Pre-exponential factor in<Emphasis Type="Italic">a</Emphasis>-Se<Subscript>75</Subscript>In<Subscript>25-<Emphasis Type="Italic">x</Emphasis></Subscript>Pb<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript> thin films

Temperature dependence of d.c. conductivity is studied ina- Se₇₅In_25-x Pb _x thin films wherex is varied from 0–10. From these measurements, the values of the pre-exponential factor (σ₀) and activation energy (ΔE) are calculated for each glassy alloy. An approximate linear dependence of ln σ₀ on AE is observed in this glassy system with good agreement between the expected and calculated σ₀ values using Meyer-Neldel rule. Linear dependence of ln σ₀ on ΔE in case of amorphous materials indicates that the conduction band tails a finite energy distance towards the valence band and Fermi level is controlled by fixed dominant hole levels deeper in the gap.     

Superconducting Properties of Iodine-Intercalated Bi<Subscript>2</Subscript>Sr<Subscript>2</Subscript>Ca<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>10+<Emphasis Type="Italic">x</Emphasis></Subscript>

The superconducting properties of iodine-intercalated high-temperature superconducting Bi₂Sr₂Ca₂Cu₃O_10+x phase (Bi-2223) were systematically studied. It was found that for samples containing a significant amount of Bi₂Sr₂CaCu₂O_8+x , iodine intercalation results in the dramatic decrease of the inter-granular critical current density, as well as a significant decrease of the critical temperature (T _c), the critical current density in the grains (J _cg), and of the amount of Bi-2223. For samples with a large amount of Bi-2223, T _c changes insignificantly, whereas J _cg can even increase. We argue that the different behavior of the superconducting parameters is the result of various oxygen concentrations, and we explain the effect of iodine intercalation based on the parabolic dependence between T _c and the number of holes per CuO₂ layer. The H(T) curves (determined from the peak position in the loss signal of ac susceptibility) for intercalated samples deviate significantly from the quasi 2D-like behavior, pointing toward an enhancement of the 3D fluctuations of vortices. For the change in the values and dimensionality of the flux pinning in the process of the intercalation, we attempted a qualitative explanation based on the models proposed in literature.     

Dielectric properties of Na<Subscript>1-<Emphasis Type="Italic">x</Emphasis></Subscript>K<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>NbO<Subscript>3</Subscript> in orthorhombic phase

Pellets of ceramic Na_1−xK_xNbO₃ (x = 0, 0.2 and 0.5), were prepared by conventional solid-state reaction method. Prepared samples were characterized using XRD and SEM. The frequency and temperature variation of dielectric constant, loss tangent and dielectric conductivity of prepared samples were measured in the frequency range from 10 KHz-1 MHz, and in the temperature range from 50–250°C for x = 0.2 and 0.5, and between 50 and 480°C for x = 0 compositions. It was observed that the dielectric constant and loss tangent decrease, and conductivity increases with increasing frequency. Near the transition temperature the material shows anomalous behaviour for the observed properties, and the peaks of dielectric constant and loss tangent were observed shifting towards lower temperature with increasing frequency.     

Solid-state reactions in the system Li<Subscript>2</Subscript>CO<Subscript>3</Subscript>-Na<Subscript>2</Subscript>CO<Subscript>3</Subscript>-Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>-Ta<Subscript>2</Subscript>O<Subscript>5</Subscript>

The formation mechanisms of Li _x Na_{1 ?x} Ta _y Nb_{1 ? y} O₃ perovskite solid solutions in the Li₂CO₃-Na₂CO₃-Nb₂O₅-Ta₂O₅ system have been studied by x-ray diffraction, differential thermal analysis, thermogravimetry, IR spectroscopy, and mass spectrometry at temperatures from 300 to 1100°C. The results indicate that the synthesis of Li _x Na_{1 ? x} Ta _y Nb_{1 ? y} O₃ solid solutions involves a complex sequence of consecutive and parallel solid-state reactions. An optimized synthesis procedure for Li _x Na_{1 ? x} Ta _y Nb_{1 ? y} O₃ solid solutions is proposed.     

