New fluorine‐containing bissalicylidenimine–titanium complexes for olefin polymerization

Three new titanium complexes bearing salicylidenimine ligands—bis[(salicylidene)‐2,3,5,6‐tetrafluoroanilinato]titanium(IV) dichloride ( 1 ), bis[(3,5‐di‐tert‐butylsalicylidene)‐2,3,5,6‐tetrafluoroanilinato]titanium(IV) dichloride ( 2 ), and bis[(3,5‐di‐tert‐butylsalicylidene)‐4‐trifluoromethyl‐2,3,5,6‐tetrafluoroanilinato]titanium(IV) dichloride ( 3 )—were synthesized. The catalytic activities of 1 – 3 for ethylene polymerization were studied with poly(methylaluminoxane) (MAO) as a cocatalyst. Complex 1 was inactive in ethylene polymerization. Complex 2 at a molar ratio of cocatalyst to pre catalyst of Al_MAO/Ti = 400–1600 showed very high activity in ethylene polymerization comparable to that of the most efficient metallocene complexes and titanium compounds with phenoxy imine and indolide imine chelating ligands. It gave linear high‐molecular‐weight polyethylene [weight‐average molecular weight (M_w) ≥ 1,700,000. weight‐average molecular weight/number‐average molecular weight (M_w/M_n) = 4–5] with a melting point of 142°C. The ability of the 2 /MAO system to copolymerize ethylene with hexene‐1 in toluene was analyzed. No measurable incorporation of the comonomer was observed at 1:1 and 2:1 hexene‐1/ethylene molar ratios. However, the addition of hexene‐1 had a considerable stabilizing effect on the ethylene consumption rate and lowered the melting point of the resultant polymer to 132°C. The 2 /MAO system exhibited low activity for propylene polymerization in a medium of the liquid monomer. The polymer that formed was high‐molecular‐weight atactic polypropylene (M_w ～ 870,000, M_w/M_n = 9–10) showing elastomeric behavior. The activity of 3 /MAO in ethylene polymerization was approximately 70 times lower than that of the 2 /MAO system. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 95: 1040–1049, 2005     

FI Catalysts: A New Family of High Performance Catalysts for Olefin Polymerization

This paper reviews a new family of olefin polymerization catalysts. The catalysts, named FI catalysts, are based on non‐symmetrical phenoxyimine chelate ligands combined with group 4 transition metals and were developed using “ligand‐oriented catalyst design”. FI catalysts display very high ethylene polymerization activities under mild conditions. The highest activity exhibited by a zirconium FI catalyst reached an astonishing catalyst turnover frequency (TOF) of 64,900 s ^–1 atm ^–1, which is two orders of magnitude greater than that seen with Cp₂ZrCl₂ under the same conditions. In addition, titanium FI catalysts with fluorinated ligands promote exceptionally high‐speed, living ethylene polymerization and can produce monodisperse high molecular weight polyethylenes (M_w/M_n<1.2, max. M_n>400,000) at 50 °C. The maximum TOF, 24,500 min ^–1 atm ^–1, is three orders of magnitude greater than those for known living ethylene polymerization catalysts. Moreover, the fluorinated FI catalysts promote stereospecific room‐temperature living polymerization of propylene to provide highly syndiotactic monodisperse polypropylene (max. [rr] 98%). The versatility of the FI catalysts allows for the creation of new polymers which are difficult or impossible to prepare using group 4 metallocene catalysts. For example, it is possible to prepare low molecular weight (M_v∼10³) polyethylene or poly(ethylene‐co‐propylene) with olefinic end groups, ultra‐high molecular weight polyethylene or poly(ethylene‐co‐propylene), high molecular weight poly(1‐hexene) with atactic structures including frequent regioerrors, monodisperse poly(ethylene‐co‐propylene) with various propylene contents, and a number of polyolefin block copolymers [e.g., polyethylene‐b‐poly(ethylene‐co‐propylene), syndiotactic polypropylene‐b‐poly(ethylene‐co‐propylene), polyethylene‐b‐poly(ethylene‐co‐propylene)‐b‐syndiotactic polypropylene]. These unique polymers are anticipated to possess novel material properties and uses.     

