SiC-Whisker-Reinforced Al2O3 Composites by Free Sintering of Coated Powders

SiC whiskers were coated with a thick cladding of finegrained Al₂O₃ powder by controlled heterogeneous precipitation in a concentrated suspension of whiskers. After calcination, the coated whiskers were compacted by cold isostatic pressing and sintered at a constant heating rate of 5°C/min in a helium atmosphere. The parameters which control the coating process and the sintering characteristics of the consolidated powders are reported. Starting with an initial matrix density of 40–45% of the theoretical, composites containing up to ≅20 vol% whiskers (aspect ratio ≅15) were sintered freely to nearly theoretical density below 1800°C. By comparison, a similar composite formed by mechanical mixing of the whiskers and the precipitated Al₂O₃ powder reached a density of only 68% of the theoretical after sintering under identical conditions. For a fixed whisker content, the sinterability of the composites formed from the coated whiskers shows a fairly strong dependence on the whisker aspect ratio.     

Pressureless Sintering of High-Density ZrB2–SiC Ceramic Composites

Ultra-high-temperature ceramic composites of ZrB₂ 20 wt%SiC were pressureless sintered under an argon atmosphere. The starting ZrB₂ powder was synthesized via the sol–gel method with a small crystallite size and a large specific surface area. Dry-pressed compacts using 4 wt% Mo as a sintering aid can be pressureless sintered to ∼97.7% theoretical density at 2250°C for 2 h. Vickers hardness and fracture toughness of the sintered ceramic composites were 14.82±0.25 GPa and 5.39±0.13 MPa·m^1/2, respectively. In addition to the good sinterability of the ZrB₂ powders, X-ray diffraction and scanning electron microscopy results showed that Mo formed a solid solution with ZrB₂, which was believed to be beneficial for the densification process.     

Critical Current Densities in Thin Ceramic Tapes of Superconducting Ba2YCu3O7

Tape-cast slurries of Ba₂YCu₃O₇ powders offer a convenient means of preparing sintered ceramic samples for critical current density (J_c) measurements where the transport cross section is small and the current electrode areas are large. Samples were sintered from 900° to 1000°C and characterized for bulk density, grain size, phase composition, T_c, and J_c. Bulk density and grain size both increase with sintering temperature while all samples were single-phase perovskite except for those sintered at 900°C. The onset temperature for superconductivity is constant at about 93 K while the transition sharpens to R=0 at about 92 K for the densest samples. J_c rises with sintering temperature to a maximum of ∼10³ A/cm². A linear relationship between J_c and bulk density is predicted from microstructural considerations.     

Ultra-Fine Ba2Ti9O20 Powders Synthesized by Inverse Microemulsion Processing and their Microwave Dielectric Properties

A double–inverse microemulsion (IME) process is used for synthesizing nano-sized Ba₂Ti₉O₂₀ powders. The crystallization of powders thus obtained and the microwave dielectric properties of the sintered materials were examined. The IME-derived powders are of nano-size (∼21.5 nm) and possess high activity. The BaTi₅O₁₁, intermediate phase resulted when the IME-derived powders were calcined at 800°C (4 h) in air. However, high-density Ba₂Ti₉O₂₀ materials with a pure triclinic phase (Hollandite like) can still be obtained by sintering such a BaTi₅O₁₁ dominated powders at 1250°C/4 h. The phase transformation kinetics for the IME-derived powders were markedly enhanced when air was replaced by O₂ during the calcinations and sintering processes. Both the calcination and densification temperatures were reduced by around 50°C compared with the process undertaken in air. The microwave dielectric properties of sintered materials increase with the density of the samples, resulting in a large dielectric constant ( K ≅39) and high-quality factor ( Q × f ≅28 000 GHz) for samples possessing a density higher than 95% theoretical density, regardless of the sintering atmosphere. Overfiring dissociates Ba₂Ti₉O₂₀ materials and results in a poor-quality factor.     

