Synthesis and properties of novel aromatic polyamides with xanthene cardo groups

Two novel monomers, 9,9‐bis[4‐(4‐carboxyphenoxy)phenyl]xanthene (BCAPX) and 9,9‐bis[4‐(4‐aminophenoxy)phenyl]xanthene (BAPX) were prepared in two main steps starting from nucleophilic substitution of 9,9‐bis(4‐hydroxyphenyl)xanthene (BHPX) with p‐fluorobenzonitrile and p‐chloronitrobenzene, respectively. Using triphenyl phosphite and pyridine as condensing agents, two series of polyamides containing xanthene cardo groups with the inherent viscosities (0.82–1.32 dL/g) were prepared by polycondensation from BCAPX with various aromatic diamines or from BAPX with various aromatic dicarboxylic acids in an N‐methyl‐2‐pyrrolidone (NMP) solution containing dissolved calcium chloride, respectively. All new polyamides were amorphous and readily soluble in various polar solvents such as N,N‐dimethylformamide (DMF), NMP, N,N‐dimethylacetamide (DMAc) and pyridine. These polymers showed relatively high glass transition temperatures between 264 and 308°C, decomposition temperatures at 10% weight loss ranging from 502 to 540°C and 488 to 515°C in nitrogen and air, respectively, and char yields at 800°C in nitrogen higher than 56%. Transparent, flexible, and tough films of these polymers cast from DMAc solutions exhibited tensile strengths ranging from 86 to 109 MPa, elongations at break from 13 to 22%, and initial moduli from 2.15 to 2.63 GPa. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and characterization of novel soluble cardo poly(arylene ether ketone)s containing xanthene structures

9,9‐Bis(4‐hydroxyphenyl)xanthene (BHPX), a bisphenol monomer, was synthesized in 82% yield from xanthenone in a one‐pot, two‐step synthetic procedure. Four novel aromatic poly(ether ketone)s (PEKs) based on BHPX were prepared via a nucleophilic aromatic substitution polycondensation with four difluorinated aromatic ketones. The polycondensation proceeded in tetramethylene sulfone in the presence of anhydrous potassium carbonate and afforded the new cardo PEKs in nearly quantitative yields with inherent viscosities of 0.77–0.85 dL/g. High molecular weight PEKs having number‐average molecular weights (M_n's) in the range of 38,900–40,600 g/mol with the polydispersity index ranged from 1.97 to 2.06 are all amorphous and show high glass transition temperatures ranging from 210°C to 254°C, excellent thermal stability, and the temperatures at the 5% weight loss are over 538°C with char yields above 60% at 700°C in nitrogen. These new PEKs are all soluble in polar aprotic solvents such as N‐methyl‐2‐pyrrolidone and N, N′‐dimethylacetamide and could also be dissolved in chloroform and tetrahydrofuran. All the polymers formed transparent, strong, and flexible films with tensile strengths of 78–84 MPa, Young's moduli of 2.54–3.10 GPa, and elongations at break of 14–18 %. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and characterization of new poly(amide‐imide)s based on 1,4‐bis(trimellitimido)‐2,5‐dichlorobenzene

A series of new aromatic poly(amide‐imide)s were synthesized by the triphenyl phosphite‐activated polycondensation of the diimide‐diacid, 1,4‐bis(trimellitimido)‐2,5‐dichlorobenzene (I), with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidone (NMP), pyridine, and calcium chloride. The poly(amide‐imide)s had inherent viscosities of 0.88–1.27 dL g⁻¹. The diimide‐diacid monomer (I) was prepared from 2,5‐dichloro‐p‐phenylenediamine with trimellitic anhydride. All the resulting polymers were amorphous and were readily soluble in a variety of organic solvents, including NMP and N,N‐dimethylacetamide. Transparent, flexible, and tough films of these polymers could be cast from N,N‐dimethylacetamide or NMP solutions. Cast films had tensile strengths ranging from 92 to 127 MPa, elongations at break from 4 to 24%, and initial moduli from 2.59 to 3.65 GPa. The glass transition temperatures of these polymers were in the range of 256°–317°C, and the 10% weight loss temperatures were above 430°C in nitrogen. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 73: 271–278, 1999     

