高碱灰渣-煤矸石砖的酸雨淋溶分

文章指出只有充分了解酸雨对高碱灰渣-煤矸石砖的淋溶特性,从而可以进一步确定高碱灰渣-煤矸石砖在使用过程中的安全性能.实验的结果显示模拟酸雨淋溶对高碱灰渣-煤矸石碱的影响不大.     

高溶物煤矸石制砖工艺研究

研究使用可溶物（如碱、硫）含量高的煤矸石制砖的工艺，采用该工艺制作的砖具有质量好，煤矸石用量大，社会效益好等特点，为煤矸石大批量利用找到了一条有效途径。     

用高碱灰渣和煤矸石制烧结砖

1煤矸石及煤矸石砖的矿物组合特征煤矸石具有一定的热值(2.06～6.28kJ/kg)。新汶矿业集团于1999年用煤矸石作内燃料,开发出煤矸石全自养内燃砖生产工艺。产品隔音,隔热,强度高,外形美观,市场效益好。目前山东省和国内已有几十条煤矸石砖生产线。新汶矿业集团良庄煤矸石砖的原料     

电厂燃烧黑液-水煤浆所排灰渣用于制砖的可行性

目前,国内外用造纸黑液与煤制备洁净燃料已有报道,在中小锅炉上燃烧处理已获得成功,但将其用于电站锅炉的研究还是空白。新矿集团与圣龙集团联合开发的黑液-水煤浆发电供热项目,无疑是一项开创性的工作。黑液-水煤浆碱含量高,燃烧后的废弃物具有高碱性。而新矿集团与圣龙集团的工程上马后,每年将产生大量高碱性灰渣,考虑到不再走先污染后治理的老路,青岛科技大学化学系承担了处理该高碱粉煤灰渣的研究任务。1摇高碱粉煤灰与普通粉煤灰的成分差别3个高碱灰渣样品包括炉壁灰、炉底渣和烟管实灰,其化学成分见表1。表1摇黑液-水煤浆高碱灰渣化学…     

高硫煤矸石内燃砖对隧道窑的危害及其对策

本文对硫在煤矸石中存在的形式进行了阐述;通过对煤矸石中含硫量的高低来判断高硫煤矸石。通过高硫煤矸石内燃砖焙烧实例,分析高硫煤矸石对焙烧窑危害形成的机理,并针对性地找出应对策略和预防措施。     

粉煤灰砖建筑物的裂缝类型及预防措施

株洲市是个新型的工业城市,由于工业的发展,相应地产生了不少的废气、废水、废渣,如不及时处理,势必影响城市环境卫生。遵照毛主席关于“综合利用很重要,要注意”的伟大教导,化害为利,变废为宝,在株洲市委领导下,利用粉煤灰、炉渣、电石渣、煤矸石等工业废料,生产了各种墙体材料:如煤灰砖、灰渣砖、矸石砖、碳化砖等等,广泛应用于民用和     

免烧结煤矸石透水砖的试验研究

研究以煤矸石为主要原料制备免烧结煤矸石透水砖,探讨了煤矸石粒径、煤矸石与水泥质量比、成型压力对免烧结煤矸石透水砖的透水系数和劈裂抗拉强度的影响。试验结果表明,较优工艺参数为煤矸石粒径为4.75～9.5 mm,煤矸石与水泥的质量比为3∶1,成型压力为4 MPa,采用该工艺参数所制备的透水砖性能较优,其透水系数为2.34×10-2 cm/s,劈裂抗拉强度为1.4 MPa。     

高碱灰渣掺入粘土中烧砖的可行性分析

根据圣龙集团造纸厂附近粘土的化学组成及粘土砖的矿物成分,对高碱灰渣掺入粘土中的化学成分特征、矿物成分特征进行了分析,并且确定了高碱灰渣的最佳掺入比例.     

