补强剂和共混工艺对PA/PVC/NBR三元共混弹性体性能的影响

在选择三元共聚尼龙（PA）、聚氯乙烯（PVC）、丁腈橡胶（NBR）为主体材料，制备PA／PVC／NBR（10／30／60）三元共混弹性体的工作基础上，进一步探讨了填料品种和用量，共混温度，加料顺序等因素PA／PVC／NBR三元共混弹性体的影响。试验结果表明：在PA／PVC／NBR（10／30／60）共混体系中，补强型填料的补强效果优于非补强型的填料，6种填料补强效果依次是：快压出炭黑＞半补强炭黑＞白炭黑＞活性重质，CaCO3＞陶土＞滑石粉，快压出炭黑的适宜用量是20－50份。在制备PA／PVC／NBR三元共混物时，适宜的共混温度是122－140℃，并且采用二段法混工艺制得的共混物性能优于采用一段法共混工艺。     

PVC／NBR／BR三元共混弹性体的制备与研究

本文重点叙述了聚氯乙烯(PVC)、丁腈橡胶(NBR)、顺丁橡胶(BR)三元共混弹性体的制备与研究,通过添加顺丁胶后,三元共混体的冲击回弹性、耐磨性及耐寒性均比二元PVC/NBR共混物得以改善,但拉仲强度、断裂伸长率及耐油性降低。获得最佳综合性能的共混比为PVC:NBR:BR=30:60:10(重量比)。实验表明,PVC/NBR/BR三元共混弹性体是复相体系,有较好的相容性。     

高聚合度聚氯乙烯/聚甲醛/丁腈橡胶三元共混弹性体的研究

采用机械共混、化学交联工艺制备高聚合度聚氯乙烯 (HMWPVC) /聚甲醛 (POM) /丁腈橡胶 (NBR)三元共混弹性体合金。重点讨论了 HMWPVC/ POM/ N BR共混比、PVC树脂的相对分子质量、NBR橡胶的丙烯腈含量、硫化体系等因素对弹性体性能的影响。 HMWPVC/ POM/ NBR共混弹性体的力学性能、耐油耐溶剂性能优于PVC/ POM/ NBR共混弹性体。采用动态粘弹谱仪、扫描电子显微镜等现代分析技术研究了 HMWPV C/ POM/ NBR三元共混弹性体的微观结构 ,结果显示 H MWPVC/ POM/ NBR(10 / 10 / 80 )三元共混弹性体的 tgδ- T谱上只出现一个峰值 ,其对应的玻璃化转变温度为 - 0 .8℃ ,三元共混弹性体具有较好的相容性     

PVC／POM／NBR三元共混弹性体的研究

采用高温机械共混、化学交联工艺制备PVC/POM/NBR三元共混弹性体。重点讨论了PVC/POM/NBR共混比、PVC树脂的分子量、NBR橡胶的丙烯腈含量、硫化体系等因素对共混弹性体性能的影响。结果表明,PVC/POM/NBR（20/10/70）三元共混弹性体具有优异的物理机械性能和耐油耐溶剂性能。用动态粘弹谱仪和扫描电子显微镜等现代分析技术研究其微观结构,结果显示PVC/POM/NBR（20/10/70）三元共混弹性体的tgδ-T谱上只出一个峰值,其对应的玻璃化转变温度为 3.7℃,表现出较好的相容性。     

配合剂和共混工艺对PVC／POM／NBR三元共混弹性体性能的影响

在制备PVC／POM／NBR三元共混弱性体的研究基础上,进一步探讨了防老剂品种及用量、炭黑品种及用量、增塑剂品种、共混工艺等因素对共混物力学性能的影响。结果表明：选择PVC／POM／NBR（20／10／70）100,半补强炭黑30－45,防老剂MB1.0－1.5,硫黄硫化体系及适量DOP,并选择共混温度175－180℃,共混时间4－5min以及采用先将PCV与NBR制成二元共混物再与已塑化的POM共混制成三元共混物为共混工艺,可制得综合性能较佳的PVC／POM／NBR三元共混弹性体。     

PVC/TPU/NBR三元共混物的制备及性能研究

对PVC／热塑性聚氨酯（TPU）／SR三元共混物的性能进行研究，重点讨论NBR品种、TPU／NBR并用比、PVC聚合度、增塑剂DOP和硫化剂DCP用量对PVC／TPU／NBR三元共混物性能的影响。结果表明。PVC／TPU／NBR-3604三元共混物的物理性能较优；PVC／TPU／NBR-3604三元共混物的拉断伸长率和拉断永久变形均随着PVC聚合度的增大基本呈上升趋势；随着增塑剂DOP用量的增大，共混物的邵尔A型硬度、拉伸强度、撕裂强度和拉断永久变形均基本呈下降趋势，拉断伸长率增大；随着硫化剂DCP用量的增大。共混物的拉伸强度和拉断伸长率变化不大，撕裂强度基本呈逐渐减小的趋势。不同PVC／TPU／SR三元共混物的扫描电子显微镜照片表明，NBR与PVC和TPU的相容性较好。     