High‐optical transparency and low‐dielectric constant of new organosoluble polyamides containing trifluoromethyl and xanthene groups

A series of fluorinated polyamides was prepared directly by low‐temperature polycondensation of a new cardo diacid chloride, 9,9‐bis[4‐(4‐chloroformylphenoxy)phenyl]xanthene (BCPX), with various diamines containing trifluoromethyl substituents in N,N‐dimethylacetamide (DMAc). Almost all polyamides showed excellent solubility in amide‐type solvents such as DMAc and could also be dissolved in pyridine, m‐cresol, and tetrahydrofuran. These polymers had inherent viscosities between 0.77 and 1.31 dL g^?1, and their weight‐average molecular weights and number‐average molecular weights were in the range of 69,000–102,000 and 41,000–59,000, respectively. The resulting polymers showed glass transition temperatures between 240–258°C and 10% weight loss temperatures ranging from 484°C to 517°C and 410°C to 456°C in nitrogen and air, respectively, and char yields at 800°C in nitrogen higher than 55%. All polymers were amorphous and could be cast into transparent, light‐colored, and flexible films with tensile strengths of 81–100 MPa, elongations at break of 8–12%, and tensile modulus of 1.6–2.1 GPa. These polymers had low‐dielectric constants of 3.34–3.65 (100 kHz), low‐moisture absorption in the range of 0.76–1.91%, and high transparency with an ultraviolet–visible absorption cut‐off wavelength in the 322–340 nm range. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and characterization of poly(ether amide ether ketone)/poly(ether ketone ketone) copolymers

A new monomer, N,N′‐bis(4‐phenoxybenzoyl)‐m‐phenylenediamine (BPPD), was prepared by condensation of m‐phenylenediamine with 4‐phenoxybenzoyl chloride in N,N‐dimethylacetamide (DMAc). A series of novel poly(ether amide ether ketone) (PEAEK)/poly(ether ketone ketone) (PEKK) copolymers were synthesized by the electrophilic Friedel‐Crafts solution copolycondensation of terephthaloyl chloride (TPC) with a mixture of diphenyl ether (DPE) and BPPD, over a wide range of DPE/BPPD molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone (NMP) in 1,2‐dichloroethane (DCE). The influence of reaction conditions on the preparation of copolymers was examined. The copolymers obtained were characterized by different physicochemical techniques. The copolymers with 10–25 mol % BPPD were semicrystalline and had remarkably increased T_gs over commercially available PEEK and PEKK due to the incorporation of amide linkages in the main chains. The copolymers III and IV with 20–25 mol % BPPD had not only high T_gs of 184–188°C, but also moderate T_ms of 323–344°C, having good potential for the melt processing. The copolymers III and IV had tensile strengths of 103.7–105.3 MPa, Young's moduli of 3.04–3.11 GPa, and elongations at break of 8–9% and exhibited outstanding thermal stability and good resistance to organic solvents. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and properties of novel copolymers of poly(ether ketone diphenyl ketone ether ketone ketone) and poly(ether amide ether amide ether ketone ketone)

New monomers, 4,4′‐bis(4‐phenoxybenzoyl)diphenyl (BPOBDP) and N,N′‐bis(4‐phenoxybenzoyl)?4,4′‐diaminodiphenyl ether (BPBDAE), were conveniently synthesized via simple synthetic procedures from readily available materials. Novel copolymers of poly(ether ketone diphenyl ketone ether ketone ketone) (PEKDKEKK) and poly(ether amide ether amide ether ketone ketone) (PEAEAEKK) were synthesized by electrophilic Friedel‐Crafts solution copolycondensation of isophthaloyl chloride (IPC) with a mixture of BPOBDP and BPBDAE, over a wide range of BPOBDP/BPBDAE molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone (NMP) in 1,2‐dichloroethane (DCE). The copolymers obtained were characterized by different physico‐chemical techniques. The copolymers with 10–40 mol% BPBDAE are semicrystalline and had remarkably increased T_gs over commercially available PEEK and PEKK due to the incorporation of amide and diphenyl linkages in the main chains. The copolymers IV and V with 30–40 mol% BPBDAE had not only high T_gs of 185–188°C, but also moderate T_ms of 326–330°C, having good potential for the melt processing. The copolymers IV and V had tensile strengths of 101.7–102.3 MPa, Young's moduli of 2.19–2.42 GPa, and elongations at break of 13.2–16.6% and exhibited high thermal stability and excellent resistance to organic solvents. POLYM. ENG. SCI., 54:1757–1764, 2014. © 2013 Society of Plastics Engineers     

