垂直结构GaN基LED用Ni/Ag反射镜电极

Ni/Ag/Ti/Au金属系反射镜电极广泛用于GaN基垂直结构发光二极管(LED)的传统制造工艺.这种电极需要进行高温长时间整体退火才能获得高质量的欧姆接触,但对电极的反射率和器件性能影响较大.介绍了一种新工艺方法,该方法将电极分解为接触层和反射层,降低反射层经历的退火温度和时间,获得了拥有良好的欧姆接触特性和高反射率的反射镜电极,解决了传统电极光学性能和电学性能相互制约的问题.首先生长极薄的Ni/Ag作为接触层,对接触层进行高温长时间退火后再生长厚层Ag作为反射层,之后再进行一次低温退火.使得对反射起主要作用的反射层免于高温长时间退火,相较于传统Ni/Ag/Ti/Au电极,该方法在获得更优良的欧姆接触的同时,提升了电极的反射率.在氧气氛围下进行500℃接触层退火3 min,400℃整体退火1 min后,电极的比接触电阻率为1.7×l0-3Ω·cm2,同时在450 nm处反射率为93％.     

p型GaN上Pd/NiO/Al/Ni反射电极欧姆接触的热稳定性研究

研究了p型GaN上Pd/NiO/Al/Ni反射电极欧姆接触的比接触电阻率、热稳定性,以及光学反射率。与传统Pd/Al/Ni电极相比,Pd/NiO/Al/Ni电极的欧姆接触在氮气环境中经300℃下热处理10min后,仍保持低比接触电阻率(小于5×10-4Ω·cm2)和高反射率(大于80%@365nm)。研究获得的优化Pd/NiO层厚度为1nm/2nm,此时的Pd/NiO/Al/Ni反射电极既能形成良好的欧姆接触,拥有低比接触电阻率,又能减少对紫外光的吸收,保持高反射率。研究表明适当的NiO层厚度能够有效地防止热处理过程中上层Al金属向p-GaN表面层的渗入,对于制备高质量的Al基反射电极至关重要。     

n型4H-SiC上Ni/Pt和Ti/Pt欧姆接触(英文)

研究了Ni/Pt和Ti/Pt金属在n型4H-SiC上的欧姆接触。在1 020℃退火后,Ni/Pt与n型4H-SiC欧姆接触的比接触电阻为2.2×10-6Ω·cm2。Ti/Pt与n型4H-SiC欧姆接触的比接触电阻为5.4×10-6Ω·cm2,退火温度为1 050℃。虽然Ni的功函数比Ti的功函数高,但是Ni比Ti更容易与n型4H-SiC形成欧姆接触。使用能谱分析仪(EDX)分析了Ni/Pt和Ti/Pt金属与4HSiC接触面的元素,观察到C原子相对于Pt原子的原子数分数随退火温度的变化而不同。实验验证了在n型4H-SiC中退火导致的碳空位起施主作用是有利于欧姆接触形成的主要原因。     

两步合金法制作p-GaN高反电极

利用两步合金法获得了能与p-GaN形成良好欧姆接触的高反射电极.电极的构成采用透明电极 高反射金属方案,厚的Ag层或Al层覆盖在合金后的Ni/Au上以提高电极的反射率,以Pt和Au作为覆盖层,可有效地防止Ag的氧化和团聚,短时间的热处理有助于Ag基电极反射率的提高.可靠性测试表明Ag基电极的稳定性较好,对于Al基电极,热处理后反射镜上出现暗斑,导致其反射率的下降.最终获得了波长在460nm处反射率为74%的Ag基高反射电极.     

p型GaAs欧姆接触性能研究

为了研究半导体光电器件p-GaAs欧姆接触的特性,利用磁控溅射在p-GaAs上生长Ti厚度在10~50 nm范围、Pt厚度在30~60 nm范围的Ti/Pt/200 nm Au电极结构。利用传输线模型测量了具有不同的Ti、Pt厚度的Ti/Pt/200 nm Au电极结构接触电阻率,研究了退火参数对欧姆接触性能的影响,同时分析了过高温度导致电极金属从边缘向内部皱缩的机理。结果表明,Ti厚度为30 nm左右时接触电阻率最低,接触电阻率随着Pt厚度的增加而增加;欧姆接触质量对退火温度更敏感,退火温度达到510 ℃时电极金属从边缘向内部皱缩。采用40 nm Ti/40 nm Pt/200 nm Au作为半导体光电器件p-GaAs电极结构,合金条件为420 ℃,30 s可以形成更好的欧姆接触。     

