Synthesis, low-temperature sintering and the dielectric properties of the ZnO-(1 − x)TiO2-xSnO2 (x = 0.04-0.2)

ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) ceramics were prepared by conventional mixed-oxide method combined with a chemical processing. Fine particle powders were prepared by chemical processing to activate the formation of compound and to improve the sinterability. One wt.% of V₂O₅ and B₂O₃ with the mole ratios of 3:1 were used to lower the sintering temperature of ceramics. The effect of Sn content on phase structure and dielectric properties were investigated. The results show that the substituting Sn for Ti accelerates the hexagonal phase transition to cubic phase, and an inverse spinel structure Zn₂(Ti_1−xSn_x)O₄ solid solution forms. The best dielectric properties obtained at x = 0.12. The ZnO-0.88TiO₂-0.12SnO₂ ceramics sintered at 900 °C exhibit a good dielectric property: ?_r = 29 and tan δ = 9.86 × 10⁻⁵. Due to their good dielectric properties, low firing characteristics, ZnO-(1 − x)TiO₂-xSnO₂ (x = 0.04-0.2) can serve as the promising microwave dielectric capacitor.     

Heterophase structures and their quantitative characteristics in (1 − x)Pb(Fe1/2Nb1/2)O3 − xPbTiO3 near the morphotropic phase boundary

Features of phase coexistence in solid solutions of (1 − x)Pb(Fe_1/2Nb_1/2)O₃ − xPbTiO₃ with the perovskite-type structure are studied at 0.05 ≤ x ≤ 0.08. The role of elastic matching of the tetragonal P4mm and monoclinic Cm phases of the ferroelectric nature is considered near the morphotropic phase boundary. Model concepts on the stress relief in heterophase structures are developed and applied to interpret the phase content in (1 − x)Pb(Fe_1/2Nb_1/2)O₃ − xPbTiO₃. Good agreement between the calculated and experimental dependences of the volume fraction of the tetragonal phase on x is observed. It is shown that the studied phase coexistence under conditions for the complete stress relief can take place at elastic matching of the single-domain monoclinic phase and the tetragonal phase split into two types of 90° domains.     

Synthesis of nanocrystalline xCuFe2O4-(1 − x)BiFeO3 magnetoelectric composite by chemical method

xCuFe₂O₄-(1 − x)BiFeO₃ spinel-perovskite nanocomposites with x = 0.1, 0.2, 0.3 and 0.4 were prepared using citrate precursor method. X-ray diffraction (XRD) analysis showed phase formation of xCuFe₂O₄-(1 − x)BiFeO₃ calcined at 500 °C. Transmission electron microscopy (TEM) shows formation of nanocrystallites of xCuFe₂O₄-(1 − x)BiFeO₃ with an average particle size of 40 nm. Variation of dielectric constant and dielectric loss with frequency showed dispersion in the low frequency range. Coercivity, saturation magnetization and squareness have been found to vary with concentration of ferrite phase and annealing temperature due to the increase in crystallite size. Squareness and coercivity increased with an increase in annealing temperature up to 500 °C and then decreased with a further increase in temperature to 600 °C. Magnetoelectric effect of the nanocomposites was found to be strongly depending on the magnetic bias and magnetic field frequency.     

Structural, magnetic and dielectric properties of Bi1−ySryFe(1−y)(1−x)Sc(1−y)xTiyO3 (x = 0-0.2, y = 0.1-0.3) ceramics

In this study, bulk ceramics with general formula Bi_1−ySr_yFe_{(1−y)(1−x)}Sc_(1−y)xTi_yO₃ (x = 0-0.2, y = 0.1-0.3 mol%) were prepared by traditional solid-state reaction method. As a comparison, bulk BiFeO₃ (BF) was also sintered by rapid sintering method. Their structural, magnetic, dielectric properties were investigated. X-ray diffraction analysis indicated that apart from a small amount of secondary phase detected in BF, all other samples crystallized in pure perovskite structure and maintained original R3c space group. The room temperature M-H curves were obtained. While BF had a coercive magnetic field (H_c) of 150 Oe, Bi_1−ySr_yFe_1−yTi_yO₃ solid solutions had a much larger value (for y = 0.1, 0.2, 0.3, H_c were 4537, 5230 and 3578 Oe, respectively). Sc³⁺ substitution decreased the H_c values of these solid solutions remarkably, and resulted in soft magnetic properties, as well as a decrease of the dielectric loss. At 1 MHz, the tan δ of Bi_0.7Sr_0.3Fe_0.7(1−x)Sc_0.7xTi_0.3O₃ with x = 0.05, 0.1, 0.15, 0.2 were 0.1545, 0.1078, 0.1046 and 0.1701, respectively.     

