High-Temperature Erosive Behavior of Plasma Sprayed Cr<Subscript>3</Subscript>C<Subscript>2</Subscript>-NiCr/Cenosphere Coating

This research examines the deposition of Cr₃C₂-NiCr/cenosphere and Cr₃C₂-NiCr coatings on MDN 321 steel through the process of plasma spray. In this process, the solid particle erosion test is established at 200, 400, 600 °C with 30° and 90° impact angles. Alumina erodent is adopted to investigate the erosive behavior of the coating at higher temperatures. The properties of the Cr₃C₂-NiCr/cenosphere coating are established based on the microhardness, the adhesive strength, the fracture toughness, and the ductility. To quantify volume loss as a result of erosion, an optical profilometer is used. At higher temperature, decrease in the erosion volume loss of Cr₃C₂-NiCr/cenosphere and Cr₃C₂-NiCr coatings is observed. The erosion-resistive property of Cr₃C₂-NiCr/cenosphere coating is higher than that of MDN 321 steel by 76%. This property is influenced by high-temperature stability of mullite, alumina, and protective oxide layer that is formed at elevated temperatures. The morphology of eroded coating discloses a brittle mode of material removal.     

Development and Application of Binary Suspensions in the Ternary System Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>-TiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> for S-HVOF Spraying

Compositions in the system Cr₂O₃-TiO₂-Al₂O₃ are among the most used ceramic materials for thermally sprayed coating solutions. Cr₂O₃ coatings present good sliding wear resistance; Al₂O₃ coatings show excellent insulation behavior and TiO₂ striking corrosion properties. In order to combine these properties, coatings containing more than one oxide are highly interesting. The conventional spraying process is limited to the availability of binary feedstock powders with defined compositions. The use of suspensions offers the opportunity for tailor-made chemical compositions: within the triangle of Cr₂O₃-TiO₂-Al₂O₃, each mixture of oxides can be created. Criteria for the selection of raw materials as well as the relevant aspects for the development of binary suspensions in the Cr₂O₃-TiO₂-Al₂O₃ system to be used as feedstock for thermal spraying are presented. This formulation of binary suspensions required the development of water-based single-oxide suspensions with suitable behavior; otherwise, the interaction between the particles while mixing could lead up to a formation of agglomerates, which affect both the stability of the spray process and the coating properties. For the validation of this formulation procedure, binary Cr₂O₃-TiO₂ and Al₂O₃-TiO₂ suspensions were developed and sprayed using the S-HVOF process. The binary coatings were characterized and discussed in terms of microstructure and microhardness.     

Effects of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Nano-Particles on Corrosion Performance of Plasma Electrolytic Oxidation Coatings Formed on 6061 Aluminum Alloy

Corrosion resistance improvement of plasma electrolyte oxidation coatings on 6061 aluminum alloy in silicate electrolyte containing Al₂O₃ nano-particles was studied, with particular emphasis on the microstructure, coating growth, and corrosion behavior in 3.5 wt.% NaCl solution. The microstructure of coatings, their thickness, and phase composition were characterized using scanning electron microscopy and x-ray diffraction. All characterization data showed that the maximum coating thickness and lowest amount of porosity were obtained in a low concentration of KOH, a high concentration of Na₂SiO₃, and moderate concentration of Al₂O₃ nano-particles in the electrolyte. This combination describes the optimum plasma electrolytic oxidation electrolyte, which has the best conductivity and oxidizing state, as well as the highest incorporation of electrolyte components in the coating growth process. On the other hand, incorporation and co-deposition of Al₂O₃ nano-particles were more pronounced than SiO₃ ^2? ions in some level of molar concentration, which is due to the higher impact of electron discharge force on the adsorption of Al₂O₃ nano-particles. The electrochemical results showed that the best protective behavior was obtained in the sample having a coat with the lowest porosity and highest thickness.     

