熔体处理工艺对6005A铝合金铸锭质量的影响

针对6005A铝合金铸锭的熔铸工艺,采用低倍组织分析、拉伸测试、金相分析等手段对不同熔体停留时间生产的铸锭进行分析,研究了熔体处理工艺对铝合金显微组织及力学性能的影响。结果表明:熔体停留时间对铸锭的晶粒尺寸、疏松等级、晶粒圆整度、力学性能均有不同程度的影响。当熔体停留时间≤5 h,铸锭晶粒尺寸随熔体停留时间的延长而缓慢增大,晶粒圆整度、力学性能等基本维持不变;当熔体停留时间超过5 h时,晶粒尺寸急剧增大,晶粒圆整度、力学性能等显著降低。熔炼过程中控制熔体停留时间≤5h,可降低由于熔体停留所带来的不利影响。     

铝合金车轮铸造用A356合金的熔体处理

本文详细讨论了铝合金车轮用A356合金的精炼除气、晶粒细经及变质处理的机理，并介绍了本公司所采用的熔体处理方法及实际效果。     

流变压铸工艺参数对半固态A356铝合金充填性的影响

研究了半固态A356铝合金浆料的成形温度、压射比压和压射冲头速度对半固态A356铝合金流变压铸充填性的影响.实验结果表明:较高的半固态A356铝合金浆料的成形温度有利于获得良好的充填性.压射比压和压射冲头速度对半固态A356铝合金浆料充填性也具有较大的影响.在本实验条件下,压射冲头速度越大或压射比压越大,充填性越好.试片的壁厚对半固态A356铝合金浆料的充填性影响较大,试片壁厚越大,越容易充填.此外,采用低过热度浇注和弱电磁搅拌技术制备的A356铝合金浆料和流变压铸试片的组织分布很均匀,有利于获得优质的半固态压铸件.     

浇注温度对合金熔体冷却规律和半固态组织的影响

介绍了一种实验室自主研发的轻合金半固态浆料制备设备——锥桶式流变成形机(TBR),该设备利用刻有凸纹和沟槽的内、外锥桶的相对转动,使合金熔体在凝固过程中受到剧烈的剪切搅拌,从而获得合金半固态浆料.对TBR工艺的传热模型进行了推导,以A356为实验材料得出制备的A356铝合金半固态浆料温度与浇注温度的关系式,同时分析了不同浇注温度下合金熔体的冷却规律和获得的半固态组织形貌.结果表明,适当降低A356合金熔体的浇注温度可以延长初生固相受到的剪切时间和增加剪切次数,从而获得细小、均匀的半固态组织.当浇注温度为640℃时,初生固相平均晶粒尺寸为68μm,形状因子为0.82.     

半固态A356合金重熔加热时初生相的组织演变

利用低过热度浇注技术制备了半固态A356铝合金坯料,研究了半固态温度区间重熔加热时半固态A356铝合金坯料的初生相形貌的转变过程.结果表明,在半固态两相区保温,半固态A356合金的初生相逐渐团球化,该过程随保温温度的升高而加快.半固态A356铝合金晶粒的圆度与保温温度和保温时间的关系不大,但晶粒的尺寸随着保温温度和保温时间的增加而增大.半固态A356合金试样重熔加热最佳工艺制度为583℃下保温30min,其晶粒平均等积圆直径为80μm,晶粒平均圆度为0.83.     

带有晶粒细化剂的铝合金半固态铸造工艺

美国专利US7025113本方法是把钛基晶粒细化剂混合入亚共晶铝硅合金半固态浆料中,用以细化半固态浆料中的初晶铝。所涉及的专利工艺是把钛硼合金与亚共晶铝硅合金液混合,在半固态铸造中控制初晶铝相的形态尺寸和分布。本发明能使晶粒细化技术很好地应用于铝硅亚共晶合金的半固态铸造。     

熔体过热处理对K465合金晶粒和碳化物的影响

 研究了用CaO坩埚真空感应熔炼、再经不同的熔体过热处理后,K465铸造高温合金晶粒尺寸的变化以及合金中碳化物的形貌和分布特征。结果表明：在浇注温度相同的条件下,未经熔体过热处理时,合金晶粒为普通等轴晶,碳化物为块状MC碳化物;熔体过热处理温度在1 600~1 750 ℃之间时,晶粒尺寸随处理温度升高而长大,〖JP2〗初生MC碳化物从块状转变为汉字草书体群团形式,而且呈现出温度升高,MC碳化物变细、群团变小的趋势;过热处理温度超过1 750 ℃时,草书体群团MC碳化物随温度升高晶粒尺寸不断减小并呈细小点状均匀分布。     

加热制度对氮微合金化HRB500E方坯晶粒度的影响

在加热温度1 080~1 250℃及保温时间5~30 min的条件下,研究了加热制度对氮微合金化HRB500E方坯奥氏体晶粒平均尺寸的影响。结果表明:在试验条件范围内,试验方坯的奥氏体晶粒尺寸随加热温度的升高、均热时间的延长而变大;当控制保温时间在15~25 min及加热温度1 080~1 200℃时,奥氏体晶粒长大速度较慢,晶粒平均尺寸比较细小、均匀;通过对试验数据的拟合,得到了在1 200℃以下方坯加热温度与原始奥氏体晶粒尺寸的关系模型。     

