Synthesis and characterization of poly(HEMA‐co‐MMA)‐g‐POSS nanocomposites by combination of reversible addition fragmentation chain transfer polymerization and click chemistry

New hybrid poly(hydroxyethyl methacrylate‐co‐methyl methacrylate)‐g‐polyhedral oligosilsesquioxane [poly(HEMA‐co‐MMA)‐g‐POSS] nanocomposites were synthesized by the combination of reversible addition fragmentation chain transfer (RAFT) polymerization and click chemistry using a grafting to protocol. Initially, the random copolymer poly(HEMA‐co‐MMA) was prepared by RAFT polymerization of HEMA and MMA. Alkynyl side groups were introduced onto the polymeric backbones by esterification reaction between 4‐pentynoic acid and the hydroxyl groups on poly(HEMA‐co‐MMA). Azide‐substituted POSS (POSS? N₃) was prepared by the reaction of chloropropyl‐heptaisobutyl‐substituted POSS with NaN₃. The click reaction of poly(HEMA‐co‐MMA)‐alkyne and POSS? N₃ using CuBr/PMDEATA as a catalyst afforded poly(HEMA‐co‐MMA)‐g‐POSS. The structure of the organic/inorganic hybrid material was investigated by Fourier transformed infrared, ¹H‐NMR, and ²⁹Si‐NMR. The elemental mapping analysis of the hybrid using X‐ray photoelectron spectroscopy and EDX also suggest the formation of poly(HEMA‐co‐MMA)‐anchored POSS nanocomposites. The XRD spectrum of the nanocomposites gives evidence that the incorporation of POSS moiety leads to a hybrid physical structure. The morphological feature of the hybrid nanocomposites as captured by field emission scanning electron microscopy and transmission electron microscopic analyses indicate that a thick layer of polymer brushes was immobilized on the POSS cubic nanostructures. The gel permeation chromatography analysis of poly(HEMA‐co‐MMA) and poly(HEMA‐co‐MMA)‐g‐POSS further suggests the preparation of nanocomposites by the combination of RAFT and click chemistry. The thermogravimetric analysis revealed that the thermal property of the poly(HEMA‐co‐MMA) copolymer was significantly improved by the inclusion of POSS in the copolymer matrix. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Synthesis of polypropylene graft copolymers from a hydroxyl‐groups‐containing polypropylene precursor via atom‐transfer radical polymerization

Isotactic polypropylene graft copolymers, isotactic[polypropylene‐graft‐poly(methyl methacrylate)] (i‐PP‐g‐PMMA) and isotactic[polypropylene‐graft‐polystyrene] (i‐PP‐g‐PS), were prepared by atom‐transfer radical polymerization (ATRP) using a 2‐bromopropionic ester macro‐initiator from functional polypropylene‐containing hydroxyl groups. This kind of functionalized propylene can be obtained by copolymerization of propylene and borane monomer using isospecific MgCl₂‐supported TiCl₄ as catalyst. Both the graft density and the molecular weights of i‐PP‐based graft copolymers were controlled by changing the hydroxyl group contents of functionalized polypropylene and the amount of monomer used in the grafting reaction. The effect of i‐PP‐g‐PS graft copolymer on PP‐PS blends and that of i‐PP‐g‐PMMA graft copolymer on PP‐PMMA blends were studied by scanning electron microscopy. Copyright © 2006 Society of Chemical Industry     

Effect of reaction conditions on grafting ratio and properties of starch nanocrystals‐g‐polystyrene

Starch nanocrystals‐g‐polystyrene (StN‐g‐PS) was synthesized by free radical emulsion copolymerization of starch nanocrystals with styrene. The effect of polymerization conditions on grafting efficiency (GE) and grafting ratio (GR) were investigated. It was found that during graft copolymerization procedure both GE and GR increase with increasing monomer concentration and reaction time. As a result the high GE and high GR can be achieved. The good linear fit of the GR with A_St/A_OH (the absorption strength ratio of aromatic ring peaks and hydroxyl group peaks) confirmed that during graft copolymerization, FTIR spectra can be used as a simple method for determining GR. X‐ray diffraction showed that the crystallinity of StN‐g‐PS decreased slightly with increasing GR. Grafted polystyrene side chains can improve the interface compatibility of starch nanocrystals with the hydrophobic polymer matrix. The mechanical properties of StN‐g‐PS/rubber nanocomposites can be obviously enhanced. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40571.     

