回流焊对SnAgCu焊点IMC及剪切强度的影响

研究了回流焊次数对Sn-0.3Ag-0.7Cu-xNi/Cu(x=0,0.05)焊点的界面反应及其剪切强度的影响。结果表明:随着回流焊次数的增加,界面金属间化合物(IMC)Cu6Sn5和(Cu1-xNix)6Sn5的厚度均增加。在钎料中添加w(Ni)为0.05%,可有效抑制IMC的生长,与回流焊次数无关。回流焊次数对Sn-0.3Ag-0.7Cu/Cu和Sn-0.3Ag-0.7Cu-0.05Ni/Cu的剪切强度影响都不大,五次回流焊后剪切强度略有下降,剪切强度分别为21MPa和25MPa。发现断裂面部分在钎料中,部分在钎料和IMC之间。     

Intermetallic growth kinetics for Sn-Ag, Sn-Cu, and Sn-Ag-Cu lead-free solders on Cu, Ni, and Fe-42Ni substrates

Soldering with the lead-free tin-base alloys requires substantially higher temperatures (∼235–250°C) than those (213–223°C) required for the current tin-lead solders, and the rates for intermetallic compound (IMC) growth and substrate dissolution are known to be significantly greater for these alloys. In this study, the IMC growth kinetics for Sn-3.7Ag, Sn-0.7Cu, and Sn-3.8Ag-0.7Cu solders on Cu substrates and for Sn-3.8Ag-0.7Cu solder with three different substrates (Cu, Ni, and Fe-42Ni) are investigated. For all three solders on Cu, a thick scalloped layer of η phase (Cu₆Sn₅) and a thin layer of ε phase (Cu₃Sn) were observed to form, with the growth of the layers being fastest for the Sn-3.8Ag-0.7Cu alloy and slowest for the Sn-3.7Ag alloy. For the Sn-3.8Ag-0.7Cu solder on Ni, only a relatively uniform thick layer of η phase (Cu,Ni)₆Sn₅ growing faster than that on the Cu substrate was found to form. IMC growth in both cases appears to be controlled by grain-boundary diffusion through the IMC layer. For the Fe-42Ni substrate with the Sn-3.8Ag-0.7Cu, only a very thin layer of (Fe,Ni)Sn₂ was observed to develop.     

Reliability investigation and interfacial reaction of ball-grid-array packages using the lead-free Sn-Cu solder

The interfacial reactions between two Sn-Cu (Sn-0.7Cu and Sn-3Cu, wt.%) ball-grid-array (BGA) solders and the Au/Ni/Cu substrate by solid-state isothermal aging were examined at temperatures between 70°C and 170°C for 0 to 100 days. For the Sn-0.7Cu solder, a (Cu,Ni)₆Sn₅ layer was observed in the samples aged at 70–150°C. After isothermal aging at 170°C for 50 days, the solder/Ni interface exhibited a duplex structure of (Cu,Ni)₆Sn₅ and (Ni,Cu)₃Sn₄. For the Sn-3Cu solder, only the (Cu,Ni)₆Sn₅ layer was formed in all aged samples. Compared to these two Sn-Cu solders, the Cu content in the (Cu,Ni)₆Sn₅ layer formed at the interface increased with the Cu concentration in the Sn-xCu solders. And, the shear strength was measured to evaluate the effect of the interfacial reactions on the mechanical reliability as a function of aging conditions. The shear strength significantly decreased after aging for 1 day and then remained nearly unchanged by further prolonged aging. In all the samples, the fracture always occurred in the bulk solder. Also, we studied the electrical property of Cu/Sn-3Cu/Cu BGA packages with the number of reflows. The electrical resistivity increased with the number of reflows because of an increase of intermetallic compound (IMC) thickness.     

