Effect of in-situ formed Mg2Ni/Mg2NiH4 compounds on hydrogen storage performance of MgH2

Magnesium-based hydrogen storage materials (MgH₂) are promising hydrogen carrier due to the high gravimetric hydrogen density; however, the undesirable thermodynamic stability and slow kinetics restrict its utilization. In this work, we assist the de/hydrogenation of MgH₂ via in situ formed additives from the conversion of an MgNi₂ alloy upon de/hydrogenation. The MgH₂–16.7 wt%MgNi₂ composite was synthesized by ball milling of Mg powder and MgNi₂ alloy followed by a hydrogen combustion synthesis method, where most of the Mg converted to MgH₂, and the others reacted with the MgNi₂ generating Mg₂NiH₄, which produced in situ Mg₂Ni during dehydrogenation. Results showed that the Mg₂Ni and Mg₂NiH₄ could induce hydrogen absorption and desorption of the MgH₂, that it absorbed 2.5 wt% H₂ at 473 K, much higher than that of pure Mg, and the dehydrogenation capacity increased by 2.6 wt% at 573 K. Besides, the initial dehydrogenation temperature of the composite under the promotion of Mg₂NiH₄ decreased greatly by 100 K, whereas it is 623 K for MgH₂. Furthermore, benefiting from the catalyst effect of Mg₂NiH₄ during dehydrogenation, the apparent activation energy of the composite reduced to 73.2 kJ mol⁻¹ H₂ from 129.5 kJ mol⁻¹ H₂.     

Remarkable kinetics of novel Ni@CeO2–MgH2 hydrogen storage composite

Magnesium hydroxide (MgH₂) has excellent reversibility and high capacity, and is one of the most promising materials for hydrogen storage in practical applications. However, it suffers from high dehydrogenation temperature and slow sorption kinetics. Rare earth hydrides and transition metals can both significantly improve the de/hydrogenation kinetics of MgH₂. In this work, MgH₂–Mg₂NiH₄–CeH_2.73 is in-situ synthesized by introducing Ni@CeO₂ into MgH₂. The unique coating structure of Ni@CeO₂ facilitates homogeneous distribution of synergetic CeH_2.73 and Mg₂NiH₄ catalytic sites in subsequent ball milling process. The as-fabricated composite MgH₂-10 wt% Ni@CeO₂ powders possess superior hydrogenation/dehydrogenation characteristics, absorbing 4.1 wt% hydrogen within 60 min at 100 °C and releasing 5.44 wt% H₂ within 10 min at 350 °C. The apparent activation energy of MgH₂-10 wt% Ni@CeO₂ is determined to be 84.8 kJ/mol and it has favorable hydrogen cycling stability with almost no decay in capacity after 10 cycles.     

Synthesis of low-cost biomass charcoal-based Ni nanocatalyst and evaluation of their kinetic enhancement of MgH2

In this study, a low-cost biomass charcoal (BC)-based nickel catalyst (Ni/BC) was introduced into the MgH₂ system by ball-milling. The study demonstrated that the Ni/BC catalyst significantly improved the hydrogen desorption and absorption kinetics of MgH₂. The MgH₂ + 10 wt% Ni/BC-3 composite starts to release hydrogen at 187.8 °C, which is 162.2 °C lower than the initial dehydrogenation temperature of pure MgH₂. Besides, 6.04 wt% dehydrogenation can be achieved within 3.5 min at 300 °C. After the dehydrogenation is completed, MgH₂ + 10 wt% Ni/BC-3 can start to absorb hydrogen even at 30 °C, which achieved the absorption of 5 wt% H₂ in 60 min under the condition of 3 MPa hydrogen pressure and 125 °C. The apparent activation energies of dehydrogenation and hydrogen absorption of MgH₂ + 10 wt% Ni/BC-3 composites were 82.49 kJ/mol and 23.87 kJ/mol lower than those of pure MgH₂, respectively, which indicated that the carbon layer wrapped around MgH₂ effectively improved the cycle stability of hydrogen storage materials. Moreover, MgH₂ + 10 wt% Ni/BC-3 can still maintain 99% hydrogen storage capacity after 20 cycles. XRD, EDS, SEM and TEM revealed that the Ni/BC catalyst evenly distributed around MgH₂ formed Mg₂Ni/Mg₂NiH₄ in situ, which act as a “hydrogen pump” to boost the diffusion of hydrogen along with the Mg/MgH₂ interface. Meanwhile, the carbon layer with fantastic conductivity enormously accelerated the electron transfer. Consequently, there is no denying that the synergistic effect extremely facilitated the hydrogen absorption and desorption kinetic performance of MgH₂.     