动态硫化制备PA/SAN/NBR合金冲击性能的研究

采用酚醛树脂（PF）、DCP和硫磺等硫化体系对PA／SAN／NBR共混体系进行动态硫化,研究了该共混体系的缺口冲击强度、冲击行为和分散相形态。结果发现,PF比其它硫化体系更有效,可制得超韧的PA／SAN／NBR（50／25／25）合金;SEM照片表明,随着PF用量增加,共混体系中分散相粒子变小,形态变规则,动态硫化体系的相容性变好。     

ABS/PBT/弹性体三元共混合金的研究

研究了弹性体NBR和SBS对ABS／PBT共混合金体系的力学性能和熔体质量流动速率的影响，并对共混合金的相容性进行了研究。结果表明：加入弹性体NBR后，共混合金在保持较好刚性的同时，断裂伸长率和韧性得到了较大的改善。当NBR用量为20份时，共混合金的断裂伸长率提高了313％，冲击强度提高了54％；SBS对ABS／PBT共混合金的增韧效果不明显，加入弹性体后，ABS／PBT共混合金体系的粘度增大，MFR降低，但仍明显好于纯ABS。     

NBR/PVC共混物耐溶剂性能的研究

考察了NBR／PVC共混比和NBR／PVC与EPDM,IIR或PU三元硫化共混物在天那水中的体积变化和物理性能变化。结果表明,当NBR／PVC以70／30共混时,二元共混物的耐溶剂性能最好;NBR／PVC／PU共混比为50／20／30时,三元共混物耐天那水性能最好,经天那水浸泡后的性能变化很小。     

NBR/三元尼龙/二元尼龙三元共混型热塑性弹性体制备工艺与性能的研究

在开炼机上用动态硫化法制备了NBR／三元尼龙／二元尼龙三元共混型热塑性弹性体。研究了共混工艺、返炼次数、动态硫化温度、二元尼龙用量等因素对材料性能的影响。NBR／三元尼龙／二元尼龙三元共混型热塑性弹性体不仅具有优异的耐溶剂性，而且其物理性能也较好。     

PA6含量对PVC/PA6共混物形态结构与力学性能的影响

以EVA-g-MAH为相容剂,将PVC与自制的低熔点PA6共混制备了PVC/PA6共混物。通过扫描电子显微镜(SEM)和力学性能测试研究了PA6含量对PVC/PA6共混物形态结构及力学性能的影响。SEM分析结果显示:随着PA6含量的增加,PVC/PA6共混物的分散相尺寸逐渐增大,当PA6含量为10%时,共混物中分散相的分散尺寸最小为1μm;当PA6含量为50%时,共混物为两相共连续结构;当PA6含量为60%时,共混物中PA6为连续相,PVC为分散相。力学性能测试结果表明:当PA6含量为10%时,共混物的缺口冲击强度和拉伸强度都较PVC有明显提高,分别提高了约50%与30%,达到了6.29kJ/m2和60MPa。采用差示扫描量热仪(DSC)研究了PVC/PA6共混物的结晶温度,检测结果显示:PVC/PA6共混物呈现非晶结构。     

NBR/PVC共混胶的结构与性能

采用机械共混法和乳液共沉法制备了NBR/PVC共混胶,通过差示扫描量热仪(DSC)和场发射扫描电子显微镜(FE-SEM)对共混胶的微观形貌、结构进行了表征,考察了共混方式和共混胶配比对其力学性能的影响,并比较了共混胶、CPE、P-83对硬质/软质PVC的改性效果。结果表明:①与机械共混胶相比,乳液共沉胶混合得更均匀,分散性更好,其分子级混合程度更好;②乳液共沉胶试样的力学性能在总体上优于机械共混胶;③对于硬质PVC,CPE的改性效果优于其他改性剂;④对于软质PVC,乳液共沉胶的改性效果最好,特别是对撕裂强度的提高非常明显。     

