增刚母料在BOPP烟包装膜中的应用

通过在聚丙烯(PP)中添加自主研发的增刚母料,研究增刚母料对PP熔融与结晶性能的影响,以及增刚母料添加量对双向拉伸PP(BOPP)烟包装膜性能的影响.研究表明:当增刚母料质量分数为20％时,改性PP的熔体流动速率从PP的3.2 g/10 min提高到21.5 g/10 min,熔点降低10.2℃,结晶温度降低16.9℃...     

BOPP烟膜专用多功能改性母料的研究

开发了双向拉伸聚丙烯(BOPP)烟膜专用多功能改性母料，从厚度指标、力学性能、热收缩性能和光学性能等方面与进口改性母料的使用特性进行了对比。结果表明：新开发的改性母料的各项使用性能指标均相当或好于进口改性母料，批量生产和使用证明了该产品的品质指标和使用性能的稳定性。     

时效稳定型高收缩BOPP烟膜的研究

研究了温度和时间对双向拉伸聚丙烯(BOPP)烟膜热收缩率的影响。结果表明:在生产下线的1周内,BOPP薄膜的聚集态结构处于不稳定状态,薄膜的热收缩率下降较快;夏季由于温度高,热收缩率比冬季降低速度快,特别是在1个月后,下降的幅度加大。针对此问题开发出一种时效稳定母料并应用于高收缩烟膜,取得了良好的效果。在明显提高烟膜热收缩率的同时,改善了热收缩率的稳定性,特别使夏季高温下烟膜的热收缩率有较大比例的提高,钝化了热收缩率对温度的敏感性。研究表明该母料对烟膜的力学性能、光泽度、雾度、热封性能、爽滑性能以及加工性能没有负面影响.     

BOPP薄膜抗静电性能的研究

为改善薄膜的抗静电性能,在双向拉伸聚丙烯(BOPP)薄膜中添加一种自制的抗静电母料,并与添加进口抗静电母料的BOPP薄膜进行对比。结果表明:两种抗静电母料在BOPP薄膜的拉伸性能、光学性能、热收缩率和摩擦性能上基本没差异;在抗静电性能方面,不管是电晕面还是非电晕面,新开发BOPP薄膜抗静电性能均优于对比样;新开发BOPP薄膜电晕面的抗静电性能有明显改善,静电半衰期比较平稳,且一个月内的抗静电效果的持续性很好。     

增刚剂在聚丙烯中的应用研究

探讨了氢化石油树脂增刚剂在聚丙烯中的应用,结果表明:该增刚剂能够增大PP的熔体指数,降低加工温度,改善加工性能;同时降低了PP的雾度,改善了PP的光学性能,也提高了PP的刚性。     

提高BOPP香烟包装膜品质的探讨

对共挤双向拉伸聚丙烯(BOPP)香烟膜和涂覆BOPP香烟膜的生产方法、物理性能及使用效果进行了分析比较,指出共挤BOPP香烟膜的发展前景,并提出了改进品质的一些途径和方法。     

氢化石油树脂对流延聚丙烯薄膜性能的影响

本文重点研究氢化石油树脂加入流延聚丙烯薄膜后,薄膜性能的变化和改善。不同含量的氢化石油树脂(C9)被加入聚丙烯薄膜,其质量分数控制在0～20%。研究表明,氢化石油树脂的质量分数达到20%,流延薄膜的水汽透过率下降41.3%。薄膜的纵横向拉伸强度与氢化石油树脂添加量之间影响不大,而纵向拉伸强度逐渐下降。氢化石油树脂加入,会大幅度减小雾度,但对透光率影响较小。随着氢化石油树脂的质量分数增加到20%,热封温度从172℃降低到166℃。     

增刚剂在BOPP收缩膜中的应用研究

本文研究了氢化石油树脂增刚剂对BOPP收缩膜生产工艺条件和产品性能的影响，总结了通过合适的添加比例和工艺条件来控制薄膜的质量。     

烟包BOPP抗粘连剂开发与性能研究

用新开发的抗粘连母料进行小试,研究了抗粘连母料所生产的双向拉伸聚丙烯(BOPP)条包烟抗粘力、摩擦因数和光学性能等。研究表明:与进口母料相近的粘连力,并且在光学性能方面有一定优势,但是薄膜的摩擦因数偏大,需进一步深入研究。     

