Sintering of Si3N4-Y2O3-Al2O3

Sintering kinetics of the system Si₃N4-Y2O₃-Al₂O3 were determined from measurements of the linear shrinkage of pressed disks sintered isothermally at 1500° to 1700°C. Amorphous and crystalline Si₃N₄ were studied with additions of 4 to 17 wt% Y₂O₃ and 4 wt% A1₂O₃. Sintering occurs by a liquid-phase mechanism in which the kinetics exhibit the three stages predicted by Kingery's model. However, the rates during the second stage of the process are higher for all compositions than predicted by the model. X-ray data show the presence of several transient phases which, with sufficient heating, disappear leaving mixtures of β ' -Si₃N₄ and glass or β '-Si₃N₄, α '-Si₃N₄, and glass. The compositions and amounts of the residual glassy phases are estimated.     

Solid-Liquid Equilibria in the System Si3N4-AlN-Si02-A12O3

Solid-liquid equilibria at 1750°C and subsolidus phase relations in the system Si₃N₄−AlN-SiO₂−Al₂O₃ were determined for the composition region bounded by the β-Si₃N₄ solid solution line and silica-alumina join X-ray diffraction and optical microscopy were used to determine the phases present in specimens cooled rapidly after equilibration. The extent of a single liquid-phase region and the tie lines for the βsolid solution + liquid field at 1750°C were established from quantitative X-ray diffractometry and lattice parameter measurements of βsolid solutions in equilibrium with liquid. The results were corroborated by optical microscopy and melting behavior observations. A new composition, Si₁₂Al₁₈O₃9N₈, is suggested for the x₁ phase. The lowest melting temperature in the system is ≅ 1480°C and the corresponding composition is 10 eq% Al-90 eq%O.     

Phase Equilibrium Studies in the System Iron Oxide-Al2O3-Cr2O3

Subsolidus phase relations in the system iron oride-Al₂O₂-Cr₂O₃ in air and at 1 atm. O₂ pressure have been studied in the. temperature interval 1250° to 1500°C. At temperatures below 1318° C. only sesquioxides with hexagonal corundum structure are present as equilibrium phases. In the temperature interval 1318° to 1410°C. in air and 1318° to 1495° C. at 1 atm. O₂, pressure the monoclinic phase Fe₂O₃. Al₂O₃ with some Cr₂O₃ in solid solution is present in the phase assemblage of certain mixtures. At temperatures above 1380°C. in air and above 1445°C. at 1 atm. O₂ pressure a complex spinel solid solution is one of the phases present in appropriate composition areas of the system. X-ray data relating d- spacing to composition of solid solution phases are given.     

Phase Equilibria and Ionic Conductivity in the System ZrO2−Yb2O3−Y2O3

The phase equilibria in the zirconia-rich part of the system ZrO₂−Yb₂O₃−Y₂O₃ were determined at 1200°, 1400°, and 1650°C. The stabilizing effects of Yb₂O₃ and Y₂O₃ were found to be quite similar with <10 mol% of either being necessary to fully stabilize the cubic fluorite-structure phase at 1200°C. The two binary ordered phases, Zr₃Yb₄O₁₂ and Zr₃Y₄O₁₂, are completely miscible at 1200°C. These were the only binary or ternary phases detected. The ionic conductivities of ternary specimens in this system were measured using the complex impedance analysis technique. For a given level of total dopant, the substitution of Yb₂O₃ for Y₂O₃ gives only minor increases in specimen conductivity.     

Influence of Non-Stoichiometry on the Structure and Properties of Ba(Zn1/3Nb2/3)O3 Microwave Dielectrics: I. Substitution of Ba3W2O9

A narrow region of Zn-vacancy-containing cubic perovskites was formed in the (1− x )Ba₃(ZnNb₂)O₉−( x )Ba₃W₂O₉ system up to 2 mol% substitution ( x =0.02). The introduction of cation vacancies enhanced the stability of the 1:2 B-site ordered form of the structure, Ba(Zn_{1− x} □ _x )_1/3(Nb_{1− x} W _x )_2/3O₃, which underwent an order–disorder transition at 1410°C, ∼35° higher than pure Ba(Zn_1/3Nb_2/3)O₃. The Zn vacancies also accelerated the kinetics of the ordering reaction, and samples with x =0.006 comprised large ordered domains with a high lattice distortion ( c/a =1.226) after a 12 h anneal at 1300°C. The tungstate-containing solid solutions can be sintered to a high density at 1390°C, and the resultant ordered ceramics exhibit some of the highest microwave dielectric Q factors ( Q × f =1 18 000 at 8 GHz) reported for a niobate-based perovskite.     

