One Method of Determination of the Effective Absorption Coefficient in Pulsed Laser Irradiation of Metals

An experimentaltheoretical method of determination of the absorption coefficients in laser treatment of metals has been proposed based on the solution of the boundaryvalue axisymmetric problem of heat conduction for a halfspace and metallographic measurements of the dimensions of the thermalhardening zone.     

Deformation in spinel

Stoichiometric MgAl₂O₄ spinel was deformed in compression at temperatures from 1790 to 1895 C and the dislocation structures analysed by transmission electron microscopy. {1 1 1}1 1 0 slip was observed on both the primary and cross-slip systems, and there was much secondary slip as well; all six 1 1 0 Burgers vectors were present in electron micrographs. This secondary slip leads to very high work-hardening rates, approximately/70 at 1790 C, where is the shear modulus. Since it is known that deformation in nonstoichiometric (alumina-rich) spinel crystals occurs by {1 1 0}1 1 0 slip, the electrostatic and geometric aspects of 1/4 110 dislocations moving on {1 1 1} and {1 1 0} planes are considered in some detail. It is porposed that the octahedral cation vacancies present in non-stoichiometric spinel diffuse to dislocations during deformation and thus favour {1 1 0} slip.     

Effect of Intense Self-Irradiation on the Phase Composition of Metallic Plutonium

The crystal structure of film samples of "high-level" (based on ²³⁸Pu) and low-level (based on ²³⁹Pu) metallic plutonium during their prolonged (up to 343 days) storage (self-irradiation) at room temperature was studied by X-ray diffraction. In the samples of high-level plutonium, the -Pu and -Pu lattices coexist. In the period of 40-60 days, the other known crystal modifications of plutonium (-Pu, -Pu, -Pu, and -Pu) are also present. Low-level plutonium had only the -Pu lattice. A possible origin of this phenomenon is discussed.     

Thermal diffusivity of inhomogeneous systems

The possibility of analyzing the nonsteady temperature fields of inhomogeneous systems using the quasi-homogeneous-body model is investigated.Notation t, t_I, t_i temperature of quasi-homogeneous body inhomogeneous system, and i-th component of system - a, , c thermal diffusivity and conductivity and volume specific heat of quasi-homogeneous body - a_{i i}, c_i same quantities for the i-th component - q heat flux - S, V system surface and volume - x, y coordinates - macrodimension of system - dimensionless temperature Fo=a/² - Bi=/ Fourier and Biot numbers - N number of plates - =h/ ratio of micro- and macrodimensions - _V, volumeaveraged and mean-square error of dimensionless-temperature determination - time - m_i i-th component concentration Translated from Inzhenerno-Fizicheskii Zhurnal, Vol. 39, No. 1, pp. 126–133, July, 1980.     

Temperature dependence of the experimental penetration depth of superconducting thin films

Experimental magnetic field penetration depths (t, d, H) of the stable and superheated Meissner state were calculated as a function of temperature for various applied magnetic fields and various film thicknesses for two cases: (1) (t)/d and (2) 2(t)/d ( is the Ginzburg-Landau penetration depth,d is the film thickness, is the GL parameter). The results of the first case should be a useful tool for obtaining (0) of amorphous superconducting thin films.¹ This work was supported in part by NSF Grant No. INT 8006927.     

Precipitate strengthening mechanisms in magnesium zinc alloy single crystals

The mechanical behaviour of Mg-5.1 wt % Zn alloy single crystals was studied in the 4.2 to 300° K temperature range. Quenched crystals have activation energies and volumes best associated with the cutting of small clusters of Zn atoms by dislocations. Fully hardened crystals contain fine ₁ and occasional ₂ precipitates with an average ₁ interparticle spacing of 330 to 660 Å. Strengthening in these crystals is mainly ascribed to the cutting of ₁ particles by dislocations. In the overaged condition ₁, ₂ and equilibrium particles are present and lead to a considerable temperature-dependence unusual for an overaged condition. Analysis of this temperature-dependence suggests that below 77° K the relatively easy cutting of ₁ particles by dislocations takes place in addition to the cutting of ₂ and particles. Above 77° K the difficult cutting of ₂ and particles alone controls the deformation, ₁ being more easily cut with the aid of thermal fluctuations.     