Synthesis and properties of polyamides based on 5,5′‐bis[4‐(4‐aminophenoxy)phenyl]‐hexahydro‐4,7‐methanoindan

A new diamine 5,5′‐bis[4‐(4‐aminophenoxy)phenyl]‐hexahydro‐4,7‐methanoindan ( 3 ) was prepared through the nucleophilic displacement of 5,5′‐bis(4‐hydroxylphenyl)‐hexahydro‐4,7‐methanoindan ( 1 ) with p‐halonitrobenzene in the presence of K₂CO₃ in N,N‐dimethylformamide (DMF), followed by catalytic reduction with hydrazine and Pd/C in ethanol. A series of new polyamides were synthesized by the direct polycondensation of diamine 3 with various aromatic dicarboxylic acids. The polymers were obtained in quantitative yields with inherent viscosities of 0.76–1.02 dl g⁻¹. All the polymers were soluble in aprotic dipolar solvents such as N,N‐dimethylacetamide (DMAc) and N‐methyl‐2‐pyrrolidone (NMP), and could be solution cast into transparent, flexible and tough films. The glass transition temperatures of the polyamides were in the range 245–282 °C; their 10% weight loss temperatures were above 468 °C in nitrogen and above 465 °C in air. © 2000 Society of Chemical Industry     

Synthesis and properties of new poly(amide‐imide)s based on 2,5‐bis(trimellitimido)chlorobenzene

A series of new aromatic poly(amide‐imide)s were synthesized by the triphenyl phosphite‐activated polycondensation of the diimide‐diacid, 2,5‐bis(trimellitimido)chlorobenzene (I) with various aromatic diamines in a medium consisting of N‐methyl‐2‐pyrrolidone (NMP), pyridine, and calcium chloride. The poly(amide‐imide)s had inherent viscosities of 0.76–1.42 dL g⁻¹. The diimide‐diacid monomer (I) was prepared from 2‐chloro‐p‐phenylenediamine with trimellitic anhydride. Most of the resulting polymers showed an amorphous nature and were readily soluble in a variety of organic solvents, including NMP and N,N‐dimethylacetamide. Transparent, flexible, and tough films of these polymers could be cast from N,N‐dimethylacetamide or NMP solutions. Their cast films had tensile strengths ranging from 74 to 95 MPa, elongations at break from 7 to 11%, and initial moduli from 1.38 to 3.25 GPa. The glass transition temperatures of these polymers were in the range of 233°–260°C, and the 10% weight loss temperatures were above 450°C in nitrogen. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 1691–1701, 1999     

Synthesis and properties of new soluble poly(amide‐imide‐imide)s

A new‐type tetraimide‐dicarboxylic acid ( I ) was synthesized starting from the ring‐opening addition of p‐aminobenzoic acid (p‐ABA), 4,4'‐oxydiphthalic anhydride (ODPA), and 4,4'‐methylenedianiline (MDA) at a 2:2:1 molar ratio in N‐methyl‐2‐pyrrolidone (NMP), followed by cyclodehydration to the diacid I. A series of poly(amide‐imide‐imide)s ( III _a‐i ) with inherent viscosities of 0.78–1.45 dL/g was prepared by triphenyl phosphite‐activated polycondensation from the tetraimide‐diacid I with various aromatic diamines ( II _a‐i ) in a medium consisting of NMP, pyridine, and calcium chloride. Most of the polymers were readily soluble in a variety of organic solvents such as NMP, N,N‐dimethyl acetamide, dimethyl sulfoxide, and even in less polar m‐cresol. Compared with those of the corresponding poly(amideimide)s IV _a‐i , the solubilities of poly(amide‐imide‐imide)s III _a‐i were greatly improved. Polymers III _a‐h afforded tough, transparent, and flexible films, which had tensile strengths ranging from 87 to 107 MPa, elongations at break from 9% to 14%, and initial moduli from 2.0 to 2.4 GPa. The glass transition temperatures of polymers were recorded at 270°C–309°C. They had 10% weight loss at temperatures in the range of 540°C–570°C and left more than 52% residue even at 800°C in nitrogen.     

