注射成形钕铁硼粘结磁体研究的现状及前景

论述了注射成形钕铁硼粘结磁体的特点及发展趋势，分析了其生产工艺中的四个关键因素。包括磁粉，粘结剂与耦联剂，注射过程，充磁过程，并对这四个关键因素的研究状况作了综合评述，认为今后对注射成形钕铁硼粘结磁体的研究开发将集中在四个主要的方面。     

快淬钕铁硼永磁合金及粘结磁体

综述了快淬钕铁硼磁粉、各向同性粘结钕铁硼磁体、各向异性钕铁硼磁粉及粘结磁体、双相纳米复合磁粉及粘结磁体的国内外现状、前景以及粘结NdFeB磁体的应用。     

注射成形粘结钕铁硼磁体复合粉研究

磁体的注射成形是一种高效生产的近净成形技术。为了制备出具有较好综合性能的注射成形粘结钕铁硼永磁材料,研究了粘结剂对注射成形磁体的磁性能、加工性能及力学性能的影响;分析了硅烷系列的偶联剂、复合润滑剂和抗氧剂等添加剂对注射成形磁体性能的影响。结果表明,用MQP-B快淬钕铁硼磁粉和尼龙12粘结剂制备出了剩余磁感应强度为0.539 T,磁感矫顽力为345.37 k A/m,内禀矫顽力为681.02 k A/m,最大磁能积为47.37 k J/m3的注射成形钕铁硼磁体。     

注射成形粘结钕铁硼磁体制造工艺

磁体的注射成形是一种高效生产的近净成形技术。本文说明了注射成形粘结钕铁硼磁体用复合粉和磁体的制造工艺及性能测试方法。研究了粘结剂、添加剂的含量以及磁粉装载量对注射成形磁体的加工性能、磁性能及力学性能等的影响规律。并从微观上揭示了其机理。用MQP-B快淬钕铁硼磁粉和尼龙12粘结剂制备出了磁性能为Br:0.539 T,Hcb:345.37 k A/m,Hci:681.02 k A/m,(BH)max:47.37 k J/m3的注射成形钕铁硼磁体。     

粘结钕铁硼磁环在高性能永磁式步进电动机上的应用

钕铁硼粘结磁体是一种将钕铁硼磁粉与高分子树脂或塑料或低熔点合金及各种添加剂均匀混合,用模压、挤出或注射成形等方法制成的复合永磁材料。国内外对其机理的研究已比较深入,本课题仅就钕铁硼粘结磁体特别是应用于高性能永磁式步进电动机的粘结钕铁硼多极磁环的制备工艺中的关键问题进行了研究,内容包括：（１）专用粘结剂的选择;（２）磁粉选择;（３）薄壁磁环自动压制成形;（４）表面防锈处理方式的选择;（５）多极充磁;（６）磁环转子整体注射成形。结果表明：在解决了上述关键工艺问题后,粘结钕铁硼多极磁环已批量应用于高性能永磁式步进电动机,替代进口或使原有的电机升级换代     

粉末注射成形在永磁材料中的应用

讨论了粉末注射成形在粘结磁体生产中的应用和烧结磁体研究开发的现状。介绍了注射成形用磁粉的多种制造方法,常用注射成形粘结磁体和杂合磁体的基本性能及应用。分析了影响注射成形磁体性能的技术关键。指出了粉末注射成形在生产低成本、高精度、高性能磁体的技术优势。     

北科大近终形粘结磁体研究项目顺利通过验收

3月 2 6日 ,北京市科技计划项目“近终形粘结磁体的研究及各向异性NdFeB磁粉中试”顺利通过验收 ,该项目由北京科技大学曲选辉教授领导的课题组承担的。其中 ,各向异性NdFeB磁粉、磁体的性能指标全部超出合同要求 ,自主开发的径轴向两用磁场注射成形机达国际先进水平 ,并获北京市科学技术二等奖。该项目的目标是建立一条年产 30t的各向异性NdFeB磁粉中试生产线 ,解决粘结磁体精密成形关键技术及设备问题 ,推广近终形粘结磁体的应用领域北科大近终形粘结磁体研究项目顺利通过验收     

工艺参数对注射成形各向异性粘结NdFeB磁体性能的影响

研究了注射温度、模具温度、注射压力及注射速度对注射成形各向异性粘结NdFeB磁体的磁性能及力学性能的影响，并分析了其原因。结果表明：注射温度及模具温度对磁体磁性能影响较大，而注射压力则对磁体的抗压强度影响较大。在最佳的注射参数下，获得了最大磁能积和抗压强度分别为90kJ／m^3及130MPa的高性能粘结磁体。     

注射成形烧结钕铁硼永磁体的工艺特点及发展趋势

论述了注射成形烧结钕铁硼永磁体的工艺特点及发展趋势,分析了其生产工艺中的四个关键因素,包括磁粉、粘结剂与添加剂、注射过程和脱脂,并结合目前研究现状对这四个关键因素作了综合评述,介绍了热塑性体系和水溶性体系粘结剂在注射Nd-Fe-B烧结磁体中的应用;在分析现状的基础上,指出了现阶段存在的问题和发展方向.     

