20Cr2Ni4A钢齿轮浅层渗碳热处理工艺研究

采用金相和剥层分析法对20Cr2Ni4A钢齿轮浅层渗碳处理工艺进行研究。结果表明,采用860℃渗碳,经淬火+低温回火处理后,渗碳层厚度为0.6~0.8 mm,表面硬度为58~62 HRC,心部硬度为35~47 HRC,所得金相组织符合标准要求。     

20CrMnTi钢齿轮表面剥落失效分析

某厂生产的一批装载机用桥箱传动齿轮在反馈的失效件中,齿面剥落损坏约占损坏总数的80%～90%.该批齿轮的模数为10,材料为20CrMnTi钢,外形尺寸为φ40 mm ×258 mm,热处理工艺为920℃×350 min强渗碳、860℃×120 min扩散→860 ℃淬火→(160±10)℃ × 120 min回火.技术要求表面硬度58～64 HRC,心部硬度33～45 HRC;     

20Cr2Ni4A钢齿轮的热处理

一种20Cr2Ni4A钢齿轮要求进行渗碳、淬火处理,达到0.8～1.0 mm的渗层深度、58～62 HRC的表面硬度和34～45 HRC的心部硬度。试验了3种渗碳淬火工艺,最后确定的热处理工艺为:920℃渗碳4 h缓冷,650℃高温回火4 h炉冷至350℃空冷,810℃保温3 h油淬,190℃回火两次。     

提高20Cr2Ni4A钢齿轮渗碳淬火硬度的试验研究

针对20Cr2Ni4A钢制造的中大型齿轮在不允许冷处理的条件下渗碳淬火硬度偏低的问题,通过对渗碳淬火碳势、中间高温回火工艺、淬火温度的优化,在不冷处理的情况下使齿轮硬度提高了2 HRC以上至58~61 HRC,显微组织良好,达到了预期目的。试验发现,该材料渗碳后经过高温回火再重新加热淬火时,为了提高表面及次表面硬度,渗碳扩散碳势、渗碳降温保温阶段碳势和淬火碳势在碳化物不超标的前提下要尽量提高;反复试验与检测证明,中间高温回火也会导致渗碳层一定深度内碳含量的降低,从而影响渗碳淬火硬度,故高温回火时不仅要注意回火不足更要防止过回火,高温回火次数过多时间过长,淬火后硬度不升反降。     

工业机器人用SCM420钢行星齿轮热处理工艺的优化

针对工业机器人用SCM420钢制行星齿轮热处理畸变问题,采用改进的正火工艺以调整渗碳前的预备组织,并设计合理的装料方案和冷却方式等措施,同时在渗碳过程中采用阶梯升温的工艺,有效地控制了渗碳淬火过程中齿轮畸变。结果表明,采用优化正火后可得到均匀一致的铁素体+珠光体的组织,硬度为175 ~180 HBW。随后经渗碳淬火回火后,批量生产的行星齿轮表面硬度、心部硬度和有效硬化层深度均值分别为59.74 HRC、40.44 HRC和0.530 mm。渗碳层中的马氏体级别为1级,残留奥氏体和碳化物级别为1~2级;心部组织级别为1~2级。齿轮精度、平面翘曲、齿沟振幅和齿形齿筋等全部满足技术要求。     

重载汽车20CrMnMo齿轮激光淬火热处理工艺

为研究20CrMnMo齿轮经激光淬火后的硬度值和微观组织以及与其他热处理方式相比的差异,采用"渗碳淬火"和"渗碳后不同参数的激光淬火"等工艺方法处理了一批齿轮;测定其齿面硬度值并对数据进行Matlab软件分析;采用扫描电子显微镜(SEM)对典型试样进行显微组织观察;测定和分析部分试样的晶粒度。结果表明:"渗碳后激光淬火"齿面的硬度值最高可达61.4 HRC,比渗碳淬火齿轮高2.3 HRC左右;渗碳后激光淬火的高硬度值试样的微观组织为致密的针状马氏体与板条状马氏体的混合,晶粒度为9级左右,有熔融现象的试样微观组织为回火索氏体,且不同激光参数处理的试样其微观组织类型和尺寸差别较大。因此20CrMnMo齿轮可以通过渗碳后的激光淬火工艺获得较高的硬度值、较好的微观组织和晶粒度。     

变速器从动齿轮的热处理工艺改进

图1为某汽车变速器一档从动齿轮示意图,其材料为20CrMoH钢,技术要求表面硬度(82±2)HRA,心部硬度30～43 HRC,有效硬化层深度0.5～0.7 mm,显微组织检验按HB 5492-1991<航空钢制件渗碳、氮碳共渗金相组织检验标准>进行,热处理后周节累计误差≤0.04 mm.齿轮加工工艺路线;锻造-等温正火-粗车-精车-滚齿-剃齿-渗碳淬火、回火-清理抛丸-精磨内孔-装机使用.齿轮渗碳淬火、回火处理后的齿形、齿向、周节累计畸变大,致使在装配试车过程出现齿轮接触精度低,噪声大的故障.因此,改进渗碳淬火工艺及装炉方式,控制热处理后的畸变量,是提高齿轮接触精度降低噪声的关键.     