Effects of trimesic acid-Ni based metal organic framework on the hydrogen sorption performances of MgH2

A metal-organic framework based on Ni (II) as metal ion and trimasic acid (TMA) as organic linker was synthesized and introduced into MgH₂ to prepare a Mg-(TMA-Ni MOF)-H composite through ball-milling. The microstructures, phase changes and hydrogen storage behaviors of the composite were systematically studied. It can be found that Ni ion in TMA-Ni MOF is attracted by Mg to form nano-sized Mg₂Ni/Mg₂NiH₄ after de/rehydrogenation. The hydriding and dehydriding enthalpies of the Mg-MOF-H composite are evaluated to be −74.3 and 78.7 kJ mol⁻¹ H₂, respectively, which means that the thermodynamics of Mg remains unchanged. The absorption kinetics of the Mg-MOF-H composite is improved by showing an activation energy of 51.2 kJ mol⁻¹ H₂. The onset desorption temperature of the composite is 167.8 K lower than that of the pure MgH₂ at the heating rate of 10 K/min. Such a significant enhancement on the sorption kinetic properties of the composite is attributed to the catalytic effects of the nanoscale Mg₂Ni/Mg₂NiH₄ derived from TMA-Ni MOF by providing gateways for hydrogen diffusion during re/dehydrogenation processes.     

Catalysis derived from flower-like Ni MOF towards the hydrogen storage performance of magnesium hydride

Herein, a novel flower-like Ni MOF with good thermostability is introduced into MgH₂ for the first time, and which demonstrates excellent catalytic activity on improving hydrogen storage performance of MgH₂. The peak dehydrogenation temperature of MgH₂-5 wt.% Ni MOF is 78 °C lower than that of pure MgH₂. Besides, MgH₂-5 wt.% Ni MOF shows faster de/hydrogenation kinetics, releasing 6.4 wt% hydrogen at 300 °C within 600 s and restoring about 5.7 wt% hydrogen at 150 °C after dehydrogenation. The apparent activation energy for de/hydrogenation reactions are calculated to be 107.8 and 42.8 kJ/mol H₂ respectively, which are much lower than that of MgH₂ doped with other MOFs. In addition, the catalytic mechanism of flower-like Ni MOF is investigated in depth, through XRD, XPS and TEM methods. The high catalytic activity of flower-like Ni MOF can be attributed to the combining effect of in-situ generated Mg₂Ni/Mg₂NiH₄, MgO nanoparticles, amorphous C and remaining layered Ni MOF. This research extends the knowledge of elaborating efficient catalysts via MOFs in hydrogen storage materials.     

Trimesic acid-Ni based metal organic framework derivative as an effective destabilizer to improve hydrogen storage properties of MgH2

Herein, a new type of trimesic acid-Ni based metal organic framework (TMA-Ni MOF) was synthesized and then, its derivative Ni@C was introduced into MgH₂ as destabilizer through high energy ball milling to prepare a Mg–Ni@C–H composite. X-ray diffraction analyses indicate the formation of Mg₂Ni/Mg₂NiH₄ as major phases after dehydrogenation/rehydrogenation of the composite, respectively. Two hydrogen absorption plateaus are observed in the Mg–Ni@C–H composite, corresponding to the hydrogenation of Mg and Mg₂Ni, with the enthalpy change values of −75.8 and −52.3 kJ mol⁻¹ H₂ respectively. Thus, it can be concluded that a destabilization effect is brought by Ni@C on thermodynamic properties of MgH₂. In addition, the hydriding/dehydriding kinetics of MgH₂ is notably accelerated with the addition of Ni-based MOF derivative. The activation energy values of both hydrogen absorption and desorption are significantly lowered down with the assistance of Ni@C. Moreover, stable hydrogen de/absorption capacity and kinetics are remained during 25 cycles of high-rate re/dehydrogenation, which can be ascribed to the carbon-wrapped structure of the composite, with which the aggregation of the nanosized particles can be evidently avioded.     