CrO2-Cr2O3 Phase Boundary Under High O2 Pressures

The phase boundary between CrO₂ and Cr₂O₃ was reinvestigated under high O₂ pressures by using a new type of gas compressor. The boundary curve can be represented as log Po₂= 7.16-(3579/ T ). Using the observed data, Δ G °, Δ H °, and Δ S ° for the reaction 2CrO₂⇋Cr₂O₃+½O₂ were calculated to be: Δ G °= -(1.55/100) T +7.60 kcal/mol, Δ H °= -8.19 kcal/mol, and Δ S °= (-15.8/ T )+0.0155 kcal/mol.     

Hot-Pressing of Si3N4 with Y2O3 and Li2O as Additives

The rates of densification and phase transformation undergone by α-Si₃N₄ during hot-pressing in the presence of Y₂O₃, Y₂O₃−2SiO₂, and Li₂0−2Si0₂ as additives were studied. Although these systems behave less simply than MgO-doped Si₃N₄, the data can be interpreted during the early stages of hot-pressing as resulting from a solution-diffusion-reprecipitation mechanism, where the diffusion step is rate controlling and where the reprecipitation step invariably results in the formation of the β-Si₃N₄ phase.     

Phase Relations and Ordering in the Systems MgO-Y2O3-ZrO2 and CaO-MgO-ZrO2

The phase relations in the systems MgO-Y₂O₃-ZrO₂ and CaO-MgO-ZrO₂ were established at 1220° and 1420°C. The system MgO-Y₂O₃-ZrO₂ possesses a much-larger cubic ZrO₂ solid solution phase field than the system CaO-MgO-ZrO₂ at both temperatures. The ordered δ phase (Zr₃Y₄O₁₂) was found to be stable in the system ZrO₂-Y₂O₃ at 1220°C. Two ordered phases φ₁ (CaZr₄O₉) and φ₂ (Ca₆Zr₁₉O₄₄) were stable at 1220°C in the system ZrO₂-CaO. At 1420°C no ordered phase appears in either system, in agreement with the previously determined temperature limits of the stability for the δ, φ₁, and φ₂ phases. The existence of the compound Mg₃Y_zO₆ could not be confirmed.     

High-Quartz Solid Solution Phases from Thermally Crystallized Glasses of Compositions Li2O2,MgO).Al2O3,nSiO2

Thermally crystallized glasses of compositions (Li₂,O₂, MgO).Al₂O₃.nSiO₂ were studied by X-ray powder diffraction methods. High-quartz solid solution phases developed at relatively low temperatures and, for n 3.5, transformed at higher temperatures to keatite solid solution phases. Associated phases, if present, were Mg spinel and/or cordierite, or a few other trace phases. The a crystallographic axis (a₀) of high-quartz solid solutions decreased with increase of MgO and/or SiO₂. The c crystallographic axis (c₀) decreased with increasing MgO; it also decreased with increasing SiO₂, but only when MgO content was low. X-ray diffraction photographs of single crystals of high-quartz solid solutions of compositions LiaO.Al₂O₃.nSiO₃ demonstrated that the maintenance of a basic high-quartz structure is the basis of the solid solution relation. Three modifications of the high-quartz structure were recognized in the Li₂O-Al₂O₃−SiO₃ system. These modifications were based on the occurrence and positions of superlattice reflections. The high-quartz solid solution from Li₂O Al₂O₃−2SiO₂, showing streaky reflections in its precession photographs, suggested a defective structure. The term "high-quartz solid solution," with or without additional prefixes specifying the compositional series and modification, was considered the preferred nomenclature for these solid solution phases.     

Polymorphism and Thermodynamic Stability of Zn7Sb2O12

The composition Zn_2.33Sb_0.67O₄ (or Zn₇Sb₂O₁₂) exists in two polymorphic forms. The thermodynamically stable, low-temperature orthorhombic β form transforms to the high-temperature cubic α-polymorph with a spinel structure at 1225°±25°C. The transformation is fully reversible but slower in the α→β direction and therefore, it is easy to preserve the high-temperature α-polymorph to lower temperatures where it is kinetically stable but thermodynamically metastable. It is also possible to synthesize the α-polymorph directly at low temperatures, e.g., 900°C. This synthesis, of a phase that is thermodynamically stable only at high temperatures, but which has sufficient kinetic stability to exist metastably at low temperatures, represents an example of Ostwald's law of successive reactions in which the first phase to crystallize from a reaction mixture is not necessarily the equilibrium phase of lowest free energy. The crystal structure of the α-polymorph has been confirmed by Rietveld refinement of X-ray powder diffraction data to be an inverse spinel, (Zn)[Sb_2/3Zn_4/3]O₄, in which octahedral sites contain a disordered, random mixture of Zn and Sb and tetrahedral sites are fully occupied by Zn.     

