Material and methods: CAD/CAM blocks of 2-mm thickness were sectioned with a slow-speed diamond-saw sectioning machine. The slabs were then embedded in autopolymerizing acrylic resin (n = 12), and resin cements were applied to the surface of the specimens. All specimens were stored in water for 24 h and subjected to 5000 thermal cycles. Bond strength was measured by means of the shear bond strength test. The data were statistically analyzed by two-way ANOVA and Tukey LSD post hoc tests.
Results: The results of the two-way ANOVA test indicated that the bond strength values varied significantly depending on the CAD/CAM restorative materials, resin cements, and interaction of these variables (p < 0.05). The RNC group showed the highest bond strength for Panavia F 2.0 (p < 0.05); there were no significant differences among other CAD/CAM materials for Panavia F 2.0 (p > 0.05). The LDG group showed the highest bond strength for Multilink N, it was followed by the ZLDC group (p < 0.05); there were no significant differences between RNC and HC groups (p > 0.05).
Conclusions: Choosing resin cements for restorations should be done carefully because bond strength values vary significantly depending on the resin cement and CAD/CAM restorative material. 相似文献
Methods: Occlusal surfaces of 48 extracted human molars were ground to expose flat superficial dentin surfaces. Specimens were randomly divided into two main groups according to the tested self-etch adhesive system either: One-step self-etch (AdperTM easy-one) or two-step self-etch (AdperTM SE Plus). Each adhesive system was applied on the prepared dentin surfaces followed one of these techniques: (1) Passive application of a single layer, (2) Active application of single layer, (3) Passive application of double adhesive layer (with light curing in between), and (4) Active application of double adhesive layers. Resin composite was packed inside micro-tubes fixed on the bonded dentin surfaces and light cured for 40 s. All specimens were stored in artificial saliva either for 24 h or 3 months before testing. Microshear bond strength test was employed using a universal testing machine at a crosshead speed of 0.5 mm/min.
Results: AdperTM SE Plus showed higher significant microshear bond strength in compared with AdperTM easy-one. For both adhesive systems active application showed higher significant microshear bond strength to dentin than passive application. Double application of adhesive systems showed lower microshear bond strength than single application.
Conclusion: Active application of self-etch adhesives could improve the dentin microshear bond strength. Double application with curing in between the layers did not improve the bond strength to the tested adhesive. 相似文献
Material and methods: Flattened dentine surfaces from 30 bovine incisors were bonded with five one-step one-bottle self-etch adhesives (iBond, Clearfil S3 Bond, AdheSE One F, G-Bond, Optibond all-in-one) and one two-step self-etching adhesive (Clearfil SE Bond). Composite buildups were done with microhybrid resin composite. Bonded samples were sectioned into resin–dentine sticks of 0.8 mm2 cross section. Randomly selected 20 sticks were tested directly by microtensile bond strength testing machine, whereas another randomly selected 20 sticks were tested after being stored in solution of 10% NaOCl for 5 h. Data were analyzed by two-way analysis of variance (ANOVA) and Tukey’s honest significant difference (HSD) tests (p < 0.05).
Results: All adhesives exhibited similar dentine bond strength with exception of G-Bond. After NaOCl storage, μTBS reduced in all groups significantly. The lowest μTBS were found for G-Bond. Rest of one-step self-etch adhesives presented similar μTBS with two-step self-etch adhesive.
Conclusion: Interfaces of resin–dentine bonding are susceptible to NaOCl degradation. The amount of the destruction depends on adhesive system. NaOCl degradation of the nonresin encapsulated collagen fibers might decrease long-term stability of resin bonding with dentine. 相似文献
Methods: Dentin specimens (n = 240) were divided into 2 groups: Group GC: GrandioSO, and Group GF: GrandioSO Heavy Flow. These groups were subdivided into 6: FM: Futurabond M – light cured, FDCC: Futurabond Dual Cure – chemical cured, FDCL: Futurabond Dual Cure – light cured, CS3: Clearfil S3 – light cured, CDCC: Clearfil Dual Cure – chemical cured, and CDCL: Clearfil Dual Cure – light cured. Resin blocks were build up on the dentin surface. Half of samples on each group were cut to obtain resin/dentin sticks (1 × 1 mm). The other half was first submitted to thermomechanical aging. The dentin/resin sticks were submitted to microtensile bond strength test and the results were analyzed using three-way ANOVA and Tukey’s test (α = 5%).