“Smart” membrane materials: Preparation and characterization of PVDF‐g‐PNIPAAm graft copolymer

In this research, a smart membrane material of graft copolymer of poly(vinylidene fluoride) with poly(N‐isopropylacrylamide) (PVDF‐g‐PNIPAAm) was synthesized by atom transfer radical polymerization (ATRP) using poly(vinylidene fluoride) (PVDF) as a macroinitiator and direct initiation of the secondary fluorinated site PVDF facilitates grafting the N‐isopropylacrylamide comonomer. The copolymers were characterized by Fourier transform infrared (FTIR), ¹H NMR, gel‐permeation chromatography (GPC), and X‐ray photoelectron spectroscopy (XPS). The temperature‐sensitive membrane was prepared from the PVDF‐g‐PNIPAAm graft copolymers by the phase inversion method. The effects of temperature on the flux of pure water of membrane was investigated. The results showed that alkyl fluorides were successfully applied as ATRP initiators in the synthetic condition and the flux of pure water through the PVDF‐g‐PNIPAAm membrane depended on the temperature change. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 1482–1486, 2007     

Syntheses and biodegradability of benzylated waste pulps and graft copolymers from PBzs and L‐lactic acid

Benzylated waste pulps (PBzs) were synthesized from treated waste pulp (Pulp), and benzyl chloride with phase transfer catalyst (PTC), and graft copolymers (PBz‐g‐LA) were synthesized from PBzs and L‐lactic acid (LA). Thermal properties, solubility, crystallinity, and biodegradability of the obtained PBzs and graft copolymers were investigated. PBzs with the degree of substitution (DS) higher than 1.5 showed T_g and T_m in DSC measurement. All PBz‐g‐LA exhibited no T_m. However, the graft copolymers obtained from lower DS PBzs having no T_g, exhibited T_g. The solubility of PBzs enhanced with increasing DS, and the crystallinity of PBzs reduced with increasing DS because of hydrophobicity and steric effect of benzyl groups. The solubility of graft copolymers was similar to that of original PBzs. Biodegradation tests for PBzs, Pulp, and graft copolymers were performed using cellulase in 0.1 M acetate buffer solution (pH 5.5) at 37°C. All samples showed biodegradability though the biodegradation rate decreased with increasing DS of PBz. In PBz‐g‐LA, the initial biodegradation rate was faster than that of original PBz because of hydrolysis of LA units. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2658–2664, 2004     

Preparation of chelating fabrics by radiation‐induced grafting of itaconic acid and acrylonitrile onto polypropylene nonwoven fabrics and subsequent amination of graft copolymer

A mixture of acrylonitrile (AN) and itaconic acid (IA) was cografted onto polypropylene (PP) nonwoven fabrics by preirradiation method. The effects of graft polymerization conditions such as temperature, reaction time, Mohr's salt concentration, solvent mixture ratio, and comonomer composition on the total grafting yield were investigated. The addition of AN as a comonomer increased the amount of IA that reacted with PP fabrics. An increase in the temperature from 40 to 60°C increased the grafting rate, but the final grafting yield decreased at high temperature. The addition of 0.01 wt % Mohr's salt to the reaction medium leaded to a sharp increase of grafting yield. The accelerative effect of solvent medium on the grating yield was higher in dimethylformamide (DMF) and methanol mixtures, when compared with DMF or methanol. Chelating fabrics was synthesized by subsequent amination of grafted fabric with ethylene diamine (EDA) and phenylhydrazine (PH). The conversion yield reached maximum value at about 90% for 80% PP‐g‐AN‐IA fabrics at 90°C. At same amination conditions, the conversion yield is higher when PP‐g‐AN‐IA fabrics react with EDA compared with PH. FT‐IR data indicate that amine groups were introduced onto PP‐g‐AN‐IA fabric through amide linkage between grafted AN or IA and EDA or PH. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

