Nanoscale Analyses of High-Nickel Concentration Martensitic High-Strength Steels

Austenite reversion in martensitic steels is known to improve fracture toughness. This research focuses on characterizing mechanical properties and the microstructure of low-carbon, high-nickel steels containing 4.5 and 10 wt pct Ni after a QLT-type austenite reversion heat treatment: first, martensite is formed by quenching (Q) from a temperature in the single-phase austenite field, then austenite is precipitated by annealing in the upper part of the intercritical region in a lamellarization step (L), followed by a tempering (T) step at lower temperatures. For the 10 wt pct Ni steel, the tensile strength after the QLT heat treatment is 910 MPa (132 ksi) at 293 K (20 °C), and the Charpy V-notch impact toughness is 144 J (106 ft-lb) at 188.8 K (?84.4 °C, ?120 °F). For the 4.5 wt pct Ni steel, the tensile strength is 731 MPa (106 ksi) at 293 K (20 °C) and the impact toughness is 209 J (154 ft-lb) at 188.8 K (?84.4 °C, ?120 °F). Light optical microscopy, scanning electron and transmission electron microscopies, synchrotron X-ray diffraction, and local-electrode atom-probe tomography (APT) are utilized to determine the morphologies, volume fractions, and local chemical compositions of the precipitated phases with sub-nanometer spatial resolution. The austenite lamellae are up to 200 nm in thickness, and up to several micrometers in length. In addition to the expected partitioning of Ni to austenite, APT reveals a substantial segregation of Ni at the austenite/martensite interface with concentration maxima of 10 and 23 wt pct Ni for the austenite lamellae in the 4.5 and 10 wt pct Ni steels, respectively. Copper-rich and M₂C-type metal carbide precipitates were detected both at the austenite/martensite interface and within the bulk of the austenite lamellae. Thermodynamic phase stability, equilibrium compositions, and volume fractions are discussed in the context of Thermo-Calc calculations.     

Effect of Mn Addition on Microstructural Modification and Cracking Behavior of Ferritic Light-Weight Steels

In the present study, effects of Mn addition on cracking phenomenon occurring during cold rolling of ferritic light-weight steels were clarified in relation to microstructural modification involving κ-carbide, austenite, and martensite. Four steels were fabricated by varying Mn contents of 3 to 12 wt pct, and edge areas of steel sheets containing 6 to 9 wt pct Mn were cracked during the cold rolling. The steels were basically composed of ferrite and austenite in a band shape, but a considerable amount of κ-carbide or martensite existed in the steels containing 3 to 6 wt pct Mn. Microstructural observation of the deformed region of fractured tensile specimens revealed that cracks which were initiated at ferrite/martensite interfacial κ-carbides readily propagated along ferrite/martensite interfaces or into martensite areas in the steel containing 6 wt pct Mn, thereby leading to the center or edge cracking during the cold rolling. In the steel containing 9 wt pct Mn, edge cracks were found in the final stage of cold rolling because of the formation of martensite by the strain-induced austenite to martensite transformation, whereas they were hardly formed in the steel containing 12 wt pct Mn. To prevent or minimize the cracking, it was recommended that the formation of martensite during the cooling from the hot rolling temperature or during the cold rolling should be suppressed, which could be achieved by the enhancement of thermal or mechanical stability of austenite with decreasing austenite grain size or increasing contents of austenite stabilizers.     