Mechanical properties and microstructure of β-SiAION-β-SiC composites by pressureless sintering

-SiAION--SiC composites containing up to 12 wt% -SiC were prepared by pressureless sintering. The strength of composites at room temperature remained relatively unchanged, whereas strength at 1200 °C increased for composites. The fracture toughness (K _IC) for composites was higher than that for -SiAION ceramics. The maximum value was 5.4 MPa m^1/2 for 6 wt% -SiC, and this was an improvement of 15% in comparison with -SiAION ceramics. From SEM observations, an improvement inK _IC values was attributed to crack deflections and branching-off of cracks. Intra-granular fractures were frequently observed in -SiAION. From TEM observations, -SiAION crystals were nanocomposites, within which existed the fine crystals in -SiAION crystal. For composite, -SiAION and -SiC crystals were directly in contact. The mismatching zone was observed in -SiC.     

Microstructural study of two LAS-type glass-ceramics and their parent glass

The two glass-ceramics studied here derive from the complex system (MgO,ZnO,Li₂O)-Al₂O₃-SiO₂ and are obtained by controlled devitrification of the same parent glass. Although they have the same chemical composition, one is a -quartz (or -eucryptite) type while the other one is a -spodumene glass-ceramic. A detailed microstructural analysis of these materials has been performed at different scales by several complementary characterization methods (SEM, TEM, DTA, XRD and FTIR). This extensive study has shown the great microstructure difference (grain distribution, grain size, nature of vitreous and crystalline phases) between these two glass-ceramics obtained from the same parent glass.     

Measuring the torque of driving shafts

Conclusions By means of this torque metter, with it's powerful ring ring electrical dynamometer, it is possible to measure the torque of driving shafts of underground beltc onveyers, and on any machine which has chain and sprocket couplings.     

Temperature effects on the properties of Ge thin films

The effects of substrate temperature (T_s) on the properties of vacuum evaporated p-type Ge thin films have been investigated for 25s<400°C. Increase in the substrate temperature improves the crystallinity and increases the grain size resulting a gradual change from amorphous to polycrystalline structure which was attained above a substrate temperature of 225°C. Low resistive (1×10^–2 ohm-cm) and high mobility (280 cm²/V·s) films were obtained at T_s=400°C. It has been observed that the conduction mechanism in polycrystalline films was dominated successively by hopping, tunneling and thermionic emission as the sample temperature was increased from 40 to 400 K. In amorphous samples, conduction was described in terms of different hopping mechanisms.     

New Types of Resistance Strain Gauges Made of Semiconductor Whiskers

We created resistance strain gauges on the basis of threadlike semiconductor monocrystals of tellurium and selenium and investigated their deformation characteristics under uniaxial tension and compression (up to ± 2.6·10^–3) and hydrostatic pressure (up to 5·10⁸ Pa). Their characteristics are compared with the parameters of resistance strain gauges made of p-type silicon. We developed electric contacts for selenium crystals and concluded that resistance strain gauges are promising for investigation of composite materials under triaxial compression.     

Study of Broadband Long-Focus Optics for Synchrotron Infrared Diagnosis of Low-Energy Electron Beams

A special optical device for measuring the geometry and current parameters in electron rings by synchrotron infrared radiation is designed, fabricated, and studied. The optical elements of the device are made of an optical ceramic and operate at 1–8 m. The study results are presented.     