Nd2O3-Doped Sialons with ZrO2/ZrN Additions Formed by Sintering and Hot Isostatic Pressing

β-sialon and Nd₂O₃-doped α-sialon materials of varying composition were prepared by sintering at 1775° and 1825°C and by glass-encapsulated hot isostatic pressing at 1700°C. Composites were also prepared by adding 2–20 wt% ZrO₂ (3 mol% Nd₂O₃) or 2–20 wt% ZrN to the β-sialon and α-sialon matrix, respectively. Neodymium was found to be a fairly poor α-sialon stabilizer even within the α-phase solid solution area, and addition of ZrN further inhibited the formation of the α-sialon phase. A decrease in Vickers hardness and an increase in toughness with increasing content of ZrO₂(Nd₂O₃) or ZrN were seen in both the HIPed β-sialon/ZrO₂(Nd₂O₃) composites and the HIPed Nd₂O₃-stabiIized α-sialons with ZrN additions.     

Conversion from β-Ce2O3·11Al2O3 to α-Al2O3 in Tetragonal ZrO2 Matrix

Composites of β-Ce₂O₃·11Al₂O₃ and tetragonal ZrO₂ were fabricated by a reductive atmosphere sintering of mixed powders of CeO₂, ZrO₂ (2 mol% Y₂O₃), and Al₂O₃. The composites had microstructures composed of elongated grains of β-Ce₂O₃·11Al₂O₃ in a Y-TZP matrix. The β-Ce₂O₃·11Al₂O₃ decomposed to α-Al₂O₃ and CeO₂ by annealing at 1500°C for 1 h in oxygen. The elongated single grain of β-Ce₂O₃·11Al₂O₃ divided into several grains of α-Al₂O₃ and ZrO₂ doped with Y₂O₃ and CeO₂. High-temperature bending strength of the oxygen-annealed α-Al₂O₃ composite was comparable to the β-Ce₂O₃·11Al₂O₃ composite before annealing.     

Phase Equilibria in the Ga2O3In2O3 System

Subsolidus phase relationships in the Ga₂O₃–In₂O₃ system were studied by X-ray diffraction and electron probe microanalysis (EPMA) for the temperature range of 800°–1400°C. The solubility limit of In₂O₃ in the β-gallia structure decreases with increasing temperature from 44.1 ± 0.5 mol% at 1000°C to 41.4 ± 0.5 mol% at 1400°C. The solubility limit of Ga₂O₃ in cubic In₂O₃ increases with temperature from 4.X ± 0.5 mol% at 1000°C to 10.0 ± 0.5 mol% at 1400°C. The previously reported transparent conducting oxide phase in the Ga-In-O system cannot be GaInO₃, which is not stable, but is likely the In-doped β-Ga₂O₃ solid solution.     

Phase Equilibrium Studies in the System Iron Oxide- A12O3 in Air and at 1 Atm. O2 Pressure

Phase equilibrium data, obtained by using the quenching technique, are presented for the system iron oxide-A1₂O₃ in air and at 1 atm. O₂ pressure in the temperature interval 1085° to 1725°C. Stability ranges of the various phases are delineated, and approximate compositions of crystalline and liquid phases are determined. Special attention is focused on the phase Fe₂O₃·A1₂O₃(ss) and its stability relationships.     

Modification of αAI2O3 Platelet/ZrO2 Matrix Interface by Epitaxial Growth of β-AI2O3 on the α-AI2O3

An epitaxial β-alumina crystal growth method was used to modify α-AI₂O₃ platelet surfaces before inclusion as a reinforcing phase in partially stabilized zirconia (3Y-TZP). The as-grown surface phase was Na-β"-AI₂O₃. This was converted to Ca-β"-AI₂O₃ by ion exchange, as the latter is more temperature-stable at composite sintering temperatures. The conditions of formation, thermal stability, and chemical compatibility of these interfacial phases were examined. α-AI₂O₃ platelets with Ca-β"-AI₂O₃ film were incorporated into 3Y-TZP. The β"-AI₂O₃/ZrO₂ interface was found to promote platelet debonding and pullout, thus enhancing the α-AI₂O₃ platelet/crack interactions during the fracture process.     

Crystallization of MgO-CaO-SiO2-P2O5 Glass

The crystallization behavior of a glass with a composition of 40 wt% 3CaO · P₂O₅−60 wt% CaO · MgO · 2SiO₂ was investigated. The primary crystalline phase was apatite with a dendritic form and ellipsoidal shape. β-(3CaO · P₂O₅) and CaO · MgO · 2SiO₂ were crystallized as samples heated to 990°C, and a three-layer structure was obtained. The development and morphology of this construction were explained by both the surface crystallization of the apatite and CaO · MgO · 2SiO₂ and the bulk crystallization of apatite and the CaO · MgO · 2SiO₂-β-(3CaO · P₂O₅) composite.     

