Upconversion Luminescence of Gd<Subscript>2</Subscript>O<Subscript>3</Subscript> Nanocrystals Doped with Er<Superscript>3+</Superscript> and Yb<Superscript>3+</Superscript> Ions

The upconversion luminescence (UCL) of nanocrystalline gadolinium oxide (Gd₂O₃) doped with Er³⁺ and Yb³⁺ ions has been studied in the temperature range of 90–400 K. The nanocrystals were synthesized by chemical vapor deposition and possessed a cubic crystalline structure with an average particle size within 48–57 nm. It is established that the USL intensity in the red (⁴F_9/2 → ⁴I_15/2 transition in Er3+ ion) and green (⁴S_3/2 → ⁴I_15/2 transition) spectral regions depends on the sample temperature and concentration of dopant ions, as well as on the additional structural defects (anion vacancies) created in the crystal lattice by the introduction of Zn²⁺ ions or irradiation with high-energy (10 MeV) electrons. The luminescence efficiency and spectrum of the upconversion phosphor are determined by energy transfer processes.     

Highly efficient cooperative up-conversion of Yb<Superscript>3+</Superscript> in NaYF<Subscript>4</Subscript>

Strong blue cooperative up-conversion emission around 475 nm has been observed in Yb³⁺-doped hexagonal NaYF₄. The influence of concentration of the Yb³⁺ ion on the luminescence intensity is investigated. It is found that the sample shows the strongest cooperative luminescence when the Yb³⁺ ion concentration is 75%. The investigation shows that hexagonal NaYbF₄ is an efficient blue up-converted phosphor, which might be potentially applicable in three-dimensional solid-state fluorescence display.     

Influence of Mn<Superscript>2+</Superscript> on the up-conversion emission performance of Mn<Superscript>2+</Superscript>, Yb<Superscript>3+</Superscript>, Er<Superscript>3+</Superscript>: ZnWO<Subscript>4</Subscript> green phosphors

The Mn²⁺, Yb³⁺, Er³⁺: ZnWO₄ green phosphors are synthesized successfully through the high temperature solid state reaction method. The micro-structure and morphology have been investigated by means of XRD and EDS. The doped concentrations of Mn²⁺, Yb³⁺, Er³⁺ are measured by ICP. The absorption spectra and emission spectra with different doped concentrations of Mn²⁺ are presented to reveal the influence of Mn²⁺ on the green up-conversion performance. Excited with 970 nm LED, the up-conversion emission peak at 547 nm is obtained and the CIE spectra as well as the green light photo are also presented. The results indicate that the Mn²⁺ ions play the role of the luminescence adjustment in the up-conversion process, which can improve the up-conversion green emission intensity effectively. The luminescence adjustment mechanism of Mn²⁺ ions in Mn²⁺, Yb³⁺, Er³⁺: ZnWO₄ green phosphors has been discussed. The crystal parameters of Dq, B and C are calculated to evaluate the energy level split effect.     

Luminescence of GaS:Er<Superscript>3+</Superscript> and GaS:Er<Superscript>3+</Superscript>,Yb<Superscript>3+</Superscript> layered crystals

Data are presented on the 300-K photoluminescence in GaS crystals doped with Er³⁺ or codoped with Er³⁺ and Yb³⁺. IR excitation (λ_ex = 976 nm) gives rise to anti-Stokes luminescence in GaS:Er³⁺ (0.1 at %) and GaS:Er³⁺,Yb³⁺ (0.1 + 0.1 at %) and leads to an increased intensity of the emission due to the ⁴ I _11/2 → ⁴ I _15/2 transitions. The anti-Stokes luminescence is shown to result from consecutive absorption of two photons by one Er³⁺ ion, and the increased intensity of Er³⁺ luminescence in GaS: Er³⁺,Yb³⁺ is due to energy transfer from Yb³⁺ to Er³⁺.     

