低截留分子量聚醚砜超滤膜

以聚醚砜(PES)为原料,均苯三甲酸(TMA)为添加剂,采用浸没沉淀相转化法制备聚醚砜超滤基膜,之后将聚乙烯醇(PVA)溶液涂覆在膜表面,经加热交联得到低截留分子量超滤膜。实验结果表明,随着聚乙烯醇浓度升高,截留分子量先减小再增加;随着热处理温度的升高,水通量减少,截留分子量减小。聚乙烯醇质量浓度为0.1%,80℃加热10 min,膜的截留分子量为900,纯水通量为6.10 L/(m~2·h)。红外光谱分析证实PVA与TMA反应生成了交联结构。     

二氧化硅填充聚醚砜超滤膜

本文通过在聚醚砜中引入活性炭粉和无定型二氧化硅粒子，以N，N-二甲基甲酰胺为溶剂，以水为凝固浴，利用相转化湿法成膜机理，制得了一系列不同粒子含量的聚醚砜超滤平板膜。通过扫描电子显微镜对膜结构进行了观察和对比研究，并对膜的纯水通量和鸡蛋卵清蛋白的截留进行了测试，结果发现：二氧化硅的加入，改变了铸膜液的浊点组成；产生了大量的界面空隙，即界面孔：增加了膜孔的贯通性；提高了膜的亲水性；使膜的通量大大提高，并且保持了很好的截留率。而活性炭粉填充聚醚砜超滤膜的综合性能远远差于二氧化硅填充聚醚砜超滤膜。     

聚醚砜和磺化聚醚砜膜结构及性能研究

采用电镜和孔径分布测定仪对自制聚醚砜( PES)和磺化聚醚砜(SPES)膜进行表征,根据Darcy-Poiseuille定律研究PES膜和SPES膜过滤牛血清蛋白液(BSA)阻力分布情况.结果表明,PES膜孔径为0.22～0.27 μm,初始纯水通量为642 L·m-2·h-1,过滤质量浓度为1 g·L-1的BSA溶液时平衡通量为30.4～31.9 L·m-2· h-1; SPES膜孔径为5.2～11.1 nm,初始纯水通量为8.1 L·m-2·h-1,质量浓度为1 g·L-1的BSA时平衡通量为3.4～6.9 L· m-2·h-1.过滤时PES膜阻力主要集中在吸附和堵孔阻力,2者相加为总阻力的91.1％;而SPES膜阻力主要集中在膜本身的阻力,为总阻力的41.8％,其次为堵孔阻力,占总阻力的38.3％.经清洗后,PES膜的纯水通量可以恢复到82％,而SPES膜可以恢复到494％.     

杂萘联苯聚醚砜超滤膜的研制

以杂萘联苯聚醚砜(PPES)为膜材料,N-甲基-2-吡咯烷酮(NMP)为溶剂,采用相转化法制备了非对称超滤膜.结果表明,聚合物浓度的变化、添加剂含量的变化、凝胶浴温度或停留蒸发时间的改变都会影响超滤膜的性能,所制得的PPES超滤膜在0.1 Mpa的操作压力下对PEG10000的截留率高于95%,纯水通量可达632 L·m-2·h-1.     

磺化聚醚砜超滤膜的制备研究

本文研究了磺化聚醚砜的制备和膜性能的测试 ,通过选择适当的配方研制性能稳定的较小孔径的超滤膜。该膜在 0 .2Mpa操作压力下对聚乙二醇 1 0 0 0 0的截留率大于 95 % ,水通量为 5 5L/m2 H ,通过扫描电镜观察膜的断面结构 ,结果表明 :PES膜断面形态属于典型的非对称指状孔结构 ,SPES膜断面形态是海绵层结构     

不同截留分子量超滤膜包浓缩狂犬病病毒的效果

目的比较不同截留分子量超滤膜包浓缩狂犬病病毒(rabies virus,RV)的效果。方法将RV固定毒3aG-V株按0.01 MOI比例接种至Vero细胞中,制备RV原液,分别用截留分子量100 KD和300 KD的膜包超滤浓缩60倍,β-丙内酯灭活后,验证病毒液浓缩过程膜下液的病毒灭活效果;采用Sepharose 4FF凝胶层析纯化灭活的病毒浓缩液,Lowry法测定病毒浓缩液和纯化液中的蛋白质含量;酶联免疫法测定病毒浓缩过程膜下液、浓缩液和纯化液中的RV抗原含量。结果 100 KD和300 KD的超滤膜包均能有效截流RV,3次试验膜下液RV抗原含量均为0 IU/ml,观察期内小鼠均健存。300 KD膜包超滤的浓缩液和纯化液比100 KD超滤膜包超滤的浓缩液和纯化液中杂蛋白含量低,抗原含量高。结论截留分子量300 KD的膜包比100 KD的膜包更适用于RV的浓缩。     