佛山研发出高品质BOPP、BOPA、CPE薄膜添加剂

正近日,佛山市运通晨塑料助剂有限公司成功研发出多种深受客户好评的高性价比产品,其中主打产品珠光母料、消光母料和用于CPE卫生材料透气膜的透气料尤为突出,占有一定的市场份额。而公司的其他主要产品,双向拉伸聚丙烯(BOPP)、双向拉伸聚酯(BOPET)、双向拉伸尼龙(BOPA)等薄膜的抗静电母料、增挺剂、乳白母料、增黏剂、防粘连剂、爽滑开口剂等功能性薄膜专用料和添加剂,在同行业也有较大的竞争力。     

BOPP烟膜现状

简述了BOPP烟膜的分类和主要控制性能，介绍了BOPP烟膜专用树脂及主要添加的功能母料的应用现状。     

Preparation and characterization of biaxially oriented polypropylene film with high molecular orientation in the machine direction by sequential biaxial stretching

Novel approach of applying the ternary polymer blend of long‐chain branched polypropylene (LCB‐PP), conventional polypropylene (PP), and hydrogenated polydicyclopentadiene (hDCPD) has been employed to tensilize biaxially oriented polypropylene (BOPP) film in the machine direction (MD) by successive sequential biaxial stretching method. It is found that the addition of LCB‐PP improves the MD stretchability of the BOPP film of PP/hDCPD blend. Depending on the content of LCB‐PP, LCB‐PP/PP/hDCPD ternary blend could be biaxially stretched up to the MD stretching ratio (MDX) of 12 without film breakage whereas that of PP (conventional BOPP film) resulted in the MDX up to 6. This excellent MD stretchability enabled to tensilize the BOPP film in the MD, where Young's modulus in the MD could be increased up to 4.9 GPa, twice higher than that of conventional BOPP film. The orientation of total molecular chains and that of crystalline molecular chains were evaluated by in‐plane distribution of refractive indices and wide‐angle X‐ray diffraction, respectively. The results are discussed from the viewpoint of deformation behavior during stretching process. Moreover, the resultant film had a dimensional stability substantially equivalent to that of conventional one, in spite of the higher stretching ratio, and an improved moisture barrier property. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

增刚剂在BOPP收缩膜中的应用研究

探讨了生产BOPP收缩膜时,在芯层加入不同比例的氢化石油树脂增刚剂后对生产工艺条件和产品性能的影响,从而通过正确使用增刚剂来控制所要求的薄膜品质。     

氟弹性体类加工助剂改性双向拉伸薄膜用PP

采用氟弹性体加工助剂母粒(简称母粒)对聚丙烯(PP)进行改性,考察了双向拉伸薄膜用PP(BOPP)的光学性能、力学性能和加工性能。结果表明:母粒对PP结晶度有一定影响,可提高结晶速率,且助剂质量分数为0.06%时对PP结晶度的影响最大;母粒会降低BOPP薄膜雾度,与只在BOPP薄膜的芯层加入母粒相比,在芯层和表层同时加入母粒,更易降低BOPP薄膜雾度;仅在BOPP薄膜芯层加入母粒,薄膜的光泽度更好;薄膜纵向的力学性能有所下降,但都能满足标准要求,母粒还能降低PP熔体表观黏度及剪切应力,改善加工性能。     

BOPP烟用包装膜专用树脂结构性能研究

对气相法聚丙烯生产的双向拉伸聚丙烯(BOPP)烟用包装膜专用树脂F 1002进行了结构性能研究。研究结果表明，烟用包装膜专用树脂具有特征性分子量及其分布，即既含有较高的分子量组分，又含有适量低分子量组分，从而保证其在双向拉伸成型工艺中具有较高的熔体强度及熔体流动稳定性，使得制品厚度均匀性优异。同时，适宜的等规指数(96．5％～97．5％)及其等规序列分布特性，使采用均聚型烟用包装膜专用树脂加工成型的BOPP薄膜具有挺度高，满足烟用包装膜的特性要求。     

BOPP烟用包装膜专用树脂F 1002的开发与生产

以调整催化剂A1／Si及聚合釜内氢气／丙烯等聚合工艺的关键问题为技术开发重点，在气相法工艺200kt／a聚丙烯工业生产装置上，开发和生产了双向拉伸聚丙烯烟用包装膜专用树脂F1002。F 1002的熔体流动指数为2．6～3．0g/10min，屈服拉伸强度大于或等于30MPa，等规指数为96．5％～97．5％，雾度小于或等于6％。用户使用反映，F 1002成型性好．制品具有挺度高、透明性好等优点。     

BOPP薄膜光学性能的时效性及影响因素

研究了生产时间和存储时间对BOPP薄膜光学性能和光学性能稳定性的影响。分析了影响薄膜光学性能的主要因素,这包括氢化石油树脂、粘连剂、静电剂、爽滑剂、加工温度、生产线速度等配方和工艺因素,提出了一些可行的改进措施。