动态硫化体系对POE/PP热塑性弹性体性能的影响

研究了不同硫化体系对动态硫化聚烯烃弹性体(POE)/聚丙烯(PP)热塑性弹性体机械性能的影响。结果表明,2,5-二甲基-2,5-双(过氧化叔丁基)(DBPH)作为交联剂最合适,用量为1.56 phr的时候性能最好;三烯丙基异氰酸(TAIC)作为助交联剂最合适,用量为0.195～0.39 phr时最好。     

不同硫化剂含量对动态硫化COPA/SIR热塑性弹性体性能及形态结构的影响

在动态硫化过程中,加入不同含量的硫化剂2,5-二甲基-2,5-二(叔丁基过氧基)己烷(DBPH),共混制备出共聚酰胺(COPA)/硅橡胶(SIR)热塑性弹性体,并利用万能电子拉伸机、动态热分析仪、高压毛细管流变仪和扫描电子显微镜镜分析了不同含量的DBPH对COPA/SIR热塑性弹性体性能及结构的影响。结果表明,不同的硫化剂含量对动态硫化制备出的COPA/SIR热塑性弹性体在力学性能及形态结构上均有影响,硫化剂含量较低时硫化不完全,而当硫化剂较高时会过度交联,导致力学性能不佳。     

硅橡胶/TPU动态硫化热塑性弹性体的配方和加工工艺的研究

以热塑性聚氨酯弹性体(TPU)和有机硅橡胶(SIR)为基体,通过Hakke密炼机采用动态硫化的方法制备了热塑性弹性体(TPV)。研究了不同制备条件下得到的TPV的性能。结果表明,TPU/SIR共混物质量比为50∶50、密炼机加工温度为180℃、转速为70 r/min、硫化时间为4 min时,TPV的加工性能、力学性能、毛细管流变性能和微观形态达到一个较好的平衡点。     

动态硫化法制备三元乙丙橡胶/聚酰胺热塑性弹性体

采用动态硫化技术制备了三元乙丙橡胶(EPDM)／聚酰胺(PA)热塑性弹性体,研究了增容剂种类及用量、硫化体系及其用量、加料顺序、PA用量对其性能的影响,用扫描电镜分析了其相态结构。结果表明,用13份(质量份,下同)的氯化聚乙烯作为增容剂时,对该共混体系的增容效果最好;硫黄硫化体系是EPDM／PA热塑性弹性体的最佳硫化剂,当硫黄用量为2份时,既保证了该热塑性弹性体中的橡胶相能充分交联,又可避免过硫化对产品性能造成的负面影响;PA用量为35份的EPDM／PA热塑性弹性体具有良好的力学性能、耐溶剂性能和耐热老化性能;EPDM以平均粒径为2～5μm的粒子形态均匀分布于PA连续相中。     

乙烯-乙酸乙烯酯共聚物/聚甲醛动态硫化热塑性弹性体的制备

以1,1-二叔丁基过氧基-3,3,5-三甲基环己烷(Luperox231)/N,N’-间苯撑双马来酰亚胺(HVA-2)为硫化体系,采用反应挤出动态硫化法制备了乙烯-乙酸乙烯酯共聚物(EVA)/聚甲醛(POM)动态硫化热塑性弹性体。结果表明,EVA/POM动态硫化热塑性弹性体的综合力学性能明显改善,拉伸强度可达到12 MPa左右,但断裂伸长率较低;螺杆转速和挤出机加工温度对EVA/POM动态硫化热塑性弹性体的力学性能有影响,为制备性能良好的EVA/POM动态硫化热塑性弹性体,螺杆转速设定为250r/min,挤出机加工温度为145~175℃;Luperox231用量的增加使动态硫化热塑性弹性体的拉伸强度和断裂伸长率、永久变形以及肖D硬度均下降,而HVA-2用量的增加使动态硫化热塑性弹性体的拉伸强度和永久变形呈先降低后升高的趋势。     

动态硫化TPU/EVM共混物的结构与性能研究

采用熔融共混法制备热塑性聚氨酯(TPU)/乙烯-乙酸乙烯酯橡胶(EVM)动态硫化共混物,并对其结构与性能进行研究.结果表明,TPU/EVM共混体系实施动态硫化的最佳共混比为75/25,硫化剂BIPB用量为0.8份时共混物性能最佳,且不同共混比的TPU/EVM共混物需要的硫化剂最佳用量不同;动态硫化后的EVM以较大尺寸的相畴分散在TPU中;TPU/EVM动态硫化共混物返炼后仍具有较高的重复使用价值.     