Dual-tuning of de/hydrogenation kinetic properties of Mg-based hydrogen storage alloy by building a Ni-/Co-multi-platform collaborative system

The Mg-based hydrogen storage alloy with multiple platforms is successfully prepared by ball milling Co powder and Mg-RE-Ni precursor alloy, and its hydrogen storage behavior was investigated in detail by XRD, EDS, TEM, PCI, and DSC methods. The ball-milled alloy consists of the main phase Mg, the catalytic phases Mg₂Ni, Mg₂Co as well as a small amount of Mg₁₂Ce, and convert into the MgH₂–CeH_2.73-Mg₂NiH₄–Mg₂CoH₅ composite after hydrogenation. The composite has three PCI platforms corresponding to the reversible de/hydrogenation reaction of Mg/MgH₂, Mg₂Ni/Mg₂NiH₄ and Mg₆Co₂H₁₁/Mg₂CoH₅. Among them, the transformation between Mg₂Ni and Mg₂NiH₄ triggers the “spill-over” effect which promote the decomposition of MgH₂ phases and enhances the hydrogen desorption kinetics. Meanwhile, the conversion of the Mg₆Co₂H₁₁ to Mg₂CoH₅ phase induces the “chain reaction” effect, which leads to preferential nucleation of Mg phase and improves the hydrogen absorption kinetics. Therefore, the Mg-RE-Ni-Co alloy has a double improvement on hydrogen absorption and desorption kinetics. Concretely, the alloy has an optimal hydrogen absorption temperature of 200 °C, at which it can absorb 5.5 wt. % H₂ within 40 s. Under the conditions, the capacity of absorption almost reaches the maximum reversible value (about 5.6 wt. %). Besides, the alloy has a dehydrogenation activation energy of 67.9 kJ/mol and can desorb 5.0 wt. % H₂ within 60 min at the temperature of 260 °C.     

Hydrogen sorption in MgH2-based composites: The role of Ni and LiBH4 additives

In the present work we investigate the hydrogen sorption properties of composites in the MgH₂–Ni, MgH₂–Ni–LiH and MgH₂–Ni–LiBH₄ systems and analyze why Ni addition improve hydrogen sorption rates while LiBH₄ enhance the hydrogen storage capacity. Although all composites with Ni addition showed significantly improved hydrogen storage kinetics compared with the pure MgH₂, the fastest hydrogen sorption kinetics is obtained for Ni-doped MgH₂. The formation of Mg₂Ni/Mg₂NiH₄ in Ni-doped MgH₂ composite and its microstructure allows to uptake 5.0 wt% of hydrogen in 25 s and to release it in 8 min at 275 °C. In the MgH₂–Ni–LiBH₄ composite, decomposition of LiBH₄ occurs during the first dehydriding leading to the formation of diborane, which has a Ni catalyst poison effect via the formation of a passivating boron layer. A combination of FTIR, XRD and volumetric measurements demonstrate that the formation of MgNi₃B₂ in the MgH₂–Ni–LiBH₄ composite happens in the subsequent hydriding cycle from the reaction between Mg₂Ni/Mg₂NiH₄ and B. Activation energy analysis demonstrates that the presence of Ni particles has a catalytic effect in MgH₂–Ni and MgH₂–Ni–LiH systems, but it is practically nullified by the addition of LiBH₄. The beneficial role of LiBH₄ on the hydrogen storage capacity of the MgH₂–Ni–LiBH₄ composite is discussed.     

Characterization of Mg–20 wt% Ni–Y hydrogen storage composite prepared by reactive mechanical alloying

Mg–20 wt% Ni–Y composite was successfully prepared by reactive mechanical alloying (RMA). X-ray diffraction (XRD) measurement showed that both MgH₂ and Mg₂NiH₄ co-exist in the milled composite. The composite exhibits excellent hydrogen sorption kinetics and does not need activation on the first hydrogen storage process. It can absorb 3.92 and 5.59 wt% hydrogen under 3.0 MPa hydrogen pressure at 293 and 473 K in 10 min, respectively, and desorb 4.67wt% hydrogen at 523 K in 30 min under 0.02 MPa hydrogen pressure. The equilibrium desorption pressure of the composite are 0.142, 0.051 and 0.025 MPa at 573, 543 and 523 K, respectively. The differential scanning calorimetry (DSC) measurement showed that dehydrogenation of Mg–20 wt% Ni–Y composite was depressed about 100 K comparing to that of milled pure MgH₂. It is deduced that both the catalysis effect of Mg₂Ni and YH₃ distributed in Mg substrate and the crystal defects formed by RMA are the main reason for improving hydrogen sorption kinetics of the Mg–20 wt% Ni–Y composite.     