A new synthetic approach to asymmetric amphiphilic ABA′ block copolymers by ATRP and click reactions

Well‐defined asymmetric amphiphilic ABA′ block copolymers composed of poly(ethylene oxide) monomethylene ether (MPEO) with different molecular weights as A or A′ block and poly(styrene) (PS) as B block were synthesized by the combination of atom transfer radical polymerization (ATRP) and click reactions. First, bromine‐terminated diblock copolymer poly(ethylene oxide) monomethylene ether‐block‐poly(styrene) (MPEO‐PS‐Br) was prepared by ATRP of styrene initiated with macroinitiator MPEO‐Br, which was prepared from the esterification of MPEO and 2‐bromoisobutyryl bromide. Then, the azido‐terminated diblock copolymers MPEO‐PS‐N₃ were prepared through the bromine substitution reaction with sodium azide. Propargyl‐terminated MPEO with a different molecular weight was prepared under the basic condition from propargyl alcohol and p‐toluenesulfonyl‐terminated MPEO, which was prepared through the esterification of MPEO and p‐toluenesulfochloride using pyridine as solvent. Asymmetric amphiphilic ABA′ block copolymers, with a wide range of number–average molecular weights from 1.92 × 10⁴ to 2.47 × 10⁴ and a narrow polydispersity from 1.03 to 1.05, were synthesized via a click reaction of the azido‐terminated diblock copolymers and the propargyl‐terminated MPEO in the presence of CuBr and 1,1,4,7,7‐pentamethyldiethylenetriamine (PMDETA) catalyst system. The structures of these ABA′ block copolymers and corresponding precursors were characterized by NMR, IR, and GPC. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Reactive melt blending of PS‐POSS hybrid nanocomposites

Hybrid nanocomposites of polystyrene (PS) and methacryl phenyl polyhedral oligomeric silsesquioxane (POSS) were synthesized by reactive melt blending in the mixing chamber of a torque rheometer using dicumyl peroxide (DCP) as a free radical initiator and styrene monomer as a chain transfer agent. The effects of mixing intensity and composition on the molecular structure and morphology of the PS‐POSS hybrid nanocomposites were investigated. The degree of POSS hybridization (α_POSS) was found to increase with the POSS content, DCP/POSS ratio, and rotor speed. For the PS‐POSS materials processed in the absence of styrene monomer, an increase in the α_POSS led to a reduction in the molecular weight by PS chain scission, as a consequence of the free radical initiation. On the other hand, the use of styrene monomer as a chain transfer agent reduces the steric hindrance in the hybridization reaction between POSS and PS, enhancing the degree of POSS hybridization and avoiding PS degradation. The PS‐POSS morphology consists of nanoscale POSS clusters and particles and microscale crystalline POSS aggregates. PS‐POSS with higher α_POSS values and lower amounts of nonbound POSS showed improved POSS dispersion, characterized by smaller interfacial thickness (t) and greater Porod inhomogeneity lengths (l_p). The processing‐molecular structure–morphology correlations analyzed in this study allow the POSS dispersion level in the PS‐POSS materials to be tuned by controlling the reactive melt blending through the choice of the processing conditions. These insights are very useful for the development of PS‐POSS materials with optimized performance. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Grafting of poly(3‐hydroxyalkanoate) and linoleic acid onto chitosan

