Microstructure and stress corrosion cracking in simulated heat-affected zones of duplex stainless steels

The effects of nitrogen content and the cooling rate on the reformation of austenite in the Gleeble simulated heat-affected zone (HAZ) of 2205 duplex stainless steels (DSSs) were investigated. The variation of stress corrosion cracking (SCC) behavior in the HAZ of 40 wt% CaCl₂ solution at 100 °C was also studied. Grain boundary austenite (GBA), Widmanstatten austenite (WA), intergranular austenite (IGA) and partially transformed austenite (PTA) were present in the HAZ. The types and amounts of these reformed austenites varied with the cooling rate and nitrogen content in the DSS. U-bend tests revealed that pitting corrosion and selective dissolution might assist the crack initiation, while the types and amounts of reformed austenite in the HAZ affected the mode of crack propagation. The presence of GBA was found to promote the occurrence of intergranular stress corrosion cracking. WA, IGA and PTA were found to exhibit a beneficial effect on SCC resistance by deviating the crack propagation path.     

Microelectrochemical corrosion study of super martensitic welds in chloride-containing media

Pitting corrosion was studied in welded joints of supermartensitic stainless steels. The electrochemical behavior of three different weldment zones (weld metal (WM), parent metal (PM) and heat affected zone (HAZ)) was characterized independently using an electrochemical minicell through potentiodynamic and potentiostatic techniques. The minicell design selected for this work has the additional advantage of showing promise for service application. Macro-electrochemical characterization was also used to provide a basis for comparison and check the effectiveness of minicell techniques in characterizing the corrosion resistance of welded super martensitic stainless steels. Minicell experiments exhibit a great capacity to discriminate between the different welding zones. The electrochemical response can be correlated with the microstructure of the different zones. Thermal cycles resulting from the welding procedure do not have an important effect on the amount of retained austenite or on the values of the pitting potential E_P in the HAZ.     

Effect of high temperature heat treatment on intergranular corrosion of AlMgSi(Cu) model alloy

Copper containing 6000-series aluminium alloys may become susceptible to intergranular corrosion (IGC) as a result of improper thermomechanical processing. Effect of cooling rate after solution heat treatment on the corrosion behaviour of a model AlMgSi(Cu) alloy of nominal composition (wt%) 0.6 Mg, 0.6 Si, 0.2 Fe, 0.2 Mn and 0.1 Cu was investigated. Slow cooling rates were simulated by isothermal treatment for predetermined times in lower temperature baths immediately after solution heat treatment. Treatment for 10-100 s at temperatures below 400 °C introduced susceptibility to IGC. Longer heat treatment at the same temperatures introduced susceptibility to pitting. A corrosion resistant time zone was found between the zones of IGC and pitting at temperatures lower than 350 °C. Quenching in water after solution heat treatment prevented IGC. IGC was related to microgalvanic coupling between the noble Q-phase (Al₄Mg₈Si₇Cu₂) grain boundary precipitates and the adjacent depleted zone. Pitting was attributed to coarse particles in the matrix. Possible mechanisms causing the corrosion resistant intermediate zone are discussed. The results indicate possible methods for obtaining increased corrosion resistance of similar alloys by proper thermal processing.     

Microstructure, heat treatment and pitting corrosion of 13CrNiMo plate and weld metals

Potentiodynamic measurements together with SEM were used to analyze susceptibility to pitting corrosion of 13CrNiMo plate metals. Volume fractions of austenite in tempered conditions affect pitting resistance. Characteristic potentials (critical pitting and repassivation) increase according to the retained austenite content. Results correspond to a structural refinement resulting from a double tempering procedure. A comparison is made with results from weld metal samples. The importance of this evaluation is to be able to determine pitting resistance, either in a service application, or in laboratory test programs.     

Microstructure and pitting corrosion resistance of annealed duplex stainless steel

The transition from metastable to stable pitting was studied in 0.5 M NaCl water solution for two cast duplex stainless steels under different microstructural conditions achieved by annealing in the range from 900 °C to 1200 °C. The ensuing microstructural changes in heat treated steels were defined and correlated with established pitting potentials (E_p) and sites of corrosion damage initiation. The variations in E_p have been discussed in terms of secondary phases precipitation. The critical condition for pit stability was quantified and used to select an appropriate microstructural state, resulting in the higher potential at which stable pit growth is first observed.     