磺化聚醚砜(SPES)/聚醚砜(PES)合金超滤膜的研究

本文研究了磺化聚醚砜 (SPES) /聚醚砜 (PES)合金组份变化对膜性能的影响 ,通过选择适当的合金比例研制得到超滤膜 ,在 0 .2Mpa操作压力下 ,对聚乙二醇分子量为 1万的截留率大于 90 % ,水通量为 80L/m2 ·h ,对阴离子脱盐率PO3 -4 >SO2 -4 >CL-。通过扫描电镜观察膜的断面结构 ,结果表明 :PES膜断面形态属于典型的非对称指状孔结构 ,SPES/PES膜断面形态是致密的海绵状结构 ,致密层部分比SPES薄 ,SPES膜断面形态是较厚的海绵状结构 ,致密层部分多     

聚醚砜超滤膜的研制

本文以新型工程塑料聚醚砜为原料,制备出了聚醚砜超滤膜。此种膜对10万分子量的聚乙烯醇截留率可达95％以上,透水率可达2.5ml/(cm~2·h)以上。对膜的制备条件,如原料配比、制膜液的浓度、环境温度和蒸发时间、凝固浴的温度和浓度等进行了较详细地研究。     

超滤膜截留性能测定方法

本文对用聚乙二醇、卵清蛋白和牛血清白蛋白作为基准物质测定超滤膜截留性能的方法进行了比较 ,并对其可靠性进行了探讨。结果表明 ,用聚乙二醇法测量膜截留率是不可靠的 ,而应采用卵清蛋白、牛血清白蛋白等球形生物分子作为基准物质。     

金属-聚乙烯醇-二醋酸纤维素共混复合亲水超滤膜的制备

在大孔径金属纤维毡上制备了金属-聚乙烯醇-二醋酸纤维素(金属-PVA-CA)共混复合超滤膜及金属-NaCl改性PVA-CA共混复合超滤膜。该复合超滤膜在操作压力为0.25-0.45 MPa,处理质量浓度为1000 mg/L的含油乳化液,可获得40-70 L／(m2·h)的透液通量,COD截留在90％以上。研究还表明金属-NaCl改性PVA-CA共混复合超滤膜的综合性能略优于金属-PVA-CA共混复合超滤膜。     

低截留分子质量新型聚芳醚腈酮超滤膜的研制

以新型聚芳醚腈酮为膜材料 ,以N -甲基 - 2 -吡咯烷酮 (NMP)为溶剂 ,研究了聚合物浓度、添加剂种类及含量、凝胶浴温度等对超滤膜性能的影响。结果表明 ,聚合物质量分数以 1 2 %～ 1 3 %为合适的制膜浓度 ,以聚乙二醇PEG - 4 0 0为添加剂时获得了高截留率和高水通量的超滤膜。随着凝胶浴温度的升高 ,水通量明显增大 ,而截留率有所下降 ,而共聚物的浓度增加则有相反的效果。制得的超滤膜具有较低的截留分子量 (PEG- 2 0 0 0 ) ,将制得的超滤膜用于达旦黄、黄X-G等染料的分离 ,截留率均达 90 %以上     

聚乙烯醇-醋酸纤维素共混超滤膜的制备与性能研究

用聚乙烯醇(PVA)、醋酸纤维素(CA)、冰醋酸、水为制膜原料,用相转化制备了PVA-CA共混超滤膜.在一定范围内研究了不同膜液组成对超滤膜性能的影响,得到了较佳的膜液配方.制备的PVA-CA共混超滤膜在操作压力0.30MPa下,处理质量浓度为1000mg/L的水油型模拟含油乳化液,其渗透速率约40L/(m2@h2),除油率可达90%以上,并且此超滤膜的耐水性和溶胀性均优于未改性的PVA超滤膜.     

聚砜超滤膜与低分子有机物交互作用的研究

选取聚砜平板超滤膜,采用间歇错流循环方式对离子型表面活性剂与低分子有机物的混合料液进行分离,考察了表面活性剂的浓度、操作压力等因素对超滤过程的影响,研究料液与膜之间的交互作用。结果表明,有机物与表面活性剂的混合料液的通量均高于自来水的通量;表面活性剂的浓度低于临界胶束浓度(CMC)时,膜通量随其浓度的增加而增加,而高于CMC时通量略有下降;改变操作压力,混合溶液的通量随压力的降低而减小,其中苯酚的通量变化不大,但均保持较高的渗透通量。     

Preparation and properties of soluble copolysulfoneimide and performance of solvent‐resistant ultrafiltration membrane