Poly(3‐hydroxy octanoate) (PHO), poly(3‐hydroxy butyrate‐co‐3‐hydroxyvalerate) (PHBV), and linoleic acid were grafted onto chitosan via condensation reactions between carboxylic acids and amine groups. Unreacted PHAs and linoleic acid were eliminated via chloroform extraction and for elimination of unreacted chitosan were used 2 wt % of HOAc solution. The pure chitosan graft copolymers were isolated and then characterized by FTIR, ¹³C‐NMR (in solid state), DSC, and TGA. Microbial polyester percentage grafted onto chitosan backbone was varying from 7 to 52 wt % as a function of molecular weight of PHAs, namely as a function of steric effect. Solubility tests were also performed. Graft copolymers were soluble, partially soluble or insoluble in 2 wt % of HOAc depending on the amount of free primary amine groups on chitosan backbone or degree of grafting percent. Thermal analysis of PHO‐g‐Chitosan graft copolymers indicated that the plastizer effect of PHO by means that they showed melting transitions T_ms at 80, 100, and 113°C or a broad T_ms between 60.5–124.5°C and 75–125°C while pure chitosan showed a sharp T_m at 123°C. In comparison of the solubility and thermal properties of graft copolymers, linoleic acid derivatives of chitosan were used. Thus, the grafting of poly(3‐hydroxyalkanoate) and linoleic acid onto chitosan decrease the thermal stability of chitosan backbone. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103:81–89, 2007     

Thermo‐ and pH‐responsive behaviors of graft copolymer and blend based on chitosan and N‐isopropylacrylamide

Thermo‐ and pH‐sensitive polymers were prepared by graft polymerization or blending of chitosan and poly(N‐isopropylacrylamide) (PNIPAAm). The graft copolymer and blend were characterized by Fourier transform‐infrared, thermogravimetric analysis, X‐ray diffraction measurements, and solubility test. The maximum grafting (%) of chitosan‐g‐(N‐isopropylacrylamide) (NIPAAm) was obtained at the 0.5 M NIPAAm monomer concentration, 2 × 10⁻³ M of ceric ammonium nitrate initiator and 2 h of reaction time at 25°C. The percentage of grafting (%) and the efficiency of grafting (%) gradually increased with the concentration of NIPAAm up to 0.5 M, and then decreased at above 0.5 M NIPAAm concentration due to the increase in the homopolymerization of NIPAAm. Both crosslinked chitosan‐g‐NIPAAm and chitosan/PNIPAAm blend reached an equilibrium state within 30 min. The equilibrium water content of all IPN samples dropped sharply at pH > 6 and temperature > 30°C. In the buffer solutions of various pH and temperature, the chitosan/PNIPAAm blend IPN has a somewhat higher swelling than that of the chitosan‐g‐NIPAAm IPN. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 78: 1381–1391, 2000     

Synthesis and characterization of antimicrobial polylactide via ring‐opening polymerization and click chemistry methods

Novel biodegradable polylactide (PLA) copolymers bearing pendant antimicrobial agent groups were successfully fabricated with a combination of ring‐opening copolymerization and copper(I)‐catalysed azide–alkyne cycloaddition click reaction in a two‐step reaction procedure. First, biodegradable PLA copolymers bearing azido groups were synthesized by the ring‐opening copolymerization of l ‐lactide and 2,2‐ bis(azidomethyl)trimethylene carbonate in the presence of 1‐dodecanol as protic co‐initiator and tin(II) 2‐ethylhexanoate (Sn(Oct)₂) as the catalyst. Then, alkyne functionalized quaternary ammonium salts were attached onto the azido groups of the copolymers via a Huisgen 1,3‐dipolar cycloaddition reaction to give PLA imparting antimicrobial activity. The chemical structure and composition of the copolymers were clearly confirmed using ¹H NMR and Fourier transform infrared spectroscopies and gel permeation chromatography. Thermal phase transition temperatures (T_m and T_g) and the thermal stability of the polymers were investigated by DSC and TGA experiments, respectively. The antimicrobial activity tests were carried out against Gram‐negative (Escherichia coli) and Gram‐positive (Staphylococcus aureus) bacteria by the drop plate method. It was observed that antimicrobial agents are more active in the polymeric form than in the monomeric form. Also, the activity depends on the compositional ratio and the length of the alkyl group on the ammonium salts. © 2018 Society of Chemical Industry     