Effect of Nano-Si<Subscript>3</Subscript>N<Subscript>4</Subscript> Additives and Plasma Treatment on the Dry Sliding Wear Behavior of Plasma Sprayed Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-8YSZ Ceramic Coatings

In this paper, the effect of nano-Si₃N₄ additives and plasma treatment on the wear behavior of Al₂O₃-8YSZ ceramic coatings was studied. Nano-Al₂O₃, nano-8YSZ (8 wt.% Y₂O₃-stabilized ZrO₂) and nano-Si₃N₄ powders were used as raw materials to fabricate four types of sprayable feedstocks. Plasma treatment was used to improve the properties of the feedstocks. The surface morphologies of the ceramic coatings were observed. The mechanical properties of the ceramic coatings were measured. The dry sliding wear behavior of the Al₂O₃-8YSZ coatings with and without Si₃N₄ additives was studied. Nano-Si₃N₄ additives and plasma treatment can improve the morphologies of the coatings by prohibiting the initiation of micro-cracks and reducing the unmelted particles. The hardness and bonding strength of AZSP (Al₂O₃-18 wt.% 8YSZ-10 wt.% Si₃N₄-plasma treatment) coating increased by 79.2 and 44% compared to those of AZ (Al₂O₃-20 wt.% 8YSZ) coating. The porosity of AZSP coating decreased by 85.4% compared to that of AZ coating. The wear test results showed that the addition of nano-Si₃N₄ and plasma treatment could improve the wear resistance of Al₂O₃-8YSZ coatings.     

Cold spray of SiC and Al<Subscript>2</Subscript>O<Subscript>3</Subscript> with soft metal incorporation: A technical contribution

Al + SiC, Al + Al₂O₃ composites as well as pure Al, SiC, and Al₂O₃ coatings were prepared on Si substrates by the cold gas dynamic spray process (CGDS or cold spray). The powder composition of metal (Al) and ceramic (SiC, Al₂O₃) was varied into 1:1 and 10:1 wt.%, respectively. The propellant gas was air heated up to 330 °C and the gas pressure was fixed at 0.7 MPa. SiC and Al₂O₃ have been successfully sprayed producing coatings with more than 50 μm in thickness with the incorporation of Al as a binder. Also, hard ceramic particles showed peening effects on the coating surfaces. In the case of pure Al metal coating, there was no crater formation on hard Si substrates. However, when Al mixed with SiC and Al₂O₃, craters were observed and their quantities and sizes depended on the composition, aggregation and size of raw materials.     

Thermal Spray Deposition,Phase Stability and Mechanical Properties of La<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript>/LaAlO<Subscript>3</Subscript> Coatings

This paper deals with the deposition of La₂Zr₂O₇ (LZO) and LaAlO₃ (LAO) mixtures by air plasma spray (APS). The raw material for thermal spray, single phase LZO and LAO in a 70:30 mol.% ratio mixture was prepared from commercial metallic oxides by high-energy ball milling (HEBM) and high-temperature solid-state reaction. The HEBM synthesis route, followed by a spray-drying process, successfully produced spherical agglomerates with adequate size distribution and powder-flow properties for feeding an APS system. The as-sprayed coating consisted mainly of a crystalline LZO matrix and partially crystalline LAO, which resulted from the high cooling rate experienced by the molten particles as they impact the substrate. The coatings were annealed at 1100 °C to promote recrystallization of the LAO phase. The reduced elastic modulus and hardness, measured by nanoindentation, increased from 124.1 to 174.7 GPa and from 11.3 to 14.4 GPa, respectively, after the annealing treatment. These values are higher than those reported for YSZ coatings; however, the fracture toughness (K _IC) of the annealed coating was only 1.04 MPa m^0.5.     

