退火处理对单道次轧制镁合金薄板组织的影响

变形镁合金因其优越的性能越来越受到国内外研究者的重视。采用单道次轧制的方法轧制出厚度为0.4 mm的AZ31镁合金薄板。对轧制后的薄板在不同温度、不同保温时间下进行退火处理,分析薄板在不同退火条件下的微观组织变化。结果表明:薄板经退火处理后组织变得更加细小均匀,平均晶粒尺寸为5μm。退火温度和保温时间共同影响着薄板的晶粒度,在320℃退火并保温80 min时平均晶粒度最小,仅有4.02μm。     

加热速率对Nb-IF钢退火组织及织构特征的影响

以一种冷轧Nb-IF钢为研究对象,研究了不同加热速率下退火板的微观组织和织构特征.结果表明：当加热速率由10℃/s增加到150℃/s时,再结晶晶粒平均直径由16.72μm细化到13.8μm;当加热速率高于100℃/s时,平均晶粒直径变化趋于平缓.试验钢完全再结晶晶粒以大角晶界为主,随加热速率变化,其含量在81.3%～86.9%范围内波动,重位点阵（CSL）含量在34.1%～44.5%之间波动.在快速加热退火和普通加热退火条件下,试验钢均可获得强烈的γ织构,强点密度在f（g）=9.01～10.42范围内.     

快淬纳米复合Nd9Fe80Co4Nb1B6永磁合金相结构与磁性能研究

利用X线衍射仪、振动样品磁强计等测试手段研究了纳米复合Nd9Fe80Co4Nb1B6合金的相结构与磁性能,结果表明:淬速为20 m/s的合金,经710℃退火处理后,合金软硬磁性相的晶粒尺寸细小,两相之间具有较强的交换耦合作用,合金具有优良的综合磁性能,即剩磁为0.95 T,矫顽力达到540 kA/m,最大磁能积为112 kJ/m3.选择适当的快淬速度有利于改善退火后合金的相结构,提高合金的综合磁性能.     

退火温度对Ti-IF钢性能及织构的影响

对冷轧压下率为80%、厚1 mm的Ti-IF钢经不同温度退火处理后进行拉伸试验,测量其塑性应变比r值。观察退火试样的显微组织,并利用电子背散射衍射技术（EBSD）对其性能和再结晶织构进行分析。结果表明,冷轧试验钢分别在780、810、840℃退火3 min后,均发生了再结晶;随着退火温度的升高,大多数晶粒尺寸由5-6μm增大到9-10μm;试验钢的r值随退火温度升高而增大;退火钢再结晶织构表现为强烈的{111}织构,主要由{111}〈110〉和{111}〈112〉两类取向晶粒组成。     

热处理对微型磁致伸缩材料传感器磁性能的影响

采用MEMS技术制备了尺寸为500μm×100μm×15μm的微尺度磁致伸缩材料传感器,发现MEMS技术沉积过程中传感器内部不可避免地产生了内应力,对传感器磁性能带来不利影响.对徽尺度磁致伸缩材料传感器进行真空热处理,旨在消除内应力,进一步提高传感器磁学性能.结果表明:真空退火可减小或消除传感器内应力,提高磁学性能,其中最佳退火温度为250℃,时间为2h.该温度下退火不仅可完全释放传感器内应力,还可以改善波谱质量,提高共振频率.     

锆合金的晶粒观测与亚结构分析

为了研究锆合金包壳管再结晶退火的程度及合金的晶粒尺寸,用直线截点法、同心圆截点法以及晶粒度软件法分别对经塑性变形后再结晶退火的国产M5、法国产M5以及国产N18锆合金包壳管晶粒尺寸进行了观测,并用透射电子显微分析观察了合金的亚结构.结果表明:法产M5包壳管的晶粒尺寸为(3.73±0.107)μm,位错较少,再结晶退火程度良好;国产M5包壳管的晶粒尺寸为(3.63±0.239)μm,存在混晶,位错密度高,再结晶退火程度不足,国产N18包壳管的晶粒尺寸为(5.37±0.079 2)μm,位错较少,发生了沉淀相变,再结晶退火程度已经过度.     

