Synthesis and luminescence properties of a novel UV-emitting phosphor Sr<Subscript>3</Subscript>P<Subscript>4</Subscript>O<Subscript>13</Subscript>:Ce<Superscript>3+</Superscript>

The ultraviolet (UV)-emitting Sr₃P₄O₁₃:Ce³⁺ phosphors were synthesized via the solid-state reaction method, and their structural, morphological and luminescence properties were characterized by X-ray diffraction analysis, scanning electron microscopy, photoluminescence spectroscopy. The obtained results indicate that these phosphors can be effectively excited by short-wavelength ultraviolet (<300 nm), and exhibit long-wavelength ultraviolet (300–380 nm) emission with nanosecond-level fluorescence lifetime corresponding to the parity-allowed 5d–4f transitions of Ce³⁺. The concentration-quenching phenomenon of Ce³⁺ in Sr₃P₄O₁₃ host was also studied, in which the critical energy transfer distance between Ce³⁺ ions and concentration quenching mechanism were determined.     

Single phased Sr<Subscript>3</Subscript>La(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>:Eu<Superscript>2+</Superscript>/Mn<Superscript>2+</Superscript> phosphors: solid state synthesis,tunable luminescence and potential applications in white light LEDs

A series of Sr₃La(PO₄)₃:Eu²⁺/Mn²⁺ phosphors were synthesized by a solid state reaction. The phase and the optical properties of the synthesized phosphors were investigated. The XRD results indicate that the doped Eu²⁺ and Mn²⁺ ions do not change the phase of Sr₃La(PO₄)₃. The peak wavelengths of Eu²⁺ single doped and Eu²⁺/Mn²⁺ codoped Sr₃La(PO₄)₃ phosphors shift to longer wavelength due to the larger crystal field splitting for Eu²⁺ and Mn²⁺. The increases of crystal field splitting for Eu²⁺ and Mn²⁺ are induced by the substitution of Sr²⁺ by Eu²⁺ and Mn²⁺ in Sr₃La(PO₄)₃ host. Due to energy transfer from Eu²⁺ to Mn²⁺ in Sr₃La(PO₄)₃:Eu²⁺/Mn²⁺ phosphors, tunable luminescence was obtained by changing the concentration of Mn²⁺. And the white light was emitted by Sr₃La(PO₄)₃:3.0 mol%Eu²⁺/4.0 mol%Mn²⁺ and Sr₃La(PO₄)₃:3.0 mol%Eu²⁺/5.0 mol%Mn²⁺ phosphors.     

Luminescence studies on Eu<Superscript>2+</Superscript> and Tb<Superscript>3+</Superscript> doped Ca<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript> phosphors

Eu²⁺ and Tb³⁺ doped Ca₂MgSi₂O₇ phosphors were synthesized by conventional solid-state reaction. The phase formation was confirmed by X-ray powder diffraction technique and refined lattice parameters were calculated by rietveld refinement process using Celref v3. The photoluminescence (PL) excitation and emission spectra were investigated. The phosphors exhibited broaden green emitting luminescence peaking at 520 nm when excited at 374 nm source. Morphological studies were carried out using Scanning electron microscopy (SEM) images of the sample with optimum PL emission. The dependence of photoluminescence intensity on co-dopant concentration and the kinetic parameters were also reported. Time resolved fluorescence spectroscopy (TRFS) is used to investigate the decay in luminescence signals with respect to time. The sample proved to be a good long lasting material, which makes it useful in emergency signs, textile printing, textile exit sign boards and electronic instrument dial pads etc.     