Mechanical Properties of Layered La<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript> Thermal Barrier Coatings

Lanthanum zirconate (La₂Zr₂O₇) has been proposed as a promising thermal barrier coating (TBC) material due to its low thermal conductivity and high stability at high temperatures. In this work, both single and double-ceramic-layer (DCL) TBC systems of La₂Zr₂O₇ and 8 wt.% yttria-stabilized zirconia (8YSZ) were prepared using air plasma spray (APS) technique. The thermomechanical properties and microstructure were investigated. Thermal gradient mechanical fatigue (TGMF) tests were applied to investigate the thermal cycling performance. The results showed that DCL La₂Zr₂O₇ + 8YSZ TBC samples lasted fewer cycles compared with single-layered 8YSZ TBC samples in TGMF tests. This is because DCL La₂Zr₂O₇ TBC samples had higher residual stress during the thermal cycling process, and their fracture toughness was lower than that of 8YSZ. Bond strength test results showed that 8YSZ TBC samples had higher bond strength compared with La₂Zr₂O₇. The erosion rate of La₂Zr₂O₇ TBC samples was higher than that of 8YSZ samples, due to the lower critical erodent velocity and fracture toughness of La₂Zr₂O₇. DCL porous 8YSZ + La₂Zr₂O₇ had a lower erosion rate than other SCL and DCL La₂Zr₂O₇ coatings, suggesting that porous 8YSZ serves as a stress-relief buffer layer.     

High-Temperature Oxidation of Nickel-Based Cermet Coatings Containing WC and Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Nanosized Particles

This paper investigates the high-temperature oxidation of cermet coatings composed of two types of nanosized particles (WC and a mixture of WC and Al₂O₃) incorporated in nickel and produced by co-electrodeposition. For this purpose, high-temperature oxidation tests were conducted at three temperatures (500, 600, and 700 °C) in dry air with 6 time intervals up to 96 h and mass changes at each specific time interval was measured. Statistical techniques were used to calculate the oxidation rate constants (k) and growth-rate time constants (a) for all coatings. The confidence intervals associated with tests were also calculated. The results showed linear to sub-parabolic oxidation rates for coatings composed of only WC particles and sub-liner to liner oxidation rates for coating with both WC and Al₂O₃ particles. The reduction in oxidation rates for coatings with both WC and Al₂O₃ particles were correlated to the addition of Al₂O₃ particles in the matrix.     

Tribocorrosion Behavior of Fe-Based Amorphous Composite Coating Reinforced by Al<Subscript>2</Subscript>O<Subscript>3</Subscript> in 3.5% NaCl Solution

Although corrosion and friction/wear behavior of Fe-based amorphous coatings and their composites has been extensively studied during the past decade, there is very limited work related to tribocorrosion behavior. In this paper, the tribocorrosion behavior of a Fe-based amorphous composite coating reinforced with 20 wt.% Al₂O₃ particles was investigated in a 3.5% NaCl solution on a ball-on-disk tester and was compared to the monolithic amorphous coating and 316L stainless steel (SS). The results showed that the amorphous composite coating exhibited the highest tribocorrosion resistance among the three materials tested, as evidenced by the lowest coefficient of friction (~0.3) and tribocorrosion wear rate (~1.2 × 10^?5 mm³/N·m). In addition, potentiodynamic polarization measurements before and during tribocorrosion testing demonstrated that corrosion resistance of the amorphous composite coating was not influenced so much by mechanical loading compared to the amorphous coating and the 316L SS. Observations on the worn surface revealed a corrosion-wear- and oxidational-wear-dominated tribocorrosion mechanism for the composite coatings. The excellent tribocorrosion resistance of the composite coating results from the effect of chemically stable Al₂O₃ phase which resists oxidation and delamination during sliding, along with poor wettability with corrosive NaCl droplets.     

Effect of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Content on Electrical Breakdown Properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/Cu Composite

Al₂O₃/Cu composites were prepared by external addition of Al₂O₃, and the effect of Al₂O₃ content on microstructure, density, hardness, electrical conductivity and vacuum electrical breakdown properties was studied. The results show that with increasing Al₂O₃ addition, the density of Al₂O₃/Cu composite significantly decreases, the hardness sharply increases and then slowly decreases, but the electrical conductivity invariably decreases. The vacuum breakdown test shows that with increasing Al₂O₃ addition, the breakdown strength first sharply increases and then decreases when the Al₂O₃ content exceeds 1.2 wt.%; the chopping current always exhibits a decreasing trend and the arc life first increases and then decreases. According to the morphology of arc erosion and analysis, the arc erosion resistance increases and then decreases sharply. In the range of experiments, the optimal arc erosion resistance of Al₂O₃/Cu composite can be obtained with the addition of 1.2 wt.% Al₂O₃.     