New ferromagnetics based on manganese-alloyed chalcopyrites A<Superscript>II</Superscript>B<Superscript>IV</Superscript>C<Stack><Subscript>2</Subscript><Superscript>V</Superscript></Stack>

This review describes the principles of semiconductor spintronics, represents the physicochemical properties of materials based on manganese-alloyed A^IIB^IVC₂^V compounds, considers the results from theoretical simulation of magnetic properties of A^IIB^IVC₂^V alloyed with 3d metals, summarizes the basic approaches to explanation of ferromagnetism with Curie points above room temperature arising in A^IIB^IVC₂^V:Mn, and indicates promising ways to synthesize and study magnetic semiconductors based on chalcopyrites A^IIB^IVC₂^V in order to produce a suitable material for spintronic devices.     

Synthesis and properties of laser-active liquids POCl<Subscript>3</Subscript>-SbCl<Subscript>5</Subscript>-<Superscript>235</Superscript>UO<Stack><Subscript>2</Subscript><Superscript>2+</Superscript></Stack>-Nd<Superscript>3+</Superscript>

The effect of the synthesis conditions on the properties of inorganic laser-active liquids POCl₃-SbCl₅-²³⁵UO ₂ ²⁺ -Nd³⁺ is considered. The kinetic dependences of the U(IV) content and decay time of the Nd³⁺ luminescence in POCl₃-SbCl₅-²³⁵UO ₂ ²⁺ -Nd³⁺ solutions for various synthesis procedures at 380 K have been obtained. In POCl₃-SbCl₅-²³⁵UO ₂ ²⁺ -Nd³⁺ solutions, nonradiative energy transfer Nd³⁺ → U⁴⁺ is observed, and quenching of the Nd³⁺ luminescence is described by the Stern-Volmer law: k _q = (6.4 ± 0.6) × 10⁵ l mol^?1 s^?1. Laser liquids POCl₃-SbCl₅-²³⁵UO ₂ ²⁺ -Nd³⁺ with neodymium concentration of up to 0.7 M, uranyl concentration of up to 0.1 M, and decay time of the Nd³⁺ luminescence of up to 220 μs have been prepared for the first time.     

X-ray diffraction study of the Cu<Subscript>2</Subscript>Se-In<Subscript>2</Subscript>Se<Subscript>3</Subscript>-Cr<Subscript>2</Subscript>Se<Subscript>3</Subscript> system near CuInCr<Subscript>2</Subscript>Se<Subscript>5</Subscript>

The structure of three compounds in the Cu₂Se-In₂Se₃-Cr₂Se₃ system near CuInCr₂Se₅ is determined by single-crystal x-ray diffraction: CuInCr₄Se₈ (I), Cu₂In₂Se₄ (II), and Cu_0.5In_0.5Se (III). I has a cubic (spinel type) structure: a = 10.606(4) Å, Z = 4, sp. gr. F43m. II has a pseudotetragonal (sphalerite type) structure: a = 5.774(2) Å, c = 11.617(6) Å. The structure of II was solved in a reduced unit cell with a = 5.774(2) Å, b = 5.774(2) Å, c = 7.095(6) Å, = 113.95(5)°, = 113.95(5)°, = 90.00(4)°, Z = 1, sp. gr. P1. III has a triclinic cell (disordered structure of II): a = 4.088(1) Å, b = 4.091(2) Å, c = 4.101(1) Å, = 60.05(1)°, = 60.08(1)°, = 89.98(4)°, Z = 1, sp. gr. P1. The Cu and In atoms in I sit in inequivalent tetrahedral sites, and the Cr atoms reside in octahedral interstices of the close packing of Se atoms. The bond lengths are In–Se = 2.538(6), Cr(1)–Se(1) = 2.514(7), Cr(1)–Se(2) = 2.576(8), and Cu–Se = 2.437(5) Å. In II, all of the atoms sit in tetrahedral sites; the mean bond lengths are In–Se = 2.578(6) and Cu–Se = 2.44(1) Å. In III, the Cu and In atoms are fully disordered in the same tetrahedral site; the mean Cu(In)–Se bond length is 2.508(6) Å.Translated from Neorganicheskie Materialy, Vol. 40, No. 12, 2004, pp. 1435–1439.Original Russian Text Copyright © 2004 by Antsyshkina, Sadikov, Koneshova, Sergienko.     