<Emphasis Type="Italic">In Situ</Emphasis> Local Measurement of Austenite Mechanical Stability and Transformation Behavior in Third-Generation Advanced High-Strength Steels

Austenite mechanical stability, i.e., retained austenite volume fraction (RAVF) variation with strain, and transformation behavior were investigated for two third-generation advanced high-strength steels (3GAHSS) under quasi-static uniaxial tension: a 1200 grade, two-phase medium Mn (10 wt pct) TRIP steel, and a 980 grade, three-phase TRIP steel produced with a quenching and partitioning heat treatment. The medium Mn (10 wt pct) TRIP steel deforms inhomogeneously via propagative instabilities (Lüders and Portevin Le Châtelier-like bands), while the 980 grade TRIP steel deforms homogenously up to necking. The dramatically different deformation behaviors of these steels required the development of a new in situ experimental technique that couples volumetric synchrotron X-ray diffraction measurement of RAVF with surface strain measurement using stereo digital image correlation over the beam impingement area. Measurement results with the new technique are compared to those from a more conventional approach wherein strains are measured over the entire gage region, while RAVF measurement is the same as that in the new technique. A determination is made as to the appropriateness of the different measurement techniques in measuring the transformation behaviors for steels with homogeneous and inhomogeneous deformation behaviors. Extension of the new in situ technique to the measurement of austenite transformation under different deformation modes and to higher strain rates is discussed.     

Structure-property relations and the design of Fe-4Cr-C base structural steels for high strength and toughness

Some design guidelines for improving strength-toughness combinations in medium car-bon structural steels are critically reviewed. From this, quaternary alloy development based on Fe/Cr/C steels with Mn or Ni additions for improved properties is described. Transmission electron microscopy and X-ray analysis reveal increasing amounts of retained austenite in these alloys with Mn content up to 2 wt pct and Ni additions at 5 wt pct after quenching from 1100°C. A corresponding improvement in toughness properties is also found. Grain refining results in a further increase in the amount of retained austenite. In addition, the excellent combinations of strength and toughness in these quaternary alloys are attributed to the production of dislocated lath martensite from a homogeneous austenite phase free from undissolved alloy carbides. The question of thermal instability of retained austenite following tempering is considered in detail and it is shown that the decomposition of retained austenite is closely related to the ease of nucleation and growth of cementite. Thus, graphitizing alloying elements such as Ni are beneficial in postponing the decomposition of retained austenite. Formerly with the Lawrence Berkeley Laboratory, Berkeley, CA This paper is based on a presentation made at a symposium on “Precipitation Processes in Structural Steels” held at the annual meeting of the AIME, Denver, Colorado, February 27 to 28, 1978, under the sponsorship of the Ferrous Metal-lurgy Committee of The Metallurgical Society of AIME.     

Replacement of Ni by Mn in High-Ni-Containing Austenitic Cast Steels used for Turbo-Charger Application

High-temperature tensile properties of austenitic cast steels fabricated by replacing Ni by Mn in a 20 wt pct Ni-containing steel were investigated. In a steel where 8 wt pct Ni was replaced by 9.2 wt pct of Mn, 17.4 and 9.8 pct of ferrite existed in equilibrium phase diagrams and actual microstructures, respectively, because a role of Mn as an austenite stabilizer decreased, and led to deterioration of high-temperature properties. When 2 to 6 wt pct Ni was replaced by 2.3 to 6.9 wt pct Mn, high-temperature properties were comparable to those of the 20 wt pct Ni-containing steel because ferrites were absent, which indicated the successful replacement of 6 wt pct Ni by Mn, with cost reduction of 27 pct.     

Effect of manganese on the stability of austenite in Fe-Cr-Ni alloys

The phase equilibria between austenite and ferrite in the Fe-Cr-Mn-Ni quaternary system have been computed in the temperature range of 900 ° to 1150 °, using recent thermodynamic interaction parameters. From the computed results, the effectiveness of Mn in replacing Ni as an austenite stabilizer has been evaluated as a function of composition and temperature. The results show that, for 18 wt pct Cr alloys, the computed Ni equivalent of Mn is around zero and becomes negative at higher Cr contents, which is rather surprizing. The function of Mn in 200-type stainless steels is then not so much to stabilize austenite but to supplement the role of Cr in increasing the solubility in austenite of N, which appears to be the more important austenite-stabilizing element.     