Crystal structure and luminescence property of a single-phase white light emission phosphor Sr<Subscript>3</Subscript>YNa(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>F:Dy<Superscript>3+</Superscript>

A series of single-phase Sr₃YNa(PO₄)₃F:Dy³⁺ phosphors were successfully synthesized via a conventional solid state reaction process. The powder X-ray diffraction patterns were utilized to confirm the phase composite and crystal structure. The phosphor could be excited by the ultraviolet visible light in the region from 300 to 420 nm, and it shown two dominant emission bands peaking at 484 nm (blue light) and 580 nm (yellow light) which originated from the transitions of ⁴F_9/2→⁶H_15/2 and ⁴F_9/2→⁶H_13/2 of Dy³⁺, respectively. The optimum dopant concentration of Dy³⁺ ions was confirmed to be 7 mol% in Sr₃YNa(PO₄)₃F:Dy³⁺ system and the concentration quenching mechanism is dipole–dipole interaction. The lifetime values of Dy³⁺ ions at different concentrations (x?=?0.03, 0.05, 0.07, 0.09 and 0.11) were determined to be about 0.855, 0.759, 0.686, 0.606 and 0.546 ms, respectively. The thermal stability of luminescence of Sr₃YNa(PO₄)₃F:0.07Dy³⁺ phosphor was also investigated and the activated energy was deduced to be 0.228 eV, which shows good thermal stability. The chromaticity coordinates fall in the white-light region calculated by the emission spectrum. These results show that Sr₃YNa(PO₄)₃F:Dy³⁺ phosphor can be a promising white emitting phosphor for white LEDs.     

Effect of sintering temperature on the emission-spectrum-shape-evolution of Sr<Subscript>2</Subscript>SiO<Subscript>4</Subscript>:Eu<Superscript>2+</Superscript> phosphor

Color rendering index and color temperature are the key factors for the LEDs application. The two points are closely related to the emission spectrum shape of phosphors. As the key factors for the LEDs application, both the above aspects are closely dependent on the emission spectrum shape of phosphors. In this study, the emission spectrum shape has been adjusted via a home designed route. A combination of structural, morphological, and optical characterization techniques has been used to study the shape evolution mechanism. The structural results show that the Sr₂SiO₄ phase has not been changed with the sintering temperature increasing, but the emission spectrum shape has changed dramatically, meanwhile, the colorimetric coordinate moves from blue-green to green region. Gaussian fitting method has been used to treat the emission spectrum, and the as-obtained results indicate the emission spectrum contains two single bands, which come from the 4f⁷(⁷S_7/2)–4f⁶(⁷F_J)5d¹ transition of Eu²⁺ on the different Sr sites in the Sr₂SiO₄ crystal. The intensity of the two single bands is driven by sintering temperature, because of the difference between the energy barrier of the Eu²⁺ occupying the different Sr sites in the matrix crystal. Moreover, the mechanism of the above phenomenon has also been studied by means of first principles method, and the obtained results agree well with the former deduction.     

Sr<Subscript>3</Subscript>GdLi(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>F: Sm<Superscript>3+</Superscript> phosphor: preparation and luminescence properties evaluation

A series of Sr₃Gd_1?xLi(PO₄)₃F: xSm³⁺ (x?=?0.02, 0.04, 0.06, 0.08) phosphors were synthesized by a high-temperature solid state method. The Sm³⁺ activated Sr₃GdLi(PO₄)₃F phosphors can be efficiently excited by the wavelengths in the range from 350 to 450 nm, which matches perfectly with that of the commercial near-UV LED chips. The optimal doping concentration of Sr₃Gd_1?xLi(PO₄)₃F: xSm³⁺ phosphors was determined to be x?=?0.04, corresponding to the quantum efficiency of 2.23%, and the CIE chromaticity coordinates (x?=?0.5172, y?=?0.4641). The concentration quenching mechanism of Sm³⁺ in Sr₃GdLi(PO₄)₃F host is mainly attributed to the dipole–dipole interaction, which was confirmed by the fluorescent lifetimes. The effect of temperature on the photoluminescence property of Sr₃GdLi(PO₄)₃F: Sm³⁺ was investigated. 90% of the intensity is preserved at 150 °C. In addition, a white light emitting diode (WLED) lamp was fabricated by a 405 nm n-UV LED chip coated with Sr₃Gd_0.96Li(PO₄)₃F:0.04Sm³⁺ phosphor and commercial yellow phosphor (YAG: Ce³⁺) of a certain mass ratio. The present work indicates that the Sr₃GdLi(PO₄)₃F: Sm³⁺ orange–red-emitting phosphors tend to be potential application in n-UV WLED.     