动态硫化EPDM/高聚合度PVC热塑性弹性体力学性能的研究

采用动态硫化的方法制备了三元乙丙橡胶（EPDM）/高聚合度聚氯乙烯（HPVC）热塑性弹性体。考察了PVC聚合度、橡塑比、增塑剂添加量、硫化剂用量（质量分数）及不同促进剂配比对体系性能影响,研究了动态硫化工艺条件（硫化时间和硫化温度）对体系性能的影响。实验结果表明：采用动态硫化方法,选用HPVC-2500、橡塑比为30/70、DOP用量为35份、硫化用量为0.4份及合适促进体系,可以制得性能优良的EPDM/HPVC热塑性弹性体,拉伸强度能达到15.18 MPa,断裂伸长率能达到544%。     

NBR/PVC热塑性弹性体的性能研究及应用

选用不同硫化体系,用动态硫化法制备了丁腈橡胶(NBR)/聚氯乙烯(PVC)热塑性弹性体,考察了硫化体系、增塑剂邻苯二甲酸二辛酯(DOP)用量、填料种类、NBR与PVC的质量比对热塑性弹性体性能的影响.结果表明,采用过氧化二异丙苯/硫磺复合硫化体系硫化的热塑性弹性体的性能较好;炭黑的增强效果优于白炭黑和轻质碳酸钙;DOP用量增加,热塑性弹性体的综合力学性能下降;NBR与PVC的质量比增加,热塑性弹性体的柔性增加.所研制的NBR/PVC经压延塑化造粒、注射成型可以制得某品牌汽车的油箱密封垫片,极大地提高了生产效率,提高了市场竞争力.     

动态硫化型PVC/PNBR热塑性弹性体性能的研究

选用硫磺硫化体系,用动态硫化法制备PVC/PNBR热塑性弹性体。考察了硫化体系对性能的影响,比如硫磺的用量、促进剂的用量以及硫磺与促进剂的质量比率;同时考察了增塑剂的用量及填料对体系性能的影响。结果表明,制得的热塑性弹性体具有优异的力学性能。     

改性胶粉/EPDM/PP热塑性弹性体的制备与性能研究

以乙丙橡胶(EPDM)、聚丙烯(PP)和胶粉等为主要原料,采用动态硫化的方法制备了改性胶粉/EPDM/PP热塑性弹性体,研究了溴化丁基橡胶(BIIR)用量、胶粉的改性剂、热塑性弹性体的硫化剂对改性胶粉/EPDM/PP热塑性弹性体力学性能和耐老化性能的影响,并通过电子扫描电镜观察了热塑性弹性体内部的微观结构。研究结果表明,BIIR用量为12份时,热塑性弹性体的力学性能最优,耐老化性能良好;使用10份松香、6份50%大蒜汁、2份BIIR并用作为改性剂改性的胶粉所制备的热塑性弹性体力学性能最优,耐老化性能良好;使用促进剂TT、硫黄和201树脂并用作为硫化剂所制备的热塑性弹性体力学性能和耐老化性能最优;经过松香、50%大蒜汁和BIIR改性后的胶粉与橡胶基体以及聚丙烯间相界面比较模糊,分散均匀性较好。     

团状模塑料/三元乙丙橡胶共混物的表征及其性能的影响因素

用团状模塑料(DMC)与三元乙丙橡胶(EPDM)共混,以EPDM为连续相、DMC为分散相,制备了DMC/EPDM共混物,并对其微观结构进行了表征,研究了DMC与EPDM的质量比、过氧化物硫化荆的种类和用量以及白炭黑的用量对共混物性能的影响.结果表明,DMC和EPDM的界面作用强,相容性好;过氧化苯甲酰(BPO)作硫化荆要好于用过氧化二异丙苯;当DMC与EPDM的质量比为90/100、BPO为5份、白炭黑为50份时,共混物的力学性能和耐热老化性较好.     