Results: ANOVA showed significant influence for adhesive (p = 0.0000) and aging (p = 0.0001). No significant influence of the composite viscosity on bond strength was observed (ANOVA: p = 0.0861). For adhesive, the results of Tukey’s test (MPa) were CDCC: 13.44 (±5.13)a; FM: 14,01 (±2.71)a; CDCL: 14.51 (±4.98)a; FDCC: 18.66 (±7.13)b; CS3: 18.80 (±6.50)b; FDCL: 19.18 (±7.39)b. For aging: AGED: 14.99 (±6.32)a; NOT AGED: 17.87 (±5.97)b.
Conclusion: Composite resin viscosities did not influence on the bond strength. Type of cure of the adhesives had influence on the bond strength. Thermomechanical aging decreased the bond strength. 相似文献
Materials and Methods: Thirty-three bovine incisors were used in this study. After the labial enamel surfaces were highly polished, they were etched, water sprayed, and air-dried. Afterward, the enamel surfaces were treated with or without (control) one of three PAEs-containing primers (40%MDP, Ivoclar Vivadent; Resulcin AquaPrime A + B, DMG; Xeno V, Dentsply), water sprayed, and air-dried. Subsequently, an adhesive Heliobond (Ivoclar Vivadent) was applied and resin composite (Core Build-up, Bisco) was placed incrementally. They were prepared into multiple beams of about 1 × 1 × 8 mm for MTBS tests. The enamel surfaces and resin–enamel interfaces were analyzed by SEM and TEM. The data were analyzed by two-way ANOVA and LSD test.
Results: Using PAEs-containing primers could increase the enamel MTBS (p < 0.05). The primer MDP produced higher MTBS than the primer Resulcin AquaPrime A + B and Xeno V. The SEM findings revealed the primed enamel surfaces were covered with a thin or glue-like layer of monomer-calcium salts of PAEs and the residual enamel crystallites, and various micro-porosities were detected within the hybrid layers. The TEM findings revealed the hydroxyapatite crystallites were tightly covered by the adhesive, the adhesive mixed with resin composite, or sparse irregular enamel crystallites.
Conclusion: The application of PAEs-containing primers on the etched enamel substrate could significantly increase the immediate enamel bond strengths. However, this effect was dependent on the individual PAEs-containing primer used. 相似文献
Materials and methods: Class V cavities were prepared on the buccal surfaces of 40 extracted human third molars. Forty box-shaped cavities were divided into four groups, based on the desensitizers used (n = 10). All teeth were restored with the same bonding agent and composite material. No desensitizer was applied in the control group. In the experimental groups, BisBlock, Gluma and Universal bonding agents were the desensitizers. The desensitizers were applied after completion of composite restorations according to manufacturers’ instructions. All specimens were then thermocycled at 5–55 °C, with a 10-s dwell time for 500 cycles. The samples were then immersed in 0.5% methylene blue dye for 24 h, sectioned into two equal halves, evaluated for microleakage using a stereomicroscope at 30× magnification and scored on a scale of 0–3. The data were analysed using the Kruskal–Wallis test at the significance level p < 0.05.
Results: There were no significant differences in microleakage after desensitizer application (p > 0.05). However, based on the obtained numerical values in our study, while the BisBlock and bonding groups showed lower microleakage at the occlusal margin, BisBlock, Gluma and bonding group showed lower microleakage at the gingival margin compared to the control group.
Conclusions: The application of desensitizers as a post-treatment option could be considered an advisable procedure to minimize microleakage. 相似文献
Material and methods: Partially stabilized monolithic zirconia blocks (inCoris TZI) were cut into three different thicknesses (0.5, 1.0, and 2.0 mm) and the specimens were divided into four color groups (A1, A2, A3, and A4). The light transmittance of each specimen was measured. Panavia F 2.0 or Variolink N resin cement was applied into teflon mold and irradiated using the light emitting diode curing unit for 20 s under monolithic zirconia specimen (n = 10). The resin cement specimens were stored at room temperature under dry conditions. The DC of each specimen was measured by Fourier transform infrared-attenuated total reflection (FT-IR/ATR) spectroscopy after the 1st and 10th day. Data were analyzed with two-way analysis of variance (ANOVA), two-way repeated measures ANOVA, three-way repeated measures ANOVA, and the Tukey least significant difference (LSD) tests (α = 0.05).
Results: The light-cure resin cement groups showed higher DC than the dual-cure resin cement groups (p < 0.05). The DC of both resin cements reduced with an increase in the thickness and darkening of the color of monolithic zirconia specimens. There was a statistically meaningful increase in the 10th-day values for dual-cure resin cement (p < 0.05), whereas there were no significant differences between the 1st- and 10th-day values for light-cure resin cement (p > 0.05).