Study on thermal enhancement mechanism of POSS‐containing hybrid nanocomposites and relationship between thermal properties and their molecular structure

In this study, a series of poly(4‐acetoxystyrene) (PAS)‐octavinyl polyhedral oligomeric silsesquioxane (POSS) blends and the polystyrene (PS)‐octavinyl POSS blends were prepared by the solution‐blending method and characterized with Fourier transform infrared (FTIR), X‐ray diffraction (XRD), transmission electron microscopy (TEM), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA) techniques. The results show that the glass‐transition temperature (T_g) of the PAS‐POSS blends increases at a relatively low POSS content and then decreases at a relatively high POSS content. POSS can effectively improve the thermal stability of the PAS‐POSS blends at low POSS content, and T_g of PAS‐POSS blends decreases with the increase in POSS content at relatively high POSS content. However, the T_g of the PS‐POSS blends persistently decreases even at very low POSS content. T_g change mechanism was investigated in detail by XRD, TEM, and FTIR spectra. The influence mechanism of POSS content and dispersion in composites, and parent polymer structure on thermal properties of the blends was investigated in detail. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Ceric ion‐induced graft copolymerization of acrylamide on cationic guar gum at low temperature

The solution polymerization of acrylamide (AM) on cationic guar gum (CGG) under nitrogen atmosphere using ceric ammonium sulfate (CAS) as the initiator has been realized. The effects of monomer concentration and reaction temperature on grafting conversion, grafting ratio, and grafting efficiency (GE) have been studied. The optimal conditions such as 1.3 mol of AM monomer and 2.2 × 10^?4 mol of CAS have been adopted to produce grafted copolymer (CGG1‐g‐PAM) of high GE of more than 95% at 10°C. The rates of polymerization (R_p) and rates of graft copolymerization (R_g) are enhanced with increase in temperature (<35°C).The R_p is enhanced from 0.43 × 10^?4 mol L^?1 s^?1 for GG‐g‐PAM to 2.53 × 10^?4 mol L^?1 s^?1 for CGG1‐g‐PAM (CGG1, degree of substitute (DS) = 0.007), and R_g from 0.42 × 10^?4 to 2.00 × 10^?4 mol L^?1 s^?1 at 10°C. The apparent activation energy is decreased from 32.27 kJ mol^?1 for GG‐g‐PAM to 8.09 kJ mol^?1 for CGG1‐g‐PAM, which indicates CGG has higher reactivity than unmodified GG ranging from 10 to 50°C. Increase of DS of CGG will lead to slow improvement of the polymerization rates and a hypothetical mechanism is put forward. The grafted copolymer has been characterized by infrared spectroscopy, thermal analysis, and scanning electron microscopy. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 3715–3722, 2007     

Synthesis and characterization of graft copolymer (guar gum–g–N‐vinyl‐2‐pyrrolidone) and investigation of metal ion sorption and swelling behavior

Graft copolymer of N‐vinyl‐2‐pyrrolidone with guar gum was synthesized and its reaction conditions were optimized for better yield using potassium peroxymonosulfate (PMS) and glycolic acid (GA) as a redox initiator. The effect of PMS, GA, hydrogen ions, guar gum, and N‐vinyl‐2‐pyrrolidone (NVP) along with reaction time and temperature were studied by determining the grafting parameters: grafting ratio, efficiency, conversion, add‐on, homopolymer, and rate of grafting. It was observed that the maximum yield occurred at with a time of 120 min at a temperature of 45°C and a guar gum concentration of 0.4 g/L concentration. The graft copolymer was characterized by infrared spectroscopy and thermal analysis. The activation energy for the grafted and ungrafted gum was calculated. It was observed that the graft copolymer was thermally more stable than the pure gum. The swelling and metal ion sorption behavior of guar gum and guar gum‐g‐N‐vinyl‐2‐pyrrolidone also were studied. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 2480–2489, 2006     