MgCNi3 prepared by powder metallurgy for improved hydrogen storage properties of MgH2

With the depletion of global energies resources, improvement of hydrogen storage properties of materials like MgH₂ is of great interest for future efficient renewable resources. In this study, a novel antiperovskite MgCNi₃ was synthesized by powder metallurgy then introduced into Mg to fabricate MgMgCNi₃ composite. The hydrogen storage properties of the obtained MgMgCNi₃ composite were evaluated. MgMgCNi₃ showed a high capacity of hydrogen storage and fast kinetics of hydrogen uptake/release at relatively low temperatures. About 4.42 wt% H₂ was absorbed within 20 min at 423 K, and 4.81 wt% H₂ was reversibly released within 20 min at 593 K. By comparison, milled MgH₂ absorbed only 0.99 wt% H₂ and hardly underwent any hydrogen evolution under the same conditions. In addition, MgMgCNi₃ composite showed outstanding cycling stability, with hydrogen absorption capacity retention rates reaching 98% after ten cycles at 623 K. The characterization analyses revealed that MgCNi₃ and Mg formed Mg₂NiH₄ hydride and carbonaceous material during hydrogenation, where Mg₂NiH₄ induced dehydrogenation of MgH₂ and carbon played a dispersive role during the composite reaction. Both features synergistically benefited the hydrogen storage properties of MgH₂.     

Excellent synergistic catalytic mechanism of in-situ formed nanosized Mg2Ni and multiple valence titanium for improved hydrogen desorption properties of magnesium hydride

Nowadays, catalytic doping has been regarded as one of the most promising and effective methods to improve the sluggish kinetics of magnesium hydride (MgH₂). Herein, we synthesized Ni/TiO₂ nanocomposite with the particle sizes about 20 nm by an extremely facile solvothermal method. Then, the Ni/TiO₂ nanocomposite was doped into MgH₂ to enhance its reversible hydrogen storage properties. A remarkably enhancement of de/rehydrogenation kinetics of MgH₂ can be achieved by doped with Ni/TiO₂ nanocomposite, compared to that solely doped with Ni or TiO₂ nanoparticles. The hydrogen desorption peak temperature of MgH₂Ni/TiO₂ is 232 °C, which is 135.4 °C lower than that of ball-milled MgH₂ (367.4 °C). Moreover, the MgH₂Ni/TiO₂ can desorb 6.5 wt% H₂ within 7 min at 265 °C and absorb ∼5 wt% H₂ within 10 min at 100 °C. In particular, the apparent activation energy of MgH₂Ni/TiO₂ is obviously decreased from 160.5 kJ/mol (ball-milled MgH₂) to 43.7 ± 1.5 kJ/mol. Based on the analyses of microstructure evolution, it is proved that metallic Ni particles can react with Mg easily to form fine Mg₂Ni particles after dehydrogenation, and the in-situ formed Mg₂Ni will transform into Mg₂NiH₄ in the subsequent rehydrogenation process. The significantly improved hydrogen absorption/desorption properties of MgH₂Ni/TiO₂ can be ascribed to the synergistic catalytic effect of reversible transformation of Mg₂Ni/Mg₂NiH₄ which act as “hydrogen pump”, and the multiple valence titanium compounds (Ti^4+/3+/2+) which promote the electrons transfer of MgH₂/Mg.     

