用与抄液体包装纸板原纸的SCAN云杉CTMP和桦木BK浆料性能的研究

本文阐述了使用ＳＣＡＮ云杉ＣＴＭＰ和ＢＫＰ配抄液体包装纸板（ＬＰＢ）时，浆料的配比和游离度对液体包装纸板芯层和液体包装板原纸物理强度指标的影响。通过实验及电子显微镜和光学显微镜对ＬＰＢ原纸表面和截面的纤维结合形成的观察，证明了用ＣＴＭＰ代替漂白化学浆与桦木ＢＫＰ配抄ＬＰＢ芯层是要的，并探索了ＣＴＭＰ适宜的配用量及合理的游离范围。     

液体包装纸板原纸的研究

本文通过实验阐述了使用斯堪的纳维亚云杉ＣＴＭＰ和松木ＢＫＰ配抄液体包装纸板原纸时，浆料的配比和游离度变化对浆料中纤维筛分含量、液体包装纸板原纸（面、芯、底三层）的物理强度指标的影响，并通过电子显微镜和光学显微镜观察，对纤维形态和相互间结合情况进行了研究，从而探索了ＣＴＭＰ适宜的配用量和合理的游离度范围。     

松木BKP和桦木BKP与云杉CTMP配抄液体包装纸板原纸性能的比较

研究了SCAN云杉CTMP分别与松木BKP和桦木BKP配抄液体包装纸板（LPB）原纸有关浆料的配比,以及比较了CTMP纸浆游离度的变化纤维筛分含量、纤维形态和层间结合情况的影响、抄造出的LPB芯层和原纸在物理强度指标等性能上的差异,确定了CTMP浆抄造液体包装纸板原纸适宜的配用量和游离度范围。     

毛竹CMP与马尾松KP配抄B等薄牛皮箱纸板

对江西抚州造纸厂利用毛竹ＣＭＰ与马尾松ＫＰ配抄定量２００ｇ／ｍ２以下本色Ｂ等牛皮箱纸板生产实践中若干问题及改造措施作了介绍。实践表明，用３２％～３５％马尾松ＫＰ和６５％～６８％毛竹ＣＭＰ配比，可以生产出组织均匀、物理指标达到Ｂ等、定量为１７５～２００ｇ／ｍ２的牛皮箱纸板。     

涂布纸板原纸的质量要求

涂布纸板包括涂布白纸板、涂布箱纸板、铸涂白纸板及涂布白卡纸。它们是以白纸板或箱纸板为原纸,经铸涂或颜料涂布加工而成。主要用于制作卡片、折叠纸盒和纸箱的原料。涂布纸板用原纸的质量不仅直接影响生产、加工过程及最终产品质量,而且对商品包装、贮存、运输环节的质量也有极大影响。笔者认为满足生产、加工及商品流通要求的原纸应有以下基本要求。１多层结构和相应的浆料配比涂布纸板原纸由配有３～８个成形器的纸板机抄造而成。浆层分作面层、衬层、芯层和底层。每层用１～３只成形器抄造。各层浆料配比、辅料及助剂量因最终产品品…     

红麻制浆

介绍了制红麻硫酸盐浆（ＫＰ）和化学热磨机械浆（ＣＴＭＰ）的试验结果，并通过与冷云杉硫酸盐浆（ＫＰ）和磨石磨木浆（ＳＧＷ）、响叶杨化学热磨机械浆（ＣＴＭＰ）比较证明：红麻硫酸盐浆（ＫＰ）和红麻化学热磨机械浆具有得率高、强度好等优点，经漂白后可代替或部分代替漂白硫酸盐木浆（ＢＫＰ）配抄新闻纸或其它文化印刷用纸。     

