Rate of interfacial reaction between molten CaO-SiO2-Al2O3-Fe x O and CO-CO2

Measurements of the rates of reduction of iron oxide from molten CaO-SiO₂-Al₂O₃-Fe _x O slags by Ar-CO mixtures have been made using a thermogravimetric method. The apparent first-order rate constant, with respect to the partial pressure of CO, of the gas/slag interfacial reaction was deduced from the measured rates, where the effects of the mass transfer in the gas and slag phases were minimized. It was found that the apparent first-order rate constant decreased with the concentration of ‘FeO’ from 100 to 20 wt pct, whereas it remained essentially constant in the range from 5 to 20 wt pct ‘FeO’. At a given iron oxide concentration, the reduction-rate constant increased significantly with an increase in the CaO/SiO₂ ratio. For fixed slag compositions, the reduction rate increased slightly with the oxidation state of the slags. When the rate constant is expressed in the form of k=k′(Fe³⁺/²⁺)^α, the values of α range from 0.15 to 0.25. The effect of temperature in the range from 1673 to 1873 K on the reduction rate of iron oxide in a 40.4CaO-40.4SiO₂-14.2Al₂O₃-5‘FeO’ (wt pct) slag was studied. The calculated activation energy, based on these results, is 165 kJ/mol.     

Effects of CaO, Al2O3, and MgO additions on the copper solubility, ferric/ferrous ratio, and minor-element behavior of iron-silicate slags

The effects of CaO, Al₂O₃, and MgO additions, singly or in combination, on the copper solubility, the Fe³⁺/Fe²⁺ ratio in slag, and on the minor-element behavior of silica-saturated iron silicate slags were examined at 1250 °C and a p _O2 of 10⁻¹² to 10⁻⁶ atm. The results indicated that copper solubility in slag was lowered with the addition of CaO, MgO, and Al₂O₃, in decreasing order. The Fe³⁺/Fe²⁺ ratio in the slag decreased with the additions, but this effect was smaller at lower oxygen potentials. The presence of small amounts (about 4 pct) of CaO, Al₂O₃, and MgO in the slag resulted in increased absorption of Bi and Sb into molten copper, but had a smaller effect at large additions (about 8 to 11 pct). The distribution behavior of Pb was a function of oxygen partial pressure, which indicates the oxidic dissolution of Pb in the slag as PbO, while the behavior of Bi, Sb, and As was found to be independent of oxygen potential, supporting the atomic (neutral) dissolution hypothesis of these elements in the slag. The distribution behavior of Pb and As was not significantly affected by the additions. The activity coefficients of Bi and Sb in the slags were determined to be as follows: (1) for no addition, γ _Bi=40 and γ _Sb=0.4; (2) for small additions (about 4.4 pct), γ _Bi=70 to 85 and γ _Sb=0.8; and (3) for large additions (about 8 to 11 pct), γ _Bi=60 to 75 and γ _Sb=0.5 to 0.7.     

Thermodynamics of Arsenic in FeOx-CaO-SiO<Subscript>2</Subscript> Slags

The distribution of arsenic between calcium ferrite slag and liquid silver (wt pct As in slag/ wt pct As in liquid silver) with 22 wt pct CaO and between iron silicate slag with 24 wt pct SiO₂ and calcium iron silicate slags was measured at 1573 K (1300 °C) under a controlled CO-CO₂-Ar atmosphere. For the calcium ferrite slags, a broad range of oxygen partial pressure (10^–11 to 0.21 atm) was covered, whereas for the silicate slags, the oxygen partial pressure was varied from 10^–9 to 3.1 × 10^–7 atm. The measured relations between the distribution ratio of As and the oxygen partial pressure indicates that the oxidation state of arsenic in these slags is predominantly As³⁺ or AsO_1.5. The measured distribution ratio of arsenic between the calcium ferrite slag and the liquid silver was about an order of magnitude higher than that of the iron silicate slag. In addition, an increasing concentration of SiO₂ in the calcium-ferrite-based melts resulted in decreases in the distribution of arsenic into the slag. Through the use of measured equilibrium data on the arsenic content of the metal and slag in conjunction with the composition dependent on the activity of arsenic in the metal, the activity of AsO_1.5 in the slags was deduced. These activity data on AsO_1.5 show a negative deviation from the ideal behavior in these slags.     