Microwave synthesis and luminescence properties of YVO<Subscript>4</Subscript>:Eu<Superscript>3+</Superscript>

Europium-doped YVO₄ phosphors have been synthesized using microwave radiation of 700 W power. The uniformity and high rate of microwave heating, as well as “nonthermal” effects of microwave radiation, considerably accelerate the decomposition of precursors and YVO₄:Eu³⁺ synthesis. The europium concentration was varied from 1 to 8 at %. The luminescence intensity of YVO₄:Eu³⁺ was shown to depend on Eu³⁺ concentration, with a maximum at 8 at % Eu³⁺. According to transmission electron microscopy data, the synthesized phosphors consist of nanoparticles 6 to 8 nm in size, with an appreciable degree of agglomeration.     

Roles of doping ions in persistent luminescence of SrAl<Subscript>2</Subscript>O<Subscript>4</Subscript>:Eu<Superscript>2+</Superscript>, RE<Superscript>3+</Superscript> phosphors

The polycrystalline Eu²⁺ and RE³⁺ co-doped strontium aluminates SrAl₂O₄:Eu²⁺, RE³⁺ were prepared by solid state reactions. The UV-excited photoluminescence, persistent luminescence and thermo-luminescence of the SrAl₂O₄:Eu²⁺, RE³⁺ phosphors with different composition and doping ions were studied and compared. The results showed that the doped Eu²⁺ ion in SrAl₂O₄:Eu²⁺, Dy³⁺ phosphors works as not only the UV-excited luminescent center but also the persistent luminescent center. The doped Dy³⁺ ion can hardly yield any luminescence under UV-excitation, but can form a electron trap with appropriate depth and greatly enhance the persistent luminescence and thermo-luminescence of SrAl₂O₄:Eu²⁺. Different co-doping RE³⁺ ions showed different effects on persistent luminescence. Only the RE³⁺ ion (e.g. Dy³⁺, Nd³⁺), which has a suitable optical electro-negativity, can form the appropriate electron trap and greatly improve the persistent luminescence of SrAl₂O₄:Eu²⁺. Based on above observations, a persistent luminescence mechanism, electron transfer model, was proposed and illustrated.     

Optical properties of Eu<Superscript>3+</Superscript> activated SrLa<Subscript>2</Subscript>O<Subscript>4</Subscript> red-emitting phosphors for WLED applications

The SrLa_2?xO₄:xEu³⁺ phosphors are synthesized through high-temperature solid-state reaction method at 1473 K with various doping concentration. Their phase structures, absorption spectra, and luminescence properties are investigated by X-ray diffraction (XRD), UV–Vis spectrophotometer and photoluminescence spectrometry. The intense absorption of SrLa_2?xO₄:xEu³⁺ phosphors have occurred around 400 nm. The prominent luminescence spectra of the prepared phosphors exhibited bright red emission at 626 nm. The doping concentration 0.12 mol% of Eu³⁺ is shown to be optimal for prominent red emission and chromaticity coordinates are x?=?0.692, y?=?0.3072. Considering the high colour purity and appropriate emission intensity of Eu³⁺ doped SrLa₂O₄ can be used as red phosphors for white light emitting diodes (WLEDs).     