(5 − x)BaO-xMgO-2Nb2O5 ceramics prepared using a reaction-sintering process

(5 − x)BaO-xMgO-2Nb₂O₅ (x = 0.5 and 1; 5MBN and 10MBN) microwave ceramics prepared using a reaction-sintering process were investigated. Without any calcinations involved, the mixture of BaCO₃, MgO, and Nb₂O₅ was pressed and sintered directly. MBN ceramics were produced after 2-6 h of sintering at 1350-1500 °C. The formation of (BaMg)₅Nb₄O₁₅ was a major phase in producing 5MBN ceramics, and the formation of Ba(Mg_1/3Nb_2/3)O₃ was a major phase in producing 10MBN ceramics. As CuO (1 wt%) was added, the sintering temperature dropped by more than 150 °C. We produced 5MBN ceramics with these dielectric properties: ?_r = 36.69, Qf = 20,097 GHz, and τ_f = 61.1 ppm/°C, and 10MBN ceramics with these dielectric properties: ?_r = 39.2, Qf = 43,878 GHz, and τ_f = 37.6 ppm/°C. The reaction-sintering process is a simple and effective method for producing (5 − x)BaO-xMgO-2Nb₂O₅ ceramics for applications in microwave dielectric resonators.     

Electrochemical behaviors of Li[Li(1−x)/3Mn(2−x)/3Nix/3Cox/3]O2 cathode series (0 < x < 1) synthesized by sucrose combustion process for high capacity lithium ion batteries

A mixed cathode material between Li₂MnO₃ and Li[Mn_1/3Ni_1/3Co_1/3]O₂ for high capacity lithium secondary batteries was introduced in this study. It was prepared using the sucrose combustion process because this is a simple process. The oxidation states of Mn, Co and Ni ions in the pristine Li[Li_(1−x)/3Mn_(2−x)/3Ni_x/3Co_x/3]O₂ compounds were confirmed to be tetravalent, trivalent and divalent, respectively, via XANES measurements. Electrochemical charge/discharge studies showed that the highest first discharge capacity of 224 mAh/g was obtained in composition of x = 0.5 at a 0.2 C rate. The oxidation state of the Co and Ni ions in the Li[Li_1/6Mn_1/2Ni_1/6Co_1/6]O₂ changed to higher oxidation states, but that of the Mn ions did not change.     

Morphotropic phase boundary in high temperature ferroelectric xBi(Zn1/2Ti1/2)O3 − yPbZrO3 − zPbTiO3 perovskite ternary solid solution

A bismuth and lead oxide based perovskite ternary solid solution xBi(Zn_1/2Ti_1/2)O₃ − yPbZrO₃ − zPbTiO₃ (xBZT − yPZ − zPT) was investigated as an attempt to develop a high T_C ferroelectric material for piezoelectric sensor and actuator applications. A morphotropic phase boundary (MPB) between rhombohedral and tetragonal phases was determined through an XRD study on a pseudobinary line 0.1BZT − 0.9[xPT − (1 − x)PZ] for composition 0.1Bi(Zn_1/2Ti_1/2)O₃ − 0.5PbZrO₃ − 0.4PbTiO₃. Enhanced piezoelectric and ferroelectric activities were observed for MPB composition with dielectric constant ε_r′ ~ 23,000 at Curie temperature (T_C) ≈ 320 °C, remanent polarization (P_r) = 35 μC/cm², piezoelectric coefficient (d₃₃) = 300 pC/N, unipolar strain = 0.15%, and electromechanical coupling coefficient (k_P) = 0.45.     

Eu-Mössbauer spectroscopic and X-ray diffraction study on EuyM1−yO2−x (0 ≤ y ≤ 1.0) (M = Th, U)