Conclusion: The use of light-cure resin cement can be suggested for the luting of monolithic zirconia restorations. 相似文献
Methods: Seven hundred and twenty stainless steel brackets were divided into 3 groups according to the adhesive system used (Transbond XT light-cure adhesive [TXT], Transbond LR capsule [LR], and Light Bond light-cure adhesive paste [LB]), and each group was divided into 2 subgroups according to light-curing procedure (LED or halogen). Brackets were bonded with adhesives onto tooth buccal surfaces and polymerized. Each specimen contained 24 brackets that simulated the oral environment (n = 5). The specimens were immersed in a 75% ethanol/water solution at 37 °C for 10 min, 1 h, 1 d, 7 d, 14 d, and 30 d, respectively. Eluted monomers (Bis-GMA, UDMA, and TEGDMA) were detected using HPLC.
Results: There was residual monomer release at all time periods, and the highest amount of release was observed cumulatively on the 30th day. The cumulative Bis-GMA released from adhesives was not different (p > 0.05). The cumulative TEGDMA released from adhesives was statistically different (p < 0.05). There was no statistical difference between QTH and LED light-curing units for each adhesive (p > 0.05).
Conclusions: The release of residual monomers stays at a high level for a long time after polymerization. The total leaching of residual monomers from the Light Bond light-cure sealant resin plus Light Bond light-cure adhesive paste was higher than that of other materials for both curing units. Different curing units (LED or QTH) did not affect the monomer release from the orthodontic adhesives. 相似文献
Methods: Experimental materials were made by incorporating 2 wt% of Biosilicate® into Fuji II LC® (FL) and Vitremer® (VT) powders. Disks of RMGICs (with and without Biosilicate®) measuring 0.5 cm (diameter) × 0.5 mm (thickness) were fabricated and polished. Samples were stored at 37 °C in dry or immersed in distilled water for 30 days. Digital images (20 × 20 μm) from the surfaces were obtained by means of an atomic force microscopy. Three images were acquired for each sample, and four nanoroughness measurements were performed in each image. Nanoroughness (Ra, nm) was assessed by Nanoscope Software V7. Data were analyzed with ANOVA and Student–Newman–Keuls multiple comparisons (p < 0.05). SEM images were obtained for surface topography analysis.
Results: FL was significantly rougher than VT (p < 0.05) in wet and dry conditions. The addition of Biosilicate® increased the surface roughness in VT and decreased in FL, regardless of the storage media (p ≤ 0.05). No differences existed between materials and storage conditions after Biosilicate® addition. Significance: The Biosilicate® particles addition produced changes on the surface nanoroughness of the RMGICs. These changes depended on the particles size of the original cements in dry conditions. In water storage, dissolution of the Biosilicate® particles, a silica-rich gel formation, and a hydroxyl carbonate apatite precipitation on the surface of the materials changed the nanoroughness surface. FL was the roughest in both conditions.
Significance: The Biosilicate® particles addition produced changes on the surface nanoroughness of the RMGICs. These changes depended on the particles size of the original cements in dry conditions. In water storage, dissolution of the Biosilicate® particles, a silica-rich gel formation, and a hydroxyl carbonate apatite precipitation on the surface of the materials changed the nanoroughness surface. FL was the roughest in both conditions. 相似文献
Material and Methods: Ninety third-molar teeth extracted for various reasons were used in this study. All the teeth were prepared with a standard V cavity on the buccal surface. Then the teeth were randomly allocated to one of 6 groups of 15 teeth; Group 1 benzalkonium chloride, Group 2 chlorhexidine gluconate, Group 3 sodium hypochloride, Group 4 diode laser, Group 5 ozone gas, Group 6 control group- no disinfection was applied. Primer was applied to the cavities, then bond and 10-s polymerization. Clearfil AP-X was used in the cavities as a hybrid composite and polymerized for 20 s. The samples then underwent 1000 thermal cycles of 30-s application, in baths at temperatures between 5 ± 2 °C and 55 ± 2 °C. All the samples were stirred in 0.5% basic phuxine solution and the sections taken under stereomicroscope were examined and photographed at 15 × magnification. SEM analysis was made and the obtained results were statistically evaluated with the Kruskal–Wallis test.
Results: No significant difference was seen between the groups in respect of the microleakage values of both the occlusal and gingival edges (p < 0.05). Comparison of the microleakage values of the occlusal and gingival edges of the groups determined the least leakage to be in the ozone group (p < 0.05).