Densification of Cr2O3-ZrO2 Ceramics by Sintering

Cr₂O₃ and ZrO₂ were mixed in various ratios and pressed to form compacts, which were then sintered in carbon powder. Compacts with >30 wt% Cr₂O₃ were sintered to densities >98% of true density at 1500°C. This method of sintering in carbon powder can be used to prepare very dense Cr₂O₃-ZrO₂ ceramics at a relatively low temperature, (∼1500°C) without additives.     

New Uniformly Porous CaZrO3/MgO Composites with Three-Dimensional Network Structure from Natural Dolomite

Porous CaZrO₃/MgO composites with a uniform three-dimensional (3-D) network structure have been successfully synthesized using reactive sintering of highly pure mixtures of natural dolomite (CaMg(CO₃)₂) and synthesized zirconia powders with LiF additive. Equimolar dolomite and zirconia powders doped with 0.5 wt% LiF were cold isostatically pressed at 200 MPa and sintered at 1100–1400°C for 2 h in air. Through the liquid formation via LiF doping, strong necks were formed between constituent particles before completion of the pyrolysis of dolomite, resulting in the formation of a 3-D network structure. During and after the formation of the network structure, CO₂ was given off to form a homogeneous open-pore structure. The pore-size distribution was very narrow (with pore size ∼ 1 μm), and the porosity was controllable (e.g., ∼30%–50%) by changing the sintering temperature. The porous composites can be applied as filter materials with good structural stability at high temperatures.     

Homogeneous ZrO2–Al2O3 Composite Prepared by Nano-ZrO2 Particle Multilayer-Coated Al2O3 Particles

ZrO₂–Al₂O₃ nanocomposite particles were synthesized by coating nano-ZrO₂ particles on the surface of Al₂O₃ particles via the layer-by-layer (LBL) method. Polyacrylic acid (PAA) adsorption successfully modified the Al₂O₃ surface charge. Multilayer coating was successfully implemented, which was characterized by ξ potential, particle size. X-ray diffraction patterns showed that the content of ZrO₂ in the final powders could be well controlled by the LBL method. The powders coated with three layers of nano-ZrO₂ particles, which contained about 12 wt% ZrO₂, were compacted by dry press and cold isostatically pressed methods. After sintering the compact at 1450°C for 2 h under atmosphere, a sintered body with a low pore microstructure was obtained. Scanning electron microscopy micrographs of the sintered body indicated that ZrO₂ was well dispersed in the Al₂O₃ matrix.     

In Situ Synthesis of Ultrafine ZrB2–SiC Composite Powders and the Pressureless Sintering Behaviors

Ultrafine ZrB₂–SiC composite powders have been synthesized in situ using carbothermal reduction reactions via the sol–gel method at 1500°C for 1 h. The powders synthesized had a relatively smaller average crystallite size (<200 nm), a larger specific surface area (∼20 m²/g), and a lower oxygen content (∼1.0 wt %). Composites of ZrB₂+20 wt% SiC were pressureless sintered to ∼96.6% theoretical density at 2250°C for 2 h under an argon atmosphere using B₄C and Mo as sintering aids. Vickers hardness and flexural strength of the sintered ceramic composites were 13.9±0.3 GPa and 294±14 MPa, respectively. The microstructure of the composites revealed that elongated SiC grain dispersed uniformly in the ZrB₂ matrix. Oxidation from 1100° to 1600°C for 30 min showed no decrease in strength below 1400°C but considerable decrease in strength with a rapid weight increment was observed above 1500°C. The formation of a protective borosilicate glassy coating appeared at 1400°C and was gradually destroyed in the form of bubble at higher temperatures.     