Development of Multiphase Microstructure with Bainite, Martensite, and Retained Austenite in a Co-Containing Steel Through Quenching and Partitioning (Q&P) Treatment

The quenching and partitioning (Q&P) treatment of steel aims to produce a higher fraction of retained austenite by carbon partitioning from supersaturated martensite. Q&P studies done so far, relies on the basic concept of suppression of carbide formation by the addition of Si and/or Al. In the present study Q&P treatment is performed on a steel containing 0.32 C, 1.78 Mn, 0.64 Si, 1.75 Al, and 1.20 Co (all wt pct). A combination of 0.64 Si and 1.75 Al is chosen to suppress the carbide precipitation and therefore, to achieve carbon partitioning after quenching. Addition of Co along with Al is expected to accelerate the bainite transformation during Q&P treatment by increasing the driving force for transformation. The final aim is to develop a multiphase microstructure containing bainite, martensite, and the retained austenite and to study the effect of processing parameters (especially, quenching temperature and homogenization time) on the fraction and stability of retained austenite. A higher fraction of retained austenite (~13 pct) has indeed been achieved by Q&P treatment, compared to that obtained after direct-quenching (2.7 pct) or isothermal bainitic transformation (9.7 pct). Carbon partitioning during martensitic and bainitic transformations increased the stability of retained austenite.     

Development of New High-Strength Carbide-Free Bainitic Steels

An attempt was made to optimize the mechanical properties by tailoring the process parameters for two newly developed high-strength carbide-free bainitic steels with the nominal compositions of 0.47 pct C, 1.22 pct Si, 1.07 pct Mn, 0.7 pct Cr (S1), and 0.30 pct C, 1.76 pct Si, 1.57 pct Mn, and 0.144 pct Cr (S2) (wt pct), respectively. Heat treatment was carried out via two different routes: (1) isothermal transformation and (2) quenching followed by isothermal tempering. The results for the two different processes were compared. The bainitic steels developed by isothermal heat treatment were found to show better mechanical properties than those of the quenched and subsequently tempered ones. The effect of the fraction of the phases, influence of the transformation temperatures, the holding time, and the stability of retained austenite on the mechanical properties of these two steels was critically analyzed with the help of X-ray diffraction, optical metallography, scanning electron microscopy, and atomic force microscopy. Finally, a remarkable combination of yield strength of the level of 1557 MPa with a total elongation of 15.5 pct was obtained.     

Effects of Ni on austenite stability and fracture toughness in high Co-Ni secondary hardening steel

Three kinds of high Co-Ni secondary hardening steels with different Ni contents were studied.The nanoscale austenite layers formed at the interface of matensite laths were observed.Both observation and diffusion kinetic simulation results showed that both Ni and Co did not obtain enough time to get the equilibrium content in this system.The Ni content in austenite layers decreased significantly,and Co content increased slightly with the decrease of Ni content in overall composition.The austenite stability was estimated by Olson-Cohen model,in which both chemical and mechanical driving force could be calculated by equilibrium thermodynamic and Mohr′s circle methods,respectively.Simulation and mechanical test results showed that the decrease of Ni content in austenite layers would cause the change of austenite stability and decrease the fracture toughness of the steels.When the Ni content in the overall composition was lower than 7wt.%,the Ni content inγphase would be lower than 20 wt.%.And the simulation value of Mσs(stress-induced critical martensite transformation temperature)would be up to 80°C,which was about 60°C higher than room temperature.Based on the analysis,the Ni content in the overall composition of high Co-Ni secondary hardening steels should be higher than 8wt.% in order to obtain a good fracture toughness.     