Studies on de/rehydrogenation characteristics of nanocrystalline MgH2 co-catalyzed with Ti,Fe and Ni

In the present study, we have investigated the combined effect of different transition metals such as Ti, Fe and Ni on the de/rehydrogenation characteristics of nano MgH₂. Mechanical milling of MgH₂ with 5 wt% each of Ti, Fe and Ni for 24 h at 12 atm of H₂ pressure lead to the formation of nano MgH₂-Ti5Fe5Ni5. The decomposition temperature of nano MgH₂-Ti5Fe5Ni5 is lowered by 90 °C as compared to nano MgH₂ alone. It is also found that the nano MgH₂-Ti5Fe5Ni5 absorbs 5.3 wt% within 15 min at 270 °C and 12 atm hydrogen pressures. However, nano MgH₂ reabsorbs only 4.2 wt% under identical condition. An interesting result of the present study is that mechanical milling of MgH₂ separately with Fe and Ni besides refinement in particle size also leads to the formation of alloys Mg₂NiH₄ and Mg₂FeH₆ respectively. On the other hand, when MgH₂ is mechanically milled together with Ti, Fe and Ni, the dominant result is the formation of nano particles of MgH₂. Moreover the activation energy for dehydrogenation of nano MgH₂ co-catalyzed with Ti, Fe and Ni is 45.67 kJ/mol which is 35.71 kJ/mol lower as compared to activation energy of nano MgH₂ (81.34 kJ/mol). These results are one of the most significant in regard to improvement in de/rehydrogenation characteristics of known MgH₂ catalyzed through transition metal elements.     

Catalytic effect of Ni, Mg2Ni and Mg2NiH4 upon hydrogen desorption from MgH2

MgH₂ is a perspective hydrogen storage material whose main advantage is a relatively high hydrogen storage capacity (theoretically, 7.6 wt.% H₂). This compound, however, shows poor hydrogen desorption kinetics. Much effort was devoted in the past to finding possible ways of enhancing hydrogen desorption rate from MgH₂, which would bring this material closer to technical applications. One possible way is catalysis of hydrogen desorption. This paper investigates separate catalytic effects of Ni, Mg₂Ni and Mg₂NiH₄ on the hydrogen desorption characteristics of MgH₂. It was observed that the catalytic efficiency of Mg₂NiH₄ was considerably higher than that of pure Ni and non-hydrated intermetallic Mg₂Ni. The Mg₂NiH₄ phase has two low-temperature modifications below 508 K: un-twinned phase LT1 and micro-twinned phase LT2. LT1 was observed to have significantly higher catalytic efficiency than LT2.     

Remarkable synergistic effects of Mg2NiH4 and transition metal carbides (TiC,ZrC, WC) on enhancing the hydrogen storage properties of MgH2

Nanostructuring and catalyzing are effective methods for improving the hydrogen storage properties of MgH₂. In this work, transition-metal-carbides (TiC, ZrC and WC) are introduced into Mg–Ni alloy to enhance its hydrogen storage performance. 5 wt% transition-metal-carbide containing Mg₉₅Ni₅ (atomic ratio) nanocomposites are prepared by mechanical milling pretreatment followed by hydriding combustion synthesis and mechanical milling process, and the synergetic enhancement effects of Mg₂NiH₄ and transition-metal-carbides are investigated systematically. Due to the inductive effect of Mg₂NiH₄ and charge transfer effect between Mg/MgH₂ and transition-metal-carbides, Mg₉₅Ni₅-5 wt.% transition-metal-carbide samples all exhibit excellent hydrogen storage kinetic at moderate temperature and start to release hydrogen around 216 °C. Among them, 2.5 wt% H₂ (220 °C) and 4.7 wt% H₂ (250 °C) can be released from the Mg₉₅Ni₅-5 wt.% TiC sample within 1800 s. The unique mosaic structure endows the Mg₉₅Ni₅-5 wt.% TiC with excellent structural stability, thus can reach 95% of saturated hydrogen capacity within 120 s even after 10 cycles of de-/hydrogenation at 275 °C. And the probable synergistic enhancement mechanism for hydrogenation and dehydrogenation is proposed.     