Study on the damping of EVM based blends

The mechanical and damping properties of blends of ethylene‐vinyl acetate rubber(VA content >40 wt %) (EVM)/nitrile butadiene rubber (NBR) and EVM/ethylene‐propylene‐diene copolymer (EPDM), both with 1.4 phr BIPB (bis (tert‐butyl peroxy isopropyl) benzene) as curing agent, were investigated by DMA. The effect of polyvinyl chloride (PVC), chlorinated polyvinyl chloride (CPVC), and dicumyl peroxide (DCP) on the damping and mechanical properties of both rubber blends were studied. The results showed that in EVM/EPDM/PVC blends, EPDM was immiscible with EVM and could not expand the damping range of EVM at low temperature. PVC was miscible with EVM and dramatically improved the damping property of EVM at high temperature while keeping good mechanical performance. In EVM/NBR/PVC blends, PVC was partially miscible with EVM/NBR blends and remarkably widened the effective damping temperature range from 41.1°C for EVM/NBR to 62.4°C, while CPVC mixed EVM/NBR blends had an expanded effective damping temperature range of 63.5°C with only one damping peak. Curing agents BIPB and DCP had a similar influence on EVM/EPDM blends. DCP, however, dramatically raised the height of tan δ peak of EVM/NBR = 80/20 and expanded its effective damping temperature range to 64.9°C. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

氢化丁腈橡胶与聚氯乙烯或聚乙烯共混

研究氢化丁腈橡胶（HNBR）与聚氯乙烯（PVC）或聚乙烯（PE）的共混，该HNBR是用偶氨法常压氢化丁腈胶乳制得的。共混物的力学性能表明，在HNBR质量分数为40％以上时，2种共混物均呈现热性橡胶性能。HNBR／PVC共混物在拉伸强度方面呈现加和关系。热老化后HNBR／PE共混物的力学性能比NBR／PE共混物的好得多。用扫描电镜观察HNBR／PE 混物的断面形态。并用DSC曲线研究了HNBR／PE共混物的结晶变化。     

改性矿物填料增强橡胶/聚氯乙烯共混体系

研究了橡胶、增塑剂、矿物填料和表面处理剂对橡胶／聚氯乙烯(PVC)共混物力学性能的影响,用扫描电镜分析了有机胺类表面处理剂改性高岭土／丁腈橡胶(NBR)／PVC的界面结合状况。结果表明,当NBR用量为30份,邻苯二甲酸二辛酯用量为60份,有机胺类表面处理剂质量分数为3％,填充60份的超细碳酸钙或高岭土或牌号为SMF的蒙脱土时,可得到力学性能较佳的NBR／PVC共混物;不同矿物填料对NBR／PVC共混物的增强作用不同,经有机胺类表面处理剂改性后,以超细碳酸钙、高岭土和蒙脱土SMF的增强效果最为明显。     

Mechanical Properties and Thermooxidative Aging of a Ternary Blend,Pvc/Enr/Nbr,Compared with the Binary Blends of Pvc

In the quest to improve the thermooxidative aging of the poly(vinyl chloride)/epoxidized natural rubber (PVC/ENR) blend, nitrile rubber (NBR) was incorporated into the blend to yield a ternary blend of PVC/ENR/NBR. A Brabender Plasticorder with a mixing attachment was used to perform the melt mixing at 150°C and 50 rpm followed by compression molding. The mechanical properties, dynamic mechanical properties, and thermooxidative aging behavior of the ternary blend were compared with those of the binary blends (i.e., PVC/ENR and PVC/NBR). It was found that the ternary blend exhibits mechanical properties which are superior to those of PVC/ENR. A single glass transition temperature (T _g) obtained from dynamic mechanical analysis coupled with synergism in the modulus and some other mechanical properties indicate that PVC, ENR, and NBR form a single phase (miscible system) in the ternary blend. Di-2-ethyl hexylphthalate (DOP) plasti-cizer improves the aging resistance of the blends generally, whereas the presence of CaCO₃ as a filler only imparts minor influences on the properties and aging resistance of the blends.     

耐油性PA6/NBR共混物的制备与性能研究

采用不同种类的丁腈橡胶(NBR)与聚酰胺6(PA6)熔融共混制备了聚酰胺6/丁腈橡胶混合物(PA6/NBR),考察了共混过程中转矩值的变化,并研究了不同腈基含量共混物的拉伸性能及耐溶剂性能。结果表明,随着橡胶相含量的增加,共混物的熔体黏度、体积溶胀率与质量溶胀率均显著提高,但拉伸强度下降。红外光谱分析表面NBR与PA6在高温高剪切作用下存在微化学反应,并且随腈基含量的增加,PA6/NBR共混物的平衡转矩值增大,拉伸强度明显提高,耐溶剂性下降。     

聚氯乙烯/丁腈橡胶/顺丁橡胶浅色模压胶辊的研制

研究采用聚氯乙烯／丁腈橡胶／顺丁橡胶三元共混制备模压浅色胶辊的配方和工艺，主要探讨ＰＶＣ／ＮＢＲ／ＢＲ共混比，稳定剂，填充剂及硫化体系等因素对橡塑并用胶辊性能的影响。实验结果表明：选择ＰＶＣ／ＮＢＲ／ＢＲ＝３０／６０／１０，并配以过氧化物加少量硫黄的硫化体系及白炭黑等助剂，可制得综合性能较好的浅色橡塑胶辊。     

EPDM／PA增强共混的初步研究