A newly synthesized glycine derivative to control uniform and pitting corrosion processes of Al induced by SCN anions - Chemical, electrochemical and morphological studies

A newly synthesized glycine derivative (termed GlyD), 2-(4-(dimethylamino)benzylamino)acetic acid hydrochloride, was used to inhibit uniform and pitting corrosion processes of Al in 0.50 M KSCN solutions (pH 6.8) at 25 °C. For uniform corrosion inhibition study, Tafel extrapolation, linear polarization resistance and impedance methods were used, complemented with SEM examinations. An independent method of chemical analysis, namely ICP-AES (inductively coupled plasma atomic emission spectrometry) was also used to test validity of corrosion rate measured by Tafel extrapolation method. GlyD inhibited uniform corrosion, even at low concentrations, reaching a value of inhibition efficiency up to 97% at a concentration of 5 × 10⁻³ M. Results obtained from the different corrosion evaluation techniques were in good agreement. This new synthesized glycine derivative was also used to control pit nucleation and growth on the pitted Al surface based on cyclic polarization, potentiostatic and galvanostatic measurements. The pitting potential (E_pit) and the repassivation potential (E_rp) increased by the addition of GlyD. Thus GlyD suppressed pit nucleation and propagation. Nucleation of pit was found to take place after an incubation time (t_i). The rate of pit nucleation and growth decreased with increase in inhibitor concentration. Morphology of pitting was also studied as a function of the applied anodic potential and solution temperature. Cross-sectional view of pitted surface revealed the formation of large distorted hemispherical and narrow deep pits. GlyD was much better than Gly in controlling uniform and pitting corrosion processes of Al in these solutions.     

Effects of solution heat-treatment and nitrogen in shielding gas on the resistance to pitting corrosion of hyper duplex stainless steel welds

The effects of solution heat-treatment and shielding gas on the pitting corrosion of hyper duplex stainless steel (HDSS) welds were investigated in highly concentrated chloride environments. The pitting resistance of a solution heat-treated HDSS after welding with an Ar shielding gas supplemented with N₂ was greatly increased due to the dissolution of Cr₂N in α-phase, which followed the diffusion of N atoms from the α-phase to the γ-phase and an increase of the γ-phase in the weld metal and heat affected zone. It was also attributed to a decrease of the pitting resistance equivalent number difference between the two phases.     

Microsegregation-related pitting corrosion characteristics of AL-6XN superaustenitic stainless steel laser welds

Pitting corrosion resistance of laser welds of AL-6XN superaustenitic stainless steel (SASS) was investigated in acidic chloride ion medium. It was found that the critical pitting temperature (CPT) of the laser welds increased with increasing welding speed or decreasing laser power. Pitting attack preferentially occurred at selective dendrite cores of the laser welds. Analytical electron microscope (AEM) microanalysis revealed that depletion of Mo at dendrite cores due to microsegregation is the basic cause for the pitting corrosion susceptibility. The higher partition coefficient k_Mo and Mo concentration at dendrite cores of laser welds were attributed to the lower heat input welding parameters.     

Effect of heat treatment on corrosion behaviour of magnesium alloy AZ91D in simulated body fluid

The research explored ways of improving corrosion behaviour of AZ91D magnesium alloy through heat treatment for degradable biocompatible implant application. Corrosion resistance of heat-treated samples is studied in simulated body fluid at 37 °C using immersion and electrochemical testing. Heat treatment significantly affected microgalvanic corrosion behaviour between cathodic β-Mg₁₇Al₁₂ phase and anodic α-Mg matrix. In T4 microstructure, dissolution of the β-Mg₁₇Al₁₂ phase decreased the cathode-to-anode area ratio, leading to accelerated corrosion of α-Mg matrix. Fine β-Mg₁₇Al₁₂ precipitates in T6 microstructure facilitated intergranular corrosion and pitting, but the rate of corrosion was less than those of as-cast and T4 microstructures.     

Corrosion behaviour of duplex stainless steels sintered in nitrogen

Duplex stainless steels obtained through powder metallurgy (PM) technology from austenitic AISI 316L and ferritic AISI 430L powders were mixed on different amounts to obtain biphasic structures with austenite/ferrite ratio of 50/50, 65/35 and 85/15. Prepared mixes of powders have been compacted at 750 MPa and sintered in N₂-H₂ (95% and 5%) at 1250 °C for 1 h. Corrosion behaviour, using electrochemical techniques such as anodic polarization measurement, cyclic anodic polarization scan and electrochemical potentio-kinetic reactivation test and double loop electrochemical potentio-kinetic reactivation double loop test were evaluated. For duplex stainless steels, when austenite/ferrite ratio increases the corrosion potential shifts to more noble potential and passive current density decreases. The beneficial effect of annealing solution heat treatment on corrosion behaviour was established and was compared with corrosion behaviour of vacuum sintered duplex stainless steels. The results were correlated with the microstructural features.     