Emission analysis of Pr<Superscript>3+</Superscript> &; Ho<Superscript>3+</Superscript>: Ca<Subscript>4</Subscript>GdO(BO<Subscript>3</Subscript>)<Subscript>3</Subscript> powder phosphors

Emission spectral results of Pr³⁺ & Ho³⁺ ions doped Ca₄GdO(BO₃)₃ powder phosphors are reported here. XRD, SEM and FTIR measurements have been carried out for them. The emission spectrum of Pr³⁺: Ca₄GdO(BO₃)₃ has shown an emission transition ¹D₂ → ³H₄ at 606 nm with λ_exci = 480 nm (³H₄ → ³P₀) and Ho³⁺: Ca₄GdO(BO₃)₃ phosphor has shown an emission transition ⁵S₂ → ⁵I₈ at 549 nm with λ_exci = 447 nm (⁵I₈ → ⁵F₁). Emission performances of these two phosphors have been explained in terms of energy level diagrams.     

Crystal structure and luminescence property of a single-phase white light emission phosphor Sr<Subscript>3</Subscript>YNa(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>F:Dy<Superscript>3+</Superscript>

A series of single-phase Sr₃YNa(PO₄)₃F:Dy³⁺ phosphors were successfully synthesized via a conventional solid state reaction process. The powder X-ray diffraction patterns were utilized to confirm the phase composite and crystal structure. The phosphor could be excited by the ultraviolet visible light in the region from 300 to 420 nm, and it shown two dominant emission bands peaking at 484 nm (blue light) and 580 nm (yellow light) which originated from the transitions of ⁴F_9/2→⁶H_15/2 and ⁴F_9/2→⁶H_13/2 of Dy³⁺, respectively. The optimum dopant concentration of Dy³⁺ ions was confirmed to be 7 mol% in Sr₃YNa(PO₄)₃F:Dy³⁺ system and the concentration quenching mechanism is dipole–dipole interaction. The lifetime values of Dy³⁺ ions at different concentrations (x?=?0.03, 0.05, 0.07, 0.09 and 0.11) were determined to be about 0.855, 0.759, 0.686, 0.606 and 0.546 ms, respectively. The thermal stability of luminescence of Sr₃YNa(PO₄)₃F:0.07Dy³⁺ phosphor was also investigated and the activated energy was deduced to be 0.228 eV, which shows good thermal stability. The chromaticity coordinates fall in the white-light region calculated by the emission spectrum. These results show that Sr₃YNa(PO₄)₃F:Dy³⁺ phosphor can be a promising white emitting phosphor for white LEDs.     

Synthesis of Er<Superscript>3+</Superscript> and Er<Superscript>3+</Superscript> : Yb<Subscript>3+</Subscript> doped sol-gel derived silica glass and studies on their optical properties

Er₃₊ and Er₃₊ : Yb₃₊ doped optical quality, crack and bubble free glasses for possible use in making laser material have been prepared successfully through sol-gel route. The thermal and optical, including UV-visible absorption, FTIR etc characterizations were undertaken on the samples. The absorption characteristics of Er₃₊ doped samples clearly revealed the absorption due to Er₃₊ ions. On the other hand Yb₃₊ : Er₃₊ doped samples showed enhanced absorption due to² F _7/2 →² F _5/2 transition. The absorption and emission cross-section for² F _7/2 ↔² F _5/2 of Yb³⁺ were estimated. FTIR absorption spectra have clearly shown the reduction of the absorption peak intensity with heat treatment in the range 3700–2900 cm⁻¹. The 960 cm^-1 band also showed progressive decrease in the absorption band peak intensity with heat treatment. The result of the investigations with essential discussions and conclusions have been reported in this paper.     

Preparation and characterization of a new long afterglow phosphor CaSnO<Subscript>3</Subscript>: Yb<Superscript>3+</Superscript>

A new phosphor CaSnO₃: Yb³⁺ was synthesized by a traditional solid-state reaction and the luminescent properties were investigated. The phosphors are well crystallized at 1200?°C. The excitation and the emission spectra show the characteristic broad of the Sn²⁺ ion and the X-ray photoelectron spectroscopy demonstrate the existence of Sn²⁺ ions caused by the doping of Yb³⁺ ions. The CaSnO₃: Yb³⁺ phosphor showed a typical afterglow behavior when the UV source was switched off. Thermal simulated luminescence study indicated that the persistent afterglow of CaSnO₃: Yb³⁺ phosphor was generated by the suitable electron or hole traps which were resulted from doping the calcium stannate host with rare-earth ions (Yb³⁺).     

