Microstructure and Thermal Properties of Atmospheric Plasma-Sprayed Yb<Subscript>2</Subscript>Si<Subscript>2</Subscript>O<Subscript>7</Subscript> Coating

In the present work, Yb₂Si₂O₇ powder was synthesized by solid-state reaction using Yb₂O₃ and SiO₂ powders as starting materials. Atmospheric plasma spray technique was applied to fabricate Yb₂Si₂O₇ coating. The phase composition and microstructure of the coating were characterized. The density, open porosity and Vickers hardness of the coating were investigated. Its thermal stability was evaluated by thermogravimetry and differential thermal analysis (TG-DTA). The thermal diffusivity and thermal conductivity of the coating were measured. The results showed that the as-sprayed coating was mainly composed of crystalline Yb₂Si₂O₇ with amorphous phase. The coating had a dense structure containing defects, such as pores, interfaces and microcracks. The TG-DTA results showed that there was almost no mass change from room temperature to 1200 °C, while a sharp exothermic peak appeared at around 1038 °C in DTA curve, which indicated that the amorphous phase crystallized. The thermal conductivity of the coating decreased with rise in temperature up to 600 °C and then followed by an increase at higher temperatures. The minimum value of the thermal conductivity of the Yb₂Si₂O₇ coating was about 0.68 W/(m K).     

Microstructure and Thermophysical Properties of SrZrO<Subscript>3</Subscript> Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray

Strontium zirconate (SrZrO₃) thermal barrier coatings were deposited by solution precursor plasma spray (SPPS) using an aqueous precursor solution. The phase transition of the SrZrO₃ coating and the influence of the aging time at 1400 °C on the microstructure, phase stability, thermal expansion coefficient, and thermal conductivity of the coating were investigated. The unique features of SPPS coatings, such as interpass boundary (IPB) structures, nano- and micrometer porosity, and through-thickness vertical cracks, were clearly observed evidently in the coatings. The vertical cracks of the coatings remained substantially unchanged while the IPB structures gradually diminished with prolonged heat treatment time. t-ZrO₂ developed in the coatings transformed completely to m-ZrO₂ phase after heat treatment for 100 h. Meanwhile, the SrZrO₃ phase in the coatings exhibited good phase stability upon heat treatment. Three phase transitions in the SrZrO₃ coatings were revealed by thermal expansion measurements. The thermal conductivity of the as-sprayed SrZrO₃ coating was ~1.25 W m^?1 K^?1 at 1000 °C and remained stable after heat treatment at 1400 °C for 360 h, revealing good sintering resistance.     

Thermal Spray Deposition,Phase Stability and Mechanical Properties of La<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript>/LaAlO<Subscript>3</Subscript> Coatings

This paper deals with the deposition of La₂Zr₂O₇ (LZO) and LaAlO₃ (LAO) mixtures by air plasma spray (APS). The raw material for thermal spray, single phase LZO and LAO in a 70:30 mol.% ratio mixture was prepared from commercial metallic oxides by high-energy ball milling (HEBM) and high-temperature solid-state reaction. The HEBM synthesis route, followed by a spray-drying process, successfully produced spherical agglomerates with adequate size distribution and powder-flow properties for feeding an APS system. The as-sprayed coating consisted mainly of a crystalline LZO matrix and partially crystalline LAO, which resulted from the high cooling rate experienced by the molten particles as they impact the substrate. The coatings were annealed at 1100 °C to promote recrystallization of the LAO phase. The reduced elastic modulus and hardness, measured by nanoindentation, increased from 124.1 to 174.7 GPa and from 11.3 to 14.4 GPa, respectively, after the annealing treatment. These values are higher than those reported for YSZ coatings; however, the fracture toughness (K _IC) of the annealed coating was only 1.04 MPa m^0.5.     