Effect of cooling rate on growth of the intermetallic compound and fracture mode of near-eutectic Sn-Ag-Cu/Cu pad: Before and after aging

Several near-eutectic solders of (1) Sn-3.5Ag, (2) Sn-3.0Ag-0.7Cu, (3) Sn-3.0Ag-1.5Cu, (4) Sn-3.7Ag-0.9Cu, and (5) Sn-6.0Ag-0.5Cu (in wt.% unless specified otherwise) were cooled at different rates after reflow soldering on the Cu pad above 250°C for 60 sec. Three different media of cooling were used to control cooling rates: fast water quenching, medium cooling on an aluminum block, and slow cooling in furnace. Both the solder composition and cooling rate after reflow have a significant effect on the intermetallic compound (IMC) thickness (mainly Cu₆Sn₅). Under fixed cooling condition, alloys (1), (3), and (5) revealed larger IMC thicknesses than that of alloys (2) and (4). Slow cooling produced an IMC buildup of thicker than 10 μm, while medium and fast cooling produced a thickness of thinner than 5 μm. The inverse relationship between IMC thickness and shear strength was confirmed. All the fast- and medium-cooled joints revealed a ductile mode (fracture surface was composed of the β-Sn phase), while the slow-cooled joints were fractured in a brittle mode (fracture surface was composed of Cu₆Sn₅ and Cu₃Sn phases). The effect of isothermal aging at 130°C on the growth of the IMC, shear strength, and fracture mode is also reported.     

Effects of Metallic Nanoparticles on Interfacial Intermetallic Compounds in Tin-Based Solders for Microelectronic Packaging

Tin (Sn)-based solders have established themselves as the main alternative to the traditional lead (Pb)-based solders in many applications. However, the reliability of the Sn-based solders continues to be a concern. In order to make Sn-based solders microstructurally more stable and hence more reliable, researchers are showing great interest in investigating the effects of the incorporation of different nanoparticles into them. This paper gives an overview of the influence of metallic nanoparticles on the characteristics of interfacial intermetallic compounds (IMCs) in Sn-based solder joints on copper substrates during reflow and thermal aging. Nanocomposite solders were prepared by mechanically blending nanoparticles of nickel (Ni), cobalt (Co), zinc (Zn), molybdenum (Mo), manganese (Mn) and titanium (Ti) with Sn-3.8Ag-0.7Cu and Sn-3.5Ag solder pastes. The composite solders were then reflowed and their wetting characteristics and interfacial microstructural evolution were investigated. Through the paste mixing route, Ni, Co, Zn and Mo nanoparticles alter the morphology and thickness of the IMCs in beneficial ways for the performance of solder joints. The thickness of Cu₃Sn IMC is decreased with the addition of Ni, Co and Zn nanoparticles. The thickness of total IMC layer is decreased with the addition of Zn and Mo nanoparticles in the solder. The metallic nanoparticles can be divided into two groups. Ni, Co, and Zn nanoparticles undergo reactive dissolution during solder reflow, causing in situ alloying and therefore offering an alternative route of alloy additions to solders. Mo nanoparticles remain intact during reflow and impart their influence as discrete particles. Mechanisms of interactions between different types of metallic nanoparticles and solder are discussed.     

Interfacial Reactions and Microstructures of Sn-0.7Cu-<Emphasis Type="Italic">x</Emphasis>Zn Solders with Ni-P UBM During Thermal Aging

The effects of the addition of Zn to Sn-0.7Cu solders are investigated. The study is focused on the interfacial reactions, microstructures, and mechanical properties after reaction with Ni-P under bump metallurgies (UBMs). The Zn contents in Sn-0.7Cu-xZn are varied as 0.2, 0.4, and 0.8 (in wt.% unless otherwise specified). In the reaction with Ni-P UBM during thermal aging at 150°C for 1000 h, (Cu,Ni)₆Sn₅ intermetallic compounds (IMCs) are formed at the Sn-0.7Cu/UBM interface, whereas Zn is incorporated into IMCs to form (Cu,Ni,Zn)₆Sn₅ in the Zn-doped solders. As the Zn content increases, the interfacial IMC thickness is reduced. A total reduction of about 40% in IMC thickness was observed for the 0.8% Zn-doped Sn-Cu. The same IMC particles are also observed in the matrix of each solder. In Sn-0.7Cu, (Cu,Ni)₆Sn₅ particles are coarsened during aging, while (Cu,Ni,Zn)₆Sn₅ particles in the Zn-added solders are less coarsened and remain much smaller than (Cu,Ni)₆Sn₅. The growth rate of (Cu,Ni)₆Sn₅ during thermal aging is significantly suppressed by the addition of Zn. Consequently, after reaction with Ni-P UBM, the Zn-doped solders exhibit a thermally stable microstructure as measured by hardness and shear strength.     