匀胶速度对钙锶铋钛陶瓷厚膜结构的影响

用粉末—溶胶法和快速退火工艺在S i(100)基片上制备了Ca0.4Sr0.6B i4Ti4O15陶瓷厚膜。研究了匀胶速度及退火温度对厚膜结构的影响。用X射线衍射表征了厚膜的晶体结构,用扫描电镜观察了样品显微形貌。结果表明在750℃进行退火,匀胶速度为4500 r/m时样品晶粒发育良好,表面平整无裂纹,厚度约为1.5μm,且a轴取向较明显。     

挤压温度对高纯铜组织演变规律的影响

为了研究挤压温度对高纯铜微观组织和变形行为的影响规律,通过反向挤压方式对高纯铜进行不同挤压温度下的挤压实验并观察了其显微组织.结果表明,随着挤压温度的升高,高纯铜的晶粒尺寸增大.当挤压温度为650℃时,挤压棒材的平均晶粒尺寸为36μm;当挤压温度升至800℃时,挤压棒材的平均晶粒尺寸为51μm.随着变形量的增加,当挤压温度为650～700℃时,压余变形区的平均晶粒尺寸趋向于由60μm变为45μm;当挤压温度为750～800℃时,平均晶粒尺寸则趋向于由90μm变为75μm. 800℃挤压变形后晶粒内部出现大量以Σ3特殊晶界为孪晶界的111 60°退火孪晶.     

同步与异步热轧硅钢带显微组织特点

硅钢是电力电子工业不可缺少的软磁材料.突破传统的同步热轧工艺,采用异步热轧生产取向硅钢带,研究大剪切力条件下异步热轧带钢沿厚度方向显微组织的特点,为取向硅钢生产工艺的创新提供坚实的理论基础.以Fe-3%Si取向硅钢带为原材料,采取同步与异速比为1. 1的异步热轧方式来制备2. 5 mm厚的钢带,利用光学显微镜观察钢带的显微组织形貌,得出同步热轧钢带与异步热轧钢带的组织沿厚度方向呈现不均匀的分布,表层和过渡层及中心层均为等轴晶粒.同步热轧钢带过渡层及中心层平均晶粒尺寸分别为50μm及131μm,1.1异速比热轧硅钢下表面(快速面)的平均晶粒尺寸为48μm,上表面(慢速面)平均晶粒尺寸达55μm,最大晶粒尺寸出现在中心层,平均晶粒尺寸为119μm,最小晶粒尺寸位于下表面过渡层,其平均晶粒尺寸为39μm.     

锆合金的品粒观测与亚结构分析

为了研究锆合金包壳管再结晶退火的程度及合金的晶粒尺寸,用直线截点法、同心圆截点法以及晶粒度软件法分别对经塑性变形后再结晶退火的国产M5、法国产M5以及国产N18锆合金包壳管晶粒尺寸进行了观测,并用透射电子显微分析观察了合金的亚结构．结果表明：法产M5包壳管的晶粒尺寸为（3．73±0．107）μm,位错较少,再结晶退火程度良好;国产M5包壳管的晶粒尺寸为（3．63±0．239）μm,存在混晶,位错密度高,再结晶退火程度不足,国产N18包壳管的晶粒尺寸为（5．37±0．0792）μm,位错较少,发生了沉淀相变,再结晶退火程度已经过度。     

电工钢片磁特性测量中H线圈的定标

电工钢片二、三维磁特性测量研究中,H线圈的定标是电工钢片磁特性精细模拟的关键问题.针对这一问题对定标螺线管进行了磁场仿真,根据仿真结果确定了定标螺线管尺寸,按照定标要求设计了定标实验装置和整个测量系统,并根据测量实验的要求编写了基于LabVIEW软件的测量程序,完成了电工钢片磁特性研究中定标实验的数据采集.根据所采集的测量数据和H线圈的定标实验原理,计算得出了H线圈的定标结果.将理论值和实验值进行对比,通过实验证明了该解决方案是有效的,具有一定的可行性.     

