类金刚石薄膜对纯钛的磨损保护及安全性评价

评价了以TiN为过渡层的类金刚石（DLC）复合梯度膜对齿科纯钛（TA2）的磨损防护效果以及生物安全性。采用脉冲真空多弧等离子体镀膜机,在齿科纯钛表面镀制TiN梯度膜和DLC表面膜。在体外对比检测镀膜的耐磨损能力和与纯钛的结合力,同时观察检测磨损后的表面形貌和元素分布。应用MTT法评价其生物相容性。结果表明,DLC薄膜的耐磨损能力以及与纯钛的结合力明显高于其余表面处理方法,表面形貌改变小。细胞毒性实验表明,DLC膜表面的L-929细胞增值良好。复合梯度膜的应用,可以明显提高DLC镀膜与纯钛基体的结合力。耐磨试验表明,DLC复合梯度膜可以承受日常口腔刷牙的磨耗,安全可靠,可以应用于人体。     

真空电弧离子镀膜方法沉积类金刚石膜在PMMA树脂义齿表面的应用

采用电弧离子镀膜方法,以高纯石墨为碳离子源在PMMA树脂义齿表面沉积类金刚石膜.应用xps谱和Raman谱对膜层的结构进行了理论分析,对镀膜样品进行了抗磨性能实验、病理实验和临床实验.结果表明为了提高样品的膜基结合强度,必须在DLC膜与基材之间增镀一层钛氧化物作为过渡层,必须严格控制工作电压、工作室的真空度和气氛配比.     

直流磁控溅射非晶碳膜的导电性和耐蚀性

用直流磁控溅射技术在304不锈钢基体上制备导电非晶碳膜,重点研究了基体偏压对非晶碳膜微结构、导电性和耐蚀性的影响。结果表明:与纯不锈钢双极板相比,经非晶碳膜表面改性的不锈钢表面的导电性和耐蚀性均大幅度提高。当基体偏压为-200V时在质子交换膜燃料电池组装典型压力(1.5MPa)下非晶碳膜的sp2含量最高,使改性不锈钢双极板具有最低的接触电阻(16.65mΩ·cm2);在模拟质子交换膜燃料电池工作环境的腐蚀溶液中镀膜后不锈钢板的腐蚀电位显著提高,腐蚀电流明显下降。尤其在偏压-200V下薄膜具有最佳的致密性,腐蚀电位为0.25V,腐蚀电流密度为1.22×10-8A/cm2,耐蚀性能最佳。     

细胞培养法评价铁铬钼软磁合金的生物相容性

为检测口腔中所用铁铬钼软磁合金的细胞毒性，以评价其生物相容性，将材料浸提液用于体外细胞培养，进行四唑盐（MTT）比色实验来评价材料的细胞毒性。结果表明，软磁合金的细胞毒性级为Ⅰ级，纯钛的毒性为0级。软磁舍金组对细胞增殖的抑制作用大于纯钛组，但统计学分析结果显示，两种金属材料组与阴性对照组吸光度值之间的差异均无统计学意义...     

非晶碳膜的表面润湿性对生物相容性的影响

采用等离子体注入沉积方法(PⅢ-D),混合通入C2H2、Ar或N2,制备了具有不同表面润湿性的非晶碳薄膜a-CH和掺N非晶碳薄膜a-CNH.采用Raman及XPS方法对薄膜的结构进行了分析,采用血小板黏附实验评价薄膜的抗凝血性能,采用材料表面的内皮细胞培养,对材料的细胞毒性以及生物相容性进行评价.结果表明非晶碳膜的生物相容性的提高与其表面的润湿性的变化密切相关,可通过掺杂特定的元素,增加a-CH薄膜表面张力的极性倾向,提高非晶碳膜的亲水性,来进一步改进a-CH薄膜的生物相容性,特别是血液相容性.     

采用钛-铝-钼过渡层在铜基底上沉积金刚石薄膜的研究

采用钛-铝-钼过渡层研究了铜基片上金刚石薄膜的化学气相沉积.用SEM和Raman谱研究了薄膜的形貌和质量.用XRD分析了膜基间形成的化合物的成分,并进一步分析了铝的存在对膜基结合力的影响.实验证明,钛-铝-钼过渡层的存在显著提高了金刚石薄膜与铜基底的结合力.     