Vitrification phenomena in polysulfone/NMP/water system

The vitrification line for the ternary system of polysulfone (PSf)/N‐methyl‐2‐pyrrolidinone (NMP)/water was determined by differential scanning calorimeter (DSC) measurements with varying compositions. Pure PSf showed both α‐ and β‐transition temperatures (T_g,α = 187.5°C, T_g,β = −21.4°C). The T_g,α of PSf decreased with increasing solvent concentration. The T_g,α of PSf decreased linearly with the addition of NMP in the concentration range of 70–90 wt % polymer. The vitrification line was indicated in the phase diagram for the ternary system of PSf/NMP/water at 15 and 60°C. As the temperature is increased, a high polymer concentration was needed to reach the vitrification condition. The vitrification composition of the polymer in the binary system of PSf and NMP was 72.0 wt % at 15°C and 79.8 wt % at 60°C. We also found that the slope of the vitrification line changed with the temperature and that a small amount of water (10–20 wt %) can induce the vitrification of the polymer solution in the PSf/NMP/water system at 15°C. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 431–438, 1999     

Synthesis and characterization of polyamides and poly(amide‐imide)s derived from 2,6‐bis(3‐aminophenoxy)benzonitrile or 2,6‐bis(4‐aminophenoxy)benzonitrile

A series of polyamides and poly(amide‐imide)s was prepared by direct polycondensation of ether and nitrile group containing aromatic diamines with aromatic dicarboxylic acids and bis(carboxyphthalimide)s respectively in N‐methyl 2‐pyrrolidone (NMP) using triphenyl phosphite and pyridine as condensing agents. New diamines, such as 2,6‐bis(4‐aminophenoxy)benzonitrile and 2,6‐bis(3‐aminophenoxy)benzonitrile, were prepared from 2,6‐dichlorobenzonitrile with 4‐aminophenol and 3‐aminophenol, respectively, in NMP using potassium carbonate. Bis(carboxyphthalimide)s were prepared from the reaction of trimellitic anhydride with various aromatic diamines in N,N′‐dimethyl formamide. The inherent viscosities of the resulting polymers were in the range of 0.27 to 0.93 dl g^?1 in NMP and the glass transition temperatures were between 175 and 298 °C. All polymers were soluble in dipolar aprotic solvents such as dimethylsulfoxide, dimethylacetamide and NMP. All polymers were stable up to 350 °C with a char yield of above 40 % at 900 °C in nitrogen atmosphere. All polymers were found to be amorphous except the polyamide derived from isophthalic acid and the poly(amide‐imide)s derived from diaminodiphenylether and diaminobenzophenone based bis(carboxyphthalimide)s. Copyright © 2004 Society of Chemical Industry     

Synthesis and properties of novel polyamides containing sulfone‐ether linkages and xanthene cardo groups

In order to obtain polyamides with enhanced solubility and processability, as well as good mechanical and thermal properties, several novel polyamides containing sulfone‐ether linkages and xanthene cardo groups based on a new diamine monomer, 9,9‐bis[4‐(4‐aminophenoxy)phenyl]xanthene (BAPX), were investigated. The BAPX monomer was synthesized via a two‐step process consisting of an aromatic nucleophilic substitution reaction of readily available 4‐chloronitrobenzene with 9,9‐bis(4‐hydroxyphenyl)xanthene in the presence of potassium carbonate in N,N‐dimethylformamide, followed by catalytic reduction with hydrazine and Pd/C. Four novel aromatic polyamides containing sulfone‐ether linkages and xanthene cardo groups with inherent viscosities between 0.98 and 1.22 dL g^?1 were prepared by low‐temperature polycondensation of BAPX with 4,4′‐sulfonyldibenzoyl chloride, 4,4′‐[sulfonyl‐bis(4‐phenyleneoxy)]dibenzoyl chloride, 3,3′‐[sulfonyl‐bis(4‐phenyleneoxy)]dibenzoyl chloride and 4,4′‐[sulfonyl‐bis(2,6‐dimethyl‐1,4‐phenyleneoxy)]dibenzoyl chloride in N,N‐dimethylacetamide (DMAc) solution containing pyridine. All these new polyamides were amorphous and readily soluble in various polar solvents such as DMAc and N‐methylpyrrolidone. These polymers showed relatively high glass transition temperatures in the range 238–298 °C, almost no weight loss up to 450 °C in air or nitrogen atmosphere, decomposition temperatures at 10% weight loss ranging from 472 to 523 °C and 465 to 512 °C in nitrogen and air, respectively, and char yields at 800 °C in nitrogen higher than 50 wt%. Transparent, flexible and tough films of these polymers cast from DMAc solution exhibited tensile strengths ranging from 78 to 87 MPa, elongations at break from 9 to 13% and initial moduli from 1.7 to 2.2 GPa. Primary characterization of these novel polyamides shows that they might serve as new candidates for processable high‐performance polymeric materials. Copyright © 2010 Society of Chemical Industry     