熔铸工艺对6063铝建筑型材质量的影响

从合金成分、熔铸工艺，铸锭的均匀化制度以及如何提高型材表面光洁试行等方面，论述了６０６３铝合金建筑型材质量的因素及其生产过程的质量控制方法。     

加热温度对钛微合金化钢奥氏体晶粒长大的影响

通过将钛微合金化钢在箱式电炉中加热至850~1 250℃保温30 min,观察其奥氏体晶粒组织及Ti的析出粒子分布情况,研究钛微合金化钢奥氏体晶粒长大行为及Ti的固溶规律。结果表明:随着加热温度的升高,试验钢存在两个奥氏体晶粒粗化温度,分别为1 050℃和1 250℃,与Ti两种析出粒子的固溶温度相对应,但数值比固溶温度低。分析奥氏体晶粒两个阶段的长大过程发现,随着TiC析出粒子的溶解,晶粒长大激活能从265.6 k J/mol降低至239.8 k J/mol。     

电磁搅拌方式和稀土对半固态A356合金凝固组织的影响

通过双向电磁搅拌和稀土元素制备了半固态A356铝合金浆料.利用OM、XRD和SEM研究磁场频率30 Hz搅拌12 s时,无稀土、单一稀土0.5 %Ce（质量分数,下同）、混合稀土0.3 %La+0.2 %Yb以及电磁搅拌方式(单向连续搅拌、双向连续搅拌、双向间歇搅拌)对初生相形貌的影响.结果表明:在控制稀土等同总百分含量下,混合稀土对凝固组织优化程度大于单一稀土和无稀土,初生相平均等积圆直径和形状因子达到36.4 μm、0.82;在此基础上进一步对熔体施加不同搅拌方式处理,试验发现双向连续搅拌作用液态熔体形成了强烈的紊流和惯性冲击,加快了凝固体系的质量传输热量传递,晶粒尺寸和形貌相较于单向连续搅拌、双向间歇搅拌更加细小圆整.      

Effect of melt spinning on grain size and texture in Ni-Mo alloys

Chill block melt spun ribbons of nickel molybdenum alloys with molybdenum contents of 8 to 41.8 wt pct Mo have been examined for their microstructure and texture dependence on processing conditions. Linear features observed in grains solidified with a planar liquid-solid interface at the quench side of the ribbons have been identified to be due to the twins on (111),, plane formed during solidification. Grain size variation with the wheel surface speed and the alloy composition has been studied. Crystallographic texture on quench side and free surface side of the ribbons has been investigated.     

Effects of vibration on the grain morphology

Pairs of halogen lamps were heated simultaneously at various rates of temperature increase through the recrystallization temperature and were held for five hours at 120 volts. One lamp in each of 20 pairs was vibrated during lightup. Examination of the grain boundaries of the filaments revealed that 63 pct of the boundaries in the vibrated lamps were “transverse.” In the lamps not vibrated, 52 pct of the boundaries were “transverse.” The greater number of “trans- verse” grain boundaries in the vibrated lamps is attributed to grain boundary sliding, which generates additional energy to allow the grain boundary to overcome the restraint to migration provided by the strings of potassium bubbles in the lamp wire. Formerly with GE Corporate Research and Formerly with GE Corporate Research and Formerly with the Technology Division, GE Lighting, Nela Park, Formerly with the Technology Division, GE Lighting, Nela Park,     

回火温度对Q960钢小角度晶界的影响

设计了一种低合金高强度的Q960工程机械用钢.在同种成分、同种轧制和淬火工艺下,研究回火温度对Q960钢小角度晶界的影响机理.经分析得出,随着回火温度的升高,小角度晶界的频率逐渐降低且实验钢的抗拉强度和屈服强度也相应地降低,而屈强比逐渐升高.不同回火温度下小角度晶界频率的峰值均出现在取向差5°附近,即取向差较小.取向差小使得小角度晶界比较稳定,原子迁移率小.通过计算键级积分(BOI)得出,B元素对Q960钢的小角度晶界有加强作用.     

Effect of temperature and deformation histories on grain coarsening in medium carbon steel

Abstract

Hot rolling of medium carbon steel bars using a prototype mill and numerical analyses were carried out to examine quantitatively the effect of temperature and strain throughout rolling on the final grain size of the product. Cross-sections of the rolled bars were subjected to optical microscopy to investigate the effect of the instantaneous decrease in temperature owing to contact with the roll groove on grain coarsening in the vicinity of the bar surface. By analysing the grain size after rolling, the temperature history throughout rolling, and the equivalent plastic strain after rolling, it was found that the instantaneous decrease in temperature owing to contact did not affect grain coarsening unless the final values of the temperature and strain fell within a narrow band of values meeting the criteria for grain coarsening. Referring to both the present results and the authors' previous studies, criteria have been established for the prevention of grain coarsening in steel bar sizing operations.     

Bi对低温取向硅钢高温退火过程组织和织构的影响

以含Bi和不含Bi两种成分低温取向硅钢进行高温退火中断实验,借助磁测仪（MPG 200D）进行磁性能测量,借助金相显微镜观察晶粒尺寸,利用X射线衍射（XRD）对高温退火连续升温过程中织构进行研究分析。实验结果表明,添加Bi元素后,初次晶粒尺寸减小,二次再结晶晶粒尺寸增加至20~60 mm,成品磁性能更优。Bi加入后二次再结晶开始温度明显提高,含Bi试样和不含Bi试样发生晶粒异常长大的温度范围分别是1 080~1 100 ℃和1 060~1 080 ℃。织构分析结果显示,随着高温退火温度提高,{111}和{100}面织构逐渐减弱,{110}面织构和Goss织构逐渐增强,含Bi和不含Bi试样的高斯织构转变温度分别为1 100 ℃和1 080 ℃,随后高斯织构密度和体积百分比逐步增加,最终含Bi试样的高斯织构密度和体积百分比均高于不含Bi试样。