γ ? α2 Phase transformation in fractured high temperature stress rupture Ti-48Al-2Nb(at.%)

The ₂ phase transformation in fractured high temperature stress rupture Ti-48Al-2Nb(at.%) alloy has been studied by analytical electron microscopy. ₂ and phases were found at grain boundaries. ₂ layers that suspended in layers and interfacial ledge higher than 2d ₍₁₁₁₎ at /₂ interfaces were observed in the lamellar grains. These facts indicated that ₂ phase transformation and dynamic recrystallization have occurred during high temperature stress rupture deformation. It can be concluded that deformation induced ₂ phase transformation and dynamic recrystallization resulted in the presence of particles at grain boundaries. A structural and compositional transition area between deformation-induced ₂(or ) and its adjacently original (or ₂) phases was found by HREM and EDS and is suggested as a way to transform between and ₂ phase during high temperature stress rupture deformation. The transition area was formed by slide of partial dislocations on close-packed planes and diffusion of atoms.     

Observations on the mechanical properties of nickel oxide scales

The mechanical properties of NiO scales produced by the complete oxidation of high-purity (grade-1) Ni and commercial-purity (grade-A) Ni have been investigated at 700 to 1000 C. The modulus of elasticity of both grades of oxide decreased with increasing temperature, whereas the modulus of rupture for grade-A oxide exhibited a maximum at 850 C and that for grade-1 oxide decreased with increasing temperature. At 700 C, elastic deformation to fracture occurred with both oxides, whereas, at temperatures 850 C, plasticity was also observed. The plasticity of grade-1 oxide was 3 times greater than that of grade-A oxide.Creep behaviour of the oxides was studied at 900 and 1000 C. Primary and secondary creep was observed and, in both oxides, the creep rates increased with increasing temperature and load. The creep rate of grade-1 oxide was 10 to 20 times greater than that for grade-A oxide.     

p-Version hierarchical three dimensional curved shell element for heat conduction

This paper presents a finite element formulation for a three dimensional nine node p-version hierarchical curved shell element for heat conduction where the element temperature approximation can be of arbitrary order p , p , and p in the , and directions. This is accomplished by first, constructing one dimensional hierarchical approximation functions and the corresponding nodal variable operators for each of the three directions , and using Lagrange interpolating polynomials and then taking their products (sometimes also called tensor products). The element approximation functions as well as the nodal variables are hierarchical and therefore the element matrices and the equivalent heat vectors are hierarchical also i.e. the element properties corresponding to polynomial orders p , p , and p are a subset of those corresponding to (p +1), (p +1), and (p +1). The element formulation ensures C ⁰ continuity. The curved shell geometry is constructed in the usual way by taking the coordinates of the nodes lying on the middle surface of the element (=0) and the nodal thickness vectors. The element properties i.e. element matrices and the equivalent heat vectors are derived using weak formulation (or quadratic functional) of the three dimensional F ourier heat conduction equation and the hierarchical element temperature approximation. The element formulation is equally effective for very thin as well as extremely thick shells. Numerical examples are presented to demonstrate the accuracy, efficiency, modeling convenience, faster rate of convergence and over all superiority of the present formulation. The h-approximation results are presented for comparison purposes.     

Theory of RF SQUIDs Operating in the Presence of Large Thermal Fluctuations

A comprehensive analytical theory is presented for non-hysteretic RF SQUIDs operating in the adiabatic mode in the presence of large thermal fluctuations. When 1 ( = 2LI_c/₀ is the hysteresis parameter, L is the SQUID inductance, I_c is the critical current of the Josephson junction, and ₀ is the flux quantum) the theory is applicable also for RF SQUIDs operating in the non-adiabatic mode. In contrast to previous theories in which the noise is treated perturbatively and which therefore are applicable only if the product 1 ( = 2k_BT/ ₀ I_c is the noise parameter, k_B is the Boltzmann constant, and T is the absolute temperature)—the case of small thermal fluctuations—the present theory is valid for around unity or higher. In the limit 0 the theory reproduces the results of small thermal fluctuations theories. It has been found that in the presence of large thermal fluctuations the screening current in the SQUID inductance is suppressed by a factor that increases with increasing . Taking into account this new basic fact, all SQUID characteristics (output signal, transfer function, noise spectral density and energy sensitivity) have been recalculated and a good agreement with experimental data has been obtained. It has been also found that RF SQUIDs can be operated with substantially higher values of the inductance and of the noise parameter than DC SQUIDs. These two aspects, which are of particular importance at liquid nitrogen temperature, make high T_c RF SQUIDs very attractive.     