The reduction of zinc from slags by an iron-carbon melt

An experimental investigation was undertaken to study the mechanism of reduction of zinc from slags in the presence of a carbon-saturated iron melt. Batch tests were performed at 1400 °C, and the variation of the zinc and iron concentration in the slag during reduction was determined by sampling the slag at intervals during the test. In graphite crucibles, zinc in slags containing iron was reduced faster than zinc in iron-free slags, both when an iron bath was present and when it was absent. Zinc was reduced faster from slags containing iron when an iron bath was present than when an iron bath was absent. The dominant mechanism of reduction of zinc from slags containing iron appears to be the reaction of Zn²⁺ ions with Fe²⁺ ions to form zinc vapor and Fe³⁺ ions. When an iron bath is present, the Fe³⁺ ions are reduced back to Fe²⁺ predominantly by reaction with iron from the bath. Mass transfer of Fe³⁺ ions in the slag appears to be the rate-controlling step. Reduction of iron from slag by carbon occurred in parallel with the reduction of zinc, and whether there was a net increase or decrease of iron in the slag depended on the relative rates of production and consumption of iron. Lead and copper in the slag were reduced to low levels. The lead volatilized and the copper dissolved in the alloy.     

Kinetics of reduction of ferric iron in Fe2O3-CaO-SiO2-Al2O3 slags under argon, CO-CO2, or H2-H2O

The rates of reduction of ferric iron in Fe₂O₃-CaO-SiO₂-Al₂O₃ slags containing 3 to 21 wt pct Fe₂O₃ under impinging argon, CO-CO₂, or H₂-H₂O have been studied at 1370 °C under conditions of enhanced mass transfer in the slag using a rotating alumina disc just in contact with the slag surface. For a 6 wt pct Fe slag at a stirring speed of 900 rpm the observed reduction rates by 50 pct H₂-H₂O were a factor of 2 to 3 times higher than those by 50 pct CO-CO₂ and more than one order of magnitude higher than those under pure argon. The observed rates were analyzed to determine the rate-controlling mechanisms for the present conditions. Analysis of the rate data suggests that the rates under 50 pct H₂-H₂O are predominantly controlled by the slag mass transfer. The derived values of the mass-transfer coefficient followed a square-root dependence on the stirring speed for a given slag and, at a given stirring speed, a linear function of the total iron content of the slags. The rates of oxygen evolution during reduction under pure argon were shown to be consistent with a rate-controlling mechanism involving a fast chemical reaction at the interface and relatively slow mass transfer in the gaseous and the slag phases. The rates of reduction by CO-CO₂ (pCO=0.02 to 0.82 atm) were found to be likely of a mixed control by the slag mass transfer and the interfacial reaction. A significant contribution of oxygen evolution to the overall rates was observed for more-oxidized slags and for experiments with relatively low values of pCO. Assuming a parallel reaction mechanism, the estimated net reduction rates due to CO were found to be of the first order in pCO, with the first-order rate constants being approximately a linear function of the ferric concentration. This article is based on a presentation made in the “Geoffrey Belton Memorial Symposium” held in January 2000, in Sydney, Australia, under the joint sponsorship of ISS and TMS. The original symposium appeared in the October 2000 Vol. 31B issue.     

A thermodynamic study on cobalt containing calcium ferrite and calcium iron silicate slags at 1573 K

Redox equilibria, activities of cobalt, iron and their oxides in calcium ferrite and calcium ironsilicate slags, were measured through metal-slag-gas equilibrium experiments under controlled oxygen potentials (10⁻⁷ to 3 × 10⁻⁷ atm) at 1573 K. Results on the redox equilibria show that addition of CoO to calcium ferrite slag increases the equilibrium Fe³⁺/Fe²⁺ ratio in these melts. Measured activities of CoO and FeO showed positive deviations from ideal behavior, while that of Fe₂O₃ showed negative deviation. Partial substitution of CaO by SiO₂, by up to 4 wt pct SiO₂ in the calcium ferrite based melts, resulted in increases in the activity coefficients of CoO and Fe₂O₃. Phase equilibria studies on the cobalt containing CaO-FeO-Fe₂O₃-SiO₂ slags were also carried out using the drop-quench technique. Good agreement between the activity data and the liquidus temperature with respect to magnetite solid solution containing CoO was observed.     