Effect of Surface Roughness and Structure Features on Tribological Properties of Electrodeposited Nanocrystalline Ni and Ni/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Coatings

Metal matrix composite coatings obtained by electrodeposition are one of the ways of improving the surfaces of materials to enhance their durability and properties required in different applications. This paper presents an analysis of the surface topography, microstructure and properties (residual stresses, microhardness, wear resistance) of Ni/Al₂O₃ nanocomposite coatings electrodeposited on steel substrates from modified Watt’s-type baths containing various concentrations of Al₂O₃ nanoparticles and a saccharin additive. The residual stresses measured in the Ni/Al₂O₃ coatings decreased with an increasing amount of the co-deposited ceramics. It was established that the addition of Al₂O₃ powder significantly improved the coatings’ microhardness. The wear mechanism changed from adhesive-abrasive to abrasive with a rising amount of Al₂O₃ particles and coating microhardness. Nanocomposite coatings also exhibited a lower coefficient of friction than that of a pure Ni-electrodeposited coating. The friction was found to depend on the surface roughness, and the smoother surfaces gave lower friction coefficients.     

Preparation and characterization of nanostructured Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-13wt.%TiO<Subscript>2</Subscript> ceramic coatings by plasma spraying

Nanostructured and conventional Al₂O₃-13wt.%TiO₂ ceramic coatings were prepared by plasma spraying with nanostructured agglomerated and conventional powders, respectively. The microstructure and microhardness of the coatings were investigated using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and microhardness measurement. Meanwhile, the friction and wear behaviors were analyzed and compared using a ball-on-disk tribometer. The results show that the conventional coating has lamellar stacking characteristic and has some pores. However, the nanostructured coating shows a bimodal microstructure, which is composed of both fully melted regions and partially melted regions. According to the microstructural difference, the partially melted regions can be divided into liquid-phase sintered regions (a three-dimensional net or skeleton-like structure: Al₂O₃-rich submicron particles embedded in the TiO₂-rich matrix) and solid-phase sintered regions (remained nanoparticles). The microstructural characteristics of the liquid-phase sintered region are formed due to the selective melting of TiO₂ nanoparticles during plasma spraying. On the other hand, the TiO₂ and Al₂O₃ nanoparticles of the solid-phase sintered regions are all unmelted during plasma spraying. Due to the existence of nanostructured microstructures, the nanostructured coating has a higher microhardness, a lower friction coefficient, and a better wear resistance than the conventional coating.     

Preparation and oxidation behavior of a novel CeO2-modified chromizing coating

By using CeO₂ particles instead of part of Al₂O₃ particles as filler, the CeO₂ was successfully entrapped into the outer layer of the chromizing coatings on the as-deposited nanocrystalline (NC) and microcrystalline (MC) Ni films using a conventional pack-cementation method at 800 °C. For comparison, chromizing was also performed under the same condition on MC Ni film using Al₂O₃ as filler without CeO₂ particles. SEM/EDX and TEM results indicate that the refinement of Ni grain and CeO₂ entrapped into the chromizing coatings refine the grain of the chromizing coating. Oxidation at 900 °C indicates that compared with the CeO₂-free chromizing coating, the CeO₂-dispersed chromizing coating exhibits an increased oxidation resistance. For the CeO₂-dispersed chromizing coating, the refinement of Ni grain size significantly decreases the transient-oxidation scaling rate of the chromizing coatings. Together with this, the CeO₂-dispersed chromizing coating formed on NC Ni exhibits a better oxidation resistance.     