Effect of microelements addition on the interfacial reaction between Sn-Ag-Cu solders and the Cu substrate

Three kinds of Sn-Ag-based lead-free solders, Sn-3.5Ag-0.7Cu, Sn-3.5Ag-0.5Cu-0.07Ni-0.01Ge, and Sn-3.5Ag-0.07Ni (in wt.%), were selected to explore the effect of microelements (Ni and Ge) on the interfacial reaction between the solder and the Cu substrate. The thickness of the interfacial intermetallics formed with the Sn-3.5Ag-0.5Cu-0.07Ni-0.01Ge and Sn-3.5Ag-0.07Ni solders is several times that of the Sn-3.5Ag-0.7Cu solder. The added microelements converted the feature of interfacial intermetallics from pebble shape to worm shape. However, the results of x-ray diffraction (XRD) analysis suggest that the interfacial intermetallics formed with both solders have the same crystal structure. The results of energy dispersive spectroscopy (EDS) analysis show that the major interfacial intermetallic formed with the Sn-3.5Ag-0.7Cu solder is Cu₆Sn₅, while it is (Cu_x,Ni_1−x)₆Sn₅ with Sn-3.5Ag-0.5Cu-0.07Ni-0.01Ge. Ni influences the interfacial intermetallics and plays the influential role on the difference of interfacial reaction rate between liquid solder and solid Cu and the morphology of interfacial intermetallics. Additionally, the growth kinetics of the interfacial intermetallic compounds (IMCs) formed in the systems of Cu/Sn-3.5Ag-0.7Cu and Cu/Sn-3.5Ag-0.07Ni at high-temperature storage was also explored.     

Metallurgical reaction of the Sn-3.5Ag solder and Sn-37Pb solder with Ni/Cu under-bump metallization in a flip-chip package

Several international legislations recently banned the use of Pb because of environmental concerns. The eutectic Sn-Ag solder is one of the promising candidates to replace the conventional Sn-Pb solder primarily because of its excellent mechanical properties. In this study, interfacial reaction of the eutectic Sn-Ag and Sn-Pb solders with Ni/Cu under-bump metallization (UBM) was investigated with a joint assembly of solder/Ni/Cu/Ti/Si₃N₄/Si multilayer structures. After reflows, only one (Ni,Cu)₃Sn₄ intermetallic compound (IMC) with faceted and particlelike grain feature was found between the solder and Ni. The thickness and grain size of the IMC increased with reflow times. Another (Cu,Ni)₆Sn₅ IMC with a rod-type grain formed on (Ni,Cu)₃Sn₄ in the interface between the Sn-Pb solder and the Ni/Cu UBM after more than three reflow times. The thickness of the (Ni,Cu)₃Sn₄ layer formed in the Sn-Pb system remained almost identical despite the numbers of reflow; however, the amounts of (Cu,Ni)₆Sn₅ IMC increased with reflow times. Correlations between the IMC morphologies, Cu diffusion behavior, and IMC transformation in these two solder systems will be investigated with respect to the microstructural evolution between the solders and the Ni/Cu UBM. The morphologies and grain-size distributions of the (Ni,Cu)₃Sn₄ IMC formed in the initial stage of reflow are crucial for the subsequent phase transformation of the other IMC.     

Morphology and growth kinetics of intermetallic compounds in solid-state interfacial reaction of electroless Ni-P with Sn-based lead-free solders