Effect of annealing time on microstructure and morphology of thin films by sputtering deposition with (Ba<Subscript>0.3</Subscript>Sr<Subscript>0.7</Subscript>)(Zn<Subscript>1/3</Subscript>Nb<Subscript>2/3</Subscript>)O<Subscript>3</Subscript> target

The ceramic thin films have been fabricated by radio frequency (RF) magnetron sputtering technique on SiO₂ (110) substrates with (Ba_0.3Sr_0.7)(Zn_1/3Nb_2/3)O₃ target, and then the thin films were annealed at 1,150 °C for different times at O₂ atmosphere. The microstructure and morphology of the thin films were investigated as a function of the annealing times using the X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, and atomic force microscopy techniques. The results show that the microstructure, morphology, and crystallinity of the thin films can be affected by the annealing times significantly. The main phases of the samples are indexed to be Ba_0.5Sr_0.5Nb₂O₆ and Ba_0.27Sr_0.75Nb₂O_5.78, which are different from component of the (Ba_0.3Sr_0.7)(Zn_1/3Nb_2/3)O₃ target due to the volatilization of ZnO. The crystalline quality of the thin films decreases when the annealing time is shorter or longer than 30 min, and the roughness and grain size of the thin films reaches a maximum value when the annealing time is 30 min.     

Rapid synthesis and enhancement in down conversion emission properties of BaAl<Subscript>2</Subscript>O<Subscript>4</Subscript>:Eu<Superscript>2+</Superscript>,RE<Superscript>3+</Superscript> (RE<Superscript>3+</Superscript>=Y,Pr) nanophosphors

BaAl₂O₄:Eu²⁺,RE³⁺ (RE³⁺=Y, Pr) down conversion nanophosphors were prepared at 600 °C by a rapid gel combustion technique in presence of air using boron as flux and urea as a fuel. A comparative study of the prepared materials was carried out with and without the addition of boric acid. The boric acid was playing the important role of flux and reducer simultaneously. The peaks available in the XPS spectra of BaAl₂O₄:Eu²⁺ at 1126.5 and 1154.8 eV was ascribed to Eu²⁺(3d _5/2) and Eu²⁺(3d _3/2) respectively which confirmed the presence of Eu²⁺ ion in the prepared lattice. Morphology of phosphors was characterized by tunneling electron microscopy. XRD patterns revealed a dominant phase characteristics of hexagonal BaAl₂O₄ compound and the presence of dopants having unrecognizable effects on basic crystal structure of BaAl₂O₄. The addition of boric acid showed a remarkable change in luminescence properties and crystal size of nanophosphors. The emission spectra of phosphors had a broad band with maximum at 490–495 nm due to electron transition from 4f ⁶5d ¹ → 4f ⁷ of Eu²⁺ ion. The codoping of the rare earth (RE³⁺=Y, Pr) ions help in the enhancement of their luminescent properties. The prepared phosphors had brilliant optoelectronic properties that can be properly used for solid state display device applications.     

A novel blue emitting phosphor NaBa<Subscript>0.98</Subscript>Eu<Subscript>0.02</Subscript>PO<Subscript>4</Subscript> and the improvement of its luminescence properties

A novel blue-emitting phosphor NaBa_0.98Eu_0.02PO₄ was synthesized by conventional solid state reaction, and it exhibits efficient blue emission under near-ultraviolet (n-UV) excitation. The emission spectrum shows a single band centered at about 440 nm, which corresponds to the 4f⁶5d¹-4f⁷ transition of Eu²⁺. The excitation spectrum is a broad band in the wavelength range between 200 and 450 nm, which can match the emission of white light emitting diodes (LEDs) by the method of n-UV conversion. The Ca²⁺, Sr²⁺ and Mg²⁺ were co-doped into NaBa_0.98Eu_0.02PO₄ respectively. Special attention was paid to the sample co-doped with Ca²⁺ that could possess a higher luminous efficacy than the analogs co-doped with Sr²⁺ and Mg²⁺. With the co-doping of Ca²⁺, the enhanced intensity of the excitation and emission band appears. The optimum co-doping concentration of Ca²⁺ is 7 mol.%. The emission intensity of NaBa_0.91Ca_0.07Eu_0.02PO₄ phosphoris about 1.68 times than that of NaBa_0.98Eu_0.02PO₄ phosphor. The as-prepared phosphors are the potential blue phosphors for application in white LEDs.     