减少大行星齿轮渗碳淬火畸变的工艺措施

我公司生产的154t电动轮自卸车上的大行星齿轮(见图1)，材料为20Cr2Ni4A钢，要求齿面渗碳淬火，渗碳层深1．9～2．3mm，齿面硬度58～63HRC，心部及其它表面硬度35～45HRC，端面平面度≤0．6mm。     

齿轮渗碳淬火后的回火

对经渗碳和825℃淬火的8620RH钢重载齿轮分别在150℃和185℃进行1～4 h以上的回火处理。检测了齿轮的表面硬度、心部硬度、硬化层的硬度梯度和显微组织,以确定齿轮的最佳回火工艺。结果表明:在相同温度不同时间回火的齿轮的显微组织和表面硬度没有明显差异;在150℃回火的齿轮1/2齿高处的表面硬度比185℃相同时间回火的齿轮高50～60 HV1。     

20CrNi2Mo钢真空渗碳工艺及数值模拟

采用大型双室真空渗碳设备对20Cr Ni2Mo钢进行不同工艺真空渗碳淬火,结合金相、显微硬度和表面碳浓度等分析,结果表明:试样渗碳层深度为2~3 mm时,总渗碳时间为550 min,渗碳扩散时间比(渗扩比)以1∶10较合理;渗碳层深度数值模拟结果略小于实际值,对实际生产具有一定指导意义;20Cr Ni2Mo钢大型齿轮实际真空渗碳淬火处理后,表面碳浓度为0.83%,渗碳层深度为3.2 mm,碳化物别1~2级,淬火和回火后齿轮齿面硬度值分别为62.8 HRC和58.1 HRC。     

模具渗硼工艺及其发展应用

渗硼是提高模具使用寿命的重要途径，是在金属表面形成高硬度的金属硼化层，显著提高其耐磨性，且具有良好的耐热性和耐蚀性。近年来，随着渗硼工艺逐步改进和完善，已发展了复合渗、多元共渗及低温渗硼工艺，取得了良好的经济效果。     

Stainless and acid-resisting steels and alloys

Conclusions Highly alloyed steels and alloys are produced in conformity with GOST or technical specifications in thick and thin sheets, beams and channels, bars, hot-rolled and cold-rolled pipe, and rod. Castings are produced in the specialized plant of the Ministry of Chemical and Petroleum Machine Building.The technology of welding stainless steels and alloys is given in [15] and [16].TsNIIChERMET. Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 10, pp. 43–50, October, 1967.     

Nanochemistry and supramolecular chemistry of actinides and lanthanides: Problems and prospects

The possibility of using unique properties of lanthanides in the nanotechnology is demonstrated. The origination of linear and nonlinear optical properties of lanthanide compounds with phthalocyanines, porphyrins, naphthalocyanines, and their analogs in solutions and condensed state and the prospects of obtaining novel materials on their basis are discussed. Based on the electronic structure and properties of lanthanides and their compounds, namely, optical and magnetic characteristics, electronic and ionic conductivity, and fluctuating valence, molecular engines are classified. High-speed storage engines or memory storage engines; photoconversion molecular engines based on Ln(II) and Ln(III); electrochemical molecular engines involving silicate and phosphate glasses; molecular engines whose operation is based on insulatorsemiconductor, semiconductor-metal, and metal-superconductor types of conductivity phase transitions; solid electrolyte molecular engines; and miniaturized molecular engines for medical analysis are distinguished. It is shown that thermodynamically stable nanoparticles of Ln _x M _y composition can be formed by d elements of the second halves of the series, i.e., those arranged after M = Mn, Tc, and Re. Prospects of using lanthanide superconductors in nanotechnology are considered.     

ADI和CADI在冶金矿山等行业中的应用及前景

综述了ADI和CADI的耐磨性能及耐磨原理;详细介绍了ADI磨球、衬板和锤头的应用情况,认为ADI件无论在综合力学性能,还是在耐磨性、使用寿命、成本方面都优于高铬铸铁件;同时还介绍了CADI在农业机械领域的应用效果.根据我国钢铁行业的发展趋势,指出ADI和CADI耐磨件市场前景广阔.     

金刚石、CBN有序排列及择优取向工具的研发及应用

有序排列／择优取向超硬材料工具的技术创新，将广泛适用于电镀、树脂、陶瓷、金属结合剂制品工具中，使用超硬材料颗粒在结合剂中均匀排列并择优定向，以最大潜能的发挥超硬材料各个方面固有的特性。并针对不同的加工对象，有选择性的使用超硬材料各自不同的特性，从而使超硬材料工具将以经济、高质与高效的优势替代传统的超硬材料工具并将进入新兴的加工领域，为生产企业带来新的发展机遇。本文将对有序排列与择优取向技术的研究现状及其在不同的金刚石工具中的应用做一阐述。     

Hardness and elastic modulus of amorphous and nanocrystalline SiC and Si films

Hydrogen-free amorphous and nanocrystalline films were prepared by magnetron sputtering of the SiC or Si targets. Mechanical properties (hardness, elastic modulus, intrinsic stress) and film structures were investigated in dependence on the substrate bias and temperature. It was found that both hardness and elastic modulus of all amorphous a-SiC films prepared at different substrate temperatures and biases are always lower than those for bulk α-SiC single crystal while the hardness of partially crystalline SiC films is higher and the elastic modulus lower than those for α-SiC one. In contrast, both hardness and elastic modulus of all amorphous Si films are always lower than those for nanocrystalline Si films which show approximately the same value as the Si single crystal.