读者来信

编辑同志 :近期查阅贵刊登载的有关化学热磨机械浆 (ＣＴＭＰ)的论文作为参考资料 ,其中包括 1 991年第 5期“第一套国产ＣＴＭＰ生产线投入运行”以及 1 995年第二期“用国产装置生产云南松ＣＴＭＰ浆”两篇文章 ,阅后觉得此类浆属于用来配抄牛皮箱纸板、瓦楞原纸等的半化学机械浆 ,不应称作ＣＴＭＰ ,而宜称作ＣＭＰ。若仔细对照ＣＭＰ与ＣＴＭＰ的生产工艺及浆料性能等 ,还是有比较明显的差别 (见下表 ) ,因此可以避免混淆。项　目 化学热磨机械浆ＣＴＭＰ (杨木 )半化学机械浆ＣＭＰ(马尾松或云南松 ) 备　注化学处理段化学用品量 / %　…     

液体复合软包装原纸板生产工艺的研究进展

液体复合软包装原纸板需求量逐年增加,对其生产工艺的研究具有重要的社会意义和经济价值。从纸板各层作用的不同,探讨各层浆料的选择;分析原纸板施胶工艺和施胶度测定方法;并考察了原纸板的抄造工艺,为进一步探索液体复合软包装原纸板的生产提供借鉴。     

竹／木浆配抄牛皮箱纸板

介绍毛竹ＫＰ高得率浆和马尾松ＫＰ浆配抄牛皮箱纸板，纸板各项物理指标均达到了国家标准的要求。     

桦木CTMP的研究与生产

本文介绍桦木ＣＴＭＰ的开发研究结果与生产实践经验，对桦木ＣＴＭＰ的工艺技术条件，工艺控制、制浆质量和实践中的主要问题进行分析和探讨。提出在杨木ＣＴＭＰ一上生产桦木ＣＴＭＰ的可行性，并在胶印新闻纸的生产中，采用桦木ＣＴＭＰ取代了杨木ＣＴＭＰ，以满足生产要求并开辟新原料资源。     

液体复合包装原纸板生产工艺的研究进展

综述了目前国内外液体复合包装材料的发展状况、生产原纸板的浆料选择、生产过程的施胶工艺及原纸板的层间结合强度的控制,为我国自主生产液体复合包装原纸板提供借鉴。     

大叶相思制CTMP及配抄箱纸板

对大叶相思木材的纤维形态、化学组分进行了分析,并对木材制CTMP及其配抄纸板进行了研究。结果表明,此种木材虽纤维长度偏短,但纤维系含量较高,壁腔比小,木素含量高,采用NaOH和Na2SO3 混合液浸渍的一般磨浆工艺能生产出高得率的CTMP,配抄箱纸要的以质量符合国家要求。     

Über die Eignung von thermo-mechanischem und chemo-thermo-mechanischem Holzstoff (TMP und CTMP) aus Buchen- und Kiefernholz für die Herstellung von mitteldichten Faserplatten (MDF)

Medium density fibreboards (MDF) were made from beech in laboratory and pilot plant scale from thermo-mechanical (TMP) and chemo-thermo-mechanical pulps (CTMP) using both melamine reinforced urea-formaldehyde resin (UF-resin) and diphenylmethane diisocyanate polymers (PMDI). The physicalmechanical and chemical properties of the boards were evaluated. From the results the following conclusions can be drawn:

1. Both TMP and CTMP led, on using UF-resin, to MDF with very high mechanical properties exceeding the required values in European standards.
2. Pulping temperature seems to have an influence on the mechanical properties of the boards, prepared from TMP and CTMP. Increasing the pulping temperature from 150°C to 170°C negatively affects the mechanical board properties, whereas the properties of MDF from CTMP (sulfonic group content between 0.2% and 0.3%) increases by elevating the maximum pulping temperature from 150°C to 170°C.
3. The pulping chemicals in the CTMP-process (Na₂SO₃ and/or NaOH) decrease the formaldehyde release from the boards, as they act as scavengers for formaldehyde.
4. Due to higher deacetylation degree during CTMP process, MDF made from CTMP release more than 4 times acetic acid than MDF from TMP. The release of formic acid is quite different, it is in MDF, made from TMP higher than in MDF from CTMP.
5. MDF with very high mechanical properties can also be made from beech pulps (TMP) using PMDI. PMDI in combination with a formaldehyde scavenger in the middle layer and UF-resin in the surface layer leads to boards with very low formaldehyde release.