Soluble copolysulfoneimides were synthesized by thermal two‐step method in solution of N‐methyl‐2‐pyrrolidone. The used aromatic diamines were bis[4‐(3‐aminophenoxy)phenyl]sulfone (BAPS‐m) and 3,3′‐diaminosulfone, and dianhydrides were pyromellitic dianhydride, 4,4′‐oxyphthalic anhydride, and 3,3′,4,4′‐diphenylsulfone tetracarboxylic dianhydride. The molar ratio of diamines was changed to reduce the content of BAPS‐m. The thermal and mechanical properties of polyimides were investigated. The polyimide ultrafiltration membrane with molecular weight cut‐off of 10 kDa could be successfully prepared by phase‐inversion method. Various solvent (water, alcohols, acetone, and hexane) fluxes were measured to investigate solvent‐resistance and membrane behavior during solvent permeation. The activation energy relationship between hexane flux and viscosity with temperature was also studied. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 1024–1030, 2002     

磺化聚醚砜/纳米TiO2复合超滤膜制备及其抗污染机理

Membrane fouling is one of the major obstacles for reaching a high flux over a prolonged period of ultrafiltration (UF) process. In this study, a sulfonated-polyethersulfone (SPES)/nano-TiO2 composite UF membrane with good anti-fouling performance was fabricated by phase inversion and self-assembly methods. The TiO2 nanoparticle self-assembly on the SPES membrane surface was confirmed by X-ray photoelectron spectroscopy (XPS) and FT-IR spectrometer. The morphology and hydrophilicity were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM) and contact angle goniometer, respectively. The anti-fouling mechanism of composite UF membrane was discussed through the analysis of the micro-structure and component of UF membrane surface. The results showed that the TiO2 content and the micro-structure of the composite UF membrane surface had great influence on the separation and anti-fouling performance.     

新型温敏超滤膜处理印染废水的研究

印染废水中含有大量有机染料和重金属等物质,对生态环境及人类健康产生了严重的危害。以聚（N-异丙基丙烯酰胺）@聚苯乙烯（PNIPAM@PS）球形聚合物刷为主体,Cd（OH）₂纳米线作为牺牲层,聚碳酸酯（PC）膜为支撑层,经简单过滤制备得到对温度有响应性的高分子超滤膜。通过傅里叶变换红外光谱（FT-IR）、扫描电镜（SEM）、动态光散射仪（DLS）及水接触角测量仪对其进行表征,结果表明该超滤膜表面由PNIPAM@PS球形聚合物刷构成,其表面平整,结构规则,且具有良好的温度响应性。随后考察了PNIPAM@PS超滤膜对有机染料（甲基蓝和罗丹明B）和CdSe重金属颗粒的过滤效果,并通过紫外分光光度计（UV-vis）、原子荧光光谱仪（PL）等对其进行表征。结果显示,随着PNIPAM链增长、PS核粒径减小、实验操作压力增大,超滤膜的过滤效果显著改善。同时超滤膜的孔径可以通过温度实时调节,当环境温度高于PNIPAM链的LCST时,超滤膜的孔径较大;温度降低,超滤膜的孔径变小。PNIPAM@PS超滤膜的孔径可调节性使其在废水处理中有着广泛的应用前景。     

超滤膜在饮用水处理中临界通量的影响因素研究

超滤膜在临界通量以下过滤可不产生膜污染或产生极轻的膜污染,针对超滤膜在饮用水处理中的临界通量的影响因素,系统考察曝气、过滤方式和混凝沉淀预处理等对浸没式超滤膜处理松花江水临界通量的影响.结果表明,曝气强度达到10 m3/(m2·h),连续曝气可将超滤膜的临界通量提高5 L/(m2·h),曝气强度达到40 m3/(m2·...     

超滤膜技术概述

当今社会,超滤作为一种新型膜分离技术,应用的领域十分广泛,而且也获得了良好的效果。本文首先介绍了超滤技术的原理、四大有机高分子膜材料和相转化制膜中常用的浸没沉淀法和溶剂蒸发法,然后简述了超滤膜的优点、四大领域的应用、三大污染物质及防治措施,并把超滤膜技术多年后的研究方向和未来前景总结出来。指出超滤膜具有在水处理净化、食品提纯和中药分离等方面的诸多优势,接下来在广泛总结颗粒物、有机物和微生物污染的基础上,通过针对性的污染类别,遴选出高效的处理措施,并且能够显著提升超滤膜的抗菌抗污染性能,从而为超滤膜发展和实践运用提供可能。文中提出：今后研究的重点将是制备高性能、低成本、绿色化的超滤膜,并与其他膜分离技术协同作用于生产生活。     

聚丙烯腈超滤膜的制备

为了得到高性能的超滤膜,采用相转化法,以聚丙烯腈(PAN)为原料,N-甲基-吡咯烷酮(NMP)为溶剂,制备了聚丙烯腈超滤膜.采用纯水通量以及膜对牛血清蛋白(BSA)的截留率作为评价标准,并使用扫描电镜对膜结构进行表征.研究了聚合物质量分数、添加剂种类、凝胶浴温度、凝胶浴种类对膜性能的影响.研究发现:在一定范围内提高聚合...