A comparative study of solid/solid interfacial reactions of electroless Ni-P (15 at.% P) with lead-free solders, Sn-0.7Cu, Sn-3.5Ag, Sn-3.8Ag-0.7Cu, and pure Sn, was carried out by performing thermal aging at 150°C up to 1000 h. For pure Sn and Sn-3.5Ag solder, three distinctive layers, Ni₃Sn₄, SnNiP, and Ni₃P, were observed in between the solder and electroless Ni-P; while for Sn-0.7Cu and Sn-3.8Ag-0.7Cu solders, two distinctive layers, (CuNi)₆Sn₅ and Ni₃P, were observed. The differences in morphology and growth kinetics of the intermetallic compounds (IMCs) at the interfaces between electroless Ni-P and lead-free solders were investigated, as well as the growth kinetics of the P-enriched layers underneath the interfacial IMC layers. With increasing aging time, the coarsening of interfacial Ni₃Sn₄ IMC grains for pure Sn and Sn-3.5Ag solder was significantly greater than that of the interfacial (CuNi)₆Sn₅ IMC grains for Sn-0.7Cu and Sn-3.8Ag-0.7Cu solders. Furthermore, the Ni content in interfacial (CuNi)₆Sn₅ phase slightly increased during aging. A small addition of Cu (0.7 wt.%) resulted in differences in the type, morphology, and growth kinetics of interfacial IMCs. By comparing the metallurgical aspects and growth kinetics of the interfacial IMCs and the underneath P-enriched layers, the role of initial Cu and Ag in lead-free solders is better understood.     

elemental redistribution and interfacial reaction mechanism for the flip chip Sn-3.0Ag-(0.5 or 1.5)Cu solder bump with Al/Ni(V)/Cu under-Bump metallization during aging

In flip chip technology, Al/Ni(V)/Cu under-bump metallization (UBM) is currently applicable for Pb-free solder, and Sn−Ag−Cu solder is a promising candidate to replace the conventional Sn−Pb solder. In this study, Sn-3.0Ag-(0.5 or 1.5)Cu solder bumps with Al/Ni(V)/Cu UBM after assembly and aging at 150°C were employed to investigate the elemental redistribution, and reaction mechanism between solders and UBMs. During assembly, the Cu layer in the Sn-3.0Ag-0.5Cu joint was completely dissolved into solders, while Ni(V) layer was dissolved and reacted with solders to form (Cu_1−y,Ni_y)₆Sn₅ intermetallic compound (IMC). The (Cu_1−y,Ni_y)₆Sn₅ IMC gradually grew with the rate constant of 4.63 × 10⁻⁸ cm/sec^0.5 before 500 h aging had passed. After 500 h aging, the (Cu_1−y,Ni_y)₆Sn₅ IMC dissolved with aging time. In contrast, for the Sn-3.0Ag-1.5Cu joint, only fractions of Cu layer were dissolved during assembly, and the remaining Cu layer reacted with solders to form Cu₆Sn₅ IMC. It was revealed that Ni in the Ni(V) layer was incorporated into the Cu₆Sn₅ IMC through slow solid-state diffusion, with most of the Ni(V) layer preserved. During the period of 2,000 h aging, the growth rate constant of (Cu_1−y,Ni_y)₆Sn₅ IMC was down to 1.74 × 10⁻⁸ cm/sec^0.5 in, the Sn-3.0Ag-1.5Cu joints. On the basis of metallurgical interaction, IMC morphology evolution, growth behavior of IMC, and Sn−Ag−Cu ternary isotherm, the interfacial reaction mechanism between Sn-3.0Ag-(0.5 or 1.5)Cu solder bump and Al/Ni(V)/Cu UBM was discussed and proposed.     

Effect of Bi on the Interfacial Reaction between Sn-3.7Ag-xBi Solders and Cu

It was reported in previous studies that the addition of Bi could improve the wettability and reduce the melting temperature of Sn-Ag solders. This work investigates the effect of Bi on the interfacial reaction between Sn-Ag-xBi solders and the Cu substrate reflowed at 250°C for different times and thermally aged at 150°C for different durations. Five types of Sn-Ag-based solders, Sn-3.7Ag-xBi (x = 0 wt.% to 4 wt.%), were used in this study. The microstructure of the interfacial Cu-Sn intermetallic compound (IMC) layers between the solders and the Cu substrate was studied, and the thickness of the Cu-Sn IMCs in different solder/Cu systems has been measured. It was found that the thickness of the Cu-Sn IMC layer decreased with increasing amount of Bi in both the reflow and thermally aged condition. The effect of Bi addition on the interfacial reaction between the solder and the Cu substrate was discussed based on the experimental results.     

