ZrO_2改性对Co-Ru/γ-Al_2O_3催化剂F-T合成性能的影响

采用浸渍法制备Co-Ru双金属F-T合成催化剂,通过对催化剂进行BET、XRD和TPR表征,考察了ZrO2负载量对催化剂性能的影响,并在固定床反应器中研究了对合成重质烃反应性能的影响。结果表明,载体γ-Al2O3 ZrO2改性没有引起催化剂还原温度的降低,但可降低载体与Co间的相互作用;随ZrO2含量的增加,催化剂中易还原Co物种量增加;在623～693K下进行还原,催化剂具有较高的还原程度,呈现出良好的合成重质烃反应性能。同时,载体γ-Al2O3用ZrO2改性,可形成Co-ZrO2界面,使CO容易离解。在原料气n(H2)/n(CO)=2.0、503K、1.5MPa和空速800h-1下,15%Co0.4%Ru8.0%ZrO2/γ-Al2O3催化剂CO的转化率为93.27%,C5+的选择性82.56%,链生长概率0.81。     

ZrO2改性对Co-Ru/γ-Al203催化剂F-T合成性能的影响

采用浸溃法制备Co-Ru双金属F-T合成催化剂,通过对催化剂进行BET、XRD和TPR表征,考察了ZrO2负载量对催化剂性能的影响,并在固定床反应器中研究了对合成重质烃反应性能的影响.结果表明,载体γ-Al2O3,ZrO2改性没有引起催化剂还原温度的降低,但可降低载体与Co问的相互作用;随ZrO2含量的增加,催化剂中易还原Co物种量增加;在623～693K下进行还原,催化剂具有较高的还原程度,呈现出良好的合成重质烃反应性能.同时,载体γ-Al2O3用ZrO2改性,可形成Co-ZrO2界面,使CO容易离解.在原料气,n(H2)/n(CO)=2.0、503K、1.5MPa和空速800h-1下,15%Co0.4%Ru8.0%ZrO2O2/γ-Al2O3催化剂CO的转化率为93.27%,C5 的选择性82.56%,链生长概率0.81.     

Fe-Co-K/SiO_2催化剂催化F-T合成本征动力学的研究

采用浸渍法制备了Fe-Co-K/SiO2催化剂。在等温积分反应器中,在温度518~541K、压力1.00~2.60MPa、进料中n(H2)∶n(CO)=1.12~3.23、气态空速3 000~4 800h-1的条件下,研究了在Fe-Co-K/SiO2催化剂上的F-T合成本征动力学。F-T合成中CO2的生成量很少,水煤气变换反应可不予考虑,生成烃为主要反应。以CO转化率的计算值和实验值的残差平方和为目标函数,采用Levenberg-Maquardt法对动力学参数进行优化,得到了F-T合成本征动力学模型参数,反应的活化能为78.9kJ/mol。在Fe-Co-K/SiO2催化剂上的F-T合成本征动力学模型的计算值与实验值的平均偏差为8.27%,模型的计算值与实验值符合较好。     

ZrO2改性Co/AC催化剂F-T合成的研究

考察了不同含量ZrO2助剂对Co/AC催化剂F-T合成活性组分在活性炭表面上的分散状态,并与反应结果进行了关联.结果表明ZrO2助剂的加入可提高活性组分的分散度.分散度越高,其催化活性越高,同时还发现ZrO2助剂有利于重质烃的生成,并且可以抑制水中含氧化合物的生成.     

锆助剂对F-T合成Co/Al2O3催化剂的影响

考察了助剂ZrO2添加量对Co/Al2O3催化剂F-T合成反应性能的影响,并通过程序升温还原和程序升温脱附等技术对催化剂进行了表征.结果表明,助剂锆的加入对Co的分散度影响不大;添加一定量的ZrO2可以改善催化剂的还原性能,使催化活性显著提高,但ZrO2的加入对CH4、CO2和C5+烃的选择性影响不大.在一定反应温度区内,CO转化率随反应温度的增加而显著增加,但CH4和C5+烃的选择性变化不大.     