Pitting corrosion of Type 430 stainless steel under chloride solution droplet

To clarify the critical relative humidity (RH) to initiate pitting corrosion and the rusting mechanism in a marine atmospheric environment, pitting corrosion of Type 430 stainless steels under drops of MgCl₂ solutions were investigated. A pitting corrosion test was performed at different relative humidities under droplets with various diameters and thicknesses. The probability of pitting decreased as the diameter and thickness decreased. Pitting progressed only when the chloride concentration exceeded 4 M, which is the equilibrium concentration at 80% RH. Accordingly, pitting of Type 430 could be initiated when the RH was less than 80%. Additionally, a pitting corrosion mechanism of Type 430 stainless steel under droplets containing chloride ions is proposed.     

Study of the correlation between pitting corrosion and the component ratio of the dual phase in duplex stainless steel welds

Three duplex stainless steel weldments were produced by changing the chromium element to study the correlation between the pitting corrosion characteristics and the component ratio of the dual phase. The pit morphologies showed that metastable pits were generated at a lower pitting resistance equivalent number (PREN) phase. The secondary austenite phases seemed to serve as a path for the corrosive environment regardless of the ferrite number (FN). There is some discrepancy between the measured values (pitting potential (E_p) through polarization test) and expected values (sequence ranked by PREN of weaker phase) in 1 mol l⁻¹ NaCl solution at 60 °C.     

Aqueous corrosion behaviour of sintered stainless steels manufactured from mixes of gas atomized and water atomized powders

The electrochemical corrosion improvement of a powder metallurgical (PM) stainless steel is studied in this work. Water atomized (WA) ferritic AISI 434L powders have been mixed with gas atomized (GA) austenitic (AISI 316L type) and ferritic (AISI 430L type) powders and processed through the traditional PM route. The addition of GA powder to the usual WA powder decreases the mean size of the pores of the sintered stainless steels. As the bigger pores are the ones that are able to act as crevices, unlike the smaller ones - that act as closed porosity, reduction in the number of big pores tends to improve the corrosion behaviour of PM stainless steels. Reductions of the corrosion rate (i_corr) and increases of the corrosion potential (E_corr) have been measured in neutral media, with and without chlorides. Moreover, the additional beneficial effect of achieving a duplex microstructure through the addition of GA austenitic powders to the WA ferritic powders has also been verified.     

Pitting of zinc: Observations on atmospheric corrosion in tropical countries

A five-nation study has investigated the mechanisms and rates of the atmospheric corrosion of zinc and steel in tropical regions in Australia, Thailand, Indonesia, Vietnam and The Philippines. For the study, 18 exposure sites encompassing severe marine, marine, severe industrial, industrial, marine/industrial, urban and highland environments were established across the countries. At each location, zinc and steel plates were exposed for periods of three months and one year, and measurements were taken of a wide range of surface-response and climatic parameters, including gaseous SO_x and NO_x, airborne salinity, relative humidity (RH) and temperature, rainwater composition, surface temperature and time of wetness (TOW). Exposed plates were used to determine mass loss, the nature of corrosion products (using FTIR and SEM-EDS) and the morphologies of corrosion layers (via SEM-EDS). Regression analysis indicated that the prime factors controlling zinc corrosion rate were climate (temperature and rainfall) and surface-response (TOW), and surprisingly not pollutant levels, despite significant variation in SO_x levels across the sites. SEM studies indicated the presence of pitting below the oxide layers on zinc, particularly those plates exposed at marine and other sites with relatively low SO_x levels. In contrast, no pitting was observed (or pits had very low aspect ratios) in the specimens exposed at sites with high SO_x levels. The possible processes leading to the observed damage patterns are discussed.     

Pitting corrosion mechanism of Type 304 stainless steel under a droplet of chloride solutions

Pitting corrosion of Type 304 stainless steel under drops of MgCl₂ solution has been investigated to clarify the rusting mechanism in marine atmospheres. A pitting corrosion test was performed under the droplets with various combinations of the diameter and thickness (height) by exposure to a constant relative humidity. Probability of occurrence of pitting corrosion decreased with decreasing the diameter and thickness. Pitting corrosion progressed only when the [Cl⁻] exceeded 6 M (RH < 65%). In almost cases, there was a small hole (∼10 μm diameter) in the center of a single pit, which may be the trace of an inclusion particle like MnS dissolved out. The pitting corrosion mechanism of Type 304 under droplets containing chloride ions has been proposed.     

