ABS／PMMA合金性能的研究

制备了不同配比的ABS/PMMA合金,分别研究了PMMA含量、粘度对合金的缺口冲击强度、拉伸强度、热变形温度、熔体流动速率等性能的影响。结果表明：ABS中引入PMMA可以提高耐热性能;ABS与PMMA共混能提高PMMA的力学性能特别是缺口冲击强度,当ABS/PMMA中PMMA为20%时,共混物具有最优的力学性能;一般情况下,ABS/PMMA合金的流动性介于ABS和PMMA的流动性之间,采用高粘度PMMA的合金性能较佳。     

ABS/SAN/中粘度PMMA三元共混物的性能研究

制备不同配比的丙烯腈－丁二烯－苯乙烯（ABS）／苯乙烯－丙烯腈（SAN）／中粘度聚甲基丙烯酸甲酯（PMMA）合金，分别测试其缺口冲击强度、拉伸强度、热变形温度、熔体流动指数等，结果表明：ABS／SAN可以引发中粘度PMMA产生大量的银纹，从而大幅度提高共混物的冲击强度；引入中粘度PMMA可以提高ABS／SAN的耐热性能；添加中粘度PMMA，合金的流动性能呈现下降的趋势。     

ABS／PMMA合金的配比与性能

制备不同配比的ABS／PMMA合金,分别测试其缺口冲击强度、拉促强度、热变形温度、熔体指数,结果表明：1）ABS中引入PMMA强以提高耐热,2）ABS与PMMA共混能提高PMMA的力学性能特别是缺口冲击强度。3）当ABS／PMMA中PMMA为20％时,共混物具有最优的力学性能。4）一般情况下,ABS／PMMA合金的流动性介于ABS和PMMA的之间。     

超韧PA6/ABS合金的制备

以苯乙烯-马来酸酐（SMA）共聚物为增容剂，考察了ABS及SMA的含量对PA6／ABS共混体系的力学性能的影响；并利用SEM研究了PA6／ABS冲击断面的相结构。研究表明：SMA是PA6／ABS共混体系的有效增容剂。随着其含量的增加，分散相ABS粒子的尺寸减小，分散更加均匀，能显著地改善PA6／ABS共混物的冲击、拉伸和弯曲性能。在该共混体系中，ABS含量的增加能够大幅度地提高PA6／ABS共混物的冲击韧性；但当ABS含量超过10％时，将使PA6／ABS共混物的拉伸和弯曲性能明显下降。SMA的添加量为0．5％，且质量比为90／10的PA6／ABS共混体系能保持较好的加工性能，制备的PA6／ABS合金具有最佳的综合力学性能和超高韧性．Izod缺口冲击强度高达1200J／m。     

共混方式对ABS／PA6／SMA共混体系形态和力学性能的影响

以苯乙烯-马来酸酐共聚物（SMA）为反应增容剂，研究不同共混工艺和ABS／PA6配比对三共混体系聚集态结构和力学性能的影响。结果表明：SMA对共混体系增容效果显著，并明显改善了ABS／PA6共混体系的力学性能。其中当PA6用量为30份和40份时，SMA先与ABS共混再与PA6共混的方式所生成共混物的性能优于SMA先与PA6共混再与ABS共混的方式。PA6用量为30份时性能最好，共混物的分散相尺寸达到最小值0．31μm，分散相颗粒PA6周长面积比为最大值0．46，拉伸强度和冲击强度也分别为最大值63．2MPa和8．29kJ／m^2。当PA6用量达到45份时，共混方式对共混物的力学性能影响不大。研究表明，当ABS为连续相时，共混方式可以强烈地影响ABS／PA6共混物体系的聚集态结构和力学性能，而PA6和ABS向共连续相发展时，共混方式对ABS／PA6聚集态结构和力学性能则影响不大。     

ABS/HIPS相容性的研究

采用苯乙烯-马来酸酐共聚物(SMA)作为丙烯腈-丁二烯-苯乙烯共聚物/高抗冲聚苯乙烯(ABS/HIPS)的相容剂,研究了SMA对ABS/HIPS共混体系力学性能的影响,并用扫描电子显微镜对共混物的亚微观形态结构进行了分析。结果表明,SMA的加入起到了很好的增容作用。随着HIPS/SMA用量的增加,共混物的冲击性能先增大后减小,当HIPS/SMA=8.5/1.5(质量比),且HIPS/SMA质量分数为10%时,共混物的缺口冲击强度达到97.1J/m,同时拉伸强度和弯曲强度最大。     