Phase Stability of Ce-Modified La<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript> Coatings and Chemical Compatibility with YSZ

Ce-modified La₂Zr₂O₇ powders, i.e., La₂Zr₂O₇ (LZ), La₂(Zr_0.7Ce_0.3)₂O₇ (LZ7C3), and La₂(Zr_0.3Ce_0.7)₂O₇ (LZ3C7), were used to produce thermal barrier coatings by atmospheric plasma spray process. The chemical compatibility of the CeO₂-doped La₂Zr₂O₇ with the traditional YSZ was investigated in LZ-YSZ powder mixtures and LZ-YSZ bilayer coatings by x-ray diffraction and scanning electron microscope. The powder mixtures and coatings were aged at 1200 and 1300 °C for 100 h. The results showed that LZ and LZ7C3 presented single pyrochlore structure after the heat treatments at both 1200 and 1300 °C. For LZ3C7, however, fluorite structure was observed at 1300 °C, indicating a poor phase stability of LZ3C7 at the elevated temperature. The results further showed that La₂(Zr_0.3Ce_0.7)₂O₇ reacted with YSZ in the bilayer ceramic coatings due to the diffusion of cerium, zirconium, and yttrium. While for La₂Zr₂O₇(LZ) and La₂(Zr_0.7Ce_0.3)₂O₇, a better chemical compatibility with YSZ was shown.     

Dependence of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> coating thickness and annealing conditions on microstructural and electrochemical properties of LiCoO<Subscript>2</Subscript> film

We studied the dependence of Al₂O₃ coating thickness and annealing conditions on the surface morphology and electrochemical properties of Al₂O₃ coated LiCoO₂ films. The optimum coating thickness allowing for the highest capacity retention was about 24 nm. A sample consisting of Al₂O₃ coated on annealed LiCoO₂ film with additional annealing at 400 °C had a uniform coating layer between the coating materials and cathode films. This sample showed the best capacity retention of ∼91 % with a charge-cut off of 4.5 V after 30 cycles, while the bare cathode film showed a capacity retention of ∼32 % under the same conditions. The formation of second phases such as Co-Al-O was observed in the coating films by X-ray photoelectron spectroscopy (XPS). The Co-Al-O containing samples showed a higher initial capacity because of their smaller grain size, but less capacity retention than the Al₂O₃ containing samples.     

Erosion wear behaviour of plasma sprayed NiCrSiB/Al2O3 composite coating

In this work, 60 wt.% NiCrSiB–40 wt.% Al₂O₃ composite coating was produced on AISI 304 substrate material using the atmospheric plasma spraying technique. The coating surface has been characterised using a scanning electron microscope (SEM), optical microscope and X-ray diffractometer (XRD). The microhardness, porosity, density and surface roughness of the coating were measured. The adhesion strength of the coating was measured using pull off adhesion tester. The erosion behaviour of plasma sprayed coating was studied at 450 °C using hot air jet erosion testing machine. The erosion rate of coated and uncoated samples was evaluated at 30° and 90° erodent impact angles. The SEM images of the eroded samples were taken to analyse the erosion mechanism. The test results reveal that the coating protects the substrate at both 30° and 90° impact angles.     

Fabrication and Properties of Plasma-Sprayed Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/ZrO<Subscript>2</Subscript> Composite Coatings

Al₂O₃ /xZrO₂ (where x = 0, 3, 13, and 20 wt.%) composite coatings were deposited onto mild steel substrates by atmospheric plasma spraying of mixed α-Al₂O₃ and nano-sized monoclinic-ZrO₂ powders. Microstructural investigation showed that the coatings comprised well-separated Al₂O₃ and ZrO₂ lamellae, pores, and partially molten particles. The coating comprised mainly of metastable γ-Al₂O₃ and tetragonal-ZrO₂ with trace of original α-Al₂O₃ and monoclinic-ZrO₂ phases. The effect of ZrO₂ addition on the properties of coatings were investigated in terms of microhardness, fracture toughness, and wear behavior. It was found that ZrO₂ improved the fracture toughness, reduced friction coefficient, and wear rate of the coatings.     