Preparation and characterization of Eu<Superscript>3+</Superscript> activated CaSiO<Subscript>3</Subscript>, (CaA)SiO<Subscript>3</Subscript> [A = Ba or Sr] phosphors

Eu³⁺ activated CaSiO₃, (Ca, Ba) SiO₃ and (Ca, Sr) SiO₃ have been prepared by sol-gel technique. Residual solvent and organic contents in the gel were removed by firing at 100°C for 3–4 h at 300 and 600°C for 2 h. Small exothermic shoulder around 850 to 875°C, as observed in DTA curve, corresponds to crystallization temperature of the doped calcium silicate. Influence of firing temperature on the luminescence of Eu³⁺ shows the maximum emission intensity in gel fired at 850°C. Photoluminescence emission peak is observed at 614 nm due to⁵D₀ →⁷F₂ transition of Eu³⁺ ion in (Ca, Ba) SiO₃ and (Ca, Sr) SiO₃ phosphors, when excited by 254 nm. The (Ca, Ba) SiO₃ material is proposed as an efficient red phosphor.     

Synthesis and luminescence properties of Eu<Superscript>2+</Superscript>-doped Li<Subscript>2</Subscript>SrSiO<Subscript>4</Subscript>

We have studied the luminescence spectra of Li₂Sr_{1 − x} Eu _x SiO₄ (x = 0.0001–0.01) solid solutions prepared by solid-state reactions and a sol-gel process in a reducing atmosphere. The spectra show a broad band in the range 500–700 nm, centered at 578 nm, which is due to the 4f ⁶5d → 4f ⁷ transition. The luminescence excitation spectrum shows, in addition to bands due to Eu²⁺ 4f ⁷ → 4f ⁶5d transitions, a strong band centered at 174 nm, attributable to absorption in the SiO₄⁴⁻ group.     

Preparation and characterization of Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Eu phosphors by combustion process

Europium-doped yttrium phosphors were successfully synthesized by combustion process using yttrium nitrate hexahydrate [Y(NO₃)₃·6H₂O], europium nitrate [Eu(NO₃)₃·6H₂O], and carbohydrazide [CO(N₂H₃)₂]. The process takes only a few minutes to obtain Y₂O₃:Eu phosphors. The resultant powders annealed at different temperature and were investigated by X-ray diffractometer (XRD), differential thermal analyzer/thermogravimeter (DTA/TG), Fourier transform infrared spectroscopy (FTIR), photoluminescence excitation and emission spectra (PL), and transmission electron microscopy (TEM). The results showed that the formation temperature of Y₂O₃ phase is significant low, compared to solid-state reaction route of constituent oxides. For luminescence property, the emission intensity of Y₂O₃:Eu phosphors synthesized by combustion process increases steadily with increasing europium amount from 1 mol% to 5 mol%.     

The luminescent enhancement of LaPO<Subscript>4</Subscript>:Ce<Superscript>3+</Superscript>,Tb<Superscript>3+</Superscript> nano phosphors by radial aggregation

The rare earth nano phosphors can meet the challenging demand for new functional devices but their luminescence is always poor. Here we report on a simple method to prepare uniform LaPO₄:Ce³⁺,Tb³⁺ sphere-like nano aggregates from the precipitated nano phosphor crystallites without using any additive. The spontaneous aggregation is induced and controlled only by the suspension pH conditions. It is found that the 100 nm spherical aggregates can significantly improve the green emissions of the LaPO₄:Ce³⁺,Tb³⁺ nano particles. The intensity of the aggregates can be about 10 times as that of the 80 nm-sized individual ones. This study may provide a useful yet convenient strategy in the improvement and application of nano phosphors.     