A supported titanium postmetallocene catalyst: Effect of selected conditions on ethylene polymerization

Ethylene polymerization with a titanium complex [N,N‐ethylenebis(3‐methoxysalicylideneiminato)titanium dichloride] immobilized on the magnesium support with the formula MgCl₂(THF)_0.32(Et₂AlCl)_0.36 was studied. In particular, the effects of polymerization temperature, monomer pressure, and polymerization time on the activity of the catalyst and on the polyethylene properties (molecular weight and its distribution, melting point, crystallinity, and bulk density) were evaluated. The findings of investigations prove that the studied supported titanium catalyst is highly active in ethylene polymerization, and its activity increases with increasing temperature and monomer pressure. Moreover, stability of the catalytic systems is dependent on the activator type used. Me₃Al, when employed as an activator, makes the catalytic system undergo no deactivation in practice. The catalyst coupled with MAO turned out less stable. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Polyethylene‐b‐poly(ethylene glycol) diblock copolymers: New synthetic strategy and application

Polyethylene‐b‐poly (ethylene glycol) (PE‐b‐PEG) was successfully synthesized by a coupling reaction of hydroxyl‐terminated polyethylene (PE‐OH) and isocyanate‐terminated poly (ethylene glycol) (PEG‐NCO). PE‐OH was prepared by coordination chain transfer polymerization (CCTP) using 2,6‐bis[1‐(2,6‐diisopropylphenyl)imino ethyl] pyridine iron (II) dichloride /dry ethylaluminoxane (DEAO) /diethyl zinc (ZnEt₂) as catalyst and subsequent in situ oxidation with oxygen. The active centers of this catalyst system were counted, indicating that the active centers were more stable using DEAO as cocatalyst than using dry methylaluminoxane (DMAO) as cocatalyst. PEG‐NCO was synthesized through the condensation reaction of monomethylpoly(ethylene glycol) (PEG) with isophoronediisocyanate (IPDI). Subsequently, the thermal characterization, morphological characterization and the application of these diblock copolymers was investigated. The results indicated that the diblock copolymers were effective compatilizers for polyethylene/poly(ethylene glycol) blends. Meanwhile, they were excellent surface modification agents for polyethylene membrane and glass sheet, it can efficiently turn a hydrophobic surface into a hydrophilic surface, or vice versa. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42236.     

Ethylene Polymerization using Combined Ni and Ti Catalysts Supported in situ on MAO‐Modified Silica

Summary: Branched polyethylene/linear polyethylene blends (BPE/LPE) were prepared using the combined Ni(α‐diimine)Cl₂ ( 1 ) (α‐diimine = 1,4‐bis(2,6‐diisopropylphenyl)acenaphthenediimine) and {Tp^Ms*}TiCl₃ ( 2 ) (Tp^Ms* = hydridobis(3‐mesitylpyrazol‐1‐yl)(5‐mesitylpyrazol‐1‐yl)) catalysts supported in situ on methylaluminoxane (MAO)‐modified silica (4.0 wt.‐% Al/SiO₂). The polymerization reactions were performed in toluene at two different polymerization temperatures (0 and 30 °C) and several nickel molar fractions (x_Ni), using MAO as external cocatalyst. At all temperatures, the activities show an approximate linear correlation with x_Ni, indicating a non‐synergistic effect between the nickel and the titanium species. Higher activities were found at 0 °C. The melting temperatures for the polyethylene blends produced at 0 °C decrease as x_Ni increases in the medium, indicating good compatibility between the polyethylene phases made by both catalysts. The melting temperature (T_m) of the polyethylene blends was shown to depend on the order in which the catalysts were immobilized on the MAO‐modified silica support. The initial immobilization of 1 on the support ( 2 / 1 /SMAO‐4) affords polymers with a lower T_m than those produced with 1 / 2 /SMAO‐4. In addition, scanning electron microscopy (SEM) studies revealed that the spherical morphology of the supported catalyst is replicated in the polyethylene particles.

Influence of polymerization temperature on the activity of 1 / 2 /SMAO‐4 with varying x_Ni.     