Effects of La<Subscript>2</Subscript>O<Subscript>3</Subscript> on Mechanical Properties and Corrosion Resistance of H62 Brass

In this article, the effects of lanthanum oxide (La₂O₃) on the microstructure and mechanical properties of H62 brass were investigated by using the universal testing machine, Brinell hardness tester, optical microscope, and scanning electron microscope (SEM). Immersion corrosion and electrochemical measurements were carried out to identify the influence of La₂O₃ on the corrosion behavior of the H62 brass. The phase constitution, microstructure, and phase composition of the H62 brass were analyzed by x-ray diffraction, SEM, and energy-dispersive spectrometer, respectively. The results show that the microstructure of α phase changes from dendrite grains to equiaxed grains, and the content and distribution of β phase are improved significantly. When the La₂O₃ content reaches 0.8 wt.%, the H62 brass obtains favorable comprehensive mechanical properties and the strength and hardness decrease but elongation increases, which is conducive to plastic processing. In addition, under the optimum amount of 0.8 wt.% La₂O₃ content, the corrosion rate of immersion corrosion attains the minimum values: As 12.6 g m^?2 h^?1, it decreases by 24%; as the corrosion potential changes from ?1.1327 V to ?0.328 V, it increases by 70.9%; and as the corrosion current density decreases from ?2.833 mA mm^?2 to ?3.28 mA mm^?2 corrosion, it decreases by 15.78%, when compared with H62 brass.     

The Microstructure and Thermoelectric Properties of Yb-Filled Skutterudite Yb<Subscript>0.1</Subscript>Co<Subscript>4</Subscript>Sb<Subscript>12</Subscript> Under Cyclic Thermal Loading

This paper is devoted to investigating the microstructure and thermoelectric properties of Yb-filled skutterudite Yb_0.1Co₄Sb₁₂ under a cyclic thermal loading from room temperature to 773 K. The results indicate after 1000 cycles, the surface morphology changes dramatically, and clear grain boundaries appear on the surface of the sample. The grain sizes of the sample change little after 1000 cycles, and the main phase is still skutterudite; however, a trace amount of YbSb also exists. In addition, the electrical conductivity and thermal conductivity decrease distinctly after 1000 cycles, but the absolute value of the Seebeck coefficient increases a little. Consequently, the ZT value decreases slightly from 0.75 at 800 K before cycling to 0.69 after 1000 cycles. It indicates that the effect of the cyclic thermal loading on the ZT of the Yb_0.1Co₄Sb₁₂ material is not distinct.     

Elevated Temperature Solid Particle Erosion Performance of Plasma-Sprayed Co-based Composite Coatings with Additions of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and CeO<Subscript>2</Subscript>

In this paper, investigation into solid particle erosion behavior of atmospheric plasma-sprayed composite coating of CoCrAlY reinforced with Al₂O₃ and CeO₂ oxides on Superni 76 at elevated temperature of 600 °C is presented. Alumina particles are used as erodent at two impact angles of 30° and 90°. The microstructure, porosity, hardness, toughness and adhesion properties of the as-sprayed coatings are studied. The effects of temperature and phase transformation in the coatings during erosion process are analyzed using XRD and EDS techniques. Optical profilometer is used for accurate elucidation of erosion volume loss. CoCrAlY/CeO₂ coating showed better erosion resistance with a volume loss of about 50% of what was observed in case of CoCrAlY/Al₂O₃/YSZ coating. Lower erosion loss is observed at 90° as compared to 30° impact angle. The erosion mechanism evaluated using SEM micrograph revealed that the coatings experienced ductile fracture exhibiting severe deformation with unusual oxide cracks. Reinforced metal oxides provide shielding effect for erodent impact, enabling better erosion resistance. The oxidation of the coating due to high-temperature exposure reforms erosion process into oxidation-modified erosion process.     

Mechanical Properties of Layered La<Subscript>2</Subscript>Zr<Subscript>2</Subscript>O<Subscript>7</Subscript> Thermal Barrier Coatings

Lanthanum zirconate (La₂Zr₂O₇) has been proposed as a promising thermal barrier coating (TBC) material due to its low thermal conductivity and high stability at high temperatures. In this work, both single and double-ceramic-layer (DCL) TBC systems of La₂Zr₂O₇ and 8 wt.% yttria-stabilized zirconia (8YSZ) were prepared using air plasma spray (APS) technique. The thermomechanical properties and microstructure were investigated. Thermal gradient mechanical fatigue (TGMF) tests were applied to investigate the thermal cycling performance. The results showed that DCL La₂Zr₂O₇ + 8YSZ TBC samples lasted fewer cycles compared with single-layered 8YSZ TBC samples in TGMF tests. This is because DCL La₂Zr₂O₇ TBC samples had higher residual stress during the thermal cycling process, and their fracture toughness was lower than that of 8YSZ. Bond strength test results showed that 8YSZ TBC samples had higher bond strength compared with La₂Zr₂O₇. The erosion rate of La₂Zr₂O₇ TBC samples was higher than that of 8YSZ samples, due to the lower critical erodent velocity and fracture toughness of La₂Zr₂O₇. DCL porous 8YSZ + La₂Zr₂O₇ had a lower erosion rate than other SCL and DCL La₂Zr₂O₇ coatings, suggesting that porous 8YSZ serves as a stress-relief buffer layer.     