Synthesis,characterization, and thermal degradation kinetic of polystyrene‐g‐polycaprolactone

In the present study, it has been demonstrated that polystyrene‐g‐polycaprolactone (PS‐g‐PCL) was successfully prepared by “click chemistry.” For this purpose, first, poly(styrene‐co‐4‐chloromethylstyrene) (P(S‐co‐CMS)) with 4‐chloromethylstyrene content (10%) was synthesized. Second, alkyne‐functionalized polycaprolactone (PCL) was obtained using propargyl alcohol and caprolactone. P(S‐co‐CMS) and PCL were reacted in N,N‐dimethylformamide for 24 h at 25°C to give PS‐g‐PCL. The synthesized polymer was characterized by nuclear magnetic resonance (¹H‐NMR), gel permeation chromatography, Fourier transform infrared spectroscopy and thermogravimetric analysis. The apparent activation energies for thermal degradation of PS‐g‐PCL were obtained by differential (Kissenger) and integral methods (Flynn–Wall–Ozawa, Kissinger–Akahira–Sunose, Tang, Coats–Redfern, Van Krevelen et al.). The decomposition mechanism and pre‐exponential factor were calculated in terms of Coats–Redfern method. The most likely decomposition processes of first and second degradation stages were A_n type and F₃ type, respectively. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Synthesis and characterization of dextrin‐grafted polypropylene

We carried out the graft copolymerization of the water‐soluble natural polymer dextrin onto preirradiated polypropylene (PP) in an aqueous medium using benzoyl peroxide (BPO) as the radical initiator. PP was irradiated by γ rays from a Co⁶⁰ source at a constant dose rate of 3.40 kGy/h to introduce hydroperoxide linkages, which served as the sites for grafting. The graft copolymerization was studied as a function of different reaction parameters, and the maximum percentage grafting (P_g; 55%) of dextrin onto PP was obtained at optimum conditions of [BPO] = 5.165 × 10⁻² mol/L, temperature = 60°C in 120 min with 15 mL of water. Different grafting parameters, such as the percentage apparent grafting, percentage grafting, and percentage true grafting have been evaluated. The graft copolymers were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscopy. Swelling studies were carried out in pure, binary, ternary, and quaternary solvent systems composed of water, ethanol (EtOH), dimethyl sulfoxide (DMSO), and N,N‐dimethylformamide (DMF) at different ratios. The maximum swelling percentage PP‐g‐dextrin (both composite and true graft) was observed in pure DMSO and DMF followed by EtOH and water. Water‐retention studies of PP and PP‐g‐dextrin (both composite and true graft) were investigated at different time periods, temperatures, and pH values. The maximum percentage water retention of PP‐g‐dextrin (composite, 124%) was observed at 8 h and 50°C in a neutral medium (pH 7). © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Characterization of acrylic acid‐grafted PP membranes prepared by plasma‐induced graft polymerization

Acrylic acid (AA)‐g‐polypropylene (PP) membranes were prepared by grafting AA on to a microporous PP membrane via plasma‐induced graft polymerization. The grafting of AA to the PP membrane was investigated using Fourier transform infrared spectroscopy (FTIR). Pore‐filling of the membranes was confirmed by field emission‐scanning electron microscopy (FESEM) and energy dispersing X‐ray (EDX). Ion exchange capacity (IEC), membrane electric resistance, transport number and water content were measured and analyzed as a function of grafting reaction time. The prepared AA‐g‐PP membranes showed moderate electrochemical properties as a cation‐exchange membrane. In particular, membranes with a degree of grafting of 155% showed good electrical properties, with an IEC of 2.77 mmol/g dry membrane, an electric resistance of 0.4 Ω cm² and a transport number of 0.96. Chronopotentiometric measurements indicated that AA‐g‐PP membranes, with a high IEC had a sufficient conducting region in the membrane. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Preparation of thermal‐responsive poly(propylene) membranes grafted with n‐isopropylacrylamide by plasma‐induced polymerization and their water permeation