Effects of Magnetization on Thermoelectric Transport Properties of CoSb_3 Material

The effects of magnetization on the phase composition,microstructure and thermoelectric transport properties of CoSb_3 were studied systematically.The magnetic properties of CoSb_3 material were also measured at room temperature in order to confirm its magnetic category.The results of XRD and FESEM analysis indicated that the phase composition and microstructure of the CoSb_(3 )were not affected by magnetization.The results of thermoelectric transport measurement showed that the electrical and thermal transport properties of materials were also not affected by magnetization.These results were mainly attributed to the diamagnetism of the CoSb_3 material,which were consistent with the results of the magnetic properties measurement.This study is expected to provide a special research perspective for studying the effects of the external conditions on the structure and properties of thermoelectric materials.     

Microstructures and properties of 550 MPa grade high strength thin-walled H-beam steel

The microstructures and mechanical properties of 550 MPa grade lightweight high strength thin-walled H-beam steel were experimentally studied. The experimental results show that the microstructure of the air-cooled H-beam steel sample is consisted of ferrite, pearlite and a small amount of granular bainites as well as fine and dispersive V（C,N） precipitates. The microstructure of the water-cooled steel sample is consisted of ferrite and bainite as well as a small amount of fine pearlites. The microstructure of the water-cooled sample is finer than that of the air-cooled sample with the average intercept size of the surface grains reaching to 3.5 gna. The finish rolling temperature of the thin-walled high strength H-beam steel is in the range of 750 ~C-850 ~C. The lower the finish rolling temperature and the faster the cooling rate, the finer the ferrite grains, the volume fraction of bainite is increased through water cooling process. Grain refinement strengthening and precipitation strengthening are used as major strengthening means to develop 550 MPa grade lightweight high strength thin- walled H-beam steel. Vanadium partially soluted in the matrix and contributes to the solution strengthening. The 550 MPa grade high-strength thin-walled H-beam steel could be developed by direct air cooling after hot rolling to fully meet the requirements of the target properties.     

预应力混凝土用钢棒专用母材开发及应用研究

介绍了昆钢开发高效、节能新型建筑材料预应力混凝土用钢棒专用母材TS800U的生产实践,对母材力学性能、显微组织、夹杂物及断口形貌进行了研究分析,结果表明:母材断口形貌呈杯锥状或不完整杯锥状,铁素体形态为均匀的等轴晶粒组织,有利于钢棒后续加工性能的改善;断口夹杂物横向分布对钢棒延迟滞后断裂影响明显;为保证母材具有良好的加工性能,断口横向试样夹杂物宽度不得超过10μm,级别不得超过1.5级.     

低合金耐磨钢的组织与性能

低成本、高性能耐磨钢的需求增长及其开发都在进行中．本研究根据对耐磨钢性能的要求,试制了三种不同合金化方式的低合金耐磨钢,利用金相显微镜、透射电子显微镜、洛氏硬度计、万能材料试验机、夏氏冲击试验机和磨粒磨损实验机研究了其组织和性能,讨论了它们问的关系．结果表明：0．25C钢经不同工艺热处理后均获得了马氏体组织,并发生不同程度的自回火现象,硬度均大于45HRC,屈服强度大于1000MPa,抗拉强度大于1500MPa,并具有一定的塑性和韧性;在860℃淬火或920℃淬火并250℃回火后,实验钢的硬度、强度、塑性和韧性有最佳的配合,耐磨性最佳;V微合金化对钢的组织和性能没有明显影响．0．33C钢860℃或920℃奥氏体化后以等于或大于2．0％／s的冷速连续冷却或风冷至室温,回火或不回火即可得到由贝氏体与马氏体组成的混合组织,硬度超过50HRC,屈服强度大于900MPa,抗拉强度大于1500MPa,有一定的塑性和韧性,耐磨性良好,与商用淬火一回火耐磨钢类似;但由于具有高的加工硬化能力和良好的冲击韧性,在冲击条件下的耐磨性会优于商用钢．不同工艺热处理后的试验钢的磨损率随砂纸粒度和载荷增大而增大,载荷的影响较大,而磨粒的影响较小．     