Sulfide capacity of CaO-CaF2-SiO2 slags

The sulfide capacityC _S ^2- = (pct S^2-) · (P _{O 2}/P _{S 2})^1/2) of CaO-CaF₂-SiO₂ slags saturated with CaO, 3CaO · SiO₂ or 2CaOSiO₂ was determined at 1200 °C, 1250 °C, 1300 °C, and 1350 °C by equilibrating molten slag, molten silver, and CO-CO₂ gas mixtures. Higher sulfide capacities were obtained for CaO-saturated slags. A drastic decrease was observed in those values when the ratio pct CaO/pct SiO₂ is less than 2. The sulfur partition between carbon-saturated iron melts and presently investigated slags was calculated by using the sulfide capacities obtained and the activity coefficient of sulfur in carbon-saturated iron, which was also experimentally determined. For slags saturated with CaO, partitions of sulfur as high as 10,000 were obtained at 1300 °C and 1350 °C. Correlations between the sulfide capacity and other basicity indexes such as carbonate capacity and theoretical optical basicity were also discussed. Formerly with the Department of Metallurgy, The University of Tokyo.     

Iron redox equilibria in BOF slag equilibrated with ambient air

The Fe²⁺/Fe³⁺ ratio in the CaO‐MgO‐Fe₂O₃‐FeO‐SiO₂ based slag was measured under the condition of equilibrium with the ambient air at 1873 K as a fundamental study for precise slag coating control in BOF operation. The CaO/SiO₂ mass ratios of the main slag were 1, 1.5, 2, 3 and 4, and total iron mass content was in the range of 10 to 35 %. Moreover, mass contents of 1 to 13 % of MnO and 2 to 12 % of Al₂O₃ were added to the melt to evaluate their effects on the Fe²⁺/Fe³⁺ ratio. The effect of slag composition on the Fe²⁺/Fe³⁺ ratio was discussed and quantified into a form of formula. As the basicity in slag increases, the Fe²⁺/Fe³⁺ ratio decreases. The effect of iron oxide mass content is observed to be dependent on the basicity of slag. An increase in iron oxide mass content makes the Fe²⁺/Fe³⁺ ratio higher for basic slag but lower for acidic slag. It is revealed that the redox reaction of iron oxide in steelmaking slag under the ambient air is controlled by the complex anion formation reaction of iron oxide, and that the iron oxide in basic slag exists in the form of 2 or more kinds of complex anion controlling the oxygen anion content. Both Al₂O₃ and P₂O₅ increase the Fe²⁺/Fe³⁺ ratio by diluting the basic oxides as SiO₂ does, while manganese oxide lowers the Fe²⁺/Fe³⁺ ratio enormously down to nearly zero. The Fe²⁺/Fe³⁺ ratio can be described as a function of slag composition, X = (%CaO) + 0.38(%Fe₂O₃ + %FeO)+3.2(%MnO), in the equation of log(Fe²⁺/Fe³⁺) = ‐0.00107X² + 0.0721X ‐ 1.982.     

Distribution of Bi Between Slags and Liquid Copper

The distribution of Bi between liquid copper and calcium ferrite slag containing 24 wt pct CaO, iron silicate slag with 25 wt pct SiO₂, and calcium iron silicate slags was measured at 1573 K (1300 °C) under controlled CO-CO₂ atmosphere. The experimental results showed that bismuth distribution is affected by the oxygen partial pressure, and bismuth is likely to exist in slags in the 2+ oxidation state, i.e., as BiO. The distribution ratio between calcium ferrite slag and metal was found to be close to that of iron silicate slag. The Bi distribution ratio was found to decrease with increasing SiO₂ and Al₂O₃ content in slag. Increasing temperature was found to decrease the Bi distribution ratio between slag and metal. Using the measured equilibrium data on Bi content of the metal and slag and composition dependence of the activity of Bi in liquid copper, the activity and hence activity coefficient of BiO in the slag was calculated. The close value of activity coefficient of BiO in both slags at the same oxygen partial pressure indicates that the CaO-BiO and SiO₂-BiO interactions are likely to be at the same level, or the FeO _x -BiO interaction is the predominant interaction for BiO in the slag. Therefore at a constant FeO _x content in the slag, the CaO-BiO and SiO₂-BiO interactions doesn’t affect \( \gamma_{\text{BiO}} \) significantly.     