Poly(propylene) (PP) membrane grafted with poly(N‐isopropylacrylamide) (PNIPAAm), which is known to have a lower critical solution temperature (LCST) at around 32°C, was prepared by the plasma‐induced graft polymerization technique. Graft polymerization of PNIPAAm onto a PP membrane was confirmed by microscopic attenuated total reflection/Fourier transform IR spectroscopy. The grafting yield of PNIPAAm increased with the concentration of N‐isopropylacrylamide monomer and the reaction time of graft polymerization. The average pore size of the PP membrane also affected the grafting yield. From the field emission scanning electron microscopy (FE‐SEM) measurement, we observed a morphological change in the PP‐g‐PNIPAAm membrane under wet conditions at 25°C below LCST. The permeability of water through the PP‐g‐PNIPAAm membrane was controlled by temperature. The PP‐g‐PNIPAAm membrane (PN05 and PN10) exhibited higher water permeability (L_p) than the original PP substrate membrane below LCST. As the temperature increased to above LCST, L_p gradually decreased. In addition, the graft yield of PNIPAAm and the average pore size of the PP substrate influenced water permeability. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1168–1177, 2002; DOI 10.1002/app.10410     

Effect of annealing on poly(urethane‐siloxane) copolymers

The N‐substituted polyaniline (PANi) was synthesized by incorporation of bromine‐terminated polystyrene (PS‐Br) onto the emeraldine form of polyaniline. End brominated polystyrene was synthesized by atom transfer radical polymerization (ATRP) technique and then deprotonated polyaniline was reacted with PS‐Br to prepare PS‐grafted PANi (PS‐g‐PANi) copolymer through N‐grafting reaction. The degree of N‐grafting can be controlled by adjusting the molar feed ratio of PS‐Br to the number of repeat units of PANi. The microstructure and compositions of the PS‐g‐PANi copolymers with different degrees of N‐substitution were characterized by FT‐IR, elemental analysis, differential scanning calorimetry (DSC), and scanning electron microscopy (SEM). The cyclicvoltammetry shows that the electroactivity of N‐substituted PANi is strongly dependent on the degree of N‐grafting. The solubility of PS‐g‐PANi copolymers in common organic solvents such as tetrahydrofuran and chloroform was improved by increasing the degree of N‐grafting, and also the samples are partially soluble in xylene. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Synthesis and photo‐ and biodegradabilities of poly[(hydroxybutyrate‐co‐hydroxyvalerate)‐ g‐phenyl vinyl ketone]

The graft copolymer, poly[(hydroxybutyrate‐co‐hydroxyvalerate)‐g‐phenyl vinyl ketone] [P(HBV‐g‐PVK)], was synthesized by graft polymerization of phenyl vinyl ketone (PVK) onto poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) under nitrogen atmosphere using benzoyl peroxide. The structure of P(HBV‐g‐PVK) was identified by Fourier transform IR and ¹H‐NMR spectra. The effects of weight ratio of PVK to PHBV in feed, initiator concentration, reaction time, and reaction temperature on the grafting ratio and grafting efficiency were investigated. The thermal decomposition temperature of P(HBV‐g‐PVK) was 272°C. The tensile strengths of P(HBV‐g‐PVK) after photo‐ or biodegradation were significantly decreased due to degradation by UV irradiation or Aspergillus niger. The value of color difference (ΔE) of P(HBV‐g‐PVK) was greater than that of PHBV. The film surfaces of P(HBV‐g‐PVK) treated with UV irradiation and Aspergillus niger showed many pits as compared with the untreated P(HBV‐g‐PVK). It has been found that the photo‐ and biodegradabilities of P(HBV‐g‐PVK) was excellent. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 1432–1439, 1999