Synthesis of soluble and thermally stable polyimides from 3,5‐diamino‐N‐(4‐(8‐quinolinoxy) phenyl) aniline and various dianhydrides

Three novel polyimides (PIs) having pendent 4‐(quinolin‐8‐yloxy) aniline group were prepared by polycondensation of a new diamine with commercially available tetracarboxylic dianhydrides, such as pyromellitic dianhydride, 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride, and bicyclo[2.2.2]‐oct‐7‐ene‐2,3,5,6‐tetracarboxylic dianhydride. These PIs were characterized by FTIR, ¹H NMR, and elemental analysis; they had high yields with inherent viscosities in the range of 0.4–0.5 dl g⁻¹, and exhibited excellent solubility in many organic solvents such as N,N‐dimethyl acetamide, N,N′‐dimethyl formamide, N‐methyl pyrrolidone (NMP), dimethyl sulfoxide, and pyridine. These PIs exhibited glass transition temperatures (T_g) between 250 and 325° C. Their initial decomposition temperatures (T_i) ranged between 270 and 450°C, and 10% weight loss temperature (T₁₀) up to 500°C with 68% char yield at 600°C under nitrogen atmosphere. Transparent and hard polymer films were obtained via casting from their NMP solutions. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and properties of organic soluble semicrystalline poly(aryl ether ketone)s copolymers containing phthalazinone moieties

A series of poly(aryl ether ketone)s (PAEK) copolymers containing phthalazinone moieties were synthesized by modest polycondensation reaction from 4‐(4‐hydroxyl‐phenyl)‐(2H)‐phthalazin‐1‐one (DHPZ), hydroquinone (HQ), and 1,4‐bis(4‐fluorobenzoyl)benzene (BFBB). The T_g values of these copolymers ranged from 168 to 235°C, and the crystalline melting temperatures varied from 285 to 352°C. By introducing phthalazinone moieties into the main chain, the solubility of these copolymers was improved in some common polar organic solvents, such as chloroform (CHCl₃), N‐methyl‐2‐pyrrolidinone (NMP), nitrobenzene (NB) and so on. The values of 5% weight loss temperatures were all higher than 510°C in nitrogen. The crystal structures of these copolymers were determined by wide‐angle X‐ray diffraction (WAXD), which revealed that they were semicrystalline in nature, and the crystal structure of these copolymers was orthorhombic, equal to poly(ether ether ketone ketone)s. As phthalazinone content in the backbone varied from 0 to 40 mol % (mole percent), the cell parameters of these copolymers including the a, b, and c axes lengths ranged from 7.76 to 7.99 Å, 6.00 to 6.14 Å, and 10.10 to 10.19 Å, respectively. The degree of crystallinity (via differential scanning calorimetry) decreased from 37.70% to 16.14% simultaneously. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 1744–1753, 2007     

Copolymerization of N‐substituted maleimide with alkyl acrylate and its industrial applications