The reaction behavior of Fe-C-S droplets in CaO-SiO2-MgO-FeO slags

The rate of reduction of FeO in the slag by carbon in iron droplets (2.9 wt pct C, 0.01 wt pct S) was studied for CaO-SiO₂-MgO slags containing between 3 and 35 wt pct FeO and temperatures ranging from 1643 to 1763 K. The effects of Fe₂O₃ additions to the slag and sulfur variations in the metal on the reaction rate were also studied. It was found that the behavior of the metal droplets in the slag, as observed by X-ray fluoroscopy, changed significantly with FeO content in the slag. Below 10 wt pct FeO, the droplet remained intact while reacting with the slag; however, above this FeO concentration, the droplet became emulsified within the slag. The large increase in surface area of the metal droplet due to emulsification caused the rate of reaction to be one to two orders of magnitude faster than for droplets that did not become emulsified. It was suggested that when the droplet is emulsified, the surface area and reaction kinetics are greatly increased, and the rate becomes controlled by mass transfer of FeO as Fe²⁺ and O²⁻ ions in the slag to the emulsified droplet. At low FeO contents for which the droplet does not emulsify, the rate is controlled by dissociation of CO₂ on the metal. It was also found that a critical temperature exists for a given FeO content at which point the rate of CO evolution increases dramatically. Additions of Fe₂O₃ to the slag and sulfur to the metal caused significant changes to the rate of reaction possibly by affecting the emulsification behavior of the droplet.     

Thermodynamics of TiO x in blast furnace-type slags

Equilibrium studies between CaO-SiO₂-10 pct MgO-Al₂O₃-TiO_1.5-TiO₂ slags, carbon-saturated iron, and a carbon monoxide atmosphere were performed at 1773 K to determine the activities of TiO_1.5 and TiO₂ in the slag. These thermodynamic parameters are required to predict the formation of titanium carbonitride in the blast furnace. In order to calculate the activity of titanium oxide, the activity coefficient of titanium in carbon-saturated iron-carbon-titanium alloys was determined by measuring the solubility of titanium in carbon-saturated iron in equilibrium with titanium carbide. The solubility and the activity coefficient of titanium obtained were 1.3 pct and 0.023 relative to 1 wt pct titanium in liquid iron or 0.0013 relative to pure solid titanium at 1773 K, respectively. Over the concentration range studied, the effect of the TiO _x content on its activity coefficient is small. In the slag system studied containing 35 to 50 pct CaO, 25 to 45 pct SiO₂, 7 to 22 pct Al₂O₃, and 10 pct MgO, the activity coefficients of TiO_1.5 and TiO₂ relative to pure solid standard states range from 2.3 to 8.8 and from 0.1 to 0.3, respectively. Using thermodynamic data obtained, the prediction of the formation of titanium carbonitride was made. Assuming hypothetical ‘TiO₂,’ i.e., total titanium in the slag expressed as TiO₂, and using the values of the activity coefficients of TiO_1.5 and TiO₂ determined, the equilibrium distribution of titanium between blast furnace-type slags and carbon-saturated iron was computed. The value of [pct Ti]/(pct ‘TiO₂’) ranges from 0.1 to 0.2.     

Thermodynamics of iron oxide in Fe x O-dilute CaO + Al2O3 + MgO + Fe x O slags at 1873 K

In order to determine the ferrous and ferric ion capacities: 3

Measurement of FeO activity and solubility of MgO in smelting slags

In bath smelting, the FeO activity of the slag must be known to predict the equilibrium of slag-metal reactions and for effective control of the rate of reduction in the system. Also, knowledge of the solubility of MgO in these slags is useful for reducing refractory consumption. A series of measurements of the FeO activity in simulated bath smelting slags (CaO-SiO₂-Al₂O₃-MgO_sat-FeO) were conducted by the electromotive force (EMF) technique. The influence of the slag composition on the relationship between the FeO activity coefficient and FeO content was studied. It has been found that the measured FeO activity coefficient decreases with increasing FeO content in the slag and increases slightly with increasing slag basicity, which is defined as (CaO + MgO)/(SiO₂ + Al₂O₃) on a mole fraction basis. The measured values of the FeO activity coefficient are in reasonable agreement with previously published data. The solubility of MgO was also measured and found to rang from 16 to 30 pct and decrease with increasing basicity.     

A Sulfide Capacity Prediction Model of CaO-SiO2-MgO-FeO-MnO-Al2O3 Slags during the LF Refining Process Based on the Ion and Molecule Coexistence Theory