增容剂对硅橡胶/热塑性聚氨酯热塑性硫化胶性能的影响

采用动态硫化法制备了甲基乙烯基硅橡胶（MVQ）/热塑性聚氨酯（TPU）共混型热塑性硫化胶（TPV）,考察了增容剂的种类及用量对TPV力学性能及加工流变性能的影响。结果表明,随着增容剂用量的增加,TPV的力学性能呈先上升后下降的趋势。相比于乙烯丙烯酸共聚物和乙烯与乙酸乙烯嵌段共聚物,用聚烯烃弹性体接枝马来酸酐（POE-g-MAH）作为增容剂时TPV的力学性能更为优异。3种增容剂均能提高TPV中MVQ相与TPU相的相容性。当POE-g-MAH的用量为6份时,TPV中MVQ相与TPU相的玻璃化转变温度靠近程度最大,两相界面较为模糊,增容效果最佳。     

Systematic investigation on the effect of crosslinking agent type and dosage on the performance of TPU/MVQ based thermoplastic vulcanizates

Dynamic vulcanized thermoplastic polyurethane (TPU)/methyl vinyl silicone rubber (MVQ) thermoplastic vulcanizates (TPVs) were prepared in torque rheometer. The influence of the type and amount of peroxide crosslinking agent on the mechanical properties, thermal stability, micromorphology and melt flowability was systematically investigated. The results showed that the mechanical properties of the TPVs vulcanized by 2,5-dimethyl-2,5-di (tert-butyl peroxy) hexane (DBPH) first increased and then decreased with increasing the peroxide amount, while for dicumyl peroxide (DCP) vulcanizing system the mechanical properties slowly increased. Besides, the comprehensive mechanical properties vulcanized by DBPH were better than those of DCP group. The results of the thermogravimetric analysis showed that the TPVs vulcanized by DBPH had better heat stability, corresponding to the excellent thermo-oxidative aging performance and the 38% increase in tensile strength after aging. In addition, the MVQ rubber particles showed better dispersing performance for DBPH vulcanizing system. The melt flow rate of the TPVs showed a linear relationship with increasing DBPH dosage and became worse after the amount of crosslinking agent exceeded 1.5 phr. By comprehensive comparison, the TPVs have better performance when use peroxide DBPH as the crosslinking agent and the dosage is 1.5 phr.     

动态硫化三元乙丙橡胶(EPDM)/聚丙烯(PP)热塑性弹性体的力学性能

研究了双螺杆挤出机制备EPDM/PP热塑性弹性体的工艺条件对其力学性能的影响,结果显示,当橡塑比为60/40.EPDM与PP预混合两次,双螺杆挤出机转速约9.5Hz,硫化剂的量为10份时,热塑性弹性体有较好的力学性能。     

阻燃,抗静电NBR／PVC热塑性弹性体的制备

用动态硫化法制备了具有阻燃、抗静电性能的丁腈橡胶／聚氯乙烯热塑性弹性体,研究了橡塑共混比、导电炭黑、阻燃剂、硫化剂用量以及返炼等对ＴＰＥ的导电性、阻燃性及力学性能的影响。结果表明,为得到综合性能较好的热塑性弹性体,较适宜的制备条件为ＮＢＲ／ＰＶＣ配比为６０／４０、导电炭黑用量为３０、氢氧化铝用量为４０、硫黄用量为１．３。     

The effect of peroxide crosslinking on thermal,mechanical, and rheological properties of polycaprolactone/epoxidized natural rubber blends