(Co)polymerization of ethylene via nonmetallocene catalysts with diphenyl phosphoroso schiff‐base ligand

A series of novel nonmetallocene catalysts [N, O, P] with diphenyl phosphoroso ligands were synthesized by the treatment of phthaldialdehyde, substituted phenols, chlorodiphenyl phosphine with metal halides of TiCl₄ and ZrCl₄. The catalyst microstructure was characterized by ¹H NMR and EA. After activated by methylaluminoxane (MAO), these [N, O, P] catalysts were utilized to catalyze the polymerization of ethylene and the copolymerization of ethylene with 1‐octene. The results indicated that the obtained catalysts were highly efficient for ethylene polymerization and ethylene/1‐octene copolymerization. Structures and properties of the obtained polymers were measured by WAXD, DSC, GPC, and ¹³C NMR. The results indicated that polyethylene catalyzed by Cat. 3 possessed the highest weight‐average molecular weight of 1.025 × 10⁶ g/mol and the highest melting point of 136.3°C. The copolymer of ethylene/1‐octene catalyzed by Cat. 1 exhibited the highest 1‐octene incorporation content of 0.63 mol %. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42225.     

Synthesis of poly(1‐hexene)s end‐functionalized with phenols

Electrophilic alkylations of phenol/2,6‐dimethylphenol were performed with vinylidene‐terminated poly(1‐hexene)s using BF₃·OEt₂ catalyst. Vinylidene‐terminated poly(1‐hexene)s with M_n varying from 400 to 10000 were prepared by bulk polymerization of 1‐hexene at 50 to ?20 °C using Cp₂ZrCl₂/MAO catalysts. The phenol/2,6‐dimethylphenol‐terminated poly(1‐hexene)s was characterized by NMR (¹H, ¹³C), UV, IR and vapor phase osmometer (VPO). The isomer distribution (ortho, para and ortho/para) was determined by ¹³P NMR using a phosphitylating reagent, namely 2‐chloro‐1,3,2‐dioxaphospholane. The number‐average degree of functionality (F_n) >0.9 with >95% para selectivity could be achieved using low‐molecular‐weight oligomers of poly(1‐hexene)s. Copyright © 2005 Society of Chemical Industry     

Characterization of MAO‐Modified Silicas for Ethylene Polymerization

A series of methylaluminoxane (MAO)‐modified PQ and EP 12 silicas, calcined at 110, 250, and 450°C, were prepared. The resulting MAO‐modified supports were characterized by a set of complementary techniques: Fourier transform infrared spectroscopy (FT‐IR), scanning electron microscopy‐energy dispersive X‐ray spectroscopy (SEM‐EDX), small angle X‐ray scattering (SAXS), and thermal gravimetric analysis (TGA). The Al/Si ratios of the MAO‐modified PQ and EP12 silicas were in the ranges of 0.19–0.27 wt % and 0.17–0.30 wt %, respectively. MAO‐modified silicas were used in the polymerization of ethylene using an Et₂IndZrCl₂ catalyst. The MAO‐modified PQ silica showed higher activity in comparison to the MAO‐modified EP12. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 4568–4575, 2013     

Ethylene polymerization over (nBuCp)2ZrCl2/MAO catalytic system supported on aluminosilicate SBA‐15 mesostructured materials

Heterogeneous metallocene catalysts were prepared by incipient wetness impregnation of AlSBA‐15 (Si/Al = 4.8, 15, 30, 60, and ∞) mesostructured materials with (nBuCp)₂ZrCl₂/MAO. For comparative purposes commercial silica and silica–alumina (Si/Al = 4.8) supports were also impregnated with the MAO/metallocene catalytic system. A combination of X‐ray powder diffraction, nitrogen adsorption–desorption isotherms at 77 K, transmission electron microscopy, ICP‐atomic emission spectroscopy, and UV–vis spectroscopic data, were used to characterize the supports and the heterogeneous catalysts. Ethylene polymerizations were carried out in a schlenk tube at 70 °C and 1.2 bar of ethylene pressure. The polyethylene obtained was characterized by GPC, DSC, and SEM. Catalysts prepared with mesostructured SBA‐15 supports exhibited better catalytic performance than those supported on amorphous silica and silica–alumina. In general, higher ethylene polymerization activity was achieved if (nBuCp)₂ ZrCl₂/MAO catalytic system was heterogenized using supports with lower pore size in the range of the mesopores and lower Si/Al ratio. All catalysts produced high‐density polyethylene, with high crystallinity values and fibrous morphology when SBA‐15 mesostructured materials were used as supports. POLYM. ENG SCI., 2008. © 2008 Society of Plastics Engineers     