Conclusion: No statistical significance was determined between the groups. However, the mean least microleakage was found in the ozone group and the highest amount in the control group. 相似文献
ke was expressed in terms of a stagnant contribution, due to the heat conduction through the solid and the fluid in the void space, and a radial mixing contribution of the gas and liquid phases, due to the radial component of the velocity of both fluids. The radial mixing contribution of the liquid ( ke ) L was compared with radial mass dispersion data, and a satisfactory agreement was obtained.
Moreover, ( ke )was much higher than the gas mixing and the stagnant contributions.
Correlations for hw and ke ) L have been proposed in accordance with the hydrodynamic regimes of the two-phase flow. 相似文献
Nine different samplers (impactors/impingers/cyclones/ electrostatic precipitators/filtration samplers) were subjected to comparative performance testing in this work. Their end-to-end cultivation-based biological sampling efficiencies (BSEs) and PCR-/microscopy-based physical sampling efficiencies (PSEs) relative to a reference sampler (BioSampler) were determined for gram-negative and gram-positive vegetative bacteria, bacterial spores, and viruses.
Significant differences were revealed among the samplers and shown to depend on the bioaerosol's stress–sensitivity and particle size. Samplers employing dry collection had lower BSEs for stress-sensitive bioaerosols than wet collection methods, while nonfilter-based samplers showed reduced PSEs for 1 μm compared to 4 μm bioaerosols. Several samplers were shown to underestimate bioaerosol concentration levels relative to the BioSampler due to having lower sampling efficiencies, although they generally obtained samples that were more concentrated due to having higher concentration factors.
Our work may help increase user awareness about important performance criteria for bioaerosol sampling, which could contribute to methodological harmonization/standardization and result in more reliable exposure assessments for airborne pathogens and other bioaerosols of interest.
Copyright 2014 American Association for Aerosol Research 相似文献
Introduction of new technological achievements and development in the field of flame retardancy (FR)
Review of the current state of science and technology in FR
Review of applications and markets for FR products
Presentation of recent developments in local and global standardization and in testing technology
Discussion of toxicity and environmental issues
Provision of a unique opportunity for newcomers to FR research technology and marketing to become acquainted with the FR field in all its aspects
Discussion of halogen-based and non-halogen-based flame retardant chemicals, syngergism, intumescence, FR mechanisms, modeling, flame parameters, inherently FR polymers, and polymer blends 相似文献
According to literature reports and own research, PAHs presence in wastewaters is common. It was confirmed that PAHs are the components of municipal landfill leachate. Membrane techniques are one of the most interesting ways of removing PAHs from leachate.
The purpose of this article is to monitor PAHs concentration changes during the membrane (reverse osmosis - RO) leachate treatment processes. In the first stage of testing leachates were filtrated on the sand bed (pre-filtration). After the pre-filtration they were directed to the membrane module for the main filtration.
Sixteen PAHs listed by EPA were analyzed. The results with information on PAHs concentration in leachate samples were presented using HPLC with fluorescence detection (FLD). The changes in PAHs concentration were determined in leachate samples before and after pre-filtration as well as after RO. The decrease of PAHs concentration in the samples was observed after these processes. The total concentration of 16 PAHs in raw municipal landfill leachates amounted to 23.64–26.95 μg/L. The research confirmed the high efficiency in removal of PAHs while using a reverse osmosis (59–72%). Including the pre-filtration, the overall level of removed PAHs reached 81–86%. The average PAHs concentration after pre-filtration and RO was in the 4.46–4.99 μg/L range. The municipal landfill leachate with a high concentration of PAHs should be cleaned before it is discharged into the environment. 相似文献
The chelates extract these metals differently: for example, efficiency of ATPH was the highest for Hg(II) compared to PHDA, APHO, and MTAN.
The extraction efficiency was found to depend on: donor atom hardness, chelate total hardness, metal: chelate mole ratio and substituent’s electronic effects. Among all, total hardness and chelate stability are key factors and molecule of small (EHOMO – ELUMO) is more reactive, where extraction efficiency increases as molecular stability decreases. 相似文献
A correct mathematical treatment is given for calculation of the light absorption of the individual components of a multi-absorbent reaction mixture.
On the basis of the literature data and die present results, a probable chemical and reaction kinetic model was proposed to characterize the investigated reaction systems. Reaction kinetic simulations demonstrated that the model predicts a good fit to the measured data with the preferred literature rate constants, except that for the HO3 radical decomposition reaction. A reasonable reduction of this rate coefficient value is in accordance with the latest published results. 相似文献
Highlights:
Mathematical model of cascade for separation of multicomponent isotope mixture has been developed.
The model verification has been done.
The isotope transient regularities into cascade during nonstationary processes has been identified. 相似文献