酸雨环境作用下再生混凝土砖砌体抗剪性能试验研究

通过对28个经酸雨喷淋-光照腐蚀循环的再生混凝土砖砌体抗剪试件进行沿通缝截面的抗剪试验的研究,提出了再生混凝土砖砌体抗剪强度平均值计算公式,建立了再生混凝土砖砌体的抗剪强度酸雨损伤衰减模型。研究结果表明:酸雨环境对再生混凝土砖砌体的抗剪强度影响较大;随着喷淋-光照腐蚀循环次数的增多,再生混凝土砖砌体的抗剪强度表现出先增后降的趋势,且前期增长表现不明显,后期下降幅度较大。     

生活垃圾焚烧灰渣原始集料制备免烧免压砖试验研究

提出了不对灰渣进行研磨而直接采用其原始集料,并以水泥和生石灰为原料,水玻璃和氢氧化钠为激发剂,制备三免砖(免烧、免压、免磨)的简化制备工艺。研究了不同配合比、水玻璃模数、激发剂用量对灰渣砖强度的影响规律。试验结果表明:采用灰渣原始集料制备的灰渣砖强度可以满足MU10砌块的要求,所提出的三免砖制备方案能节约成本;采用灰渣细集料的灰渣砖强度优于采用灰渣粗集料;灰渣掺量越多,强度越低;水玻璃的最佳模数为1.2~1.4,激发剂用量过多会造成强度的迅速降低;灰渣砖密度与强度呈正比关系,并且二者之间有较好的线性关系。     

酸雨腐蚀砖墙抗震性能试验及恢复力模型研究

为了研究一般大气环境下酸雨作用对砌体结构抗震性能的影响,以4榀相同特性的砖墙作为研究对象,进行了酸雨模拟加速腐蚀试验和低周反复荷载试验,考察了砖墙的抗震性能随着酸雨腐蚀循环次数增加的退化现象,得到了砖墙的荷载-位移滞回曲线。通过对比各腐蚀循环次数下的试验数据,分析并建立了砖墙构件性能的退化规律。基于Ibarra-Krawinkler滞回模型建立了不同酸雨腐蚀循环次数下砖墙的退化恢复力模型,并利用OpenSees进行模型验证。结果表明该恢复力模型能够准确的描述酸雨腐蚀下砖墙构件在反复荷载作用下材料的非线性,为酸雨环境下砌体结构地震反应分析奠定基础。     

酸雨环境下老旧砖砌体的抗压性能

为研究酸雨环境下老旧砌体抗压力学性能退化规律,实验室配置了PH值分别为1.5、2.5和3.5的3种硫酸和硝酸混合溶液来模拟酸雨环境,采用完全浸泡加速腐蚀的试验方法对砖、砂浆和砖柱进行不同程度的腐蚀,并测定其抗压强度。试验表明,随着腐蚀时间的增加,砂浆试块抗压强度先增大后降低;砖试块抗压强度随腐蚀时间的增加而降低;模拟酸雨溶液PH值越小,砂浆和砖试块抗压强度降低程度也愈大;砖柱极限承载力和弹性模量均随腐蚀时间的增加而降低,且模拟酸雨溶液PH值越小,降低程度愈大;随着腐蚀时间的增加,砖柱初始刚度逐渐减小,极限破坏位移增大;模拟酸雨溶液PH值越小,砖柱在达到峰值荷载时的变形值越小,脆性愈大;基于试验结果,建立了酸雨环境下砖柱应力应变曲线上升段统一数学表达式及酸雨侵蚀后普通烧结粘土砖砌体剩余抗压强度回归公式。     

拦截式预制雨水口的研究与应用

对拦截式预制雨水口进行研究与应用,在保证雨水口过水能力的前提下,通过设置拦截器,提高了雨水井中固体废弃物的截留量,并防止臭气外逸,更好地减轻了管道淤积和防止河道污染。拦截式预制雨水口提高了市政道路雨水口的施工工效,减少了黏土砖的使用,加强了质量控制,能够更好地保护环境。     

Chemical resistance of pozzolanic plaster for earthen walls

Earth is an economical and ancient construction material. Historical earthen architecture is a heritage that must be handed over to the next generations but experience shows that these historical structures do not stand up well against the destructive action of rain. In this study, fly ash, powdered brick, hydrated lime and water were mixed to develop a pozzolanic plaster for use in conservation of earthen walls. Chemical durability, such as sulfate, salt and acid resistance of this pozzolanic plaster also was investigated. The chemical compounds employed in these tests were 2000 and 5000 ppm sodium sulfate and ammonium nitrate solutions for sulfate and salt attack. Also, the acidic media were with 1%, 5% and 10% concentrations of sulfuric acid and hydrochloric acid. All test results indicated that incorporation of fly ash in pozzolanic plaster provides a satisfactory resistance to aggressive chemicals such as sulfate, salts and acids. The developed plaster seems to be a suitable material for preservation of earthen walls since it has adequate mechanical and chemical properties in comparison with soil.     