Preparation of ethylene/1‐octene copolymers from ethylene stock with tandem catalytic system

Tandem catalysis offers a novel synthetic route to the production of linear low‐density polyethylene. This article reports the use of homogeneous tandem catalytic systems for the synthesis of ethylene/1‐octene copolymers from ethylene stock as the sole monomer. The reported catalytic systems involving a highly selective, bis(diphenylphosphino)cyclohexylamine/Cr(acac)₃/methylaluminoxane (MAO) catalytic systems for the synthesis of 1‐hexene and 1‐octene, and a copolymerization metallocene catalyst, rac‐Et(Ind)₂ZrCl₂/MAO for the synthesis of ethylene/1‐octene copolymer. Analysis by means of DSC, GPC, and ¹³C‐NMR suggests that copolymers of 1‐hexene and ethylene and copolymers of 1‐octene and ethylene are produced with significant selectivity towards 1‐hexene and 1‐octene as comonomers incorporated into the polymer backbone respectively. We have demonstrated that, by the simple manipulation of the catalyst molar ratio and polymerization conditions, a series of branched polyethylenes with melting temperatures of 101.1–134.1°C and density of 0.922–0.950 g cm^?3 can be efficiently produced. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Self‐Immobilizing Precatalysts: Norbornene‐Bridged Zirconium ansa‐Metallocenes

We report here the synthesis of new tethered biscyclopentadienyl and bisindenyl zirconocenes, bearing one unsaturation on the interannular bridge, and their use as self‐immobilizing catalysts. They proved to be active catalysts towards ethylene polymerization in solution, with activities comparable to those displayed by commercial rac‐Et(Ind)₂ZrCl₂. When tested as self‐polymerization catalysts under suitable experimental conditions, they gave colored precipitates that, once reactivated with MAO, were significantly active in ethylene polymerization, although lower than those of the corresponding catalytic systems in solution. The molecular weights of the produced polymers were similar to those obtained with the same catalysts in solution, but their distribution resulted to be broader, with values typical of heterogeneous catalytic systems. From ¹³C NMR studies we had the first spectroscopic evidence of the actual incorporation of a metallocene of this type into a polymeric chain.     

Bimodal polyethylene promoted by novel nickel complex

A novel nickel complex, bis[2‐methyl‐2,4‐bis(2′‐pyridyl)‐1H‐1,5‐benzodiazepine]nickel dichloride, displayed good activity for oligomerization and polymerization of ethylene with the assistance of a co‐catalyst, methylaluminoxane (MAO). The oligomers were mainly olefins from C₄ to C₁₀, while the highly branched polyethylene (PE) had molecular weights (M_w) in the range 19 000–34 000. Bimodal distributions of the PE were clearly observed by both DSC and GPC measurements, while the spherulitic structure of the PE was shown in the morphology. Copyright © 2004 Society of Chemical Industry     

Ethylene polymerization by 3‐oxa‐pentamethylene bridged asymmetric dinuclear titanocene/MAO system

An asymmetric 3‐oxa‐pentamethylene bridged dinuclear titanocenium complex (CpTiCl₂)₂(η⁵‐η⁵‐C₉H₆(CH₂CH₂OCH₂CH₂)C₅H₄) ( 1 ) has been prepared by treating two equivalents of CpTiCl₃ with the corresponding dilithium salts of the ligand C₉H₇(CH₂CH₂OCH₂ CH₂)C₅H₅. The complex 1 was characterized by ¹H‐, ¹³C‐NMR, and elemental analysis. Homogenous ethylene polymerization catalyzed using complex 1 has been conducted in the presence of methylaluminoxane (MAO). The influences ofreaction parameters, such as [MAO]/[Cat] molar ratio, catalyst concentration, ethylene pressure, temperature, and time have been studied in detail. The results show that the catalytic activity and the molecular weight (MW) of polyethylene produced by 1 /MAO decrease gradually with increasing the catalyst concentration or polymerization temperature. The most important feature of this catalytic system is the molecular weight distribution (MWD) of polyethylene reaching 12.4, which is higher than using common mononuclear metallocenes, as well as asymmetric dinuclear titanocene complexes like [(CpTiCl₂)₂(η⁵‐η⁵‐C₉H₆(CH₂)_nC₅H₄)] (n = 3, MWD = 7.31; n = 4, MWD = 6.91). The melting point of polyethylene is higher than 135°C, indicating highly linear and highly crystalline polymers. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Blending ultrahigh‐molecular‐weight polyethylene and poly(ethylene/10‐undecen‐1‐ol) in one nascent particle