Synthesis and luminescent characterization of YAl<Subscript>3</Subscript>(BO<Subscript>3</Subscript>)<Subscript>4</Subscript>:Tb<Superscript>3+</Superscript> phosphors

YAl₃(BO₃)₄:Tb³⁺ phosphors were fabricated by the sol–gel method. The phosphor showed prominent luminescence in green due to the magnetic dipole transition of ⁵D₄–⁷F₅. Structural characterization of the luminescent material was carried out with X-ray powder diffraction (XRD) analysis. Luminescence properties were analyzed by measuring the excitation and photoluminescence spectra. Photoluminescence measurements indicated that the phosphor exhibited bright green emission at about 541 nm under UV excitation. It is shown that the 11% of doping concentration of Tb³⁺ ions in YAl₃(BO₃)₄:Tb³⁺ phosphors is optimum.     

Green and red upconversion emissions of Er<Superscript>3+</Superscript>/Yb<Superscript>3+</Superscript>-codoped SrTiO<Subscript>3</Subscript> powder prepared by a polymeric precursor method

Ultrafine Er³⁺/Yb³⁺-codoped SrTiO₃ (SEYT) powders in cubic form have been prepared by a poly-meric precursor method. The single phase perovskite for the obtained material was observed at low temperature. An efficient infrared-to-visible conversion in SEYT perovskite will be reported. Visible emissions at 550 and 663 nm corresponding to the ²S_3/2 − ⁴I_15/2 and ⁴F_9/2 − ⁴I_15/2 transitions, respectively, were observed under continuous wave excitation at 980 nm. An enhancement of the visible upconversion luminescence in Er³⁺/Yb³⁺ codoped samples was confirmed due to efficient energy transfer from Yb³⁺ to Er³⁺ ions. The quadratic pump power dependence of these emissions indicated the contribution of two photons to the upconversion process. The text was submitted by the authors in English.     

Structural and optical characterization of RE (Eu<Superscript>2+</Superscript>, Ce<Superscript>3+</Superscript>) doped SrMg<Subscript>2</Subscript>Al<Subscript>6</Subscript>Si<Subscript>9</Subscript>O<Subscript>30</Subscript> nanocrystalline phosphor

This article present the reports on optical study of Eu²⁺ and Ce³⁺ doped SrMg₂Al₆Si₉O₃₀ phosphors, which has been synthesized by combustion method at 550 °C. Here SrMg₂Al₆Si₉O₃₀:Eu²⁺ emission band observed at 425 nm by keeping the excitation wavelength constant at 342 nm, whereas SrMg₂Al₆Si₉O₃₀:Ce³⁺ ions shows the broad emission band at 383 nm, under 321 nm excitation wavelength, both the emission bands are assigned due to 5d–4f transition respectively. Further, phase purity, morphology and crystallite size are confirmed by XRD, SEM and TEM analysis. However, the TGA analysis is carried out to know the amount of weight lost during the thermal processing. The CIE coordinates of SrMg₂Al₆Si₉O₃₀:Eu²⁺ phosphor is observed at x?=?0.160, y?=?0.102 respectively, which may be used as a blue component for NUV-WLEDs. The critical distance of energy transfer between Ce³⁺ ions and host lattice is found to be 10.65 Å.     