Ni/Au与p-GaN的比接触电阻率测量

通过采用环形传输线方法(CILM),电流-电压(I-V)曲线、表面形貌等方法,研究不同的Ni/Au厚度比和空气气氛下合金退火温度对p型氮化镓欧姆接触特性造成的影响。根据Ni/Au与p型氮化镓欧姆接触的形成机制,采用合适的Ni/Au厚度比及退火温度,得到比接触电阻率(ρc)为1.09×10-5Ω.cm2的Ni/Au-p-GaN电极,并分析了Ni在退火过程中对形成良好的欧姆接触中所起到的作用。     

二次退火对Au/Ni/Au/Ni/p-AlGaN欧姆接触组织结构的影响

在蓝宝石衬底上,利用金属-有机物化学气相沉 积(MOCVD)方法制备p-i-n结构AlGaN基体,采 用常规工艺制作台面型紫外探测器。电子束蒸发蒸镀Ni/Au/Ni/Au(20nm/20 nm)结构制备 p 电极。经空气中550℃/3min一次退火和N₂气氛中750℃/30s二次退火后得到欧姆接触。利用高分 辨透射电镜(HRTEM)和能谱(EDS)研究不同退火条件下p 电极接触的组织结构演变。结果 表明:一 次退火p电极金属层出现明显扩散,但仍维持初始的分层状态,金属/半导体接触界面产生 厚约4nm 的非晶层;二次退火后,金属电极分层现象和界面非晶层消失。金/半界面结构表现为半共 格关系,界面结 构有序性提高。Ni向外扩散,Au向内扩散,Ga扩散至金属电极,造成界面附近金属层富 集Au、Ga元素,导致p电极欧姆接触的形成。     

重掺杂p型SiC晶片Ni/Al欧姆接触特性

系统研究了Al和Ni/Al两种金属体系在重掺杂p型SiC晶片上的欧姆接触特性和电学性质。利用X射线衍射、扫描电子显微镜和综合物性测量系统对这两种电极表面的微观结构和样品的电学性质进行了表征。结果表明：在真空环境下经过800℃退火后Al电极可呈现出欧姆接触行为,其比接触电阻率为1.98×10^-3Ω·cm²,退火处理后Al电极与SiC在接触界面形成化合物Al₄C₃,有助于提高接触界面稳定性。在Ni/Al复合体系中,当Ni金属层厚度为50 nm时,其比接触电阻率显著降低至4.013×10^-4Ω·cm²。退火后Ni与SiC在接触界面生成的Ni₂Si有利于欧姆接触的形成和降低比接触电阻率。研究结果可为开发液相法生长的p型SiC晶片电子器件提供参考。     

AlGaN紫外探测器p电极的Ni/Au/Ni/Au欧姆接触结构研究

研究了AlGaN半导体p电极的Ni/Au/Ni/Au接触结构的性能和组织结构。退火 前,p电极接触具有明显的整流特性。经空气中550℃/3 min一 次退火和N2气氛中750℃/30 s二 次退火后,电极呈现出了良好的欧姆接触。采用扫描电镜(Scanning Electron Microscope, SEM)、透射 电镜(Transmission Electron Microscope, TEM)、能量分散谱仪(Energy Dispersive Spectrometer, EDS)和X射 线光电子能谱(X-ray Photoelectron Spectroscopy, XPS)观察了电极退火后金--半界面微结构的演化过程。结果表明,完全退火后的p电极 界面及金属层出现了明显的互扩散和界面反应现象;金--半界面上形成了存在良好共格/半共格关系的外延结 构。初始沉积的金属电极分层现象消失,形成了单一的电极结构。Ni向外扩散并与O发生反应,Au扩散至p-GaN 表面。在金-半接触界面上,Ga扩散至金属电极,造成界面附近的金属层中富集Au和Ga元素;Au和Ni明显扩散 至半导体表层,在金-半界面附近形成了Au、Ga和Ni富集现象。这些现象应该对于降低势垒高度和形成欧姆接触具有重要作 用。     