Effect of thermal cycles on the corrosion and mechanical properties of UNS S31803 duplex stainless steel

The microstructure and properties of UNS S31803 duplex stainless steel had been investigated following isothermally aging in a temperature range of 450–1000 °C for 10 min, which simulates a fairly long time relative to a weld thermal cycle. The results showed that specimens aged between 600 and 950 °C are subjected to precipitation of secondary phases, such as Cr₂N, σ and χ. And the most significant reduction in pitting corrosion resistance and impact energy occurs at 850 °C. Moreover, at aging temperatures below 600 °C, austenite is the preferred site for pitting initiation, which changes to precipitates modified ferrite phase at higher temperatures above 600 °C.     

Corrosion of 304 stainless steel exposed to nitric acid-chloride environments

In an effort to examine the combined effect of HNO₃, NaCl, and temperature on the general corrosion behavior of 304 stainless steel (SS), electrochemical studies were performed. The corrosion response of 304 SS was bifurcated: materials were either continuously passive following immersion or spontaneously passivated following a period of active dissolution. Active dissolution was autocatalytic, with the corrosion rate increasing exponentially with time and potential. The period of active corrosion terminated following spontaneous passivation, resulting in a corrosion rate decrease of up to five orders of magnitude. The length of the active corrosion period was strongly dependent on the solution volume-to-surface area ratio. This finding, coupled with other results, suggested that spontaneous passivation arises solely from solution chemistry as opposed to changes in surface oxide composition. Increasing NaCl concentrations promoted pitting, active dissolution upon initial immersion, a smaller potential range for passivity, longer active corrosion periods, larger active anodic charge densities preceding spontaneous passivation, and larger corrosion current and peak current densities. In contrast, intermediate HNO₃ concentrations promoted active dissolution, with continuous passivity noted at HNO₃ concentration extremes. During active corrosion, increased HNO₃ concentrations increased the anodic charge density, corrosion current density, and peak current density. The time required for spontaneous passivation was greatest at intermediate HNO₃ concentrations. Susceptibility to pitting was also greatest at intermediate HNO₃ concentrations: the pit initiation and repassivation potentials decreased with increasing HNO₃ concentration until the HNO₃ concentration exceeded a critical concentration beyond which susceptibility to pitting was entirely eliminated. Increasing solution temperature increased the susceptibility to both pitting and active dissolution.     

Role of alloyed copper on corrosion resistance of austenitic stainless steel in H2S–Cl− environment

Corrosion test, surface analysis and thermodynamic calculation were carried out in the H₂S–Cl⁻ environments to clarify the role of alloyed Cu on the corrosion resistance of austenitic alloys. The alloyed Cu improved pitting corrosion resistance in the H₂S–Cl⁻ environment. The surface film of Cu-containing alloy indicated double layer consists of copper sulfide and chromium oxide, and the copper sulfide was able to exist stably compared to iron sulfide and nickel sulfide. It is concluded that the copper sulfide would enhance the formation of chromium oxide film which improve the pitting corrosion resistance in the H₂S–Cl⁻ environment.     

Identifying the role of nanoscale heterogeneities in pitting behaviour of Al-based metallic glass

To clarify the correlation of nanoscale heterogeneity with corrosion in Al-based metallic glasses, three model alloys with a single nanoscale α-Al, Al₃Ni or Al₁₁Ce₃ phase embedded in amorphous Al-Ni-Ce alloy matrix were obtained directly by melt quenching. The results indicated that the high pitting corrosion resistance of AM alloys was not deteriorated by nanocrystalline α-Al precipitation; whereas the pitting potential was slightly decreased and considerably reduced relative to their amorphous state due to the precipitation of nanocrystalline Al₃Ni or Al₁₁Ce₃ respectively. Such a pitting sensitivity of different types of heterogeneities attributes to the nano-scale pit initiation events.     

Effect of magnetic field applied during gas metal arc welding on the resistance to localised corrosion of the heat affected zone in AISI 304 stainless steel

Resistance to localised corrosion at the heat affected zone (HAZ) of AISI 304 stainless steel gas metal arc welded (GMAW) in presence of magnetic fields of different intensity was studied. Samples of HAZ, 8 mm away from the weld centre, were subjected to electrochemical potentiokinetic reactivation to assess the degree of sensitisation (DOS). The application of magnetic field during welding induced lower DOS and better resistance to pitting corrosion in 3.5% NaCl solution than samples welded without it. Experimental findings suggest that magnetic fields enable Cr redistribution in the austenitic base metal during the welding thermal cycle reducing Cr depletion.