Annealing Dependence of Exchange Bias in MnO/Ga<Subscript>1−</Subscript><Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Mn<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>As Heterostructures

We discuss the annealing-dependence of exchange bias in Ga_{1− x} Mn _x As epilayers that are overgrown with Mn. Although pure Mn is a known antiferromagnet, we find that the as-grown Mn overlayer does not produce any exchange coupling with Ga_{1− x} Mn _x As. Rather, our studies indicate that annealing in air is essential for creating the standard signatures of exchange bias (a clear shift in the magnetization hysteresis loop and an increased coercive field). We use X-ray photoelectron spectroscopy to characterize the compositional depth profile of both as-grown and rapid thermal annealed samples. These studies demonstrate that the cleanest exchange bias arises when the Mn overlayer is completely converted into MnO.     

Potassium ion conducting K<Subscript>1 − 2<Emphasis Type="Italic">x</Emphasis></Subscript>Cd<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>FeO<Subscript>2</Subscript> solid electrolytes

New potassium ion conducting solid electrolytes based on potassium monoferrite have been prepared through partial substitution of the divalent cation Cd²⁺ on the potassium site, and their properties have been investigated. The introduction of cadmium cations sharply increases the electrical conductivity of KFeO₂ over the entire temperature range studied. In addition to the maximum in conductivity at the boundary of the K_{1 − 2x} Cd _x FeO₂ solid solution, there is a maximum at a higher cadmium content (x = 0.30–0.35). The possible origins of this maximum are discussed.     

Microstructure and magnetic properties of Ni<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Zn<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> synthesized by combustion reaction

An investigation was made of samples having a chemical formula of Ni_1−x Zn _x Fe₂O₄, where x = 0.3, 0.5 and 0.7. The samples were prepared by the reaction combustion synthesis method and sintered at 1,200 °C/2 h in a static air atmosphere. The influence of the Zn concentration on the relative density, microstructure and magnetic properties of the samples was studied. X-ray diffraction, scanning electron microscopy and magnetic hysteresis loop tracer were used to analyze the compositions. The samples were found to have a spinel cubic structure, sintered density of 92.9%–98.8% of the corresponding X-ray density, homogeneous microstructure with grain size ranging from 1.37 to 3.36 μm, maximum flux density of 0.16–0.35 T, field coercivity ranging from 17 to 168 A/m, and loss hysteresis of 1.5–105 W/kg. Increased grain growth, with fine pores inside the grains, was found to occur as the Zn concentration increased. The overall findings are discussed here in light of the existing understanding of these systems.     

Solid state synthesis and structural refinement of polycrystalline La<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Ca<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>TiO<Subscript>3</Subscript> ceramic powder

Perovskite structure based ceramic precursors have a characteristic property of substitution in the “A” site of the ABO₃ structure. This makes them a potential material for nuclear waste management in synthetic rock (SYNROC) technology. In order to simulate the mechanism of rare earth fixation in perovskite, La_x Ca_1−xTiO₃ (wherex = 0.05) has been synthesized through ceramic route by taking calculated quantities of oxides of Ca, Ti and La as starting materials. Solid state synthesis has been carried out by repeated pelletizing and sintering the finely powdered oxide mixture in a muffle furnace at 1050°C. The ceramic phase has been characterized by its powder diffraction pattern. Step analysis data has been used to determine the structure of solid solution of lanthanum substituted calcium titanate. The SEM and EDAX analyses also confirm that the CaTiO₃ can act as a host for lanthanum. X-ray data has been interpreted using CRYSFIRE and POWDERCELL softwares. Theh, k, l values for different lattice planes have been generated from the experimental data. The lanthanum substituted perovskite crystallizes in orthorhombic symmetry with space groupP n m a (#62). Following unit cell parameters have been calculated:a = 5.410,b = 7.631,c = 5.382. The calculated and observed values of corresponding intensities, 2θ, and density show good agreement. GSAS based calculation for bond distances Ti-O, Ca-O, La-O and bond angles Ti-O-Ca, Ca-O-Ca, La-O-Ti have been reported.     