A sulfide capacity prediction model of CaO-SiO₂-MgO-FeO-MnO-Al₂O₃ ladle furnace (LF) refining slags has been developed based on the ion and molecule coexistence theory (IMCT). The predicted sulfide capacity of the LF refining slags has better accuracy than the measured sulfide capacity of the slags at the middle and final stages during the LF refining process. Increasing slag binary basicity, optical basicity, and the Mannesmann index can lead to an increase of the predicted sulfide capacity for the LF refining slags as well as to an increase of the sulfur distribution ratio between the slags and molten steel at the middle and final stages during the LF refining process. The calculated equilibrium mole numbers, mass action concentrations of structural units or ion couples, rather than mass percentages of components, are recommended to represent the slag composition for correlating with the sulfide capacity of the slags. The developed sulfide capacity IMCT model can calculate not only the total sulfide capacity of the slags but also the respective sulfide capacity of free CaO, MgO, FeO, and MnO in the slags. The comprehensive contribution of the combined ion couples (Ca²⁺ + O²⁻) and (Mn²⁺ + O²⁻) on the desulfurization reactions accounts for 96.23 pct; meanwhile, the average contribution of the ion couple (Fe²⁺ + O²⁻) and (Mg²⁺ + O²⁻) only has a negligible contribution as 3.13 pct and 0.25 pct during the LF refining process, respectively. The oxygen activity of bulk molten steel in LF is controlled by the [Al]–[O] equilibrium, and the oxygen activity of molten steel at the slag–metal interface is controlled by the (FeO)–[O] equilibrium. The ratio of the oxygen activity of molten steel at the slag–metal interface to the oxygen activity of bulk molten steel will decrease from 37 to 5 at the initial stage, and further decrease from 28 to 4 at the middle stage, but will maintain at a reliable constant as 5 to 14 at the final stage during the LF refining process. The proposed high-oxygen potential layer of molten steel beneath the slag–metal interface can be quantitatively verified.     

A Thermodynamic Model of Phosphorus Distribution Ratio between CaO-SiO2-MgO-FeO-Fe2O3-MnO-Al2O3-P2O5 Slags and Molten Steel during a Top–Bottom Combined Blown Converter Steelmaking Process Based on the Ion and Molecule Coexistence Theory

A thermodynamic model for calculating the phosphorus distribution ratio between top–bottom combined blown converter steelmaking slags and molten steel has been developed by coupling with a developed thermodynamic model for calculating mass action concentrations of structural units in the slags, i.e., CaO-SiO₂-MgO-FeO-Fe₂O₃-MnO-Al₂O₃-P₂O₅ slags, based on the ion and molecule coexistence theory (IMCT). Not only the total phosphorus distribution ratio but also the respective phosphorus distribution ratio among four basic oxides as components, i.e., CaO, MgO, FeO, and MnO, in the slags and molten steel can be predicted theoretically by the developed IMCT phosphorus distribution ratio prediction model after knowing the oxygen activity of molten steel at the slag–metal interface or the Fe _t O activity in the slags and the related mass action concentrations of structural units or ion couples in the slags. The calculated mass action concentrations of structural units or ion couples in the slags equilibrated or reacted with molten steel show that the calculated equilibrium mole numbers or mass action concentrations of structural units or ion couples, rather than the mass percentage of components, can present the reaction ability of the components in the slags. The predicted total phosphorus distribution ratio by the developed IMCT model shows a reliable agreement with the measured phosphorus distribution ratio by using the calculated mass action concentrations of iron oxides as presentation of slag oxidation ability. Meanwhile, the developed thermodynamic model for calculating the phosphorus distribution ratio can determine quantitatively the respective dephosphorization contribution ratio of Fe _t O, CaO + Fe _t O, MgO + Fe _t O, and MnO + Fe _t O in the slags. A significant difference of dephosphorization ability among Fe _t O, CaO + Fe _t O, MgO + Fe _t O, and MnO + Fe _t O has been found as approximately 0.0 pct, 99.996 pct, 0.0 pct, and 0.0 pct during a combined blown converter steelmaking process, respectively. There is a great gradient of oxygen activity of molten steel at the slag–metal interface and in a metal bath when carbon content in a metal bath is larger than 0.036 pct. The phosphorus in molten steel beneath the slag–metal interface can be extracted effectively by the comprehensive effect of CaO and Fe _t O in slags to form 3CaO·P₂O₅ and 4CaO·P₂O₅ until the carbon content is less than 0.036 pct during a top–bottom combined blown steelmaking process.     