Fabrication and Microstructure Characterization of Ti3SiC2 Synthesized from Ti/Si/2TiC Powders Using the Pulse Discharge Sintering (PDS) Technique

Ti/Si/2TiC powders were prepared using a mixture method (M) and a mechanical alloying (MA) method to fabricate Ti₃SiC₂ at 1200°–1400°C using a pulse discharge sintering (PDS) technique. The results showed that the Ti₃SiC₂ samples with <5 wt% TiC could be rapidly synthesized from the M powders; however, the TiC content was always >18 wt% in the MA samples. Further sintering of the M powder showed that the purity of Ti₃SiC₂ could be improved to >97 wt% at 1250°–1300°C, which is ∼200°–300°C lower than that of sintered Ti/Si/C and Ti/SiC/C powders using the hot isostatic pressing (HIPing) technique. The microstructure of Ti₃SiC₂ also could be controlled using three types of powders, i.e., fine, coarse, or duplex-grained, within the sintering temperature range. In comparison with Ti/Si/C and Ti/SiC/C mixture powders, it has been suggested that high-purity Ti₃SiC₂ could be rapidly synthesized by sintering the Ti/Si/TiC powder mixture at relatively lower temperature using the PDS technique.     

Processing and Properties of TiB2 with MoSi2 Sinter-additive: A First Report

The densification of non-oxide ceramics like titanium boride (TiB₂) has always been a major challenge. The use of metallic binders to obtain a high density in liquid phase-sintered borides is investigated and reported. However, a non-metallic sintering additive needs to be used to obtain dense borides for high-temperature applications. This contribution, for the first time, reports the sintering, microstructure, and properties of TiB₂ materials densified using a MoSi₂ sinter-additive. The densification experiments were carried out using a hot-pressing and pressureless sintering route. The binderless densification of monolithic TiB₂ to 98% theoretical density with 2–5 μm grain size was achieved by hot pressing at 1800°C for 1 h in vacuum. The addition of 10–20 wt% MoSi₂ enables us to achieve 97%–99%ρ_th in the composites at 1700°C under similar hot-pressing conditions. The densification mechanism is dominated by liquid-phase sintering in the presence of TiSi₂. In the pressureless sintering route, a maximum of 90%ρ_th is achieved after sintering at 1900°C for 2 h in an (Ar+H₂) atmosphere. The hot-pressed TiB₂–10 wt% MoSi₂ composites exhibit high Vickers hardness (∼26–27 GPa) and modest indentation toughness (∼4–5 MPa·m^1/2).     

Mechanical Activation-Assisted Synthesis of Pb(Fe2/3W1/3)O3

Perovskite Pb(Fe_2/3W_1/3)O₃ (PFW) was prepared via a mechanical activation-assisted synthesis route from mixed oxides of PbO, Fe₂O₃, and WO₃. The mechanically activated oxide mixture, which exhibited a specific area of >10 m²/g, underwent phase conversion from nanocrystalline lead tungstate (PbWO₄) and pyrochlore (Pb₂FeWO_6.5) phases on sintering to yield perovskite PFW, although the formation of perovskite phase was not triggered by mechanical activation. When heated to 700°C, >98% perovskite phase was formed in the mechanically activated oxide mixture. The perovskite phase was sintered to a density of ∼99% of theoretical density at 870°C for 2 h. The sintered PFW exhibited a dielectric constant of 9800 at 10 kHz, which was ∼30% higher than that of the PFW derived from the oxide mixture that was not subjected to mechanical activation.     

Single-Calcination Synthesis of Pyrochlore-Free 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 and Pb(Mg1/3Nb2/3)O3 Ceramics Using a Coating Method

A coating approach for synthesizing 0.9Pb(Mg_1/3Nb_2/3)O₃–0.1PbTiO₃ (0.9PMN–0.1PT) and PMN using a single calcination step was demonstrated. The pyrochlore phase was prevented by coating Mg(OH)₂ on Nb₂O₅ particles. Coating of Mg(OH)₂ on Nb₂O₅ was done by precipitating Mg(OH)₂ in an aqueous Nb₂O₅ suspension at pH 10. The coating was confirmed using optical micrographs and zeta-potential measurements. A single calcination treatment of the Mg(OH)₂-coated Nb₂O₅ particles mixed with appropriate amounts of PbO and PbTiO₃ powders at 900°C for 2 h produced pyrochlore-free perovskite 0.9PMN–0.1PT and PMN powders. The elimination of the pyrochlore phase was attributed to the separation of PbO and Nb₂O₅ by the Mg(OH)₂ coating. The Mg(OH)₂ coating on the Nb₂O₅ improved the mixing of Mg(OH)₂ and Nb₂O₅ and decreased the temperature for complete columbite conversion to ∼850°C. The pyrochlore-free perovskite 0.9PMN–0.1PT powders were sintered to 97% density at 1150°C. The sintered 0.9PMN–0.1PT ceramics exhibited a dielectric constant maximum of ∼24 660 at 45°C at a frequency of 1 kHz.     