Reaction of Liquid Sn-Ag-Cu-Ce Solders with Solid Copper

Small amounts of the rare-earth element Ce were added to the Sn-rich lead-free eutectic solders Sn-3.5Ag-0.7Cu, Sn-0.7Cu, and Sn-3.5Ag to improve their properties. The microstructures of the solders without Ce and with different amounts (0.1 wt.%, 0.2 wt.%, and 0.5 wt.%) of Ce were compared. The microstructure of the solders became finer with increasing Ce content. Deviation from this rule was observed for the Sn-Ag-Cu solder with 0.2 wt.% Ce, and for the Sn-0.7Cu eutectic alloy, which showed the finest microstructure without Ce. The melting temperatures of the solders were not affected. The morphology of intermetallic compounds (IMC) formed at the interface between the liquid solders and a Cu substrate at temperatures about 40°C above the melting point of the solder for dipping times from 2 s to 256 s was studied for the basic solder and for solder with 0.5 wt.% Ce addition. The morphology of the Cu₆Sn₅ IMC layer developed at the interface between the solders and the substrate exhibited the typical scallop-type shape without significant difference between solders with and without Ce for the shortest dipping time. Addition of Ce decreased the thickness of the Cu₆Sn₅ IMC layer only at the Cu/Sn-Ag-Cu solder interface for the 2-s dipping. A different morphology of the IMC layer was observed for the 256-s dipping time: The layers were less continuous and exhibited a broken relief. Massive scallops were not observed. For longer dipping times, Cu₃Sn IMC layers located near the Cu substrate were also observed.     

Interfacial reaction between multicomponent lead-free solders and Ag,Cu, Ni,and Pd substrates

The interfacial reaction between two prototype multicomponent lead-free solders, Sn-3.4Ag-1Bi-0.7Cu-4In and Sn-3.4Ag-3Bi-0.7Cu-4In (mass%), and Ag, Cu, Ni, and Pd substrates are studied at 250°C and 150°C. The microstructural characterization of the solder bumps is carried out by scanning electron microscopy (SEM) coupled with energy dispersive x-ray analysis. Ambient temperature, isotropic elastic properties (bulk, shear, and Young’s moduli and Poisson’s ratio) of these solders along with eutectic Sn-Ag, Sn-Bi, and Sn-Zn solders are measured. The isotropic elastic moduli of multicomponent solders are very similar to the eutectic Sn-Ag solder. The measured solubility of the base metal in liquid solders at 250°C agrees very well with the solubility limits reported in assessed Sn-X (X=Ag, Cu, Ni, Pd) phase diagrams. The measured contact angles were generally less than 15° on Cu and Pd substrates, while they were between 25° and 30° on Ag and Ni substrates. The observed intermediate phases in Ag/solder couples were Ag₃Sn after reflow at 250°C and Ag₃Sn and ζ (Ag-Sn) after solid-state aging at 150°C. In Cu/solder and Ni/solder couples, the interfacial phases were Cu₆Sn₅ and (Cu,Ni)₆Sn₅, respectively. In Pd/solder couples, only PdSn₄ after 60-sec reflow, while both PdSn₄ and PdSn₃ after 300-sec reflow, were observed.     

微量Ce对SnAgCu焊料与铜基界面IMC的影响

配制了w(Ce)为0.1%和不加Ce的两种Sn-3.5Ag-0.7Cu焊料。在443K恒温时效,研究Ce对焊料与铜基板界面金属间化合物(IMC)的形成与生长行为的影响。结果发现,焊点最初形成的界面IMC为Cu6Sn5,时效5d后,两种焊料界面均发现有Cu3Sn形成。随着时效时间的增加,界面化合物的厚度也不断增加。焊料中添加w为0.1%的Ce后,能抑制等温时效过程中界面IMC的形成与生长,生长速率降低近1/2。并且,界面IMC的形成与生长均由扩散机制控制。     

Influence of Cu content on compound formation near the chip side for the flip-chip Sn-3.0Ag-(0.5 or 1.5)Cu solder bump during aging