Ti/Al/Ni/Au金属体系在N-polar GaN上的欧姆接触特性

利用金属有机化合物化学气相淀积(MOCVD)在SiC衬底上外延生长了N-polar GaN材料,采用传输线模型(TLM)分析了Ti/Al/Ni/Au金属体系在N-polar GaN上的欧姆接触特性.结果表明,Ti/Al/Ni/Au (20/60/10/50 nm)在N-polar GaN上可形成比接触电阻率为2.2×10-3Ω·cm2的非合金欧姆接触,当退火温度升至200℃,比接触电阻率降为1.44×10-3 Ω·cm2,随着退火温度的进一步上升,Ga原子外逸导致欧姆接触退化为肖特基接触.     

Au/BIT/PZT/BIT/p-Si(100)存储器

利用准分子激光原位淀积方法制备了BIT／PZT／BIT，PZT／BIT和BIT层状铁电薄膜，获得了电流密度－电压（I－V）回线和极化强度P－V电滞回线。在这三种结构中，Au/BIT/PZT/BIT/p-Si(100）结构的界面电位降、内建电压及频率效应是最小的。在电压转变电VT、饱和极化强度Ps及矫顽场Vc之间有三种关系，他们与I－V回线及P－V回线的关系相匹配，这种匹配关系使得以I－V回线操作的存储器将能够非挥发和非破坏读出及具有保持力。     

TiO2/n-Si/p-Si及n-PS/p-PS/Si的光伏特性

在抛光的p型单晶硅上通过扩散工艺制备pn结,采用此种硅片利用阳极腐蚀法制备多孔硅(PS).用磁控溅射镀膜机在有pn结的单晶硅表面镀上一层TiO2纳米结构薄膜,并用表面光电压谱(SPS)研究了n-PS/p-PS/Si和TiO2/n-Si/p-Si的表面光伏特性.结果表明TiO2/n-Si/p-Si和n-PS/p-PS/Si的光伏效应比n-Si/p-Si在不同程度上有所提高.在300～600 ℃热处理温度范围内TiO2/n-Si/p-Si的光伏效应随温度的升高而增强,600～800 ℃范围内随温度的升高而降低.     

A compact microstrip fed dual polarised multiband antenna for IEEE 802.11 a/b/g/n/ac/ax applications

A compact microstrip fed dual polarised multiband monopole antenna for IEEE 802.11 a/b/g/n/ac/ax communication based applications is presented. The antenna is circularly polarised in IEEE 802.11 b/g bands while linearly polarised in IEEE 802.11 a/n/ac/ax bands. The asymmetric U-shaped slot in the ground plane of proposed antenna is used to introduce the necessary 90° phase shift between two orthogonal electric field vectors necessary for circular polarisation. The Ω-shaped slot on patch is used to introduce a band elimination notch between the usable frequency bands. The radiation characteristics of the proposed antenna (at 2.4 GHz) can be changed from left hand circular polarisation (LHCP) to right hand circular polarisation (RHCP) by replacing asymmetric U-shaped slot with its mirror image on the opposite side of ground plane. The proposed antenna has a wide impedance bandwidth of 110.8% and can also be used in various applications including worldwide interoperability for microwave access (WiMAX) and IEEE 802.11p standard based V2V (Vehicle to Vehicle) communication.     