¹⁵¹Eu-Mössbauer spectroscopic and powder X-ray diffraction (XRD) study has been performed for the Eu_yM_1−yO_2−x (M = Th and U) systems over the entire composition range of 0 ≤ y ≤ 1.0. The XRD results of the Eu-Th system showed that a very wide defect-fluorite (DF) type phase in which oxygen vacancies (V_O) are disordered (x = y/2) is formed for 0 ≤ y < 0.5 and that two-phase regions sandwitching a narrow C-type (C) single phase around y ≈ 0.8 appear for 0.5 < y < 0.8 (DF + C) and 0.82 < y < 1.0 (C + B-type (monoclinic) Eu₂O₃). The Mössbauer results show that the isomer shifts (ISs) of Eu³⁺ in this system smoothly increase with Eu composition, y. The decrease of average coordination number (CN) of O²⁻ around Eu³⁺ with increasing y (CN = 8 − 2y) (x = y/2) results in the decrease of the average EuO bond length, which is due to the decrease of repulsion force between O²⁻ anions. This result confirms that the IS of Eu³⁺ correlates well with the average EuO bond length in oxide systems. For the Eu-U system, the lattice parameter, a₀, of the system decreases almost linearly with y, in accordance with the calculated a₀ versus y curve for the oxygen-stoichiometric (i.e. x = 0) fluorite-type dioxide (CN = 8). The ISs of Eu³⁺ in this composition range remain almost constant around 0.5 mm/s, which is comparable to those of pyrochlore oxides (Eu₂Zr₂O₇ and Eu₂Hf₂O₇ (y = 0.5)) with O²⁻-eight-fold coordinated Eu³⁺(CN = 8).     

Microstructure and microwave dielectric characteristics of (1 − x)Ba(Zn1/3Ta2/3)O3-xBaTi4O9 ceramics

(1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ (0.1 ≤ x ≤ 0.85) composites are prepared by mixing 1150 °C-calcined BaTi₄O₉ with 1150 °C-calcined Ba(Zn_1/3Ta_2/3)O₃ powders. The crystal structure, microwave dielectric properties and sinterabilites of the (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics have been investigated. X-ray diffraction patterns reveal that BaTi₄O₉, ordered and disordered Ba(Zn_1/3Ta_2/3)O₃ phases exist independently over the whole compositional range. The sintering temperatures of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics are about 1240 - 1320 °C and obviously lower than those of Ba(Zn_1/3Ta_2/3)O₃ ceramics. The dielectric constants (?_r) and the temperature coefficient of resonant frequency (τ_f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of BaTi₄O₉ content. Nevertheless, the bulk densities and the quality values (Q × f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of Ba(Zn_1/3Ta_2/3)O₃ content. The results are attributed to the higher density and quality value of Ba(Zn_1/3Ta_2/3)O₃ ceramics, the better grain growth, and the densification of sintered specimens added a small BaTi₄O₉ content. The (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramic with x = 0.1 sintered at 1320 °C exhibits a ?_r value of 31.5, a maximum Q × f value of 68500 GHz and a minimum τ_f value of 4.1 ppm/°C.     

Synthesis and electrochemical properties of Ti doped Li3 − xFe2 − xTix(PO4)3/C cathode materials

Li_3 − xFe_2 − xTi_x(PO₄)₃/C (x = 0-0.4) cathodes designed with Fe doped by Ti was studied. Both Li₃Fe₂(PO₄)₃/C (x = 0) and Li_2.8Fe_1.8Ti_0.2(PO₄)₃/C (x = 0.2) possess two plateau potentials of Fe³⁺/Fe²⁺ couple (around 2.8 V and 2.7 V vs. Li⁺/Li) upon discharge observed from galvanostatic charge/discharge and cyclic voltammetry. Li_2.8Fe_1.8Ti_0.2(PO₄)₃/C has higher reversibility and better capacity retention than that of the undoped Li₃Fe₂(PO₄)₃/C. A much higher specific capacity of 122.3 mAh/g was obtained at C/20 in the first cycle, approaching the theoretical capacity of 128 mAh/g, and a capacity of 100.1 mAh/g was held at C/2 after the 20th cycle.     

Synthesis of perovskite-type (La1−xCax)FeO3 (0 ≤ x ≤ 0.2) at low temperature

Gel formation was realized by adding citric acid to a solution of La(NO₃)₃·5H₂O, Ca(NO₃)₂·4H₂O, and Fe(NO₃)₂·9H₂O. Perovskite-type (La_1−xCa_x)FeO₃ (0 ≤ x ≤ 0.2) was synthesized by firing the gel at 500 °C in air for 1 h. The crystallite size (D_1 2 1) decreased with increasing x, while the specific surface area was 6.8-9.4 m²/g and independent of x. The XPS measurement of the (La_1−xCa_x)FeO₃ surface indicated that the Ca²⁺ ion content increased with increasing x, while the Fe ion content was independent of x. Catalytic activity for CO oxidation increased with increasing x.     