Fe-Co-K/SiO_2催化剂对Fischer-Tropsch合成反应的催化性能

采用浸渍法制备了Fe-Co-K/SiO2催化剂,在连续流动固定床反应器上考察了反应温度、反应压力、重时空速和n(H2)∶n(CO)对该催化剂催化Fischer-Tropsch合成反应性能的影响。实验结果表明,随反应温度的升高,催化剂的活性提高,CO转化率和CH4选择性增大,重质烃(C 5+)选择性减小;升高反应压力有利于提高CO转化率和重质烃选择性;增大重时空速不利于重质烃的生成,同时CO转化率减小,CH4选择性增大;随n(H2)∶n(CO)的增大,CO转化率和CH4选择性增大,重质烃选择性减小。Fe-Co-K/SiO2催化剂用于Fischer-Tropsch合成反应较适宜的工艺条件为:反应温度503～513 K、反应压力1.5 MPa、重时空速600～800 h-1、n(H2)∶n(CO)=2.00。     

还原时合成气H2/CO摩尔比对铁基催化剂浆态床费-托合成反应性能的影响

在浆态床反应器中,详细考察尾气循环状态下还原时合成气H2/CO摩尔比对SFT418工业铁基F-T合成催化剂还原和反应后的物相以及F-T合成反应性能的影响。结果表明：还原后催化剂的比表面积大幅度下降,平均孔径明显增大,孔体积下降。还原时合成气H2/CO摩尔比影响催化剂的还原程度、F-T合成反应活性和失活速率,在较低的H2/CO摩尔比下还原得到的催化剂中铁碳化物含量较高,F-T合成初始反应活性较高,失活速率较大;在较高H2/CO摩尔比下还原得到的催化剂中铁碳化物含量较低,F-T合成初始反应活性较低,但其失活速率比在较低的H2/CO摩尔比下还原得到的催化剂低。催化剂还原时适宜的合成气H2/CO摩尔比为20。     

Fe-Co/SiO_2双金属催化剂上费托合成反应的研究

采用浸渍法制备Fe-Co/SiO2双金属催化剂,考察了不同反应温度、压力、空速下催化剂的反应性能。实验结果表明,在230~300℃的温度范围内,随反应温度升高,催化剂活性提高,甲烷选择性上升,水煤气变换程度逐渐增大,而C2~C4烯烃/烷烃比和C5+选择性下降;压力增加有利于反应活性的提高和重质烃的合成,当压力大于1.5MPa后,CO的转化率、水煤气变换程度、C5+选择性C2~C4烯烃/烷烃比变化不太明显;随空速增加,CO转化率下降,产物中低碳烃含量增加,说明高空速不利于重质烃的生成。XRD结果表明反应前催化剂主要成分为Co3O4和Fe2O3,反应后则为Fe-Co合金。     

合成液体燃料的活性炭负载钴基催化剂的反应性能

在固定床等温积分反应器中,考察了活性炭负载钴基催化剂(Co/AC)的费托(F-T)合成反应性能,采用BET、H2-TPR和SEM等方法对Co/AC催化剂进行了表征。表征结果显示,Co/AC催化剂孔道属于微孔和中孔的混合结构,可用纯H2还原,还原温度选取350~400℃。实验结果表明,升高反应温度和反应压力、减小气态空速、增加原料气中H2与CO的摩尔比(H2/CO比),有利于提高CO的转化率;升高反应压力、降低反应温度、减小气态空速及原料气H2/CO比有利于高碳烃和高碳醇的生成。Co/AC催化剂用于F-T合成较优的工艺条件为:反应温度230℃,反应压力4.0M Pa,原料气H2/CO比2.00,气态空速2 000h-1。在该反应条件下,CO转化率为20.1%,CH4、低碳烃(C2~4)、高碳烃(C+5)、低碳醇(C1~5OH)及高碳醇(C+6OH)的选择性分别为19.1%,24.1%,36.5%,15.8%,4.5%。     

ZrO_2改性Co/活性炭催化剂对浆态床Fischer-Tropsch合成反应的催化性能

考察了ZrO2改性Co/活性炭(Zr-Co/AC)催化剂在浆态床反应器中的Fischer-Tropsch合成反应性能及反应条件对催化剂活性和选择性的影响。实验结果表明,适量添加ZrO2助剂可明显提高Co/AC催化剂对Fischer-Tropsch合成反应的催化活性,降低甲烷的选择性并提高C5+烃的选择性。当Zr-Co/AC催化剂(Co质量分数为15%)中Zr的质量分数由0增加到6%时,CO的转化率从36.4%增加到67.9%,甲烷选择性从15.4%降低到10.1%,而C5+烃的选择性从71.4%增加到79.3%。当Zr-Co/AC催化剂中Co质量分数为15%、Zr质量分数为2%时,适宜的反应条件为:温度493～503K、压力2.5～3.5MPa、气态空速500～2000h-1、催化剂在浆态液中的体积分数为2.50%。在此条件下催化剂的活性和C5+烃的选择性较高。     