Effects of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Nano-Particles on Corrosion Performance of Plasma Electrolytic Oxidation Coatings Formed on 6061 Aluminum Alloy

Corrosion resistance improvement of plasma electrolyte oxidation coatings on 6061 aluminum alloy in silicate electrolyte containing Al₂O₃ nano-particles was studied, with particular emphasis on the microstructure, coating growth, and corrosion behavior in 3.5 wt.% NaCl solution. The microstructure of coatings, their thickness, and phase composition were characterized using scanning electron microscopy and x-ray diffraction. All characterization data showed that the maximum coating thickness and lowest amount of porosity were obtained in a low concentration of KOH, a high concentration of Na₂SiO₃, and moderate concentration of Al₂O₃ nano-particles in the electrolyte. This combination describes the optimum plasma electrolytic oxidation electrolyte, which has the best conductivity and oxidizing state, as well as the highest incorporation of electrolyte components in the coating growth process. On the other hand, incorporation and co-deposition of Al₂O₃ nano-particles were more pronounced than SiO₃ ^2? ions in some level of molar concentration, which is due to the higher impact of electron discharge force on the adsorption of Al₂O₃ nano-particles. The electrochemical results showed that the best protective behavior was obtained in the sample having a coat with the lowest porosity and highest thickness.     

Formation of Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> Diffusion Barrier Between Cr-Contained Stainless Steel and Cold-Sprayed Ni Coatings at High Temperature

A novel approach to prepare a coating system containing an in situ grown Cr₂O₃ diffusion barrier between a nickel top layer and 310SS was reported. Cold spraying was employed to deposit Ni(O) interlayer and top nickel coating on the Cr-contained stainless steel substrate. Ni(O) feedstock was prepared by mechanical alloying of pure nickel powders in ambient atmosphere, acting as an oxygen provider. The post-spray annealing was adopted to grow in situ Cr₂O₃ layer between the substrate and nickel coating. The results revealed that the diffusible oxygen can be introduced into nickel powders by mechanical alloying. The oxygen content increases to 3.25 wt.% with the increase of the ball milling duration to 8 h, while Ni(O) powders maintain a single phase of Ni. By annealing the sample in Ar atmosphere at 900 °C, a continuous Cr₂O₃ layer of 1-2 μm thick at the interface between 310SS and cold-sprayed Ni coating is formed. The diffusion barrier effect evaluation by thermal exposure at 750 °C shows that the Cr₂O₃ oxide layer effectively suppresses the outward diffusion of Fe and Cr in the substrate effectively.     

Preparation of SrZrO<Subscript>3</Subscript> Thermal Barrier Coating by Solution Precursor Plasma Spray

The solution precursor plasma spray (SPPS) process is capable of depositing highly durable thermal barrier coatings (TBCs). In this study, an aqueous chemical precursor feedstock was injected into the plasma jet to deposit SrZrO₃ thermal barrier coating on metal substrate. Taguchi design of experiments was employed to optimize the SPPS process. The thermal characteristics and phase evolution of the SrZrO₃ precursor, as well as the influence of various spray parameters on the coating deposition rate, microhardness, microstructure, and phase stability, were investigated. The experimental results showed that, at given spray distance, feedstock flow rate, and atomization pressure, the optimized spray parameters were arc current of 600 A, argon flow rate of 40 L/min, and hydrogen flow rate of 10 L/min. The SrZrO₃ coating prepared using the optimized spray parameters had single-pass thickness of 6.0 μm, porosity of ~18%, and microhardness of 6.8 ± 0.1 GPa. Phase stability studies indicated that the as-sprayed SrZrO₃ coating had good phase stability in the temperature range from room temperature to 1400 °C, gradually exhibiting a phase transition from t′-ZrO₂ to m-ZrO₂ in the SrZrO₃ coating at 1450 °C with increasing time, while the SrZrO₃ phase did not change.     