Solution calorimetric study of mixing enthalpy in 0.8[xB2O3-(1 − x)SiO2]-0.2K2O glasses at 298 K

The mixing enthalpies in the 0.8[xB₂O₃-(1 − x)SiO₂]-0.2K₂O glassy system with 0 ≤ x ≤ 1 have been deduced from accurate calorimetric measurements of solution enthalpies in acidic solvent at 298 K. The substitution of SiO₂ by B₂O₃ corresponds to a negative enthalpic effect and suggests the absence of some glassy miscibility gap. The mixing enthalpies are of the same order of magnitude as mixing enthalpies usually found in molten salts.     

(1 − x)PNZ-xBT ceramics derived from mechanochemically synthesized powders

Nanosized (1−x)Pb(Zn_1/3Nb_2/3)O₃-xBaTiO₃ (PZN-BT, x=0.05, 0.10, 0.15, 0.20, 0.25, and 0.30) powders were synthesized directly from their corresponding oxide mixture via a high-energy ball milling process. Almost single phase was achieved in the composition range of PZN-BT. The grain size estimated from SEM observation was about 50 nm, being in good agreement with that (20 nm) calculated from XRD patterns. PZN-BT ceramics were also obtained by sintering the synthesized powders at 1050°C for 1 h. The grain size of the final ceramics decreases from 4.5 to 1.2 μm as BT content increases from 0.05 to 0.30. The properties, such as microstructure, lattice constant, phase composition, dielectric constant as a function of composition of the PZN-BT ceramics, were investigated and discussed.     

Order-disorder phase transitions and high-temperature oxide ion conductivity of Er2+xTi2−xO7−δ (x = 0, 0.096)

The Er_2+xTi_2−xO_7−δ (x = 0.096; 35.5 mol% Er₂O₃) solid solution and the stoichiometric pyrochlore-structured compound Er₂Ti₂O₇ (x = 0; 33.3 mol% Er₂O₃) are characterized by X-ray diffraction (phase analysis and Rietveld method), thermal analysis and optical spectroscopy. Both oxides were synthesized by thermal sintering of co-precipitated powders. The synthesis study was performed in the temperature range 650-1690 °C. The amorphous phase exists below 700 °C. The crystallization of the ordered pyrochlore phase (P) in the range 800-1000 °C is accompanied by oxygen release. The ordered pyrochlore phase (P) exists in the range 1000−1200 °C. Heat-treatment at T ≥ 1600 °C leads to the formation of an oxide ion-conducting phase with a distorted pyrochlore structure (P2) and an ionic conductivity of about 10⁻³ S/cm at 740 °C. Complex impedance spectra are used to separately assess the bulk and grain-boundary conductivity of the samples. At 700 °C and oxygen pressures above 10⁻¹⁰ Pa, the Er_2+xTi_2−xO_7−δ (x = 0, 0.096) samples are purely ionic conductors.     

Structural and electrical properties of La2−xBaxMo2O9−x/2 (x = 0-0.18)

La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) have been prepared by solid state reaction method. The lattice parameter of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) determined by XRD data refinement shows a linear dependence on the dopant Ba content x. For the specimen with a La/Ba molar ratio of 0.18-0.2, additional reflection of secondary phase exists in the XRD pattern, so the value of solubility limit for Ba in La₂Mo₂O₉ is defined in range of 0.18 < x < 0.2. As the replacement degree of La³⁺ by Ba²⁺ increases, the bulk conductivity of La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) decreases initially and then increases, a minimum value at La_1.9Ba_0.1Mo₂O_8.95 exists. Hebb-Wagner studies in argon atmosphere, which use an oxide-ion blocking electrode, show that La_2−xBa_xMo₂O_9−x/2 (x ≤ 0.18) are predominantly oxide-ion conducting in the temperature ranging from 773 to 1173 K. The average thermal expansion coefficient of La_1.84Ba_0.16Mo₂O_8.92 determined by high-temperature XRD was deduced as great as 17.5 × 10⁻⁶ K⁻¹ between 298 and 1173 K.     

Composition dependent preferential orientation, dielectric and ferroelectric properties of Pb(ZrxTi1 − x)O3 thin films derived by sol-gel process

Pb(Zr_xTi_1 − x)O₃ (x = 0.35, 0.40, 0.60, 0.65) thin films were prepared by sol-gel spin on technique. From the X-ray diffraction analysis, PZT films with Zr-rich compositions (x = 0.60 and 0.65) had (111) preferential orientation and the preferential orientation changed to (100) for Ti-rich compositions (x = 0.35 and 0.40). The dielectric measurements on the above compositions at room temperature showed that the dielectric constant values were higher in Zr-rich compositions compared to Ti-rich compositions. The ferroelectric behavior measured in terms of the remnant polarization (P_r) and coercive field (E_c) up to an applied field of 260 kV/cm depicted that the Zr-rich PZT films with (111) preferential orientation had higher P_r and lower E_c values compared to the Ti-rich PZT films with (100) preferential orientation can be understood from the domain switching mechanism.     