A series of new copolymers with desired thermal stability and mechanical properties for applications in leather industry were synthesized from various substituted maleimides and alkyl acrylates. Polymerization was carried out by a free‐radical polymerization using benzoyl peroxide (BPO) as initiator. The monomers and polymers synthesized were characterized by elemental analysis, IR, and nuclear magnetic resonance (NMR). Interestingly, these polymers were soluble in common organic solvents. Copolymer composition and reactivity ratios were determined by ¹H‐NMR spectra. The molecular weights of the polymers were determined by gel permeation chromatography. The homo‐ and copolymer of maleimide showed single‐stage decomposition (ranging from 300–580°C). The initial decomposition temperatures of poly[N‐(phenyl)maleimide] [poly(PM)], poly[N‐4‐(methylphenyl)maleimide] [poly(MPM)] and poly[N‐3‐(chlorophenyl)maleimide] [poly(CPM)] were higher compared to those of the copolymers. Heat‐resistant adhesives such as blends of epoxy resin with phenyl‐substituted maleimide‐co‐glycidyl methacrylate copolymers with improved adhesion property were developed. Different adhesive formulations of these copolymaleimides were prepared by curing with diethanolamine at two different temperatures (30°C and 60°C). © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 80: 1870–1879, 2001     

Synthesis and properties of novel copolymers of poly(ether ketone ether ketone ketone) and poly(ether ketone ketone ether ketone ketone) containing 1,4‐naphthylene moieties

A new monomer, 1,4‐bis(4‐phenoxybenzoyl)naphthalene (BPOBN), was conveniently synthesized via a simple synthetic procedure from readily available materials. A series of novel copolymers of poly(ether ketone ether ketone ketone) and poly(ether ketone ketone ether ketone ketone) containing 1,4‐naphthylene moieties were prepared by the Friedel‐Crafts acylation solution copolycondensation of terephthaloyl chloride (TPC) with a mixture of BPOBN and 4,4′‐diphenoxybenzophenone (DPOBPN), over a wide range of BPOBN/DPOBPN molar ratios, in the presence of anhydrous AlCl₃ and N‐methylpyrrolidone in 1,2‐dichloroethane. The copolymers with 10–40% BPOBN are semicrystalline and had remarkably increased T_gs over the conventional PEEK and PEKK due to the incorporation of 1,4‐naphthylene moieties in the main chains. The copolymers with 30–40 mol% BPOBN had not only high T_gs of 176–177°C, but also moderate T_ms of 332–338°C, which are suitable for the melt processing. These polymers had tensile strengths of 101.5–104.7 MPa, Young's moduli of 2.49–2.65 GPa, and elongations at break of 13.3–15.7% and exhibited high thermal stability and excellent resistance to organic solvents. POLYM. ENG. SCI., 56:566–572, 2016. © 2016 Society of Plastics Engineers     

Synthesis and properties of copolymers of poly(ether ketone ketone) and poly(ether amide ether amide ether ketone ketone)

Poly(aryl ether ketone)s (PAEKs) are a class of high‐performance engineering thermoplastics known for their excellent combination of chemical, physical and mechanical properties, and the synthesis of semicrystalline PAEKs with increased glass transition temperatures (T_g) is of much interest. In the work reported, a series of novel copolymers of poly(ether ketone ketone) (PEKK) and poly(ether amide ether amide ether ketone ketone) were synthesized by electrophilic solution polycondensation of terephthaloyl chloride with a mixture of diphenyl ether and N,N′‐bis(4‐phenoxybenzoyl)‐4,4′‐diaminodiphenyl ether (BPBDAE) under mild conditions. The copolymers obtained were characterized using various physicochemical techniques. The copolymers with 10–35 mol% BPBDAE are semicrystalline and have markedly increased T_g over commercially available poly(ether ether ketone) and PEKK due to the incorporation of amide linkages in the main chain. The copolymers with 30–35 mol% BPBDAE not only have high T_g of 178–186 °C, but also moderate melting temperatures of 335–339 °C, having good potential for melt processing. The copolymers with 30–35 mol% BPBDAE have tensile strengths of 102.4–103.8 MPa, Young's moduli of 2.33–2.45 GPa and elongations at break of 11.7–13.2%, and exhibit high thermal stability and good resistance to organic solvents. Copyright © 2010 Society of Chemical Industry     

Synthesis and characterization of new soluble polyamides from an unsymmetrical diamine bearing a bulky triaryl pyridine pendent group