Differential-flow-induced instability in a cubic autocatalator system

The formation of spatio-temporal stable patterns is considered for a reaction-diffusion-convection system based upon the cubic autocatalator, A + 2B 3B, B C, with the reactant A being replenished by the slow decay of some precursor P via the simple step P A. The reaction is considered in a differential-flow reactor in the form of a ring. It is assumed that the reactant A is immobilised within the reactor and the autocatalyst B is allowed to flow through the reactor with a constant velocity as well as being able to diffuse. The linear stability of the spatially uniform steady state (a, b) = (µ^–1, µ), where a and b are the dimensionless concentrations of the reactant A and autocatalyst B, and µ is a parameter reflecting the initial concentration of the precursor P, is discussed first. It is shown that a necessary condition for the bifurcation of this steady state to stable, spatially non-uniform, flow-generated patterns is that the flow parameter > _c(µ, ) where _c(µ,) is a (strictly positive) critical value of and is the dimensionless diffusion coefficient of the species B and also reflects the size of the system. Values of _c at which these bifurcations occur are derived in terms of µ and . Further information about the nature of the bifurcating branches (close to their bifurcation points) is obtained from a weakly nonlinear analysis. This reveals that both supercritical and subcritical Hopf bifurcations are possible. The bifurcating branches are then followed numerically by means of a path-following method, with the parameter as a bifurcation parameter, for representatives values of µ and . It is found that multiple stable patterns can exist and that it is also possible that any of these can lose stability through secondary Hopf bifurcations. This typically gives rise to spatio-temporal quasiperiodic transients through which the system is ultimately attracted to one of the remaining available stable patterns.     

Elevated temperature deformation behaviour of multi-phase Ni-20 at % Al-30 at % Fe and its constituent phases

The mechanical behaviour of the multi-phase ( + /) alloy Ni-20 at % Al-30 at % Fe and alloys similar to its constituent and / phases, Ni-30 at % Al-20 at % Fe and Ni-12 at % Al-40 at % Fe, respectively, were investigated. When tested in tension at 300 K, the alloys exhibited 20%, 2% and 28% elongation, respectively. At elevated test temperatures (700, 900 and 1100 K), the multi-phase alloy exhibited increased ductility, reaching an elongation in excess of 70% at 1100 K without necking or fracture. Similarly, the alloy demonstrated increased ductility with increasing test temperatures. In contrast, the / alloy showed greatly reduced ductility with increasing temperature and was quite brittle both at 900 and 1100 K. Thus, whilst at room temperature the / phase improved the ductility of the + / aggregate, at elevated temperatures the phase alleviated the brittleness of the / phase, thereby preventing any embrittlement of the multi-phase alloy over the temperature range 300–1100 K. Also, whilst the phase improved the room-temperature strength of the multi-phase alloy, at elevated temperatures where the phase is known to be weak, the / phase improved the strength of the multi-phase alloy up to 900 K, beyond which the strength deteriorated due to disordering and lack of anomalous strengthening in the / component.     

Chebyshev approximation for the roots of the equation BiWГ(μ)=μVГ(μ)

A minimax approximation, uniform for Bi [0, ), is developed for the roots of the equation BiW()=V(), by means of Chebyshev polynomials.Translated from Inzhenero-Fizicheskii Zhurnal, Vol. 28, No. 4, pp. 710–715, April, 1975.     

Solid state phase transformation of BaB2O4 during the isothermal annealing process

Solid-state phase transformation of BaB₂O₄ during the isothermal annealing process for both to and to were investigated using a platinum crucible. For the -phase crystal at the -phase stable temperature (> 925 °C), the phase transforms to the phase perfectly below the melting temperature of 1100 °C. Meanwhile, for the -phase crystal at the -phase stable temperature (< 925 °C), the phase transforms to the phase perfectly above 800 °C. There is some difference in phase transformation behaviour between bulk-shape crystals and the powder, caused by thermal stress.