Investigation on the Phase Diagram of LiCl-KCl-NdCl<Subscript>3</Subscript> Pseudo-Ternary System

The ternary phase diagram of LiCl-KCl-NdCl₃ system has been investigated by differential thermal analysis (DTA), followed by characterization of the coexisting phases in the solid state by x-ray diffraction, in order to understand the interactions in the NdCl₃-LiCl-KCl ternary system. The results of these experiments showed that LiCl and K₂NdCl₅ form a non binary join section. This divides the LiCl-KCl-NdCl₃ system into two quasi-ternary sections, namely (1) LiCl-KCl-K₂NdCl₅ and (2) LiCl-K₂NdCl₅-NdCl₃ systems. Both are simple eutectic ternary phase diagrams. The ternary eutectic temperatures and eutectic compositions are determined to be 316?±?3 °C and 53.9 mol.% LiCl-38.7 mol.% KCl-7.4 mol.% K₂NdCl₅ in the LiCl-KCl-K₂NdCl₅ quasi-ternary section, while the other eutectic temperature and composition are determined to be 376?±?9 °C and 46.2 mol.% LiCl-32.5 mol.% K₂NdCl₅-21.3 mol.% NdCl₃ in the LiCl-K₂NdCl₅-NdCl₃ quasi-ternary section. A quasi-ternary peritectic reaction is observed at 37.7 mol.% LiCl-36.2 mol.% KCl-26.1 mol.% K₂NdCl₅ at 445?±?1°C. The primary and secondary crystallization temperatures for the samples are deduced from the heating runs of DTA traces, and the phases responsible for the various thermal events are ascertained. Isothermal sections at chosen temperatures and polythermal liquidus projection with isothermal contours are drawn over the ternary phase field.     

Phase Formation of the Yttrium Aluminates in the Y<Subscript>2</Subscript>O<Subscript>3</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiC System

Phase formation sequence of the yttrium aluminates in the Y₂O₃-Al₂O₃-SiC ternary system as temperature increases were investigated via x-ray diffraction (XRD). Results showed that YAM (monoclinic), YAP (perovskite) and YAG (garnet) were the yttrium aluminates presented in the solid-state reacted samples at a fixed Al₂O₃:SiC ratio of 1:1. Formation of the yttrium aluminates depended on the temperature. The YAM, YAP and YAG started to form below 1150 °C, at 1300 °C, and at 1450 °C, respectively. Accordingly, two behavior phase diagrams of the Y₂O₃-Al₂O₃-SiC ternary system were recognized, one is in the temperature range of 1150-1300 °C and the other is in 1300-1450 °C, respectively. Thereafter, the phase equilibrium was reached in the temperature range of 1450-1700 °C. Effects of SiC on the phase formation processes in the ternary system were discussed.     

Tribocorrosion Behavior of Fe-Based Amorphous Composite Coating Reinforced by Al<Subscript>2</Subscript>O<Subscript>3</Subscript> in 3.5% NaCl Solution

Although corrosion and friction/wear behavior of Fe-based amorphous coatings and their composites has been extensively studied during the past decade, there is very limited work related to tribocorrosion behavior. In this paper, the tribocorrosion behavior of a Fe-based amorphous composite coating reinforced with 20 wt.% Al₂O₃ particles was investigated in a 3.5% NaCl solution on a ball-on-disk tester and was compared to the monolithic amorphous coating and 316L stainless steel (SS). The results showed that the amorphous composite coating exhibited the highest tribocorrosion resistance among the three materials tested, as evidenced by the lowest coefficient of friction (~0.3) and tribocorrosion wear rate (~1.2 × 10^?5 mm³/N·m). In addition, potentiodynamic polarization measurements before and during tribocorrosion testing demonstrated that corrosion resistance of the amorphous composite coating was not influenced so much by mechanical loading compared to the amorphous coating and the 316L SS. Observations on the worn surface revealed a corrosion-wear- and oxidational-wear-dominated tribocorrosion mechanism for the composite coatings. The excellent tribocorrosion resistance of the composite coating results from the effect of chemically stable Al₂O₃ phase which resists oxidation and delamination during sliding, along with poor wettability with corrosive NaCl droplets.     