Sn-Ag-Cu solder is a promising candidate to replace conventional Sn-Pb solder. Interfacial reactions for the flip-chip Sn-3.0Ag-(0.5 or 1.5)Cu solder joints were investigated after aging at 150°C. The under bump metallization (UBM) for the Sn-3.0Ag-(0.5 or 1.5)Cu solders on the chip side was an Al/Ni(V)/Cu thin film, while the bond pad for the Sn-3.0Ag-0.5Cu solder on the plastic substrate side was Cu/electroless Ni/immersion Au. In the Sn-3.0Ag-0.5Cu joint, the Cu layer at the chip side dissolved completely into the solder, and the Ni(V) layer dissolved and reacted with the solder to form a (Cu_1−y,Ni_y)₆Sn₅ intermetallic compound (IMC). For the Sn-3.0Ag-1.5Cu joint, only a portion of the Cu layer dissolved, and the remaining Cu layer reacted with solder to form Cu₆Sn₅ IMC. The Ni in Ni(V) layer was incorporated into the Cu₆Sn₅ IMC through slow solid-state diffusion, with most of the Ni(V) layer preserved. At the plastic substrate side, three interfacial products, (Cu_1−y,Ni_y)₆Sn₅, (Ni_1−x,Cu_x)₃Sn₄, and a P-rich layer, were observed between the solder and the EN layer in both Sn-Ag-Cu joints. The interfacial reaction near the chip side could be related to the Cu concentration in the solder joint. In addition, evolution of the diffusion path near the chip side in Sn-Ag-Cu joints during aging is also discussed herein.     

Effects of Cu contents in Pb-free solder alloys on interfacial reactions and bump reliability of Pb-free solder bumps on electroless Ni-P under-bump metallurgy

Using the screen-printed solder-bumping technique on the electroless plated Ni-P under-bump metallurgy (UBM) is potentially a good method because of cost effectiveness. As SnAgCu Pb-free solders become popular, demands for understanding of interfacial reactions between electroless Ni-P UBMs and Cu-containing Pb-free solder bumps are increasing. It was found that typical Ni-Sn reactions between the electroless Ni-P UBM and Sn-based solders were substantially changed by adding small amounts of Cu in Sn-based Pb-free solder alloys. In Cu-containing solder bumps, the (Cu,Ni)₆Sn₅ phase formed during initial reflow, followed by (Ni,Cu)₃Sn₄ phase formation during further reflow and aging. The Sn3.5Ag solder bumps showed a much faster electroless Ni-P UBM consumption rate than Cu-containing solder bumps: Sn4.0Ag0.5Cu and Sn0.7Cu. The initial formation of the (Cu,Ni)₆Sn₅ phase in SnAgCu and SnCu solders significantly reduced the consumption of the Ni-P UBM. The more Cu-containing solder showed slower consumption rate of the Ni-P UBM than the less Cu-containing solder below 300°C heat treatments. The growth rate of the (Cu,Ni)₆Sn₅ intermetallic compound (IMC) should be determined by substitution of Ni atoms into the Cu sublattice in the solid (Cu,Ni)₆Sn₅ IMC. The Cu contents in solder alloys only affected the total amount of the (Cu,Ni)₆Sn₅ IMC. More Cu-containing solders were recommended to reduce consumption of the Ni-based UBM. In addition, bump shear strength and failure analysis were performed using bump shear test.     

Morphology and Pull Strength of Sn-Ag(-Co) Solder Joint with Copper Pad

In order to clarify the effect of the addition of Co to the Sn-Ag solder, the formation and growth of an intermetallic compound (IMC) at the interface between Sn-Ag(-Co) solders and a Cu pad were investigated, and the joint strength of the solder with a Cu pad was also evaluated by a bump pull test. Binary Sn-3.5mass%Ag solder was used as the basic solder, and Sn-3.5mass%Ag-xCo solders (x = 0.1 mass%, 0.3 mass%, and 0.5 mass%) were specially prepared as Co-added solders. For the reflow process, specimens were heated in a radiation furnace at 523 K for 60 s. For the aging process, some specimens were then heat-treated in an oil bath at 423 K for 168 h, 504 h, and 1008 h. The results show that the addition of Co to the Sn-Ag solder strongly affected the formation and growth of the IMC at the interface. The results of the pull test clearly show that all solders had similar pull strengths, regardless of the Co addition, although the IMC morphology at the interface of the Sn-Ag-Co solder was quite different from that of the binary Sn-3.5Ag solder. (Received . . . ; accepted . . . )     