Effects of Impregnation Solvents on Catalytic Performance of Co-Ru-ZrO2/γ-Al2O3 Catalyst for Fischer-Tropsch Synthesis

Used ZrO₂ modified γ-Al₂O₃ as support, Co-Ru catalysts were prepared by incipient impregnation method. The effects of impregnation solvents on the performances of catalysts were examined. The catalyst was prepared with ethanol solution and high Co dispersion was obtained, exhibiting highest activity of CO hydrogenation, very low methane selectivity, and high heavy hydrocarbon C₅⁺ selectivity. The catalysts were prepared with aqueous solution and methanol solution, and the reaction behaviors were similar. The solvent isopropanol caused the lowest catalytic activity and highest methane selectivity. Increasing the reaction temperature enhanced the CO hydrogenation rate, and the CO conversion slightly increased the CO₂ selectivity and favored the formation methane and light hydrocarbons, while the chain growth probability decreased. For the catalyst prepared with ethanol, the CO conversion, the CH₄ selectivity, and the C₅⁺ selectivity were 94.16%, 5.65%, and 88.2%, respectively, and the chain growth probability was 0.87 at 493 K, 1.5 MPa, 800 h^-1, and n(H₂):n(CO) = 2.0 in feed.     

ZrO_2改性Co-Ru/γ-Al_2O_3催化剂对Fischer-Tropsch合成反应的催化性能

采用浸渍法制备了ZrO2改性Co-Ru/γ-A l2O3催化剂(以下简称催化剂),考察了反应温度、反应压力、气态空速和合成气n(H2)∶n(CO)对催化剂催化性能的影响。实验结果表明,随反应温度的升高,催化剂的催化活性提高,CH4的选择性增加,重质烃的选择性先增加后减小;升高反应压力有利于提高催化剂的催化活性、增加重质烃的选择性;增大气态空速不利于重质烃的生成;随n(H2)∶n(CO)的增大,CO的转化率和CH4的选择性增加、重质烃的选择性减小。在反应温度220℃、反应压力1.5M Pa、气态空速800h-1、n(H2)∶n(CO)=2.0的条件下,CO的转化率达到84.88%,烃的总选择性为99.63%,CH4和CO2的选择性分别为5.47%,0.37%,C5+占全部烃产物的质量分数为88.16%,重质烃的收率(以标准状况下1m3(H2+CO)计)为152.83g。     

CO_2加氢制低碳烯烃Fe/Silicalite-2催化剂研究 Ⅱ.催化剂制备研究

铁是ＣＯ２加氢制低碳烯烃的催化活性组分，其含量的增加将明显提高ＣＯ２转化率和反应产物中烃类摩分率；ＭｎＯ是Ｆｅ／Ｓｉ－２催化剂ＣＯ２加氢制低碳烯烃的有效助剂，提高ＭｎＯ含量，有利于提高ＣＯ２加氢制低碳烯烃的选择性，尤其可明显提高烃类产物中的烯、烷比值。结果还表明，ＭｎＯ助剂对甲烷生成量的影响不明显；而Ｋ２Ｏ助剂则可抑制甲烷生成，从而进一步提高低碳烯烃选择性，表明ＭｎＯ和Ｋ２Ｏ是Ｆｅ／Ｓｉ－２催化剂ＣＯ２加氢制低碳烯烃的重要助剂。     

石油裂解汽油烯羰化酯化制C7—C9混合脂肪酸酯

用八羰基二钴／吡啶为催化剂,以炼油厂蜡裂解汽油烯为原料,进行羰化酯化反应合成C7－C9混合脂肪酸甲酯,考察了各种反应条件,催化剂浓度以及甲醇含水量对反应转化率和产物酯收率的影响,在n(吡啶（／n(钴）＝0．5;1．0时,确定出反应的最佳工艺条件为：反应温度120度,反应压力4．0MPa,反应时间6h.α－烯烃的转化率为100％,酯的总收率大于99％。     