Corrosion Behavior and Microhardness of Ni-P-SiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Nano-composite Coatings on Magnesium Alloy

In the present work, nano-composites of Ni-P-SiO₂-Al₂O₃ were coated on AZ91HP magnesium alloy. The surface morphology of the nano-composite coating was studied by field emission scanning electron microscopy (FESEM). The amount of SiO₂ in the coating was determined by energy-dispersive analysis of x-ray (EDX), and the crystalline structure of the coating was examined by x-ray diffractometer (XRD). All the experiments concerning the corrosion behavior of the coating carried out in 3.5 wt.% NaCl solution and evaluated by electrochemical impedance spectroscopy (EIS) and polarization technique. The results showed that an incorporation of SiO₂ and Al₂O₃ in Ni-P coating at the SiO₂ concentration of 10 g/Land 14 g/LAl₂O₃ led to the lowest corrosion rate (i _corr = 1.3 µA/cm²), the most positive E _corr and maximum microhardness (496 VH). Furthermore, Ni-P-SiO₂-Al₂O₃ nano-composite coating possesses less porosity than that in Ni-P coating, resulting in improving corrosion resistance.     

Hydrogen storage properties of as-cast and annealed low-Co La<Subscript>1.8</Subscript>Ti<Subscript>0.2</Subscript>MgNi<Subscript>8.9</Subscript>Co<Subscript>0.1</Subscript> alloys

Low-Co La_1.8Ti_0.2MgNi_8.9Co_0.1 alloys were prepared by magnetic levitation melting followed by annealing treatment. The effect of annealing on the hydrogen storage properties of the alloys was investigated systematically by X-ray diffraction (XRD), pressure-composition isotherm (PCI), and electrochemical measurements. The results show that all samples contain LaNi₅ and LaMg₂Ni₉ phases. LaCo₅ phase appears at 1,000 °C. The enthalpy change of all hydrides is close to ?30.6 kJ·mol^?1 H₂ of LaNi₅ compound. Annealing not only increases hydrogen capacity and improves cycling stability but also decreases plateau pressure at 800 and 900 °C. After annealing, the contraction of cell volume and the increase of hydride stability cause the high rate dischargeability to reduce slightly. The optimum alloy is found to be one annealed at 900 °C, with its hydrogen capacity reaching up to 1.53 wt%, and discharge capacity remaining 225.1 mAh·g^?1 after 140 charge–discharge cycles.     

The Effects of KCl,NaCl and K<Subscript>2</Subscript>CO<Subscript>3</Subscript> on the High-Temperature Oxidation Onset of Sanicro 28 Steel

The present study investigates the early stages in the oxidation process of Sanicro 28 (Fe31Cr27Ni) stainless steel when exposed to an alkali salt (KCl, NaCl or K₂CO₃) for 2 h at 450 and 535 °C. After the exposure, the oxidized samples were analyzed with a combinatory method (CA, XPS and SEM–EDX). It was found that all three salts were corrosive, and the overall oxidation reaction rate was much higher at 535 °C than at 450 °C. There were clear differences in terms of the impact of cations (Na⁺, K⁺) and anions (Cl^?, CO₃ ^2?) on the initial corrosion process at both temperatures. When focusing on the cations, the presence of potassium ions resulted in a higher rate of chromate formation than in the presence of sodium ions. When studying the effect of anions, the oxidation of iron and chromium occurred at higher rates in the presence of both chloride salts than in the presence of the carbonate salt, and chloride salts seemed to possess higher diffusion rate in the gas phase and along the surface than carbonate salts. Moreover, at the higher temperature of 535 °C, the formed chromate reacted further to chromium oxide, and an ongoing oxidation process of iron and chromium was identified with a significantly higher reaction rate than at 450 °C.     

Microstructure and Physical Properties of Tb<Subscript>2</Subscript>TiO<Subscript>5</Subscript> Neutron Absorber Synthesized by Ball Milling and Sintering

Tb₂TiO₅ neutron absorber was synthesized by ball milling and sintering. Microstructure character of ball-milled Tb₄O₇-17.605%TiO₂ (mass fraction, %) powders and sintered bulks was analyzed using XRD, SEM and TEM. The microhardness, coefficient of thermal expansion and thermal conductivity of sintered bulks were measured. The experiment results showed that the nanocrystalline solid solution was obtained during ball milling. After 96 h of ball milling, TiO₂ was completely solved in Tb₄O₇ and the crystal size of Tb₄O₇ was up to 37 nm. The bulk materials prepared by cold isostatic pressing were sintered at 1300 °C. Tb₂TiO₅ bulks with an orthorhombic structure were obtained. The microhardness of sintered bulks, as well as the thermal conductivity, increased firstly with increasing ball milling time and then decreased. The coefficient of thermal expansion decreased initially and then increased with increasing ball milling time. For the sintered bulk with powder milled for 48 h, the highest values of both microhardness and thermal conductivity were observed, whereas the lowest coefficient of thermal expansion was exhibited. In addition, with increasing testing temperature, the thermal conductivity of sintered bulks initially fell and then rebounded while an opposite trend was found in the coefficient of thermal expansion.     