Phase Relations and Dielectric Properties in the Bi2O3–ZnO–Ta2O5 System

Dielectric properties and phase formation of Bi-based pyrochlore ceramics were evaluated for the Bi₂O₃–ZnO–Ta₂O₅ system. The compositional range r Bi₂(Zn_1/3Ta_2/3)₂O₇· (1− r )(Bi_3/2Zn_1/2)(Zn_1/2Ta_3/2)O₇ (0 ≤ r ≤ 1) in Bi₂O₃–ZnO–Ta₂O₅ was investigated to determine the relative solubility of BZT cubic (α-BZT, r = 0) and the pseudo-orthorhombic (β-BZT, r = 1) end members. It was found that extrinsic factors, such as kinetically limited phase formation and bismuth loss, contribute to apparent phase boundaries in addition to thermodynamic stability of each phase. Considering this, the locations of true phase boundaries were r < 0.30 and r ≥ 0.74 for α and β phases, respectively. Dielectric constants between 58 and 80 and low dielectric loss (tan δ < 0.003) were measured for the complete compositional range. The temperature coefficient of capacitance was controlled by composition, which was found to be <30 ppm/°C at the edge of β-phase solid solution. In addition to the excellent dielectric properties these materials can be sintered at low temperatures, which make Bi-based pyrochlores promising candidates for high-frequency electronic applications.     

Crystallization of Beta NaFeO2 from a Glass Along the Na2SiO3-Fe2O3 Join

Fine-particle beta sodium ferrite (β-NaFeO₂), rather than α-Fe₂O₃, may be responsible for superparamagnetic behavior in a glass of composition (in mole fractions) 0.37Na₂O-0.26Fe₂O₃-0.37SiO₂. The 700°C isothermal section of the phase diagram of the Na₂O-Fe₂O₃-SiO₂ system is given, showing a three-phase field bounded by Na₂SiO₃-NaFeO₂-Fe₂O₃; there is no evidence for the existence (at 700°C) of compounds of molar composition 6Na₂O-4Fe₂O₃-5SiO₂ or 2Na₂O-Fe₂O₃-SiO₂. The Moessbauer spectrum of β-NaFeO₂ has an internal magnetic field of 487 kOe at room temperature.     

Cation Ordering Transformations in the Ba(Zn1/3Nb2/3)O3-La(Zn2/3Nb1/3)O3 System

Single-phase perovskites were formed in the (1−_x)Ba(Zn_1/3Nb_2/3)O₃-( _x )La(Zn_2/3Nb_1/3)O₃ system for compositions with 0.0≤ x ≤0.6. Although the stability of the trigonal "1:2" ordered structure of the Ba(Zn_1/3Nb_2/3)O₃ end member is very limited (0.0≤ x ≤0.05), low levels of lanthanum induce a transformation to a cubic, "1:1" ordered structure that has a broad range of homogeneity (0.05≤ x ≤0.6). Samples with x > 0.6 were comprised of La₃NbO₇, ZnO, and a perovskite with x = 0.6. The cubic 1:1 phases were fully ordered and no evidence was found for a compositionally segregated microstructure. These observations could not be reconciled in terms of a "space-charge" model; rather, they supported a charge-balanced, "random-site" structure for the 1:1 cation-ordered Ba(β_1/2'β_1/2")O₃ phases.     

Phase Relations in the Pyrochlore-Rich Part of the Bi2O3−TiO2−Nd2O3 System

In this study we used solid-state synthesis to determine the phase relations in the pyrochlore-rich part of the Bi₂O₃−TiO₂−Nd₂O₃ system at 1100°C. The samples were analyzed using X-ray powder diffraction and scanning electron microscopy with energy- and wavelength-dispersive spectroscopy. A single-phase pyrochlore ceramic was obtained with the addition of 4.5 mol% of Nd₂O₃. We determined the solubility limits for the three solid solutions: (i) the pyrochlore solid solution Bi_{(1.6–1.08 x )}Nd _x Ti₂O_{(6.4+0.3 x )}, where 0.25< x <0.96; (ii) the solid solution Bi_{4− x} Nd _x Ti₃O₁₂, where 0< x <2.6; and (iii) the Nd_{2− x} Bi _x Ti₂O₇ solid solution, where 0< x <0.35. The determined phase relations in the pyrochlore-rich part are presented in a partial phase diagram of the Bi₂O₃−TiO₂−Nd₂O₃ system in air at 1100°C.