Effect of sputtering power on microstructure of dielectric ceramic thin films by RF magnetron sputtering method using (Ba<Subscript>0.3</Subscript>Sr<Subscript>0.7</Subscript>)(Zn<Subscript>1/3</Subscript>Nb<Subscript>2/3</Subscript>)O<Subscript>3</Subscript> as target

Radio frequency (RF) magnetron sputtering method was applied to prepare dielectric ceramic thin films on SiO₂ (110) substrates using (Ba_0.3Sr_0.7)(Zn_1/3Nb_2/3)O₃ microwave dielectric ceramics as target. The samples were deposited at different sputtering powers in Ar atmosphere. In particular, the microstructure and morphology of the thin films were investigated as a function of sputtering powers by X-ray diffraction (XRD), X-ray photoelectron spectroscope (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM) and transmission electron microscopy (TEM). The results show that the thin films are polycrystalline and the sputtering power significantly influences the surface morphology and microstructure of the thin films. On increasing the sputtering power, the crystallinity improves and the grain size and roughness of the thin films reach maximum values at 200 W.     

Luminescence properties of ZnO/TiO<Subscript><Emphasis Type="Bold">2</Emphasis></Subscript> nanocomposite activated by Eu<Superscript><Emphasis Type="Bold">3</Emphasis><Emphasis Type="Bold">+</Emphasis></Superscript> and their spectroscopic analysis

A new type of novel orange-red emitting Eu-doped ZnO/TiO ₂ nanocomposite phosphors have been synthesized by simple low temperature co-precipitation route. Structure and morphology of the prepared sample have been investigated using X-ray diffraction and field emission scanning electron microscopy (FESEM) techniques. XRD pattern confirmed the presence of both phases of ZnO and TiO ₂ simultaneously. The luminescence properties, such as photoluminescence (PL) excitation and emission spectra, Judd–Ofelt parameters, CIE colour coordinates and the dependence of luminescence intensity on the doping level were investigated. The luminescence spectrum characteristics of Eu ³⁺ ions have a strong dependence on Eu ³⁺ doping levels as well as ZnO/TiO ₂ ratio variations. The photoluminescence results indicate that these phosphors could be efficiently excited by near-ultraviolet radiation, which causes emissions in orange–red regions.     

SiO<Subscript>2</Subscript>/TiO<Subscript>2</Subscript> fibers from titanium-modified polycarbosilane

We developed a process for preparing SiO₂/TiO₂ fibers by means of precursor transformation method. After mixing PCS and titanium alkoxide, continuous SiO₂/TiO₂ fibers were fabricated by the thermal decomposition of titanium-modified PCS (PTC) precursor. The tensile strength and diameter of SiO₂/TiO₂ fibers are 2.0 GPa, 13 μm, respectively. Based on X-ray diffraction (XRD), scanning electron microscopy (SEM), and high resolution transmission electron microscopy (HRTEM) measurements, the microstructure of the SiO₂/TiO₂ fibers is described as anatase–TiO₂ nanocrystallites with the mean size of ~10 nm embedded in an amorphous silica continuous phase.     

Structural and Magnetic Properties of La<Subscript>2/3</Subscript>Sr<Subscript>1/3</Subscript>MnO<Subscript>3</Subscript>/SrTiO<Subscript>3</Subscript>/CoFe<Subscript>2</Subscript> Hard-Soft Magnetic Systems

We report on the growth and magnetic properties of La_2/3Sr_1/3MnO₃/SrTiO₃/CoFe₂ hard-soft magnetic systems prepared by pulsed laser deposition on SrTiO₃(001) substrates. In situ reflection high-energy electron diffraction along the [100]SrTiO₃ substrate azimuth and atomic force microscopy measurements reveal that La_2/3Sr_1/3MnO₃ and SrTiO₃ grow both in a three dimensional mode and that the roughness of the lower and upper magnetic/non-magnetic interfaces ranges between 2 and 4 Å. Cross-section transmission electron microscopy observations show that the layers are continuous, with an homogeneous thickness, and that the interfaces are mostly sharp and correlated. The magnetization curves show a two step reversal of the magnetization, with very distinct coercive fields. A small anisotropy is observed for the CoFe₂ layer with an in plane easy magnetization axis along the [110]SrTiO₃ direction. Minor magnetization loops indicate that the coupling between the magnetic layers is negligible.