Influence of Feedstock Powder Modification by Heat Treatments on the Properties of APS-Sprayed Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-40% TiO<Subscript>2</Subscript> Coatings

The formation and decomposition of aluminum titanate (Al₂TiO₅, tialite) in feedstock powders and coatings of the binary Al₂O₃-TiO₂ system are so far poorly understood. A commercial fused and crushed Al₂O₃-40%TiO₂ powder was selected as the feedstock for the experimental series presented in this paper, as the composition is close to that of Al₂TiO₅. Part of that powder was heat-treated in air at 1150 and 1500 °C in order to modify the phase composition, while not influencing the particle size distribution and processability. The powders were analyzed by thermal analysis, XRD and FESEM including EDS of metallographically prepared cross sections. Only a maximum content of about 45 wt.% Al₂TiO₅ was possible to obtain with the heat treatment at 1500 °C due to inhomogeneous distribution of Al and Ti in the original powder. Coatings were prepared by plasma spraying using a TriplexPro-210 (Oerlikon Metco) with Ar-H₂ and Ar-He plasma gas mixtures at plasma power levels of 41 and 48 kW. Coatings were studied by XRD, SEM including EDS linescans of metallographically prepared cross sections, and microhardness HV1. With the exception of the powder heat-treated at 1500 °C an Al₂TiO₅-Ti₃O₅ (tialite–anosovite) solid solution Al_2?xTi_1+xO₅ instead of Al₂TiO₅ existed in the initial powder and the coatings.     

Superior performance of high-velocity oxyfuel-sprayed nanostructured TiO<Subscript>2</Subscript> in comparison to air plasma-sprayed conventional Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-13TiO<Subscript>2</Subscript>

Air plasma-sprayed conventional alumina-titania (Al₂O₃-13wt.%TiO₂) coatings have been used for many years in the thermal spray industry for antiwear applications, mainly in the paper, printing, and textile industries. This work proposes an alternative to the traditional air plasma spraying of conventional aluminatitania by high-velocity oxyfuel (HVOF) spraying of nanostructured titania (TiO₂). The microstructure, porosity, hardness (HV 300 g), crack propagation resistance, abrasion behavior (ASTM G65), and wear scar characteristics of these two types of coatings were analyzed and compared. The HVOF-sprayed nanostructured titania coating is nearly pore-free and exhibits higher wear resistance when compared with the air plasma-sprayed conventional alumina-titania coating. The nanozones in the nanostructured coating act as crack arresters, enhancing its toughness. By comparing the wear scar of both coatings (via SEM, stereoscope microscopy, and roughness measurements), it is observed that the wear scar of the HVOF-sprayed nanostructured titania is very smooth, indicating plastic deformation characteristics, whereas the wear scar of the air plasma-sprayed alumina-titania coating is very rough and fractured. This is considered to be an indication of a superior machinability of the nanostructured coating.     

Effect of pre‐oxidation on coke formation and metal dusting of electroplated Ni3Al–CeO2‐based coatings in CO–H2–H2O

Pre‐oxidation was introduced to improve the resistance of electroplated pure, 5 µm CeO₂‐dispersed, and 9–15 nm CeO₂‐dispersed Ni₃Al coatings to coke formation and metal dusting in 24.4%CO–73.3%H₂–2.3%H₂O at 650 °C. Coke formation and metal dusting of pre‐oxidized Ni₃Al‐based coatings were retarded up to 200 h owing to a thin Al₂O₃ scale induced during pre‐oxidation. The long‐term effectiveness of pre‐oxidation nonetheless depended on the integrity of Al₂O₃ scale. The pure Ni₃Al coating suffered severe spallation after pre‐oxidation and thereby showed the worst long‐term resistance. Two pre‐treated 9–15 nm CeO₂‐dispersed Ni₃Al coatings exhibited the best long‐term resistance to carbon attack because nano‐CeO₂ particles maintained a full coverage of Al₂O₃ scale on the coatings. Two 5 µm CeO₂‐dispersed Ni₃Al coatings showed significant spallation after pre‐oxidation because of an overdoping effect and experienced coke formation and metal dusting during long‐term exposure.