Fabrication of Transparent, Sintered Sc2O3 Ceramics

We report here the fabrication of transparent Sc₂O₃ ceramics via vacuum sintering. The starting Sc₂O₃ powders are pyrolyzed from a basic sulfate precursor (Sc(OH)_2.6(SO₄)_0.2·H₂O) precipitated from scandium sulfate solution with hexamethylenetetramine as the precipitant. Thermal decomposition behavior of the precursor is studied via differential thermal analysis/thermogravimetry, Fourier transform infrared spectroscopy, X-ray diffractometry, and elemental analysis. Sinterability of the Sc₂O₃ powders is studied via dilatometry. Microstructure evolution of the ceramic during sintering is investigated via field emission scanning electron microscopy. The best calcination temperature for the precursor is 1100°C, at which the resultant Sc₂O₃ powder is ultrafine (∼85 nm), well dispersed, and almost free from residual sulfur contamination. With this reactive powder, transparent Sc₂O₃ ceramics having an average grain size of ∼9 μm and showing a visible wavelength transmittance of ∼60–62% (∼76% of that of Sc₂O₃ single crystal) have been fabricated via vacuum sintering at a relatively low temperature of 1700°C for 4 h.     

Laser Sintering of ZrB2

Preliminary results about laser sintering of zirconium diboride (ZrB₂), a good ultra high-temperature ceramics candidate, are presented. In order to evaluate a suitable sintering method, single pulsed laser and a concentric dual laser system were carried out. Two different ZrB₂ powders having ∼15 and ∼2 μm particle size were assessed for sintering. Scanning electron microscopy images showed that the concentric dual laser sintered layer using ∼2 μm particle size of ZrB₂ had relatively smooth surface morphology. X-ray diffraction results confirmed that the sintered layer mainly retained the crystalline phases as the starting powder. In addition, the rapid cooling rate of laser sintering enabled the formation of needle-like nanostructures at the sintered surface.     

Zirconium Aluminum Carbides: New Precursors for Synthesizing ZrO2–Al2O3 Composites

ZrO₂–Al₂O₃ nanocrystalline powders have been synthesized by oxidizing ternary Zr₂Al₃C₄ powders. The simultaneous oxidation of Al and Zr in Zr₂Al₃C₄ results in homogeneous mixture of ZrO₂ and Al₂O₃ at nanoscale. Bulk nano- and submicro-composites were prepared by hot-pressing as-oxidized powders at 1100°–1500°C. The composition and microstructure evolution during sintering was investigated by XRD, Raman spectroscopy, SEM, and TEM. The crystallite size of ZrO₂ in the composites increased from 7.5 nm for as-oxidized powders to about 0.5 μm at 1500°C, while the tetragonal polymorph gradually converted to monolithic one with increasing crystallite size. The Al₂O₃ in the composites transformed from an amorphous phase in as oxidized powders to θ phase at 1100°C and α phase at higher temperatures. The hardness of the composite increased from 2.0 GPa at 1100°C to 13.5 GPa at 1400°C due to the increase of density.     

Gas Pressure Sintering of Silicon Nitride Powder Coated with Al2O3 and TiO2

Gas pressure sintering kinetics of silicon nitride powder coated with 10 wt% (9:1) Al₂O₃ and TiO₂ have been studied at 1850°C with a pressure schedule of 0.3 MPa in the first stage and 1 MPa in the second stage. The rates have been analyzed with a liquid-phase sintering model. Diffusion-controlled intermediate-stage kinetics have been observed. The role of second-step pressurization with nitrogen and argon has been determined by monitoring the kinetics. Pressurization at an earlier stage (∼90% relative density) reduces the densification rate but produces a denser material at the final stage. Although final density is greater, a porous surface layer forms on samples sintered with argon pressurization at the second stage. No such porous layer is formed in the case of pressurization with nitrogen. The mechanism of the intermediate-stage kinetics has been discussed with respect to the nature of the product analyzed by XRD after sintering.     