Atom-Probe Tomographic Investigation of Austenite Stability and Carbide Precipitation in a TRIP-Assisted 10 Wt Pct Ni Steel and Its Weld Heat-Affected Zones

Newly developed low-carbon 10 wt pct Ni-Mo-Cr-V martensitic steels rely on the Ni-enriched, thermally stable austenite [formed via multistep intercritical Quench-Lamellarization-Tempering (QLT)-treatment] for their superior mechanical properties, specifically ballistic resistance. Critical to the thermal stability of austenite is its composition, which can be severely affected in the weld heat-affected zones (HAZs) and thus needs investigations. This article represents the first study of the nanoscale redistributions of C, Ni, and Mn in single-pass HAZ microstructures of QLT-treated 10 wt pct Ni steels. Local compositions of Ni-rich regions (representative of austenite compositions) in the HAZs are determined using site-specific 3-D atom-probe tomography (APT). Martensite-start temperatures are then calculated for these compositions, employing the Ghosh-Olson thermodynamic and kinetics approach. These calculations predict that austenite (present at high temperatures) in the HAZs is susceptible to a martensitic transformation upon cooling to room temperature, unlike the austenite in the QLT-treated base-metal. While C in the QLT-treated base-metal is consumed primarily in MC and M₂C-type carbide precipitates (M is Mo, Cr, V), its higher concentration in the Ni-rich regions in the HAZs indicates the dissolution of carbide precipitates, particularly M₂C carbide precipitates. The role of M₂C carbide precipitates and austenite stability is discussed in relation to the increase in microhardness values observed in the HAZs, relative to the QLT-treated base-metal. Insights gained from this research on austenite stability and carbide precipitation in the single-pass HAZ microstructures will assist in designing multiple weld cycles for these novel 10 wt pct Ni steels.     

Notch-Fatigue Properties of Advanced TRIP-Aided Bainitic Ferrite Steels

To develop a transformation-induced plasticity (TRIP)-aided bainitic ferrite steel (TBF steel) with high hardenability for a common rail of the next generation diesel engine, 0.2?pct C-1.5?pct Si-1.5?pct Mn-0.05?pct Nb TBF steels with different contents of Cr, Mo, and Ni were produced. The notch-fatigue strength of the TBF steels was investigated and was related to the microstructural and retained austenite characteristics. If Cr, Mo, and/or Ni were added to the base steel, then the steels achieved extremely higher notch-fatigue limits and lower notch sensitivity than base TBF steel and the conventional structural steels. This was mainly associated with (1) carbide-free and fine bainitic ferrite lath structure matrix without proeutectoid ferrite, (2) a large amount of fine metastable retained austenite, and (3) blocky martensite phase including retained austenite, which may suppress a fatigue crack initiation and propagation.     

Constitutive Modeling of the Mechanical Properties of V-added Medium Manganese TRIP Steel

In this study, medium Mn transformation-induced plasticity steel with the composition Fe-0.08 pct C-6.15 pct Mn-1.5 pct Si-2.0 pct Al-0.08 pct V was investigated. After intercritical annealing at 1013 K (740 °C), the steel contained coarse-grained ferrite and two ultrafine-grained (UFG) phases: ferrite and retained austenite. The material did not deform by localized Lüders band propagation: it did not suffer from this major problem as most UFG steels do. Localization of plastic flow was shown to be suppressed because of a combination of factors, including a bimodal grain size distribution, a multiphase microstructure, the presence of nanosized vanadium carbide precipitates, and the occurrence of the deformation-induced martensitic transformation of retained austenite. A constitutive model incorporating these effects was developed. The model was used to identify the factors which can lead to a further improvement of the mechanical properties of the UFG medium Mn TRIP steels.     

Optimization of Fe/Cr/C base structural Steels for improved strength and toughness

Optimization of the composition and the heat treatments to provide a microduplex structure of dislocated-autotempered lath martensite and thin film retained austenite for good combinations of mechanical properties has been attained for Fe/Cr/C base steels. Substituting 0.5 wt pct Mo to reduce Cr from 4 pct to 3 pct did not affect the microstructures nor the properties. It was found that air melting as compared to vacuum melting does not cause deterioration of toughness in Mn containing alloys but does so in Ni containing alloys. Tempered martensite embrittlement was confirmed as being due to the decomposition of retained austenite. Further improvements in the fracture toughness are achieved by double heat treatments which provide grain refinement. These alloys are considered to be very promising for structural applications.     