难熔金属与n-GaAs的欧姆接触特性

用磁控溅射系统和快速合金化法制备了Mo/W/Ti/Au多层金属和n-GaAs材料的欧姆接触,在溅射金属层之前分别用HCl溶液和(NH4)2S溶液对n-GaAs材料的表面进行处理．用传输线法对比接触电阻进行了测试,并利用俄歇电子能谱（AES）、X射线衍射图谱（XRD）对接触的微观结构进行了分析．结果表明,用(NH4)2S溶液对n-GaAs材料表面进行处理后,比接触电阻最小;在700℃快速合金化后获得最低的比接触电阻,约为4.5×10－6Ω·cm2．这是由于(NH4)2S溶液钝化处理后降低了GaAs的表面态密度,消除了费米能级钉扎效应,从而改善了难熔金属与GaAs的接触特性．     

M/M/C/m/m排队系统模型的飞机战伤抢修研究

抢修力量配置是飞机战伤抢修复杂系统的核心因素.损伤飞机在抢修系统中的停留时间是进行抢修力量配置的关键指标.首先用排队论的观点,从飞机战伤抢修系统的特性出发,结合对系统榆入过程的分析,得出抢修力量预测模型即M/M/C/m/m排队模型.然后通过对该排队系统状态转移方程求解,计算出损伤飞机在系统停留时间.最后通过实例分析,得出对战伤抢修力量配置的方法.     

Ti/Al/Ti/Au与AlGaN欧姆接触特性

研究了溅射 Ti/ Al/ Ti/ Au四层复合金属与 Al Ga N / Ga N的欧姆接触特性 ,并就环境温度对欧姆接触特性的影响进行了分析研究 .试验证实 :溅射的 Ti/ Al/ Ti/ Au与载流子浓度为 2 .2 4× 10 1 8cm- 3的 Al Ga N之间在室温下无需退火即可形成欧姆接触 .随快速退火温度的升高接触电阻降低 .快速退火时间 30 s已可实现该温度下最佳欧姆接触 .当工作温度不高于 30 0℃时接触电阻几乎不受温度的影响     

Transient analysis of the MMPP/G/1/K queue

In this paper the transient behaviour of a finite-buffer queue fed by the Markov-modulated Poisson process is studied. The results include formulas for the transforms of transient queue size distribution, transient full buffer probability and transient delay (workload). Computational issues are discussed and numerical samples presented.This material is based upon work supported by the Polish Ministry of Scientific Research and Information Technology under Grant No. 3 T11C 014 26.     

Microstructural analysis of a Au/Pt/Pd/Zn ohmic contact to an AlGaAs/GaAs heterojunction bipolar transistor

Gold-based ohmic contacts, incorporating Pt, Pd, and Zn layers, to AIGaAs/GaAs heterojunction bipolar transistors (HBTs) have been characterized using transmission electron microscopy (TEM). The metallization was deposited onto a 30 nm graded emitter layer of n-type Al_xGa_1−xAs, which was on a 30 nm emitter layer of n-type Al_0.3Ga_0.7As, with the aim of contacting the underlying 80 nm thick graded base layer of p-type Al_xGa_1−xAs. Metal layers were deposited sequentially using electron beam evaporation and the resultant metallizations were annealed at temperatures ranging from 250-500°C for up to several minutes. A minimum contact resistance of ≈8.5 × 10⁻⁷ Ω-cm² was achieved, which corresponded to the decomposition of ternary phases at the metallization/semiconductor interface, to binary phases, i.e., PdGa and PtAs₂. Long term stability tests were done on the optimum contacts. Anneals at 270°C for up to four weeks in duration produced virtually no change in microstructure, with the exception of some outward diffusion of Ga and As.     

433/868/915MHz FSK/ASK/OOK无线收发器RF2945

RF2945是RFMicroDevices公司生产的一种单片射频收发芯片,利用该芯片可在433/868/915MHzISM频段进行FSK/ASK/OOK调制和解调。由于RF2945射频收发芯片内含射频发射、射频接收、PLL合成和FSK调制/解调等电路,因而可用于接收和发送数字信号。文中介绍了RF2945的结构原理和主要特性 ,同时给出了RF2945收发器的典型应用电路和使用注意事项     

多卫星系统组合导航的可用性分析

在航空应用中,多卫星导航系统组合导航是未来的发展趋势,可用性是航空应用的主要性能要求之一。但是在截止角增大时,GPS单系统的可用性却达不到航空性能标准。针对该问题,对GPS/Galileo/BD组合系统在中国境内的可用性进行仿真分析,与GPS单系统相比,组合系统的可用性相对单系统有所提高,且截止角较大时,仍能达到可用性要求。