Mixed cation effect in xR2O-(40 − x)Na2O-50B2O3-10Bi2O3 (R = Li, K) glasses

Mass density, glass transition temperature and ionic conductivity are measured in xLi₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ and xK₂O-(40 − x)Na₂O-50B₂O₃-10Bi₂O₃ glass systems with 0 ≤ x ≤ 40 mol%. The strength of the mixed alkali effect in T_g, dc electrical conductivity and activation energy has been determined in each glass system. The magnitudes of the mixed alkali effect in T_g for the mixed Li/Na glass system are much smaller than those in the mixed K/Na glasses. The impact of mixed alkali effect on dc electrical conductivity in mixed Li/Na glass system is more pronounced than in the K/Na glass system. The results are explained based on dynamic structure model.     

Sintering behavior, microstructure and microwave dielectric properties of Li2+xTiO3 (0 ≤ x ≤ 0.2)

Sintering behavior, microstructure and microwave dielectric properties of Li_2+xTiO₃ (0 ≤ x ≤ 0.2) ceramics have been studied by X-ray diffraction (XRD), scan electron microscopy (SEM), Raman spectra, dilatometery and microwave resonant measurement in this research. Homogeneous non-stoichiometric composition with rock salt structure existed for Li_2+xTiO₃ (0 ≤ x ≤ 0.2) ceramics. The sintering temperature was successfully reduced and highly densified sample could be obtained with appropriate excessive amount of lithium (x = 0.08). A transient reactive liquid phase sintering mechanism was proposed. The preferred orientation of grain growth and micro-cracks existed in the Li₂TiO₃ (x = 0) sample disappeared in the lithium excessive samples with x ≥ 0.08. The microwave dielectric properties varied significantly with the excessive amount of lithium. Optimized microwave dielectric properties were obtained for the x = 0.08 composition: ?_r = 24.6, Q × f = 66,000 GHz, and τ_f = 22.1 ppm/°C.     

Study of flash evaporated CuIn1 − xGaxTe2 (x = 0, 0.5 and 1) thin films

CuIn_1 − xGa_xTe₂ thin films with x = 0, 0.5 and 1, have been prepared by flash evaporation technique. These semiconducting layers present a chalcopyrite structure. The optical measurements have been carried out in the wavelength range 200-3000 nm. The linear dependence of the lattice parameters as a function of Ga content obeying Vegard's law was observed. The films have high absorption coefficients (4 · 10⁴ cm^− 1) and optical band gaps ranging from 1.06 eV for CuInTe₂ to 1.21 eV for CuGaTe₂. The fundamental transition energies of the CuIn_1 − xGa_xTe₂ thin films can be fitted by a parabolic equation namely E_g1(x) = 1.06 + 0.237x − 0.082x². The second transition energies of the CuInTe₂ and CuGaTe₂ films were estimated to be: E_g2 = 1.21 eV and E_g2 = 1.39 eV respectively. This variation of the energy gap with x has allowed the achievement of absorber layers with large gaps.     

Itinerant ferromagnetism to insulating spin glass in SrRu1−xCuxO3 (0 ≤ x ≤ 0.3)

The ferromagnetic metallic oxide, SrRuO₃ (T_C ∼ 165 K) undergoes structural, magnetic and metal-insulator transitions upon substitution of Cu at the Ru-site. For x = 0.2 in SrRu_1−xCu_xO₃, the structure becomes a tetragonal with the space group I4/mcm and there is a signature of both ferromagnetic (T_C = 65 K) and antiferromagnetic (T_N = 32 K) ordering due to possible magnetic phase separation. The antiferromagnetism arises due to short range ordering of Cu- and Ru-moments. Jahn-Teller distortion of (Ru,Cu)-O₆ octahedra indicates that the copper ions are in 2+ oxidation state with ⁶t2g³eg electronic configuration. For x ≥ 0.1, narrowing of Ru-4d bandwidth by the substitution of Cu ions results in semiconducting behavior. For x = 0.3, the ac and dc susceptibility measurements indicate a spin glass behavior. The origin of spin glass behavior has been attributed to competing ferromagnetic and antiferromagnetic interactions.