Uniformly Porous Al2O3/LaPO4 and Al2O3/CePO4 Composites with Narrow Pore-Size Distribution

Porous Al₂O₃/20 vol% LaPO₄ and Al₂O₃/20 vol% CePO₄ composites with very narrow pore-size distribution at around 200 nm have been successfully synthesized by reactive sintering at 1100°C for 2 h from RE₂(CO₃)₃· x H₂O (RE = La or Ce), Al(H₂PO₄)₃ and Al₂O₃ with LiF additive. Similar to the previously reported UPC-3Ds (uniformly porous composites with a three-dimensional network structure, e.g. CaZrO₃/MgO system), decomposed gases in the starting materials formed a homogeneous open porous structure with a porosity of ∼40%. X-ray diffraction, ³¹P magic-angle spinning nuclear magnetic resonance, scanning electron microscopy, and mercury porosimetry revealed the structure of the porous composites.     

Solid-State Sintering of YBa2Cu3Ox in Different Oxygen Partial Pressures

The effect of oxygen partial pressure, ranging from 0.001 to 1.0 atm, and temperature, in the range of 930°–955°C, on the solid-state sintering kinetics of the superconducting ceramic YBa₂Cu₃O_7-δ has been studied. Isothermal compaction rates between 930° and 955°C reached a maximum at some critical PO₂ (PO₂^CRIT), with decreasing rates both above and below this oxygen partial pressure. This behavior was not observed for YBa₂Cu₃O_7-δ sintered at 960°C, when a liquid phase is present. The activation energy for sintering above PO₂^CRIT has been estimated to be ∼190 kJ/mol, whereas below PO₂^CRIT it was found to be ∼130 kJ/mol. The oxygen ion diffusion was considered to be the rate-determining step above PO₂^CRIT, while it is hypothesized that lattice strain caused by the formation of oxygen ion vacancies below PO₂^CRIT affected the rate of sintering.     

Effect of Bi2O3 Addition on the Sintering Temperature and Microwave Dielectric Properties of Zn2SiO4 Ceramics

Bi₂O₃ was added to a nominal composition of Zn_1.8SiO_3.8 (ZS) ceramics to decrease their sintering temperature. When the Bi₂O₃ content was <8.0 mol%, a porous microstructure with Bi₄(SiO₄)₃ and SiO₂ second phases was developed in the specimen sintered at 885°C. However, when the Bi₂O₃ content exceeded 8.0 mol%, a liquid phase, which formed during sintering at temperatures below 900°C, assisted the densification of the ZS ceramics. Good microwave dielectric properties of Q × f =12,600 GHz, ɛ_r=7.6, and τ_f=−22 ppm/°C were obtained from the specimen with 8.0 mol% Bi₂O₃ sintered at 885°C for 2 h.     

Fabrication of Grain-Oriented Bi2WO6 Ceramics

Grain-oriented Bi₂WO₆ ceramics were fabricated by normal sintering techniques. Platelike crystallites were initially synthesized by a fused salt process using an NaCl-KCI melt. When calcined at <800°C, the Bi₂WO₆ crystallites are 3∼5 μ m in size and, at >850°C, =100 μm. After dissolving away the salt matrix, the Bi₂WO₆ particles were mixed with an organic binder and tapecast to align the platelike crystallites. Large particles were easily oriented by tapecasting but the sinterability of the tape was poor. Preferred orientation of small particles was increased by tapecasting and grain growth during sintering further improves the degree of orientation. Sintering above the 950°C phase transition, however, results in discontinuous grain growth and low densities. Optimum conditions for obtaining highly oriented ceramics with high density occur at sintering temperatures of 900°C using fine-grained powders which yield orientation factors of =0.88 and densities of 94% theoretical.