Ultrahigh‐molecular‐weight polyethylene (UHMWPE)/polar polyethylene (PE) composites were blended in one nascent particle by in situ polymerization with a hybrid catalyst. Polystyrene‐coated SiO₂ particles were used to support the hybrid catalyst. Fe(acac)₃/2,6‐bis[1‐(2‐isopropylanilinoethyl)] was supported on SiO₂ for the synthesis of UHMWPE, whereas [PhN?C(CH₃)CH?C(Ph)O]VCl₂ was immobilized on a polystyrene layer to prepare a copolymer of ethylene and 10‐undecen‐1‐ol (polar PE). Importantly, the core part of the supports (the polystyrene layer) exhibited pronounced transfer resistance to 10‐undecen‐1‐ol; this provided an opportunity to keep the inside iron active sites away from the poisoning of 10‐undecen‐1‐ol. Therefore, UHMWPE was simultaneously synthesized with polar PE by in situ polymerization. Interestingly, the morphological results show that UHMWPE and the polar PE were successfully blended in one nascent polymer. This improved the miscibility of the composites, where most of the chains were difficult to crystallize because of the strong interactions between the PE chains and polar chains. The blends showed an extremely low crystallinity, that is, 9.9%. Finally, the hydrophilic properties of the polymer composites were examined. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46652.     

Synthesis and characterization of monomeric and polymeric pyridinylimine‐based Ni(II) complexes and their catalytic activities in ethylene oligomerization

A new polymeric ligand was synthesized through the reaction of 4‐(pyridinylimine)phenol and formaldehyde in a basic medium, and its corresponding polymer–nickel complexes were formed in a 1:1 molar ratio. The synthesized compounds were characterized using elemental and spectral analyses. The monomeric and polymeric Ni(II) complexes (C₁ and C₂, respectively) were evaluated as catalyst precursors for ethylene oligomerization, using methylaluminoxane as an activator at two different ethylene pressures. C₂ was found to be a more effective pre‐catalyst than C₁, with the co‐catalyst having a similar effect in both cases. C₂ exhibited an activity of 1.282 × 10⁶ g (mol Ni)^?1 h^?1 bar^?1, with an Al:Ni ratio of 2000:1 at room temperature and 1 atm ethylene pressure. Meanwhile C₁ exhibited an activity of 1.126 × 10⁶ g (mol Ni)^?1 h^?1 bar^?1 under similar experimental conditions. At 5 atm ethylene pressure, C₁ favoured the formation of high‐density polyethylene, whereas C₂ favoured the formation of branched low‐density polyethylene. Copyright © 2012 Society of Chemical Industry     

The architecture of hydroxy‐functionalized aPS‐b‐random copolymer‐b‐PE via one‐pot strategy combining living free radical polymerization with coordination polymerization

The copolymerization of styrene with ethylene was promoted by CpTiCl₃/BDGE/Zn/MAO catalyst system combining free radical polymerization with coordination polymerization via sequential monomer addition strategy in one‐pot. The effect of polymerization conditions such as temperature, time, ethylene pressure, and Al/Ti molar ratio on the polymerization performance was investigated. The hydroxy‐functionalized aPS‐b‐random copolymer‐b‐PE triblock copolymer was obtained by solvent extraction and determined by GPC, DSC, WAXD, and ¹³C‐NMR. The DSC result indicated that the aPS‐b‐random copolymer‐b‐PE had a T_g at 87°C and a T_m at 119°C which attributed to the T_g of aPS segment and the T_m of PE segment, respectively. The microstructure of the hydroxy‐functionalized aPS‐b‐random copolymer‐b‐PE was further confirmed by WAXD, ¹³C‐NMR, and ¹H‐NMR analysis; and these results demonstrated that the obtained block copolymer consisted of aPS segment, S‐E random copolymer segment, and crystalline PE segment. The connection polymerization of the hydroxy‐functionalized aPS with random copolymer‐b‐PE was revealed by GPC results. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Unsymmetrical α‐diimine nickel (II) complex with rigid bicyclic ring ligand: Synthesis,characterization, and ethylene polymerization in the presence of AlEt2Cl