高性能PC/ABS合金的研究

利用双螺杆挤出机制备了PC/ABS系列合金,探讨了甲基丙烯酸甲酯/丁二烯/苯乙烯共聚物(MBS)和苯乙烯/马来酸酐共聚物(SMA)对PC/ABS合金的增韧和增容作用,采用力学测试方法、扫描电子显微镜(SEM)研究了MBS和SMA对PC/ABS合金的力学性能和形态结构的影响。结果表明:在PC/ABS合金(70/30)体系中,加入6份MBS,合金的缺口冲击强度为86 kJ/m2,是没加MBS时的1.5倍左右;而拉伸强度得到了较好的保持;SMA与MBS复合起来以后,具有一定的协同效应,当SMA、MBS质量分数分别为4%、6%时,合金的缺口冲击强度达到115 kJ/m2,拉伸强度接近单独PC/ABS(70/30)合金,为56.5 MPa。     

基于快速热循环注塑工艺要求的ABS改性

在双螺杆挤出机上制备了能满足快速热循环注塑工艺要求的丙烯腈一丁二烯一苯乙烯三元共聚物（ABS）／聚甲基丙烯酸甲酯（PMMA）共混物,测试了力学性能和光学性能。结果表明,PMMA可提高ABS／PMMA共混物的拉伸强度、弹性模量和洛氏硬度．但降低了合金的冲击强度和断裂伸长率;抗氧剂抑制了聚合物共混过程中的氧化降解,提高了共混物的性能;在相同注塑工艺条件下,w（PMMA）为10％时,共混物的光泽度提高了4％。     

PMMA及AS在ABS高胶粉增韧回收ABS改性中的应用研究

利用聚甲基丙烯酸甲酯(PMMA)及丙烯腈-苯乙烯共聚物(AS)对经丙烯腈-丁二烯-苯乙烯(ABS)高胶粉增韧的回收ABS进行改性.研究表明,PMMA及AS均可以提高共混物的拉伸强度、弯曲强度及硬度,而冲击强度呈下降趋势,但除冲击强度及熔体质量流动速率外,添加PMMA的共混体系的力学性能等方面的指标优于添加AS的体系.     

ABS/PET合金的组成配比及SMA的增容化研究

以苯乙烯接枝马来酸酐共聚物(SMA)为增容剂对丙烯睛-丁二烯-苯乙烯共聚物(ABS)/聚对苯二甲酸乙二醇酯(PET)共混物进行研究,探讨了SMA用量对合金的力学性能和热稳定性的影响;并进一步研究了无增容剂下ABS与PET之间配比对合金性能的影响.研究表明:增容剂SMA用量为10 phr时,合金的冲击强度和断裂伸长率分别提高20%和50%;随着PET用量的增加,合金的弯曲强度、拉伸强度和维卡软化温度不断提高,当PET用量接近50%时发生相转变;断裂伸长率在PET的质量分数为30%时达到最低(32%).通过示差扫描量热法(DSC)测试,发现ABS破坏了PET的结晶行为,且合金中两者的玻璃化转变温度存在重合现象.通过扫描电子显微镜(SEM)和偏光显微镜观察发现,SMA增容的ABS/PET合金中PET颗粒尺寸较小且分散较好;PET晶粒在ABS中可以形成"岛"相和连续相.     

Compatibility and thermal properties of poly(acrylonitrile–butadiene–styrene) copolymer blends with poly(methyl methacrylate) and poly(styrene‐co‐acrylonitrile)

The mechanical and heat‐resistant properties of acrylonitrile–butadiene–styrene (ABS) binary and ternary blends were investigated. The relationship of compatibility and properties was discussed. The results show that poly(methyl methacrylate) (PMMA) and styrene–maleic anhydride (SMA) can improve the thermal properties of conventional ABS. The Izod impact property of ABS/PMMA blends increases significantly with the addition of PMMA, whereas that of ABS/SMA blends decreases significantly with the addition of SMA. Blends mixed with high‐viscosity PMMA are characterized by higher heat‐distortion temperature (HDT), and their heat resistance is similar to that of blends mixed with SMA. For high‐viscosity PMMA, from 10 to 20%, it is clear that blends appear at the brittle–ductile transition, which is related to the compatibility of the two phases. TEM micrographs show low‐content and high‐viscosity PMMA in large, abnormally shaped forms in the matrix. Compatibility between PMMA and ABS is dependent on both the amount and the viscosity of PMMA. When the amount of high‐viscosity PMMA varied from 10 to 20 wt %, the morphology of the ABS binary blends varied from poor to satisfactory compatibility. As the viscosity of PMMA decreases, the critical amount of PMMA needed for the compatibility of the two phases also decreases. SMA, as a compatibilizer, improved the interfacial adhesiveness of ABS and PMMA, which results in PMMA having good dispersion in the matrix. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 2652–2660, 2002     