Oxidation Behavior of TiAl<Subscript>3</Subscript>/Al Composite Coating on Orthorhombic-Ti<Subscript>2</Subscript>AlNb Based Alloy at Different Temperatures

This paper reports the oxidation behavior of TiAl₃/Al composite coating deposited by cold spray. The substrate alloy was orthorhombic-Ti-22Al-26Nb (at.%). The oxidation kinetics of the coating was tested at 650, 800, and 950 °C, respectively. The parabolic rate constant for the coating oxidized at 650 °C was k _p = 7.2 × 10⁻² mg·cm⁻²·h^−1/2 for the tested 1200 h. For the coating oxidized at 800 °C, the oxidation kinetics could be separated into two stages with k _p value of 39.8 × 10⁻² mg·cm⁻²·h^−1/2 for the initial 910 h and 17.7 × 10⁻² mg·cm⁻²·h^−1/2 for the stage thereafter. For the coating oxidized at 950 °C, the oxidation kinetics can be separated into three stages with k _p of 136.9 × 10⁻² mg·cm⁻²·h^−1/2 in the first 100 h, followed by 26.9 × 10⁻² mg·cm⁻²·h^−1/2 from 100 to 310 h, and 11.8 × 10⁻² mg·cm⁻²·h^−1/2 from 310 to 1098 h. XRD, SEM, and EPMA were used to study the microstructure of the coating. The results indicated that the oxidation took place throughout the entire coating instead of only at the surface. The aluminum phase in the composite coating was soon oxidized to Al₂O₃ in all tested cases. The aluminum in TiAl₃ phase was depleted gradually and oxidized to Al₂O₃ along with the degradation of TiAl₃ to TiAl₂ and TiAl as the temperature increased and time proceeded. AlTi₂N was also a typical oxidation product at temperature higher than 800 °C. The experimental results also indicated that the protection of the coating was attributed greatly to the interlayer formed between the coating and the substrate.     

Y2O3 and Yb2O3 Co-doped Strontium Hafnate as a New Thermal Barrier Coating Material

Y₂O₃ and Yb₂O₃ co-doped strontium hafnate powder with chemistry of Sr(Hf_0.9Y_0.05Yb_0.05)O_2.95 (SHYY) was synthesized by a solid-state reaction at 1450 °C. The SHYY showed good phase stability not only from 200 to 1400 °C but also at a high temperature of 1450 °C for a long period, analyzed by differential scanning calorimetry and x-ray diffraction, respectively. The coefficient of thermal expansion of the sintered bulk SHYY was recorded by a high-temperature dilatometer and revealed a positive influence on phase transitions of SrHfO₃ by co-doping with Y₂O₃ and Yb₂O₃. The thermal conductivity of the bulk SHYY was approximately 16% lower in contrast to that of SrHfO₃ at 1000 °C. Good chemical compatibility was observed for SHYY with 8YSZ or Al₂O₃ powders after a 24 h heat treatment at 1250 °C. The phase stability and the microstructure evolution of the as-sprayed SHYY coating during annealing at 1400 °C were also investigated.     

Effect of Microstructure on the Thermal Conductivity of Plasma-Sprayed Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-YSZ Coatings

The microstructures of three atmospheric plasma-sprayed (APS) Al₂O₃-ZrO₂ coatings were investigated using x-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The differences in the microstructures of the three Al₂O₃-ZrO₂ coatings, including their phase compositions, cracks, pores, grain sizes, and solid solutions, were analyzed in detail. A close relationship was observed between the thermal conductivities of the coatings and the microstructures, and the Al₂O₃-YSZ coatings with more spherical pores, fewer vertical cracks, and finer grains exhibited the lowest thermal conductivity of 0.91 W/m·K. Compared with YSZ coatings, Al₂O₃-YSZ coatings can exhibit lower thermal conductivity, which may be attributed to the formation of an amorphous phase, smaller grains, and Al₂O₃-YSZ solid solution.