Ultraviolet upconversion luminescence in Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Yb<Superscript>3+</Superscript>,Tm<Superscript>3+</Superscript> nanocrystals and its application in photocatalysis

Infrared-to-ultraviolet upconversion luminescence agent Y₂O₃:Yb³⁺,Tm³⁺ was prepared by a combustion method using citrate as a fuel/reductant. The prepared sample was characterized by X-ray diffraction, SEM, and fluorescence spectrophotometer. Two unusual ¹I₆ → ³H₆ (~297 nm) and ¹D₂ → ³H₆ (~363 nm) emissions from Tm³⁺ ions were observed at room temperature under 980-nm laser excitation. The change of upconversion emission intensity depending on the Yb³⁺ concentrations was discussed. The results showed that modest Yb³⁺ doping could make the upconversion emission of Tm³⁺ intense, and high Yb³⁺ concentrations might lead to fluorescence quenching. Moreover, the influence of ultraviolet upconversion luminescence on the photodegradation of methyl orange aqueous solution under solar light irradiation in the presence of TiO₂ catalyst doped with Y₂O₃:Yb³⁺,Tm³⁺ was also investigated. It was concluded from the experiment of this study that TiO₂/Y₂O₃:Yb³⁺,Tm³⁺ composite had higher photocatalytic activity than pure TiO₂ under solar light. This study would make TiO₂ utilize sunlight more efficiently and accelerate the practical application of photocatalytic technology in water treatment region.     

The comparison: photoluminescence and afterglow behavior in CaSnO<Subscript>3</Subscript>:Dy<Superscript>3+</Superscript> and Ca<Subscript>2</Subscript>SnO<Subscript>4</Subscript>:Dy<Superscript>3+</Superscript> phosphors

This paper reports the comparison of photoluminescence and afterglow behavior of Dy³⁺ in CaSnO₃ and Ca₂SnO₄ phosphors. The samples containing CaSnO₃ and Ca₂SnO₄ were prepared via solid-state reaction. The properties have been characterized and analyzed by utilizing X-ray diffraction (XRD), photoluminescence spectroscope (PLS), X-ray photoelectron spectroscopy (XPS), afterglow spectroscopy (AS) and thermal luminescence spectroscope (TLS). The emission spectra revealed that CaSnO₃:Dy³⁺ and Ca₂SnO₄:Dy³⁺ phosphors showed different photoluminescence. The Ca₂SnO₄:Dy³⁺ phosphor showed a typical ⁴F_9/2 to ⁶H_j energy transition of Dy³⁺ ions, with three significant emissions centering around 482, 572 and 670 nm. However, the CaSnO₃:Dy³⁺ phosphor revealed a broad T₁ → S₀ transitions of Sn²⁺ ions. The XPS demonstrate the existence of Sn²⁺ ions in CaSnO₃ phosphor caused by the doping of Dy³⁺ ions. Both the CaSnO₃:Dy³⁺ and Ca₂SnO₄:Dy³⁺ phosphors showed a typical triple-exponential afterglow when the UV source switched off. Thermal simulated luminescence study indicated that the persistent afterglow of CaSnO₃:Dy³⁺ and Ca₂SnO₄:Dy³⁺ phosphors was generated by the suitable electron or hole traps which were resulted from the doping the calcium stannate host with rare-earth ions (Dy³⁺).     

Persistent luminescence of Zn<Subscript>2</Subscript>GeO<Subscript>4</Subscript>:Mn<Superscript>2+</Superscript>/Pr<Superscript>3+</Superscript> phosphors

Zn₂GeO₄, Zn₂GeO₄:Mn²⁺, Zn₂GeO₄:Pr³⁺ and Zn₂GeO₄:Mn²⁺/Pr³⁺ phosphors were fabricated by a solid state reaction. The phase and luminescent properties of the fabricated phosphors were investigated. The XRD patterns show that all of the fabricated phosphors have an orthorhombic structure. The fabricated Zn₂GeO₄ shows an emission band in the range of 350–550 nm. The fabricated Zn₂GeO₄:Mn²⁺ and Zn₂GeO₄:Pr³⁺ phosphors show emission bands corresponding to Mn²⁺ and Pr³⁺ ions, respectively. The fabricated Zn₂GeO₄:Mn²⁺/Pr³⁺ phosphor shows the emission band results from Mn²⁺ and the codoped Pr³⁺ enhances the emission intensity of Mn²⁺. Moreover, Zn₂GeO₄:Mn²⁺/Pr³⁺ phosphor exhibits longer decay time than that of Zn₂GeO₄:Mn²⁺. The higher intensity and longer lifetime of Mn²⁺ emission are induced by the energy transfer from Pr³⁺ of various vacancies to Mn²⁺ in Zn₂GeO₄:Mn²⁺/Pr³⁺ phosphors.     