New unsymmetrical diamine monomer containing triaryl pyridine pendent group, 2,4‐diaminophenyl [4‐(2, 6‐diphenyl‐4‐pyridyl) phenyl]ether, was synthesized via aromatic substitution reaction of 1‐chloro‐2,4‐dinitrobenzene with 4‐(2,6‐diphenyl‐4‐pyridyl) phenol, followed by Pd/C‐catalyzed hydrazine reduction. Five Polyamides (PA) were prepared by the phosphorylation polycondensation of different dicarboxylic diacids with the diamine. Inherent viscosities of PAs were in the range 0.51–0.59 g/dL indicating formation of medium molecular weight polymers. The weight and number average molecular weights of a PA, (PA‐d), determined by GPC were 6944 g/mol and 17,369 g/mol, respectively. PAs exhibited glass‐transition temperatures (T_g) in the range 140–235°C. These polymers, essentially amorphous, were soluble in polar aprotic solvents such as DMF, NMP, DMAc, DMSO, pyridine, m‐cresol, and THF. The initial decomposition temperatures (T_i) of PAs, determined by TGA in air, were in the range 300–380°C indicating their good thermal stability. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis and characterization of poly(ether ketone ether ketone ketone)/poly(ether ether ketone ketone) copolymers containing naphthalene and pendant cyano groups

2,6‐Bis(β‐naphthoxy)benzonitrile (BNOBN) was synthesized by reaction of β‐naphthol with 2,6‐difluorobenzonitrile in N‐methyl‐2‐pyrrolidone (NMP) in the presence of KOH and K₂CO₃. Poly(ether ketone ether ketone ketone)(PEKEKK) /poly(ether ether ketone ketone) (PEEKK) copolymers containing naphthalene and pendant cyano groups were obtained by electrophilic Friedel‐Crafts polycondensation of terephthaloyl chloride (TPC) with varying mole proportions of 4,4′‐diphenoxybenzophenone (DPOBP) and 2,6‐bis(β‐naphthoxy)benzonitrile (BNOBN) using 1,2‐dichloroethane (DCE) as solvent and NMP as Lewis base in the presence of anhydrous AlCl₃. The resulting polymers were characterized by various analytical techniques, such as FTIR, DSC, TG, and WAXD. The results indicated that the crystallinity and melting temperature of the polymers decreased with increase in concentration of the BNOBN units in the polymer, the glass transition temperature of the polymers increased with increase in concentration of the BNOBN units in the polymer. Thermogravimetric studies showed that all the polymers were stable up to 536°C in N₂ atmosphere. The copolymers have good resistance to acidity, alkali, and organic solvents. Because of the melting temperature (T_m) depression with increase in the BNOBN content in the reaction system, the processability of the resultant coplymers could be effectively improved. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and properties of some novel,soluble and light‐coloured,aromatic poly(amide–imide) copolymers

A new type of tetraimide‐dicarboxylic acid (I) was synthesized starting from the ring‐opening addition of m‐aminobenzoic acid (m‐ABA), 4,4′‐oxydiphthalic anhydride (ODPA) and 4,4′‐methylenedianiline (MDA) at a 2:2:1 molar ratio in N‐methyl‐2‐pyrrolidone (NMP), followed by cyclodehydration to the diacid I. A series of soluble and light‐coloured poly(amide–imide–imide)s (III_a–j) was prepared by triphenyl phosphite‐activated polycondensation from the tetraimide‐diacid I with various aromatic diamines (II_a–j). All films cast from DMAc had cutoff wavelengths shorter than 400 nm (376–393 nm) and had b* values between 20.46 and 40.67; these polymers were much lighter in colour than those of the corresponding trimellitimide series. All polymers were readily soluble in a variety of organic solvents such as NMP, N,N‐dimethylacetamide, dimethyl sulfoxide, and even in the less polar m‐cresol and pyridine. Compared with those of corresponding ODPA–MDA polyimide, the solubilities of poly(amide–imide–imide)s III_a–j were greatly improved. Polymers III_a–j afforded tough, transparent, and flexible films, which had tensile strengths ranging from 82 to 105 MPa, elongations at break from 8 to 14%, and initial moduli from 2.0 to 2.2 GPa. The glass transition temperature of polymers were recorded at 255–288 °C. They had 10% weight loss at a temperature above 540 °C and left more than 60% residue even at 800 °C in nitrogen. © 2002 Society of Chemical Industry