Microstructure and Wear Resistance in Medium and High C Steels Treated by Quenching and Partitioning

The quenching and partitioning (Q&P) steels have shown to be promising candidates to be applied in fields where wear resistance is required. In this study, a medium and a high C steel are heat treated by Q&P and the resulting microstructure, hardness, and wear resistance are characterized. The mechanical stability of the austenite phase under wear test conditions is investigated. It is found that the stability of austenite is very high in the high C steel and decreases in the medium C steel. Additionally, the hardness and wear behavior of the Q&P-treated steels are compared with the results obtained for quenching and tempering (Q&T) treated samples, showing that, although the hardness of Q&P steels is quite lower, the obtained wear rates are similar. It means that in the studied Q&P steels, although the austenite transformation into martensite does not occur considerably, the presence of austenite might play a key role in the wear resistance.     

Third Generation 0.3C-4.0Mn Advanced High Strength Steels Through a Dual Stabilization Heat Treatment: Austenite Stabilization Through Paraequilibrium Carbon Partitioning

In excess of 30 vol. pct austenite can be retained in 0.3C-4.0Mn steels subjected to a dual stabilization heat treatment (DSHT) schedule—a five stage precisely controlled cooling schedule that is a variant of the quench and partition process. The temperature of the second quench (stage III) in the DSHT process plays an essential role in the retained austenite contents produced at carbon-partitioning temperatures of 723 K or 748 K (450° C or 475 °C) (stage IV). A thermodynamic model successfully predicted the retained austenite contents in heat-treated steels, particularly for a completely austenitized material. The microstructure and mechanical behavior of two heat-treated steels with similar levels of retained austenite (~30 vol. pct) were studied. Optimum properties—tensile strengths up to 1650 MPa and ~20 pct total elongation—were observed in a steel containing 0.3C-4.0Mn-2.1Si, 1.5 Al, and 0.5 Cr.     

Effect of Interfacial Mn Partitioning on Carbon Partitioning and Interface Migration During the Quenching and Partitioning Process

A so-called QP-LE model, in which interface condition is assumed to be Local Equilibrium (LE), has been proposed to evaluate the effect of interfacial Mn partitioning on interface migration and carbon partitioning during the Quenching and partitioning process (Q&P) of an Fe-0.3C-3.0Mn-1.5Si (wt pct) alloy. The predictions by the QP-LE model are compared with those by the conventional QP-PE model in which interface condition is assumed to be Paraequilibrium (PE). It is found that interfacial partitioning of Mn plays a significant role in carbon partitioning and the martensite/austenite interface migration during the Q&P process.     

1000MPa级高延伸率Q&P钢的实验室研究

以C-Si-Mn系TRIP钢成分为基础,设计了四种不同Si和Mn含量的合金成分,并采用不同两相区奥氏体化温度的淬火—配分(QP)工艺进行处理,得到了兼具高强度和高塑性的QP钢。其中,当奥氏体化温度为820℃时,0.18C-1.8Si-2.2Mn(质量分数,%)钢和0.18C-1.8Si-2.5Mn钢在抗拉强度达到1 000 MPa以上的同时断后延伸率仍不低于20%,显示了极佳的强塑性结合。利用SEM和XRD等对热处理材料的显微组织进行了表征,结果显示,其显微组织为铁素体、板条马氏体和一定量的残余奥氏体,残余奥氏体多呈块状且被铁素体所包围,且奥氏体化温度为820℃时,材料中的残余奥氏体含量和平均碳浓度均较高。更多且稳定的残余奥氏体在变形过程中发生TRIP效应,可以在不显著降低材料强度的情况下更有效地改善材料的塑性,这也是四种试验用钢经820℃的QP工艺处理后显示出更佳强塑性结合的主要原因。     

Phase transformational kinetics and hardenability of low-carbon,boron-treated steels