Synthesis,crystal structure and luminescence in Ca<Subscript>3</Subscript>Al<Subscript>2</Subscript>O<Subscript>6</Subscript>

Bluish green emitting phosphor, Ca₃Al₂O₆:Ce³⁺, is prepared by low-temperature combustion method. X-ray diffraction, photoluminescence, scanning electron microscopy techniques are used to characterize the synthesized phosphor. The most efficient bluish green (483 nm) emission is observed under the excitation by near UV light. The emission characteristics are credited to 5d → 4f type transitions in Ce³⁺. The luminescence properties of Eu²⁺ are predicted for the first time from those of Ce³⁺. Also, photoluminescence of Eu³⁺ is studied in the same host. The emission spectrum of Ca₃Al₂O₆:Eu³⁺ shows the peak at 592 (orange) and 614 nm (red) wavelengths. Ca₃Al₂O₆:Ce³⁺phosphor can be a potential blue phosphor for field emission display, solid-state lighting and LED.     

Synthesis and laser-excited IR luminescence of Y<Subscript>1 − <Emphasis Type="Italic">x</Emphasis></Subscript>Yb<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>PO<Subscript>4</Subscript> solid solutions

We have determined the composition range of solid solutions in the binary system YPO₄-YbPO₄ and identified the key trends in the composition dependence of their IR Stokes luminescence intensity and decay time in the range 0.96–1.1 μm. The results were used to develop a new narrow-band IR phosphor, YPO₄:Yb³⁺. Under 0.940-μm laser excitation, this phosphor offers an increased IR Stokes luminescence intensity in the range 0.96–1.1 μm (about twice as high as that of the well-known commercially available phosphors L-54 and FSD-546-2), with an afterglow time of 1700–1800 μs.     

NIR-excited NIR and visible luminescent properties of amphipathic YVO<Subscript>4</Subscript>: Er<Superscript>3+</Superscript>/Yb<Superscript>3+</Superscript> nanoparticles

This article reports the luminescence properties of amphipathic YVO₄:Er³⁺/Yb³⁺ nanoparticles (average grain size ca. 20 nm) obtained by an oleate-aided hydrothermal process. Depending on the upconversion (UPC) and downconversion (DWC) processes, they show luminescence in the visible and near-infrared (NIR) regions, respectively, by 980-nm excitation. The sample doped with Er³⁺:2.5 mol% and Yb³⁺:10 mol% showed the highest luminescence intensity in both the visible and NIR regions as a result of efficient energy transfer from Yb³⁺ to Er³⁺ ions. The hydrothermal treatment greatly enhanced both the DWC and UPC luminescence efficiencies. This is due to the reduction in the concentration of surface defects and ligands, accompanied by grain growth. NIR Fluorescence microscopy revealed for the first time that DWC luminescence is sufficiently intense for application of these nanocrystals as a NIR bioprobe.     

Color-tunable luminescence properties of Sm<Superscript>3+</Superscript>/Dy<Superscript>3+</Superscript> co-doped NaLa(MoO<Subscript>4</Subscript>)<Subscript>2</Subscript> phosphors and their energy transfer mechanism