Interfacial engineering of nickel/vanadium based two-dimensional layered double hydroxide for solid-state hydrogen storage in MgH2

As a high-density solid-state hydrogen storage material, magnesium hydride (MgH₂) is promising for hydrogen transportation and storage. Yet, its stable thermodynamics and sluggish kinetics are unfavorable for that required for commercial application. Herein, nickel/vanadium trioxide (Ni/V₂O₃) nanoparticles with heterostructures were successfully prepared via hydrogenating the NiV-based two-dimensional layered double hydroxide (NiV-LDH). MgH₂ + 7 wt% Ni/V₂O₃ presented more superior hydrogen absorption and desorption performances than pure MgH₂ and MgH₂ + 7 wt% NiV-LDH. The initial discharging temperature of MgH₂ was significantly reduced to 190 °C after adding 7 wt% Ni/V₂O₃, which was 22 and 128 °C lower than that of 7 wt% NiV-LDH modified MgH₂ and additive-free MgH₂, respectively. The completely dehydrogenated MgH₂ + 7 wt% Ni/V₂O₃ charged 5.25 wt% H₂ in 20 min at 125 °C, while the hydrogen absorption capacity of pure MgH₂ only amounted to 4.82 wt% H₂ at a higher temperature of 200 °C for a longer time of 60 min. Moreover, compared with MgH₂ + 7 wt% NiV-LDH, MgH₂ + 7 wt% Ni/V₂O₃ shows better cycling performance. The microstructure analysis indicated the heterostructural Ni/V₂O₃ nanoparticles were uniformly distributed. Mg₂Ni/Mg₂NiH₄ and metallic V were formed in-situ during cycling, which synergistically tuned the hydrogen storage process in MgH₂. Our work presents a facile interfacial engineering method to enhance the catalytic activity by constructing a heterostructure, which may provide the mentality of designing efficient catalysts for hydrogen storage.     

Enhanced hydrogen-storage properties of MgH2 by Fe–Ni catalyst modified three-dimensional graphene

High dehydrogenation temperature and slow dehydrogenation kinetics impede the practical application of magnesium hydride (MgH₂) serving as a potential hydrogen storage medium. In this paper, Fe–Ni catalyst modified three-dimensional graphene was added to MgH₂ by ball milling to optimize the hydrogen storage performance, the impacts and mechanisms of which are systematically investigated based on the thermodynamic and kinetic analysis. The MgH₂+10 wt%Fe–Ni@3DG composite system can absorb 6.35 wt% within 100 s (300 °C, 50 atm H₂ pressure) and release 5.13 wt% within 500 s (300 °C, 0.5 atm H₂ pressure). In addition, it can absorb 6.5 wt% and release 5.7 wt% within 10 min during 7 cycles, exhibiting excellent cycle stability without degradation. The absorption-desorption mechanism of MgH₂ can be changed by the synergistic effects of the two catalyst materials, which significantly promotes the improvement of kinetic performance of dehydrogenation process and reduces the hydrogen desorption temperature.     

Microstructural evolution and hydrogen storage proprieties of melt-spun eutectic Mg76.87Ni12.78Y10.35 alloy with low hydrides formation/decomposition enthalpy

Ternary eutectic Mg_76.87Ni_12.78Y_10.35 (at. %) ribbons with mixed amorphous and nanocrystalline phases were prepared by melt spinning. The microstructures of the melt-spun, hydrogenated and dehydrogenated samples were examined and compared by X-ray diffraction and transmission electron microscopy. The amorphous structure transforms into a thermally stable nanocrystalline structure with a grain size of about 5 nm during hydrogen ab/desorption cycles. The Mg, Mg₂Ni and phases with Y in the melt-spun state transform into MgH₂, Mg₂NiH₄, Mg₂NiH_0.3, YH₂ and YH₃ after hydrogenation, and transform back to Mg, Mg₂Ni and YH₂ upon subsequent dehydrogenation. The reaction enthalpy (ΔH) and entropy (ΔS) of the higher plateau pressure corresponding to Mg₂Ni hydride formation are −53.25 kJ mol⁻¹ and −107.74 J K⁻¹ mol⁻¹, respectively. The amorphous/nanocrystalline structure effectively reduces the enthalpy and entropy of Mg₂Ni hydride formation, but has little effect on Mg. The activation energy for dehydrogenation of the hydrogenated ribbons is 69 kJ mol⁻¹. This suggests that Mg–Ni–Y with ternary eutectic composition can form an amorphous/nanocrystalline structure by melt spinning, and this nanostructure efficiently improves the thermodynamics and kinetics for hydrogen storage.     