Microstructure Changes and Physical Properties of the Intermetallic Compounds Formed at the Interface Between Sn-Cu Solders and a Cu Substrate Due to a Minor Addition of Ni

The influence of Cu content and added Ni on the morphology of the intermetallic compound (IMC) layer formed at the interface between liquid Sn-Cu-based solders and a Cu substrate and on the strength of simulated solder joints was investigated. The reaction of a Sn-0.7Cu alloy with the substrate led to the formation of a thin layer of Cu₆Sn₅ (η-phase) with typical scallop morphology that did not grow with longer reaction times. Higher Cu content such as in the Sn-1.4Cu alloy led to extensive growth with increased reaction time; at long reaction times, Cu₃Sn (ε-phase) was observed at the interface between the Cu substrate and the Cu₆Sn₅ layer. A small nickel addition to the Sn-0.7Cu alloy significantly changed the IMC morphology, accelerated its growth kinetics, prevented formation of the Cu₃Sn layer, and reduced the rate of substrate dissolution.     

Soldering-induced Cu diffusion and intermetallic compound formation between Ni/Cu under bump metallization and SnPb flip-chip solder bumps

Nickel-based under bump metallization (UBM) has been widely used as a diffusion barrier to prevent the rapid reaction between the Cu conductor and Sn-based solders. In this study, joints with and without solder after heat treatments were employed to evaluate the diffusion behavior of Cu in the 63Sn-37Pb/Ni/Cu/Ti/Si₃N₄/Si multilayer structure. The atomic flux of Cu diffused through Ni was evaluated from the concentration profiles of Cu in solder joints. During reflow, the atomic flux of Cu was on the order of 10¹⁵–10¹⁶ atoms/cm²s. However, in the assembly without solder, no Cu was detected on the surface of Ni even after ten cycles of reflow. The diffusion behavior of Cu during heat treatments was studied, and the soldering-process-induced Cu diffusion through Ni metallization was characterized. In addition, the effect of Cu content in the solder near the solder/intermetallic compound (IMC) interface on interfacial reactions between the solder and the Ni/Cu UBM was also discussed. It is evident that the (Cu,Ni)₆Sn₅ IMC might form as the concentration of Cu in the Sn-Cu-Ni alloy exceeds 0.6 wt.%.     

The effect of intermetallic compound morphology on Cu diffusion in Sn-Ag and Sn-Pb solder bump on the Ni/Cu Under-bump metallization

The eutectic Sn-Ag solder alloy is one of the candidates for the Pb-free solder, and Sn-Pb solder alloys are still widely used in today’s electronic packages. In this tudy, the interfacial reaction in the eutectic Sn-Ag and Sn-Pb solder joints was investigated with an assembly of a solder/Ni/Cu/Ti/Si₃N₄/Si multilayer structures. In the Sn-3.5Ag solder joints reflowed at 260°C, only the (Ni_1−x,Cu_x)₃Sn₄ intermetallic compound (IMC) formed at the solder/Ni interface. For the Sn-37Pb solder reflowed at 225°C for one to ten cycles, only the (Ni_1−x,Cu_x)₃Sn₄ IMC formed between the solder and the Ni/Cu under-bump metallization (UBM). Nevertheless, the (Cu_1−y,Ni_y)₆Sn₅ IMC was observed in joints reflowed at 245°C after five cycles and at 265°C after three cycles. With the aid of microstructure evolution, quantitative analysis, and elemental distribution between the solder and Ni/Cu UBM, it was revealed that Cu content in the solder near the solder/IMC interface played an important role in the formation of the (Cu_1−y,Ni_y)₆Sn₅ IMC. In addition, the diffusion behavior of Cu in eutectic Sn-Ag and Sn-Pb solders with the Ni/Cu UBM were probed and discussed. The atomic flux of Cu diffused through Ni was evaluated by detailed quantitative analysis in an electron probe microanalyzer (EPMA). During reflow, the atomic flux of Cu was on the order of 10¹⁶−10¹⁷ atoms/cm²sec in both the eutectic Sn-Ag and Sn-Pb systems.