Y<Subscript>2</Subscript>O<Subscript>3</Subscript> and Nd<Subscript>2</Subscript>O<Subscript>3</Subscript> co-stabilized ZrO<Subscript>2</Subscript>-WC composites

Y₂O₃ + Nd₂O₃ co-stabilized ZrO₂-based composites with 40 vol% WC were fully densified by pulsed electric current sintering (PECS) at 1350 °C and 1450 °C. The influence of the PECS temperature and Nd₂O₃ co-stabilizer content on the densification, hardness, fracture toughness and bending strength of the composites was investigated. The best combination of properties was obtained for a 1 mol% Y₂O₃ and 0.75 mol% Nd₂O₃ co-stabilized composite densified for 2 min at 1450 °C under a pressure of 62 MPa, resulting in a hardness of 15.5 ± 0.2 GPa, an excellent toughness of 9.6 ± 0.4 MPa.m^0.5 and an impressive 3-point bending strength of 2.04 ± 0.08 GPa. The hydrothermal stability of the 1 mol% Y₂O₃ + 1 mol% Nd₂O₃ co-stabilized ZrO₂-WC (60/40) composites was compared with that of the equivalent 2 mol% Y₂O₃ stabilized ceramic. The double stabilized composite did not degrade in 1.5 MPa steam at 200 °C after 4000 min, whereas the yttria stabilized composite degraded after less than 2000 min. Moreover, the (1Y,1Nd) ZrO₂-WC composites have a substantially higher toughness (~9 MPa.m^0.5) than their 2Y stabilized equivalents (~7 MPa.m^0.5).     

Multiple Magnetic Ordering Temperatures in RuSr<Subscript>2</Subscript>Eu<Subscript>1.5</Subscript>Ce<Subscript>0.5</Subscript>Cu<Subscript>2</Subscript>O<Subscript>10−<Emphasis Type="Italic">δ</Emphasis></Subscript> System

We report synthesis and magnetic characterization of variously processed magneto-superconducting (Rutheno-cuprates) RuSr₂Eu_1.5Ce_0.5Cu₂O_10−δ . The compound crystallizes in I4/mmm tetragonal structure. Magnetization measurements showed bulk magnetic ordering and superconductivity at around 100 K and 30 K, respectively. Further, the careful examination of the low field magnetic susceptibility reveals two minor magnetic transitions at around 135 K and 200 K, in addition to the major transition at 100 K. When the samples are processed in different environments of air, O₂ and slightly pressurized O₂, the nature of magnetic transitions and the superconductivity changes dramatically. The highest superconducting transition is achieved for the high pressure O₂ annealed samples and the lowest for the air annealed one. On the other hand, the minor magnetic transitions are more prominent in air-annealed samples. Though the minor magnetic transitions are intrinsic to all variously processed samples, they are not clearly seen for higher O₂ content samples. Basically, the Ru spins order antiferro magnetically at around 200 K (first minor transition), and reorients themselves at 125 K (second minor transition) before finally ordering in canted ferromagnetic state or a spin glass structure. These results can be explained on the basis of fluctuating valance of Ru⁴⁺/Ru⁵⁺.      