     

盘磨机械浆的特征与用途(续)

<正> 3.1.4 高级纸 最佳质量的BCTMP与BKP以1:1的配比生产高级纸,再加入20％CaCO_3填料,纸的表面施胶用3％的普遍淀粉。云杉BCTMP在游离度200mL时,抗张指数44N·m/g,白度77％～78％ISO,长纤维含量42％～44％,密度350kg/m~3。有这种特性的浆适合生产压感纸、书本印刷纸和胶印纸等。     

桉木杨木混合木片CTMP制浆

讨论相同和不同的浸渍条件、磨浆工艺、原料组成、磨浆能耗条件下的混合木片磨浆。结果表明,桉木、杨木混合木片CTMP制浆过程中,随着原料中桉木比例的增加,成浆白度和抗张指数显著下降,浆张松厚度则略有升高,达到相近的游离度时磨浆能耗有所降低。而混合木片CTMP制浆过程中,随着浸渍药液中烧碱用量的增加,达相近的游离度时磨浆能耗明显降低,成浆白度和松厚度下降,纤维束含量略有增加,浆张抗张指数、撕裂指数和耐破指数则有不同程度的提高。     

缓冲包装结构对箱装苹果振动损伤与动力学特性的影响

振动是引起果品运输损伤的主要因素之一,而对果品采用合理的缓冲包装是有效降低与控制果品运输损伤的关键。采用目前果品运输中常用的6种缓冲结构对苹果实施包装,进行箱装苹果的振动试验,分析缓冲包装结构形式对果品损伤与振动传递率的影响。结果表明,同一种缓冲包装结构中中间层苹果的损伤率最大,底层苹果的损伤率次之,顶层苹果损伤率最小;采用瓦楞纸板衬垫、发泡塑料网作缓冲包装时,均可有效地降低苹果损伤率,且发泡塑料网对苹果的整体保护特性优于瓦楞纸板衬垫,瓦楞纸板隔档对苹果的损伤率有一定影响。不同的缓冲包装能不同程度地降低包装箱内苹果振动传递率。     

利用机械浆生产木质纳米纤维素

开发了一种可以利用机械浆细小纤维组分生产纳米纤维素的方法,并对木质纳米纤维素粒径分布进行表征。本次研究使用了Cril表征技术,测定TMP纳米纤维素和CTMP纳米纤维素Crill值,作均质化时间的函数。结果显示,TMP-NLC和CTMP-NLC的Crill值都与均质化时间相关。本研究的另一目的是使用木质纳米纤维素作为纸和纸板的增强剂,加入到CTMP和BKP浆料内,结果显示,在手抄片紧度相似的情况下,加入木质纳米纤维素后纸页的Z向强度和其它一些重要的机械性能指标都有所改善。     

工业级MgO的研磨及在杨木CTMP碱性H2O2漂白中的应用

采用不同的湿法研磨工艺对工业级MgO进行研磨,分析了研磨浓度、研磨转速、研磨时间、研磨介质对MgO粒径及化学反应活性的影响;分别用经不同时间研磨处理的MgO替代25% NaOH(摩尔分数)对杨木CTMP进行碱性H₂O₂漂白,研究了漂后浆料的性能。结果表明,工业级MgO湿法研磨的浓度和转速分别为10%和500 r/min,在以自来水和去离子水为研磨介质时,MgO粒径随着研磨时间的增加逐渐减小,当研磨时间40 min时MgO的化学反应活性达到最大值;而以无水乙醇为研磨介质时,MgO化学反应活性则随研磨时间的延长持续增加;与未研磨MgO相比,在H₂O₂漂白时使用研磨浓度为10%、研磨转速500 r/min、研磨时间40 min条件下获得的MgO,漂后浆张的松厚度、白度和光散射系数均下降,强度有所提高。