Using phosphogypsume and boron concentrator wastes in light brick production

In this study, use of wastes produced in phosphoric acid plants and boron concentrators in producing structural brick has been investigated. There are several parameters involved in using these wastes in brick production namely the rate of added waste, firing speed and firing temperature. The performance of these parameters can be measured by several criteria such as natural drying shortening, water absorption and weight loss. Therefore, so many experiments are needed to investigate the effects of these parameters on the bricks produced with these wastes. To this end, around 220 experiments for three different material combinations namely original waste plus normal brick clay, washed waste plus normal brick clay and normal brick clay with no additive were carried out. The results have shown that the industrial wastes produced by phosphoric acid plants can improve the performance of the bricks in terms of drying shortening, weight loss and water absorption.     

建筑结构设计与施工中易忽略的问题分析

针对建筑物结构质量的重要性通过对大挑檐和雨篷抗倾覆及抗扭、屋面找坡层荷载计算,基础底板和框架柱基础梁设计计算,砌于悬挑梁上砖墙裂缝等质量通病防治问题的分析,提醒技术人员要重视结构质量,从而保证建筑物的安全性和适用性。     

石煤钒渣页岩烧结砖的研究

利用湿法酸浸提钒产生的钒渣,研制替代部分页岩的钒渣烧结砖,制品性能达到GB 5101—2003《烧结普通砖》的要求。探讨了钒渣掺量对砖坯的可塑性、干燥敏感性、收缩性的影响以及对烧结砖强度的影响,并对钒渣烧结砖的强度机理进行了分析。     

砖混结构房屋顶层端部墙体开裂成因再认识

雨水侵入基础下的地基,改变了土体结构,从而产生房屋端部地基土与中部地基土的不均匀性,这种不均匀性等同于在端部基础上作用了附加应力,使房屋端部的整体弯曲下沉,砖混结构房屋顶层端部窗洞削弱了此处的整体性,在抵抗下沉的过程中产生附加应力应变,从而导致窗洞周围形成裂缝,这一结论揭示了此类裂缝是由温度变形原因之外的另外成因。     

某古建筑砖土结构基座病害探测分析

古建筑基座主要由砖-土材料构成,因年久失修而产生的病害问题较为严重。以某古建筑为研究对象,采用地质雷达和面波等无损探测方法,结合土壤电阻法和TDR等方法对其水害和结构病害特征进行大量现场监测,结果表明：①降雨后,基座外砖墙以内厚约3.0 m范围和内置排水管外围约1.0 m范围内的夯土层饱和度明显高于其他部位,由于外墙裂缝、内置排水管管口裂缝及海墁下部防渗层的失效等,是造成基座渗漏水、泛碱、脱皮的主要诱因;②基座顶部以下5.0 m深度范围内的砖土结构损伤较底部严重,且基座4个侧面的病害差异分布不均;③受降雨影响,基座顶部夯土层的含水率有上升趋势,基座底部的含水率明显高于基座中上部,电阻率也明显低于中上部,但基座底部夯土层和地基内含水率呈下降趋势,表明基座上部的水分有向基座底部和地基内迁移的趋势。通过多角度的相互验证研究,为深入探索古建筑基座结构病害的形成机制提供了一套可行的研究思路。     

酸雨侵蚀下水泥基材料的腐蚀损伤与评价——酸雨介质成分的影响

通过测试长期浸泡在不同酸雨中的混凝土试件相对弹性模量随侵蚀时间的变化,着重研究了酸雨酸度(pH值)及其SO24-浓度等酸雨侵蚀介质参数对水泥混凝土抗酸雨侵蚀能力的影响。研究结果表明:在酸雨静态长期浸泡环境下,水泥基材料表面和内部腐蚀损伤程度及速率与酸雨侵蚀介质H+和SO24-浓度以及产生的腐蚀产物有关;在酸雨介质其它离子成分保持不变的情况下,酸雨pH值和SO24-对受酸雨腐蚀后的水泥混凝土表面性能及其内部微观结构有着十分明显的影响,并且从酸雨侵蚀破坏过程来看,各水泥混凝土随着酸雨中的H+和SO24-浓度的增加而腐蚀越来越严重。