常化与退火工艺对50W470H无取向硅钢磁性能的影响

研究了常化温度和退火温度对冷轧无取向硅钢的显微组织和磁性能的影响。结果表明,常化温度升高,铁损呈先降低后升高的趋势,磁感应强度波动程度小。退火温度升高,铁损逐步降低,磁感应强度同样波动程度小。在常化1000℃-1050℃+退火925℃-1025℃下能获得最佳磁性能,最佳磁性能P1.5/50=2.5W/kg-2.9W/kg、磁感B50=1.74-1.76T。     

半导体硅材料微细电火花加工技术

为了拓展微细电火花加工技术的应用领域,开展了半导体硅材料的微细电火花加工技术研究,从硅材料的抗腐蚀系数、掺杂浓度、掺杂类型以及硅材料的晶向特性等几方面对硅材料的微细电火花加工性能进行研究;在自主开发的微细电火花加工机床上进行了大量工艺实验,研究了不同加工规准下不同掺杂类型硅材料的微细电火花加工工艺规律,并与加工不锈钢材料的工艺规律进行对比分析;阐述了不同工作液类型对硅材料加工后性能的影响;在此基础上进行硅材料的微结构加工实验,给出加工实例.在N型硅和P型硅上分别加工出了最窄梁宽为23μm和12μm的微细梁,并在P型硅上实现了直径为0.15 mm的微半球以及外环直径为4mm,具有24个微型叶片的微型涡轮盘的加工.     

Fe41Co7Cr15Mo14C15B6Y2合金涂层的激光制备及显微组织研究

利用激光熔覆和激光重熔的方法在低碳钢表面制备了原位生成颗粒增强铁基涂层.用X线衍射(XRD)、扫描电镜(SEM)对其相结构和微观组织进行了研究,重点分析了重熔层的组织形态和形成机制.结果表明:制备的涂层无气孔和裂纹,整个涂层的厚度为0.6~0.7 mm,重熔层厚度为50~80 μm;熔覆层主要是方向比较紊乱的树枝晶组织,重熔层内形成了细小的等轴晶组织;重熔层最高显微硬度达到了1056 HV.     

计算电磁学中电工钢片磁特性模型研究的新进展

电工钢片具有复杂的非线性磁特性，是电工产品中应用最广泛的磁性材料.为了降低能耗、实现产品综合性能的优化设计，需要在电机、电器电磁场数值分析中实现对电工钢片磁特性的精确模拟.讨论了计算电磁学中电工钢片磁特性模型研究中的几个主要问题，包括磁性材料各种磁滞模型的基本思想、不同模型的优点和局限性、电工钢片磁特性测量方法的研究进展以及与磁特性模型相对应的电磁场分析方法的研究现状.     

微碳钢铁素体区热轧试验研究

在连铸连轧生产线采用铁素体轧制技术制备微碳钢热轧薄板,并对所制备薄板的组织、性能及织构进行分析。结果表明：铁素体轧制微碳钢热轧薄板的组织为完全再结晶铁素体,平均晶粒尺寸50 m左右。相对于常规奥氏体轧制,铁素体轧制薄板的屈服强度和抗拉强度分别下降了21%和6%,延伸率略有下降。热轧薄板的塑性应变比值为0.4,明显低于常规奥氏体轧制。薄板中存在较强的{001}织构是导致值较低的主要原因。