纯钛超声微弧氧化-化学镀铜涂层的制备及抗菌性

为了赋予纯钛口腔种植体表面涂层生物活性及抗菌性,发挥酸蚀、微弧氧化技术、碱处理及化学镀铜技术各自优势,在TA2纯钛表面制备载铜生物涂层。研究了镀铜时间和温度对载铜含量及涂层表面形貌、结合力和抗菌性的影响。结果表明:钛基体酸蚀获得表面腐蚀均匀的微纳米结构,为超声微弧氧化提供了更多的氧化物生长空间;钛超声微弧氧化涂层碱处理使陶瓷层Ti O2活化,并利于载铜;利用多孔涂层进行化学镀铜时,涂层中铜元素含量随化学镀铜温度的升高和时间增长而增大,而涂层结合力随着化学镀铜时间增长而下降;50℃下化学镀铜3 min时,涂层抗菌率为98.3%,表面铜含量适宜,载铜破坏生物膜的形成使细菌黏附的微环境发生改变,造成细菌难以正常生长,实现了抗菌效果。     

细胞培养法评价铁铬钼软磁合金的生物相容性

为检测口腔中所用铁铬钼软磁合金的细胞毒性,以评价其生物相容性,将材料浸提液用于体外细胞培养,进行四唑盐(MTT)比色实验来评价材料的细胞毒性。结果表明,软磁合金的细胞毒性级为Ⅰ级,纯钛的毒性为0级。软磁合金组对细胞增殖的抑制作用大于纯钛组,但统计学分析结果显示,两种金属材料组与阴性对照组吸光度值之间的差异均无统计学意义(P>0.05)。软磁合金仅具有极微弱的细胞毒性,符合临床应用的要求,为其在义齿磁性固位体中的应用提供了生物学依据。     

钛过镀层对类金刚石薄膜的膜基结合力以及摩擦学性能的影响

采用双弧磁过滤真空弧源,在钴铬合金基体上成功地沉积了Ti/DLC多层膜,其钛过渡层利用不同的负偏压来制备.利用纳米划痕法来评价薄膜的膜基结合力,类金刚石薄膜的摩擦性能在销盘式摩擦磨损试验机进行测试.划痕法的结果均表明,增加钛的过镀层后薄膜的结合状况得到明显的改善,纳米划痕法测试膜基结合力表明其临界载荷可达到740mN,摩擦磨损实验可以看出镀膜后的样品的摩擦系数均在0.1左右,DLC薄膜可极大地改善钴铬合金的摩擦学性能.     

金刚石磨粒表面镀覆

金刚石磨粒表面镀覆是一项新型的表面技术.用镀后的磨粒做成制品时,能够改善磨粒与金属结合剂的粘结性能,大大提高制品的结合强度,延长金刚石制品的使用寿命.由于磨粒镀覆易行,使用效果好,故越来越被广泛应用.2 镀覆的方法金刚石单晶颗粒表面镀覆金属的方法有多种,如真空蒸发镀、等离子体气相相沉积,但通常采用化学镀.镀覆的金属有铜、镍和钛等.这几种金属是目前工业生产最常用的.并由单金属镀覆发展到多元金属镀覆,如镀锡-镍、钛-镍等.2.1 磨粒表面化学镀覆工艺     

纳米复合电镀的研究现状

纳米复合电镀是一种利用电化学原理制备具有某些特殊性能镀层的复合表面处理技术。首先介绍了纳米材料的特点和几种典型的纳米复合镀层形成机理,以及纳米颗粒的分散方法和对复合电镀的影响。其后重点综述了纳米复合电镀的最新研究状况及应用情况,概括了纳米复合电镀在现阶段面临的一些主要问题。     

纳米复合镀技术在注塑模具腔体表面处理中的应用

简要介绍了在传统复合镀技术基础上发展起来的纳米复合镀技术,其应用于注塑模具腔体表面处理的研究刚刚起步,将其与普通镍电刷镀技术相比较,叙述了注塑模具腔体表面实现纳米化的基本途径,说明了纳米复合电刷镀的优势,即增加镀层厚度与硬度,提高注塑模具腔体表面的耐磨性、耐疲劳性和耐腐蚀性,从而提高注塑模具的使用寿命。     

便携式直流电阻电桥QJ23A检定量程系数比方法探讨

想探讨关于检定便携式直流电阻电桥QJ23A量程系数比M的方法,根据《直流电桥》检定规程所说测量便携式直流电阻电桥的量程系数比要用整体检定法,接入电阻箱进行测量。由于QJ23A的量程倍率为七个固定的比率分别为×0.001,×0.01,×0.1,×1,×10,×100,×1000,均是10的整数次幂由此突发奇想,想用准确度更高的,年稳定性0.0003%的一等标准电阻作为被测接入电桥中测量电桥的量程系数比看看是否可行,将从测量原理,实验方法,及两种实验各种因素所引进的不确定度进行分析,探讨两种方法的区别,最终选择电阻箱法测量。     

燃气轮机叶片表面涂层的质谱分析研究

燃气轮机叶片表面涂层经腐蚀和冲蚀动态实验后，用溅射中性粒子质谱仪对其进行表面元素成分和浓度分布的分析研究，这为涂层的耐磨、耐腐蚀机理的探讨以及涂层质量的比较提供了新的实验依据。     