Polycaprolactone (PCL)/epoxidized natural rubber (ENR) blends (PCL/ENR = 70/30, 50/50 wt/wt) were prepared by a melt mixing in an internal mixer in the presence of a small amount (0.5 and 1 phr) of dicumyl peroxide. The effect of peroxide crosslinking on thermal, mechanical, and rheological properties of the blends was investigated by means of DSC, tensile test, and small amplitude oscillating rheometer, respectively. It was revealed that peroxide crosslinking enhanced degree of crystallinity of PCL phase and its non-isothermal melt crystallization temperature. The crosslinked blends behave like a thermoplastic elastomer exhibiting high elongation-at-break and fairly good elastic recovery as well as melt processibility. From melt rheological analysis, the peroxide crosslinked blends showed more pronounced shear thinning effect and higher elasticity compared to simple blends.     

聚氯乙烯/丁腈胶粉共混型热塑性弹性体

将聚氯乙烯与废丁腈胶粉经高温机械共混，制备了动态交联的共混型热塑性弹性体。讨论了共混比，硫化体系及其用量，废胶粉品种（丁腈胶粉，轮胎胶粉）等因素对热塑性弹性体性能的影响，同时将聚氯乙烯／丁腈胶粉与聚氯乙烯／轮胎胶粉制备的共混型热塑性弹性体的性能进行了比较。结果表明，以聚氯乙烯100份（质量份，下同），邻苯二甲酸二辛酯50份，丁腈胶粉80份，丁腈橡胶20份，过氧化二异丙苯0．5份，氧化锌5份及适量其他助剂可制得综合性能较好的共混型热塑性弹性体。扫描电镜结果显示该共混型热塑性弹性体具有较好的相容性。     

三元乙丙橡胶/聚丙烯动态硫化热塑性弹性体的相态结构

用扫描电镜研究了三元乙丙橡胶(EPDM)聚/丙烯(PP)动态硫化热塑性弹性体(TPV)相态结构的形成过程,探讨了交联密度、制备工艺、螺杆转速对EPDM/PP TPV相态结构的影响。结果表明,采用以酚醛树脂为硫化剂的动态硫化工艺制备的EPDM/PP TPV,其相态结构实现了由EPDM和PP组成的双连续相到以EPDM为分散相、PP为连续相的转变;当硫化剂用量为7份时,橡胶相硫化速率和交联密度最大;当螺杆转速为180 r/m in时,反应性挤出工艺较之密炼机工艺制备的EPDM/PP TPV的橡胶粒子更细小、分散更均匀。     

交联硫化体系对PP／POE／EPDM热塑性弹性体性能的影响

采用动态硫化法制备聚丙烯／聚烯烃弹性体／三元乙丙橡胶（PP/POE／EPDM）共混型热塑性弹性体,研究了交联前后不同POE／EPDM并用对比体系力学性能的影响。采用交联剂过氧化二异丙苯（DCP）及DCP／S硫化体系对PP／POE／EPDM体系进行硫化,研究了力学性能的变化。结果表明,EPDM可有效降低材料的硬度和断裂永久变形。助交联剂硫黄（S）对PP／POE／EPDM体系有较好的硫化作用,固定DCP用量为3份,S用量为0．4份时,体系力学性能最佳,交联对体系硬度影响很小。     

聚烯烃弹性体/聚丙烯热塑性弹性体的制备及力学性能

以过氧化物为硫化剂,用动态硫化法制备了聚烯烃弹性体(POE)/聚丙烯(PP)热塑性弹性体,研究了硫化剂用量、填料种类和加工次数对体系力学性能的影响。结果表明,增加硫化剂用量可以提高体系的拉伸强度,降低拉伸永久变形和压缩永久变形。碳酸钙和滑石粉对POE/PP体系无明显增强作用,炭黑的增强作用较此二者明显一些,这三种填料加入后都会使体系的扯断伸长率降低而硬度增大。加入石蜡油会使体系的扯断伸长率和压缩永久变形增大、硬度和拉伸强度降低。加工次数对POE/PP体系的力学性能无明显影响,说明体系具有较好的重复加工性能。