Effect of MgO on Liquidus Temperatures in the ZnO-“FeO”-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-CaO-SiO<Subscript>2</Subscript>-MgO System in Equilibrium with Metallic Iron

The phase equilibria in the ZnO-“FeO”-Al₂O₃-CaO-SiO₂-MgO system have been determined experimentally in equilibrium with metallic iron. Synthetic slags were equilibrated at a high temperature, quenched, and then the compositions of the phases in equilibrium were measured using electron probe X-ray microanalysis. Pseudoternary sections of the form ZnO-“FeO”-(Al₂O₃ + CaO + SiO₂) for CaO/SiO₂ = 0.71, (CaO + SiO₂)/Al₂O₃ = 5 and fixed MgO concentrations of 2, 4, and 6 wt pct have been constructed. Wustite (Fe²⁺,Mg,Zn)O and spinel (Fe²⁺,Mg,Zn)O·(Al,Fe³⁺)₂O₃ are the major primary phases in the temperature and composition ranges investigated. The liquidus temperatures are increased by 140 K in the wustite primary phase field and by 70 K in the spinel primary phase field with the addition of 6 wt pct MgO in the slag. The partitioning of MgO and ZnO between the solid and liquid phases has been discussed.     

The solution rate of alumina in CaF2-Al2 O3 slags

The rate of solution of A1₂O₃ in CaF₂ + 30 wt pct A1₂O₃ (at 1518° and 1509°C) and CaF₂ + 20 wt pct A1₂O₃ (at 1500°C) liquids has been determined. The operative process is diffusion-controlled, with an interdiffusion coefficient,D for the process varying between 8.5 and 8.1 x 10^-5 sq cms ^- 1 in the CaF₂ + 30 wt pct A1₂O₃ slags, and 4.0 × 10^-5 sq cms ^- 1 in the CaF₂ + 20 wt pct A1₂O₃ slag. Estimations of the rate at which alumina inclusions would react with these slag during the electroslag processing of steels, indicate that electrode inclusions approaching 100 μ in diam will be dissolved.     

Electrode polarization in the DC electroslag melting of pure iron

It is evident from the known ionic properties of the slags used in electroslag melting, that the dc melting process must be accompanied by Faradaic reactions on the slag/ingot and slag/electrode interfaces. The present work has determined the magnitude of the overpotentials resulting from concentration polarization at these interfaces, in the case of pure iron/CaF₂+Al₂O₃, CaF₂+CaO slags using a galvanostatic pulsing technique in an electrolytic cell. The polarization overpotential existing on an electrode in an operating ESR unit has been measured by the same technique. It is found that the potentials observed on the ESR electrode agree well with the results from the electrolytic cell. The primary anodic process is postulated to be the corrosion of iron, leading to an Fe²⁺-saturated layer on the anode surface at sufficiently high current densities. The cathodic process is suggested to be the Faradaic reduction of Al³⁺ or Ca²⁺, to give a concentration of [Al]_Fe or (Ca)_slag in the cathode interface region. This observation is supported by the fact that the cathodic potentials with respect to a C/CO reference electrode are close to those predicted from the reactions: (Al₂O₃)+3C=3CO(g)+2Al(l) or (CaO)+C=CO(g)+Ca(g) At very high current densities both the anodic and cathodic processes may convert to arcs, leading to process instability. The chemical and thermal effects of the overpotentials are briefly discussed and compared with the present results on ESR ingots of pure iron.     

Distribution of nickel between copper-nickel and alumina saturated iron silicate slags

The solubility of nickel in slag was determined by equilibrating copper-nickel alloys with alumina-saturated iron silicate slags in an alumina crucible at 1573 K. The experiments were carried out under controlled oxygen partial pressures in the range of 10^-10 to 10^-8 atm by use of suitable CO-CO₂ gas mixtures, and at Fe/SiO₂ ratio 1.34. The results showed that nickel dissolves in slag both as Ni²⁺ (nickel oxide) and Ni‡ (nickel metal), and the relation obtained was: (Wt pct Ni in slag) = (ie33-01) The activity coefficient of nickel oxide (γ^dgNio) and distribution coefficient of nickel (A_Ni) is calculated to be 0.375 and 233.3, respectively. γ^dgNio and A_Ni are found to be independent of oxygen partial pressures. The presence of alumina increases the solubility of nickel in slags.     

The sulfur partition ratio and the sulfide capacity of Na2O-SiO2 slags at 1200 °C

The sulfur partition ratio between carbon-saturated iron and Na₂O-SiO₂ slags and the sulfide capacity of these slags have been measured at 1200 °C. The two measurements are consistent with each other and the results are compared with other investigations. These slags have higher sulfide capacities and partition ratios than equivalent CaO-based slags and are thus attractive desulfurizers. Both the sulfide capacity and the partition ratio increase with increasing Na₂O. The activity coefficient of Na₂S has been calculated; it also increases with increasing Na₂O. The solubility of sulfur in a slag of 0.4 mole fraction Na₂O is estimated to be 5 pct.