Association between the Phenotypes and Genotypes of Antimicrobial Resistance in Haemophilus parasuis Isolates from Swine in Quang Binh and Thua Thien Hue Provinces,Vietnam

Haemophilus parasuis (H. parasuis) is one of the bacterial pathogens of great concern as it causes huge economic losses to the swine industry worldwide. One of the reasons why the control of H. parasuis has failed is the increase in antimicrobial resistance (AMR). The country of Vietnam has the second-largest pig production in Asia. However, there is still a lack of data about the AMR prevalence of H. parasuis in Vietnam. The purpose of this study is to investigate the prevalence of AMR and analyze the association between AMR and AMR genes (ARGs). The H. parasuis strains used in this research were isolated from swine in the Quang Binh and Thua Thien Hue Provinces, Central Vietnam, as reported in our previous study. All of the strains were tested for AMR against 25 antibacterial agents using the broth microdilution method and for the presence of ARGs using the polymerase chain reaction (PCR) method. The tested strains were shown to have a high frequency of resistance to trimethoprim/sulfamethoxazole (94.6%), followed by resistance to colistin, chloramphenicol, gentamicin, penicillin, lincomycin, and amoxicillin. The most prevalent ARGs in these strains were bla_TEM-1 (94.6%), int (76.8%), gyrA (58.9%), and rmtD (50.0%). Cefuroxime, chloramphenicol, and tobramycin resistances were strongly correlated with the presence of the ARGs bla_ROB-1 (odds ratio (OR) = 26.3, 95% confidence interval (CI) 2.7–255.7, p = 0.002), catl (OR = 25.1, 95% CI 2.4–258.9, p = 0.004), and strB (OR = 23.5, 95% CI 2.6–212.6, p = 0.001), respectively. This study reveals for the first time the current situation of H. parasuis AMR in Central Vietnam, which is helpful for the clinical control of this disease, as well as for the development of policies and clinical practice guidelines to reduce AMR in swine production in Central Vietnam.     

Cr9Mo和Cr5Mo钢的等温氧化行为

对铸态和锻态的Ｃｒ９Ｍｏ和Ｃｒ５Ｍｏ钢分别在７００℃、８００℃和９００℃下进行了为时５００ｈ的氧化试验。结果表明，在７００℃、８００℃下Ｃｒ９Ｍｏ的抗氧化性能比Ｃｒ５Ｍｏ的优越得多，而在９００℃下则相差不多。两种钢的抗氧化性能的差别主要是其表面氧化物性质不同所致。铸态和锻态抗氧化性能的差别则是由于其合金元素分布的均匀度不同，致使氧化物结构有差异造成的。     

铝及铝合金表面处理研究进展

铝合金耐磨性差、特殊条件下耐蚀性差的缺点限制了它的进一步利用,对铝合金进行表面处理长期以来一直是扩大铝合金使用范围地行之有效的方法.文章综述了铝合金的各种表面处理方法,比较了它们的优缺点,指出表面氧化是铝合金表面处理的主流,复合处理、纳米化处理将是今后铝合金表面处理的主要研究方向.     

Cu-Zr合金基体上的复合镀层的性能研究

利用复合电沉积的方法在Cu-Zr合金基体上沉积出含ZrO2微粒的Ni-ZrO2复合镀层,研究了镀层中的ZrO2微粒含量与镀液中ZrO2微粒含量的关系以及Ni-ZrO2合度层在高温条件下的抗高温氧化笥能和耐腐蚀性能,结果表明：Cu-Zr合金基体上镀覆的Ni-ZrO2复合镀层的抗高温气化性能和耐腐蚀性能得到了很大的提高。     

Impact resistance and fragmentation behaviour of glassceramics

Impact tests were carried out on five glassceramics tiles. The ballistic resistance was evaluated by the depth of penetration of the projectile into the backing. The fragmentation behaviour of the glassceramics showed that the glassceramics compared with with alumina and displayed some advantages over it.     

用溶胶-凝胶法制备保护涂层的研究进展

溶胶-凝胶(Sol-gel)法用于金属及合金表面制备保护涂层可明显提高材料在各种环境下的耐蚀性、抗高温氧化性、耐磨性等性能,从而扩大金属及其合金的应用范围.介绍了Sol-gel涂层的制备技术、涂覆工艺以及涂层热处理的一般原理及特点,总结了该技术制备保护涂层的应用现状及最新研究进展,讨论了制备单组分氧化物涂层如ZrO2涂层、SiO2涂层、CeO2涂层、Al2O3涂层、TiO2涂层,双组分氧化物涂层如ZrO2-CeO2涂层、SiO2-ZrO2涂层以及多组分氧化物涂层的制备方法及涂层对基体材料的保护作用,并对其保护机理进行了初步探讨.