｍｉｔｔｉｎｇＣＯ2ｌａｓｅｒｉｓｂａｓｅｄｏｎｔｈｅａｎｏｍａｌｏｕｓｄｉｓｐｅｒｓｉｏｎｃａｕｓｅｄｂｙｒｅｓｏ ｎａｎｃｅａｂｓｏｒｐｔｉｏｎａｔｔｈｅｗａｖｅｎｕｍｂｅｒｏｆ 94 0ｃｍ- 1[1- 3 ] .Ｈｏｗｅｖｅｒ ,ｔｈｅＩＲａｂｓｏｒｐｔｉｏｎｏｆｔｈｅｓｉｌｉｃａｇｌａｓｓｍａｉｎｌｙｔａｋｅｓｐｌａｃｅａｔｗａｖｅｌｅｎｇｔｈｓｂｅｔｗｅｅｎ 7.6 9ａｎｄ 9.6 2 μｍ ,ａｓａｒｅｓｕｌｔ,ａｌｍｏｓ…     

Li_2O、La_2O_3含量对Li_2O-La_2O_3-Ta_2O_5-SiO_2系统玻璃析晶性能的影响

电极玻璃的析晶性能是直接影响电极制作的重要因素 ,本文通过析晶实验 ,利用X射线衍射分析对Li2 O La2 O3 Ta2 O5 SiO2 系统玻璃的析晶性能进行了研究。结果表明 :引入适量的Li2 O、La2 O3能改善该系统玻璃的析晶性能。     

TiO2-SiO2复合多孔材料的低成本制备及表征

以廉价的TiCl4和工业水玻璃为原料,采用溶胶-凝胶法,用无水乙醇对湿凝胶进行溶剂交换处理,通过常压干燥工艺制备了TiO2-SiO2多孔材料.利用SEM、FTIR、BET吸附对多孔材料的形貌和性质进行了研究,分析了TiO2-SiO2多孔材料吸附和光催化降解罗丹明B的性能.结果表明,用3 mol/L的TiCl4水溶液制得的TiO2-SiO2多孔材料对罗丹明B有较高的吸附率和光解率;n(Ti): n(Si)=2:1的TiO2-SiO2多孔材料对罗丹明B有较高的吸附率.而n(Ti):n(Si)=1:2的TiO2-SiO2多孔材料对罗丹明B有较高的光解率.