Unsymmetrical α‐diimine ligand 1 was successfully synthesized via condensation of trimethylaluminum (TMA) metalated 2‐methyl‐6‐isopropyl‐aniline with rigid bicyclic aliphatic diketone camphorquinone. Syn‐ and anti‐stereoisomers were detected by ¹³C NMR in the condensation product. The corresponding α‐diimine nickel (II) complex 1 was prepared from the exchange reaction of (DME)NiBr₂ with the ligand 1 , and displayed high activity for ethylene polymerization in the presence of diethylaluminum chloride (AlEt₂Cl). The resultant polymers were confirmed by gel permeation chromatography and ¹³C NMR characterization to be broad molecular weight distribution polyethylene with various branches, and high degree of branching, even at low polymerization temperature ?10°C. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Functional polyethylene composites prepared via polymerization of ethylene with opal‐immobilized zirconocene complex

An opal‐supported zirconocene complex (OC) was prepared and employed to prepare functional polyethylene composite for the first time through in situ polymerization of ethylene. The formation mechanism of anion relating to opal was explained and the values of anions released from pristine opal and that contained in the as‐fabricated polyethylene composites were detected. The OC exhibited high catalytic activities in ethylene polymerization with methylaluminoxane (MAO) the cocatalyst. In addition to higher viscosity‐average molecular weights (M_η), experimental results also showed that the resulting polyethylene composites possessed improved anion‐releasing capacity in comparison with pristine opal in addition to increased tensile strength, Young's modulus, and onset decomposition temperature (T_onset) relative to neat polyethylene due to highly uniform dispersion of opal in polyethylene matrix. POLYM. COMPOS., 2008. © 2008 Society of Plastics Engineers     

Ethylene polymerization with iron‐based diimine catalyst supported on MCM‐41

A mesoporous molecular sieve MCM‐41 supported iron‐based diimine catalyst ( MC ) was prepared for the first time. The kinetic behavior of ethylene polymerization with MC was studied. The effects of Al/Fe molar ratio and various cocatalysts on the catalytic activity and properties of the polyethylene obtained were investigated. The results showed that good catalytic activities can be reached with cocatalyst methylaluminoxane (MAO) and triethylaluminium (TEA). Ethylene polymerization with MC gave polymers with higher molecular weight, melting temperature and onset temperatures of decomposition (T_onset) and better morphology than those obtained with the corresponding homogeneous catalyst. Copyright © 2004 Society of Chemical Industry     

Synthesis and self‐assembly of amphiphilic star‐block copolymers consisting of polyethylene and poly(ethylene glycol) segments

We report on the synthesis and self‐assembly in water of well‐defined amphiphilic star‐block copolymers with a linear crystalline polyethylene (PE) segment and two or three poly(ethylene glycol) (PEG) segments as the building blocks. Initially, alkynyl‐terminated PE (PE‐?) is synthesized via esterification of pentynoic acid with hydroxyl‐terminated PE, which is prepared using chain shuttling ethylene polymerization with 2,6‐bis[1‐(2,6‐dimethylphenyl) imino ethyl] pyridine iron (II) dichloride/methylaluminoxane/diethyl zinc and subsequent in situ oxidation with oxygen. Then diazido‐ and triazido‐terminated PE (PE‐(N₃)₂ and PE‐(N₃)₃) are obtained by the click reactions between PE‐? and coupling agents containing triazido or tetraazido, respectively. Finally, the three‐arm and four‐arm star‐block copolymers, PE‐b‐(PEG)₂ and PE‐b‐(PEG)₃, are prepared by click reactions between PE‐(N₃)₂ or PE‐(N₃)₃ and alkynyl‐terminated PEG. The self‐assembly of the resultant amphiphilic star‐block copolymers in water was investigated by dynamic light scattering, transmission electron microscopy, and atomic force microscopy. It is found that, in water, a solvent selectively good for PEG blocks; these star‐block copolymer chains could self‐assemble to form platelet‐like micelles with insoluble PE blocks as crystalline core and soluble PEG blocks as shell. The confined crystallization of PE blocks in self‐assembled structure formed in aqueous solution is investigated by differential scanning calorimetry. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013