Facilitating de/hydrogenation by long-period stacking ordered structure in Mg based alloys

We propose a simple strategy to effectively improve the hydrogenation and dehydrogenation kinetics of Mg based hydrogen storage alloys. We designed and prepared an Mg_91.9Ni_4.3Y_3.8 alloy consisting of a large quantity of long-period stacking ordered (LPSO) phases. A type of highly dispersed multiphase nanostructure, which can markedly promote the de/hydrogenation kinetics, has been obtained utilizing the decomposition of LPSO phases at first a few of hydrogenation reactions. The fine structures of LPSO phases and the microstructural evolutions of the alloy during hydrogenation and dehydrogenation reactions were in detail characterized by means of transmission electron microscopy (TEM). The LPSO phases transformed to MgH₂, Mg₂NiH₄, and YH₃ after the first hydrogenation. The highly dispersed nanostructure at macro and micro (nano) scale range remains even after several de/hydrogenation cycles. The alloy shows excellent hydrogen storage properties and its reversible hydrogen absorption/desorption capacities are about 5.8 wt% at 300 °C. Particularly, the alloy exhibits very fast dehydrogenation kinetics. The dehydrogenated sample can release approximately 5 wt% hydrogen at 300 °C within 200 s and 5.5 wt% within 600 s. We elucidate the structural mechanism of the alloy with outstanding hydrogen storage performance.     

Characterization of microstructure,hydrogen storage kinetics and thermodynamics of a melt-spun Mg86Y10Ni4 alloy

Ternary Mg₈₆Y₁₀Ni₄ alloy was successfully prepared by vacuum induction melting and subsequent melt-spinning technique. The phase composition and microstructure of the melt-spun and hydrogenated samples were characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy measurements. The melt-spun alloy had an amorphous structure, and it transformed into nanocrystalline during the first hydrogenation process. The hydrogenated sample was composed of MgH₂, Mg₂NiH₄, YH₂, and a small amount of YH₃. The hydrogen absorption/desorption kinetics and thermodynamics were measured by Sievert's apparatus at various temperatures. It was found that the melt-spun Mg₈₆Y₁₀Ni₄ alloy could be fully activated after five hydrogenation and dehydrogenation cycles at 380 °C, and it exhibited a reversible gravimetric hydrogen storage capacity of about 5.3 wt%. The enhanced hydrogen sorption kinetics during the first few cycles can be attributed to the increased specific surface caused by the pulverization and cracking of the alloy particles. The activation energy for dehydrogenation reaction was determined to be 67 kJ/mol and 71 kJ/mol by using Arrhenius equation and Kissinger equation respectively. The thermodynamics of the sample was also evaluated by pressure–composition–isotherms, and the results shown that the enthalpy and entropy changes of Mg/MgH₂ transformation in the Mg₈₆Y₁₀Ni₄ alloy were slightly higher than that of pure Mg/MgH₂.     

Structure and hydrogen storage properties of Mg2Cu1−xNix (x = 0–1) alloys

The effect of Ni-substitution on the structure and hydrogen storage properties of Mg₂Cu_1−xNi_x (x = 0, 0.2, 0.4, 0.6, 0.8, 1) alloys prepared by a method combining electric resistance melting with isothermal evaporation casting process (IECP) has been studied. The X-ray single-crystal diffraction analysis results showed that the cell volume decreases with increasing Ni concentration, and crystal structure transforms Mg₂Cu with face-centered orthorhombic into Ni-containing alloys with hexagonal structure. The Ni-substitution effects on the hydriding reaction indicated that absorption kinetics and hydrogen storage capacity increase in proportion to the concentration of the substitutional Ni. The activated Mg₂Cu and Mg₂Ni alloys absorbed 2.54 and 3.58 wt% H, respectively, at 573 K under 50 bar H₂. After a combined high temperature and pressure activation cycle, the charged samples were composed of MgH₂, MgCu₂ and Mg₂NiH₄ while the discharged samples contained ternary alloys of Mg–Cu–Ni system with the helpful effect of rising the desorption plateau pressures compared with binary Mg–Cu and Mg–Ni alloys. With increasing nickel content, the effect of Ni is actually effective in MgH₂ and Mg₂NiH₄ destabilization, leading to a decrease of the desorption temperature of these two phases.