Crystal structure of Gd<Subscript>14</Subscript>Cu<Subscript>48</Subscript>Ga<Subscript>3</Subscript> and Tb<Subscript>14</Subscript>Cu<Subscript>48</Subscript>Ga<Subscript>3</Subscript>

The compounds Gd₁₄Cu₄₈Ga₃ and Tb₁₄Cu₄₈Ga₃ have been synthesized, and their structures have been determined by powder x-ray diffraction (Gd₁₄Ag₅₁ type).     

Electrical conductivity of Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-Tm<Subscript>2</Subscript>O<Subscript>3</Subscript>-Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> solid solutions

New solid solutions, Bi_2?x?y Tm _x Nb _y O_3+δ, with tetragonal and cubic structures have been synthesized in the Bi₂O₃-Tm₂O₃-Nb₂O₅ system, and their electrical conductivity has been measured at temperatures from 670 to 1020 K. The 1020-K conductivity of the tetragonal solid solution Bi_1.8Tm_0.15Nb_0.05O_3+δ is comparable to that of Bi_1.75Tm_0.25O₃, the best conductor in the Bi₂O₃-Tm₂O₃ system.     

Thermal conductivity of Sb<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Gd<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript> solid solutions

We have measured the thermal conductivity of Bi₂Te₃-Sb₂Te₃-Gd₂Te₃ solid solutions at temperatures from ～80 to 300 K and have determined the electronic and lattice components of their total thermal conductivity and the contributions of Sb₂Te₃ and Gd₂Te₃ to their thermal resistance. The results indicate that heat in these materials is transported largely by phonons and that three-phonon processes play a key role in determining the lattice thermal conductivity of the solid solutions.     

Ho<Subscript>2</Subscript>S<Subscript>3</Subscript>-Ga<Subscript>2</Subscript>S<Subscript>3</Subscript> phase diagram

The Ho₂S₃-Ga₂S₃ system has been studied using differential thermal analysis, X-ray diffraction, microstructural analysis, microhardness tests, and density measurements, and its phase diagram has been constructed. The system contains three ternary compounds: Ho₃GaS₆, HoGaS₃, and Ho₆Ga_10/3S₁₄. Their melting behavior has been studied for the first time. The compound Ho₆Ga_10/3S₁₄ melts congruently at 1435 K; Ho₃GaS₆ and HoGaS₃ melt incongruently at 1370 and 1250 K, respectively. The Ho₂S₃-Ga₂S₃ system is a pseudobinary join of the ternary system Ho-Ga-S. At room temperature, the β-Ga₂S₃-based solid solution extends to 1.5 mol % Ho₂S₃; the Ho₂S₃ solubility in γ-Ga₂S₃ is 10 mol %. The compounds HoGaS₃ and Ho₃GaS₆ crystallize in orthorhombic symmetry (Ho₃GaS₆: a = 10.40 Å, b = 13.20 Å, c = 6.44 Å, Z = 4; HoGaS₃: a = 6.8 Å, b = 9.92 Å, a = 3.08 Å, Z = 4). Ho₆Ga_10/3S₁₄ has a hexagonal structure (a = 9.62 Å, c = 6.04 Å).     

Synthesis of Ba<Subscript>3</Subscript>ZnNb<Subscript>2</Subscript>O<Subscript>9</Subscript>−Sr<Subscript>3</Subscript>ZnNb<Subscript>2</Subscript>O<Subscript>9</Subscript> solid solution and their dielectric properties

Oxides of the type, Ba_3-xSr_xZnNb₂O₉ (0 ≤x ≤3), were synthesized by the solid state route. Oxides calcined at 1000°C show single cubic phase for all the compositions. The cubic lattice parameter (a) decreases with increase in Sr concentration from 4.0938(2) forx = 0 to 4.0067(2) forx = 3. Scanning electron micrographs show maximum grain size for thex = 1 composition (∼ 2 μm) at 1200°C. Disks sintered at 1200°C show dielectric constant variation between 28 and 40 (at 500 kHz) for different values of x with the maximum dielectric constant atx = 1.