The phase transformations and hardenability of 0.1 pct C boron-treated and boron-free steels containing Mn, Cr, Ni, or Cr plus Ni, and up to 1 pct Mo were studied. Continuous cooling transformation diagrams, hardenability characteristics, and diagrams of the ferrite start half-cooling time vs alloying were established. An unalloyed 0.1 pct C steel transforms diffusionally in the ferritic-pearlitic range when cooled from an austenitizing temperature, with a negligible contribution of the intermediate (bainitic) transformation occurring at very high rates of cooling. Molybdenum extends the range of the bainitic transformation and markedly delays the decomposition of austenite in the ferritic-pearlitic range. Boron treatment of the unalloyed (molybdenum-free) 0.1 pct C steel permits bainite formation over a wider range of fast cooling programs. At lower rates of cooling, the steel transforms diffusionally into ferrite and pearlite . Alloying additions of Mn, Cr, or Ni result in a slightly higher proportion of the bainitic transformation, which may occur over a wider range of cooling programs. When both nickel and chromium are present, a modest synergistic effect on the delay of the ferritic-pearlitic transformation may be noted. Introduction of molybdenum into all of the boron-treated 0.1 pct C steels strongly delays the decomposition of austenite into ferrite-pearlite structures and vastly expands the range of cooling programs that result in the formation of bainitic structures. In this important action, molybdenum is assisted to a smaller degree by alloying additions of manganese and chromium, and to a greater degree by nickel and chromium plus nickel. In all the steels studied, the alloying elements lower the temperatures of the bainitic transformation, thereby explaining, at least partly, the somewhat higher hardness for any specified cooling program. The observed beneficial effects of boron, molybdenum, and other alloying elements on the phase transformational behavior on continuous cooling are reflected in terms of higher hardenability.     

In Situ Thermo-magnetic Investigation of the Austenitic Phase During Tempering of a 13Cr6Ni2Mo Supermartensitic Stainless Steel

The formation of austenite during tempering of a 13Cr6Ni2Mo supermartensitic stainless steel (X2CrNiMoV13-5-2) was investigated using an in situ thermo-magnetic technique to establish the kinetics of the martensite to austenite transformation and the stability of austenite. The austenite fraction was obtained from in situ magnetization measurements. It was found that during heating to the tempering temperature 1 to 2 vol pct of austenite, retained during quenching after the austenitization treatment, decomposed between 623 K and 753 K (350 °C and 480 °C). The activation energy for martensite to austenite transformation was found by JMAK-fitting to be 233 kJ/mol. This value is similar to the activation energy for Ni and Mn diffusion in iron and supports the assumption that partitioning of Ni and Mn to austenite are mainly rate determining for the austenite formation during tempering. This also indicates that the stability of austenite during cooling after tempering depends on these elements. With increasing tempering temperature the thermal stability of austenite is decreasing due to the lower concentrations of austenite-stabilizing elements in the increased fraction of austenite. After cooling from the tempering temperature the retained austenite was further partially decomposed during holding at room temperature. This appears to be related to previous martensite formation during cooling.     

Corrosion Behavior of High Nitrogen Nickel-Free Fe-16Cr-Mn-Mo-N Stainless Steels

The purpose of the current study is to develop austenitic nickel-free stainless steels with lower chromium content and higher manganese and nitrogen contents. In order to prevent nickel-induced skin allergy, cobalt, manganese, and nitrogen were used to substitute nickel in the designed steel. Our results demonstrated that manganese content greater than 14 wt pct results in a structure that is in full austenite phase. The manganese content appears to increase the solubility of nitrogen; however, a lower corrosion potential was found in steel with high manganese content. Molybdenum appears to be able to increase the pitting potential. The effects of Cr, Mn, Mo, and N on corrosion behavior of Fe-16Cr-2Co-Mn-Mo-N high nitrogen stainless steels were evaluated with potentiodynamic tests and XPS surface analysis. The results reveal that anodic current and pits formation of the Fe-16Cr-2Co-Mn-Mo-N high nitrogen stainless steels were smaller than those of lower manganese and nitrogen content stainless steel.