CO_2加氢制低碳烯烃的Fe／Silicalite－2催化剂研究──Ⅰ．催化剂性能及反应机理探讨

Ｋ－Ｆｅ－ＭｎＯ／Ｓｉ－２催化剂具有较佳的ＣＯ２加氢合成低碳烯烃性能，并随碱金属钾助剂的添加而明显改善；其ＣＯ２加氢反应具有（１）ＣＯ２＋Ｈ２ＣＯ＋Ｈ２Ｏ和（２）ＣＯ＋（ｍ／２ｎ＋１）Ｈ２１／ｎＣｎＨｍ＋Ｈ２Ｏ两步反应机理；应用该反应机理，解释了ＣＯ２／Ｈ２比、反应温度、反应压力、反应气空速等对Ｋ－Ｆｅ－ＭｎＯ／Ｓｉ－２催化剂ＣＯ２加氢反应性能的影响；探讨了催化剂中Ｋ２Ｏ助剂的作用。     

Fe-Mn催化剂浆态床合成低碳烯烃的反应性能

在浆态床反应器中,对Fe-Mn催化剂上CO加氢合成低碳烯烃的反应性能进行了研究,考察了不同温度、空速和压力下Fe-Mn催化剂的催化性能,并借助XRD和N2物理吸附等手段对催化剂进行了表征。实验结果表明,Fe-Mn催化剂在运行300h后达到稳定运行状态。反应参数的适当调变,可有效提高Fe-Mn催化剂的活性和低碳烯烃收率,并使产物分布得到优化。在n(H2)∶n(CO)=2、320℃、2.0 MPa、合成气空速1 000 h-1的条件下,CO转化率83.10%,CH4选择性11.88%,C5+烃选择性39.06%,C2～4烃中烯烃与烷烃的质量比3.59,低碳烯烃收率38.50 g/m3(基于H2与CO的总体积)。     

CO_2加氢制低碳烯烃Fe/Silicalite-2催化剂研究 Ⅲ.K-Fe-MnO/Silicalite-2催化剂性能考察

研究开发了一种具有高催化活性和高低碳烯烃选择性的Ｋ－Ｆｅ－ＭｎＯ／Ｓｉ－２担载型催化剂；考察了Ｖ（ＣＯ２）／Ｖ（Ｈ２）比、反应温度、反应气空速和反应压力对Ｋ－Ｆｅ－ＭｎＯ／Ｓｉ－２催化剂ＣＯ２加氢反应制低碳烯烃选择性及催化活性的影响；考察催化剂稳定性及再生性能，对催化剂进行差热－热重分析结果表明，Ｋ－Ｆｅ－ＭｎＯ／Ｓｉ－２催化剂具有很好的催化稳定性能。     

Cu/Zn/Al/Mn催化剂上CO_2加氢合成甲醇的CO助催化作用

：Ｃｕ／Ｚｎ／Ａｌ／Ｍｎ４组分催化剂对ＣＯ２加氢合成甲醇原料气中ＣＯ的助催化作用进行研究。结果表明，ＣＯ占据了部分催化剂表面起逆水汽变换反应的活性位，从而降低ＣＯ２转化率，但甲醇选择性和收率得到了提高。     

添加CO_2对Fischer-Tropsch合成反应的影响

采用无梯度反应器,在Fe-Mn催化剂、不同氢碳比和反应温度下,考察了反应体系中添加CO2对Fischer-Tropsch合成反应的影响。实验结果表明,添加CO2可加快水煤气逆变换反应的速率,CO2的选择性降低。当反应体系总压不变时,在不同氢碳比和反应温度下,添加CO2降低了合成气的分压,CO转化率降低,含氧化合物的生成速率也呈下降趋势。添加CO2降低了表面氢物种的浓度,低碳烃的烯烷比增大。乙烯的再吸附及二次反应性能强于丙烯、丁烯等的再吸附及二次反应性能;随氢碳比的增大,乙烯二次加氢反应显著增强。无论添加CO2与否,乙烯选择性均随氢碳比的增大而降低,而其他轻质烃的选择性则随氢碳比的增大而增加。在本实验条件范围内,水煤气变换反应仍远离平衡。