The Sm³⁺, Dy³⁺ doped and Sm³⁺/Dy³⁺ co-doped NaLa(MoO₄)₂ spherical phosphors were hydrothermally synthesized by the EDTA-2Na mediated method. Under the excitation of 297 nm, the quenching concentration of Sm³⁺ in NaLa(MoO₄)₂ host was determined to be 13%, and the concentration quenching mechanism was discussed to be the electric quadrupole–quadrupole interaction. After Sm³⁺ and Dy³⁺ ions were co-doped into the NaLa(MoO₄)₂ host, the energy transfer behaviors resulted from Dy³⁺ to Sm³⁺ ions were investigated by the help of the luminescent spectra of the obtained phosphors. By varying co-doping concentrations of Sm³⁺/Dy³⁺ ions, the emission color of NaLa(MoO₄)₂:Sm³⁺/Dy³⁺ can be tuned from reddish-orange, pink and white to bluish-green. The CIE chromaticity coordinate, the correlated color temperature and the quantum efficiency of NaLa_0.87(MoO₄)₂:1%Sm³⁺, 12%Dy³⁺ were calculated to be (0.356, 0.320), 4353 K and 20%, respectively. Furthermore, in the temperature-dependent analysis, it presented good thermal stability, which can become a promising single-phased white-emitting phosphor for white LEDs devices. Based on these results, the possible energy transfer mechanism between Dy³⁺ and Sm³⁺ in NaLa(MoO₄)₂:Sm³⁺/Dy³⁺ was also proposed.     

Synthesis,tunable luminescence and thermal stability of Mg<Subscript>2</Subscript>Al<Subscript>4</Subscript>Si<Subscript>5</Subscript>O<Subscript>18</Subscript>:Ce<Superscript>3+</Superscript>/Mn<Superscript>2+</Superscript> phosphors

Ce³⁺/Mn²⁺ singly doped and codoped Mg₂Al₄Si₅O₁₈ phosphors were synthesized by a solid state reaction. The phase, luminescent properties and thermal stability of the synthesized phosphors were investigated. Ce³⁺ and Mn²⁺ singly doped Mg₂Al₄Si₅O₁₈ phosphors show emission bands locating in blue and yellow–red regions, respectively. In Ce³⁺ and Mn²⁺ codoped Mg₂Al₄Si₅O₁₈, tunable luminescence was obtained because of the energy transfer from Ce³⁺ to Mn²⁺. In Mg₂Al₄Si₅O₁₈:Ce³⁺/Mn²⁺ phosphors with a fixed Ce³⁺ concentration, energy transfer efficiency increases with the increasing Mn²⁺ concentration, which is confirmed by the continually decreasing intensity and shortening decay time of Ce³⁺ emission. Moreover, the luminescent properties and thermal stability provide a great significance on the applications in the field of light emitting diodes.     

Hydrothermal synthesis of NaLa(WO<Subscript>4</Subscript>)<Subscript>2</Subscript>:Eu<Superscript>3+</Superscript> octahedrons and tunable luminescence by changing Eu<Superscript>3+</Superscript> concentration and excitation wavelength

NaLa(WO₄)₂:Eu³⁺ phosphors with different Eu³⁺ concentrations have been synthesized by a hydrothermal method. The phase is confirmed by XRD analysis, which shows a pure-phase NaLa(WO₄)₂ XRD pattern for all of NaLa(WO₄)₂:Eu³⁺ phosphors. The SEM and TEM images indicate that all of NaLa(WO₄)₂:Eu³⁺ phosphors have a octahedral morphology. These suggest that the Eu³⁺ doping has no influence on the structure and growth of NaLa(WO₄)₄ particles. By monitoring the emission of Eu³⁺ at 615 nm, NaLa(WO₄)₂:Eu³⁺ phosphors show excitation bands originating from both host and Eu³⁺ ions. Under the excitation at 271 nm corresponding to WO₄ ^2? groups, emission bands coming from the ¹A₁ → ³T₁ transition with the WO₄ ^2? groups and the ⁵D₀ → ⁷F_j (j = 0, 1, 2, 3 and 4) transitions of Eu³⁺ are observed. The emission intensity relating to WO₄ ^2? groups decreases with increasing Eu³⁺ concentration. But emission intensities of Eu³⁺ increase firstly and then decreases because of concentration quenching effect. Under the excitation at 395 nm corresponding to ⁷F₀ → ⁵L₆ transition of Eu³⁺, only characteristic Eu³⁺ emission bands can be observed. The results of this work suggest that tunable luminescence can be obtained for Eu³⁺ doped NaLa(WO₄)₂ phosphors by changing Eu³⁺ concentration and excitation wavelength.