聚环氧酯的合成及其对PC/ABS相容性的影响

以双酚A环氧树脂和己二酸合成了聚己二酸环氧酯,将环氧酯作为相容剂加入到PC/ABS中通过双螺杆挤出机并注射成型制备了合金,与马来酸酐接枝聚苯乙烯（SMA）相容剂增容的合金的力学性能及分散形态进行了对比。结果表明,聚环氧酯对PC相具有良好的相容性,而SMA对ABS相的相容性较好,二者复合使用可以显著改善合金的相容性;聚环氧酯能明显提高PC/ABS合金的拉伸强度和缺口冲击强度,但过量加入会降低合金的冲击强度;SEM结果表明少量的聚环氧酯即可以使ABS分散相分布均匀,与SMA并用可以使分散相尺寸减小,提高相容性。     

CPVC/ABS/AS与CPVC/ABS共混体系性能研究

研究了丙烯腈丁二烯苯乙烯共聚物(ABS)含量对氯化聚氯乙烯(CPVC)/ABS/丙烯腈苯乙烯共聚物（AS）及CPVC/ABS共混体系力学性能、耐热性能以及阻燃性能的影响。结果表明,在CPVC/ABS/AS三元共混体系中,当ABS含量由零增加到30 %（质量分数,下同）时,共混体系的冲击强度由11.5 kJ/m2上升至39.1 kJ/m2;在CPVC/ABS二元共混体系中,当ABS含量由零增加到25 %时,共混体系的冲击强度由11.1 kJ/m2上升至52.6 kJ/m2,拉伸强度、弯曲强度和维卡软化点随着ABS含量的增加而下降;共混体系的阻燃性能与CPVC用量密切相关,在CPVC∶ABS（或ABS+AS）=6∶4时,共混体系的极限氧指数达到了31 %。     

新型耐热级SMA/ABS工程塑料合金

介绍耐热级ＳＭＡ／ＡＢＳ工程塑料合金的制备和性能,研究了ＳＭＡ、ＡＢＳ配比、增韧剂对合金性能的影响。结果表明,ＳＭＡ的加入使冲击强度下降,但加入增韧剂可提高合金的冲击强度达到或超过ＡＢＳ水平,当ＳＭＡ∶增韧剂∶ＡＢＳ＝５０∶２５∶２５时,缺口冲击强度可达２００Ｊ／ｍ。已推出通用级Ｅ－２２０用于ＰＣ改性、耐热级Ｈ２５１用于耐热要求的家电、玻纤增强级２５１Ｇ用于汽车零部件     

橡胶相结构特征对ABS树脂力学性能的影响

采用乳液聚合法合成了具有橡胶结构特征的丙烯腈丁二烯苯乙烯共聚物（ABS）,将其与苯乙烯丙烯腈共聚物（SAN）共混,制备了ABS/SAN共混物,并系统地研究了橡胶相结构特征的影响因素及其对共混物力学性能及其形变机理的影响。结果表明,随着聚丁二烯（PB）橡胶粒子粒径的增大,共混物的冲击强度提高,拉伸强度降低;随着橡胶粒子粒径的增大,共混物形变机理从单一的银纹向橡胶粒子空洞化诱发基体剪切屈服转变。     

聚甲基丙烯酸甲酯/ABS共混体系力学性能研究

采用双螺杆熔融共混工艺路线，通过选用合适牌号的聚甲基丙烯酸甲酯及ABS为基本原料，通过控制合适共混工艺条件，制备了一系列不同配比的聚甲基丙烯酸甲酯／ABS塑料合金材料。采用电子万能试验机、悬臂梁冲击实验机等测试手段对合金的力学性能进行了研究，结果表明：聚甲基丙烯酸甲酯／ABS合金材料的拉伸强度随聚甲基丙烯酸甲酯含量的增加而增大，断裂伸长率随着聚甲基丙烯酸甲酯含量的增加而减小，缺口冲击强度随聚甲基丙烯酸甲酯含量的增加而减小。     

Compatibility enhancement of ABS/polycarbonate blends

The effects of blend composition, melt viscosity of poly(acrylonitrile-butadiene-styrene) (ABS), and compatibilizing effect of poly(methyl methacrylate) (PMMA) on mechanical properties of ABS/polycarbonate (PC) blends at ABS-rich compositions were studied. As the content of PC was increased, impact strength and Vicat softening temperature (VST) were increased. As the melt viscosity of ABS was increased near to that of PC, finer distribution of dispersed PC phase and consequent enhanced impact strength and VST were observed. The compatibilizing effect of PMMA can be ascer-tained from the enhanced properties of ¼-inch notch impact strength, VST, tensilestrength, and the morphology observed by a scanning electron microscope. The improved adhesion of the ABS/PC interface by PMMA changed the fracture mechanism and reduced the notch sensitivity of blends. © 1998 John Wiley & Sons, Inc. J Appl Polym Sci 69: 533–542, 1998