温压成形制备d-HDDR各向异性钕铁硼粘结磁体的研究

研究了d-HDDR各向异性NdFeB粘结磁体温压成形过程中粘结剂、润滑剂、成形压力对磁体磁性能的影响.通过温压机理的分析,发现温压工艺的温度主要决定于粘结剂体系的黏度、软化点和凝胶时间.添加适量的润滑剂,可减小粉末间及粉末与模壁间的摩擦力,有利于提高磁体的取向度.增加成形压力能明显提高磁体的密度,从而改善磁体的磁性能.采用合适的温压工艺,可获得取向度高(94%)、磁性能优异[BHmax=159.96 kJ/m3(20.17 MG-Oe)]的粘结钕铁硼永磁体.     

Manufacturing of Injection-Molded NdFeB Magnet with (BH)max111 kJ · m-3

The bonded NdFeB magnets prepared by injection molding meet with the development tendency of the magnet in small volume, light weight and high performance ,and have a good prospect.In this paper, a modified nylonbased binder was developed for powder injection molding of NdFeB bonded magnets.The effects of pretreatment of NdFeB anisotropic magnetic powder produced with HDDR processing on the anti-oxidation behaviors of powder and the final magnetic properties of the molded bonded magnets were studied.The optimal powder loading of 65 vol% was achieved with the modified binder.It was found that the properties of the bonded magnets were mainly affected by the powder surface pretreatment and the intensity of the applied alignment magnetic field during injection molding for a certain powder.Bonded magnets with remanence of 0.820 T, intrinsic coercivity of 1140.3 kA· m-1 and maximum energy product of 111 kJ · m-3 were produced with the optimal processing.     

注射成型粘结NdFeB永磁体

介绍了粘结永磁体的制备工艺,快淬NdFeB磁粉,HDDR磁粉及粘结磁体的磁性.提出了目前注射制备NdFeB磁体的技术开发要点.     

Study on Fabrication Process of Anisotropic Injection Bonded Nd-Fe-B Magnets

This study is on the injection molding process for the fabricating anisotropic Nd-Fe-B bonded magnets. The effects of powder loading, particle size of the magnetic powder, polymer binder and the fabricating process on the magnetic and the mechanical properties of anisotropic Nd-Fe-B magnets were investigated. The proper powder loading, particle size and binder are 60%(vol%), 75–106 μm and PA 1010, respectively. The optimum condition for good magnetic properties of anisotropic injection bonded Nd-Fe-B magnets is mixing the binder and the chemicals in the temperature between 205–215 °C, injection temperature of 265 °C, the injection pressure of 5–6 MPa, the press time of 5 second, and molding temperature of 80 °C. The magnetic properties of anisotropic bonded Nd-Fe-B magnets made in above conditions from d-HDDR powder were: B_r=0.72 T, _iH_c=983 kA/m, (BH)_max=75 kJ/m^c.     

粉末注射成形在软磁材料中的应用

介绍了粉末注射成形在粘结软磁、烧结软磁生产中的应用、研究开发状况。指出粉末注射成形是能够实现低成本生产新性能、新功能的磁体制造技术,应该利用注射成形技术发挥磁性元器件结构功能一体化设计、制造的优势。     

粉末注射成形在软磁材料中的应用

介绍了粉末注射成形在粘结软磁、烧结软磁生产中的应用、研究开发状况。指出粉末注射成形是能够实现低成本生产新性能、新功能的磁体制造技术，强调利用注射成形技术实现磁性元器件结构功能一体化设计、制造的优势。     

Effect of Binder and Additives on Properties of NdFeB Bonded Magnets by Injection Moulding

Properties of NdFeB bonded magnets by injection moulding lie on many factors. The study indicates that those such as coupling agents exterior covering, binder contents, antioxidant and the selection of lubricator have significant effects on the properties of NdFeB bonded magnets. The appropriate choice of additives can improve the properties of NdFeB bonded magnet.     

磁性材料注射成形技术

概括了金属粉末注射成形技术(MIM)制造粘结永磁和烧结磁体的特点和优点。详细介绍MIM粘结永磁和烧结磁体的基本工艺过程及基本要求。综述了注射成形磁性材料的主要研究与发展方向。最后指出磁性材料注射成形技术的研究意义。